CN106045313A - Porcelain white glass - Google Patents
Porcelain white glass Download PDFInfo
- Publication number
- CN106045313A CN106045313A CN201610359768.7A CN201610359768A CN106045313A CN 106045313 A CN106045313 A CN 106045313A CN 201610359768 A CN201610359768 A CN 201610359768A CN 106045313 A CN106045313 A CN 106045313A
- Authority
- CN
- China
- Prior art keywords
- parts
- white glass
- porcelain white
- sodium sulfate
- porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses porcelain white glass which is composed of, by weight, 15-25 parts of silica, 10-35 parts of cullet, 10-20 parts of calcium oxide, 30-45 parts of quartz sand, 2-4 parts of magnesium oxide, 5-12 parts of alumina, 5-10 parts of potassium nitrate, 2-8 parts of sodium sulfate, 2-5 parts of barium chloride, 2-5 parts of fluorite, 1-6 parts of anhydrous sodium sulfate, 0.1-0.3 part of selenium powder, 0.1-0.5 part of clarifying agent and 1-4 parts of stabilizer. The porcelain white glass is low in melting temperature, so that energy consumption is lowered, raw materials are saved, resource waste is reduced, and production cost is lowered; the porcelain white glass has the advantages of uniform granularity distribution, zero environment pollution and long service life. Products produced by using the porcelain white glass are good in appearance effect, and the porcelain white glass is suitable for being used to make craftwork products and cosmetic bottles.
Description
Technical field
The present invention relates to field of glass production technology, in particular to a kind of porcelain white glass.
Background technology
Along with the development of science and technology, need to use the place of glass to become variation, glass properties index has been had tighter
Lattice and various requirement, constantly improve the performance of glass, be the urgent needs of economy and social development.Nowadays, porcelain white glass
The glass porcelain made increasingly is liked by people, but, the inferior quality of existing porcelain white glass, uniformity is bad,
The product produced and porcelain have bigger difference.Accordingly, it would be desirable to change original formula, meet the demand in market.
Summary of the invention
Present invention aim at solving the problems referred to above, it is provided that a kind of porcelain white glass.
For achieving the above object, the invention provides a kind of porcelain white glass, by forming according to the raw material of weight portion as follows: two
Silicon oxide 15 ~ 25 parts, cullet 10 ~ 35 parts, calcium oxide 10 ~ 20 parts, quartz sand 30 ~ 45 parts, magnesium oxide 2 ~ 4 parts, aluminium oxide 5 ~
12 parts, potassium nitrate 5 ~ 10 parts, 2 ~ 8 parts of sodium sulfate, barium chloride 2 ~ 5 parts, 2 ~ 5 parts of fluorite, Matrii Sulfas Exsiccatus 1 ~ 6 part, selenium powder 0.1 ~ 0.3
Part, clarifier 0.1 ~ 0.5 part and stabilizer 1 ~ 4 part.
Described porcelain white glass, by forming according to the raw material of weight portion as follows: silica 18 ~ 22 parts, cullet 15 ~ 30
Part, calcium oxide 14 ~ 18 parts, quartz sand 34 ~ 40 parts, magnesium oxide 2.2 ~ 3 parts, aluminium oxide 6 ~ 9 parts, potassium nitrate 7 ~ 8.6 parts, sodium sulfate
4 ~ 7 parts, barium chloride 3 ~ 4 parts, 3 ~ 4.3 parts of fluorite, Matrii Sulfas Exsiccatus 2 ~ 5 parts, selenium powder 0.1 ~ 0.2 part, clarifier 0.2 ~ 0.4 part and stable
Agent 2 ~ 4 parts.
Described porcelain white glass, by forming according to the raw material of weight portion as follows: silicon dioxide 20 parts, cullet 25 parts, oxidation
Calcium 15 parts, quartz sand 38 parts, magnesium oxide 2.7 parts, aluminium oxide 8 parts, potassium nitrate 8.2 parts, 5 parts of sodium sulfate, barium chloride 3.6 parts, firefly
3.3 parts of stone, Matrii Sulfas Exsiccatus 3 parts, selenium powder 0.1 part, clarifier 0.2 part and stabilizer 2.4 parts.
Beneficial effects of the present invention: this kind of porcelain white glass fusion temperature is relatively low, while reducing energy consumption, has saved former material
Material, decreases the wasting of resources, reduces production cost, have even particle size distribution, environmentally safe, the spy of length in service life
Point, the appearance of the glass of production is good, it is adaptable to processing technology goods and bottle for cosmetics.
Detailed description of the invention
The present invention takes techniques below scheme to realize: this kind of porcelain white glass, by forming according to the raw material of weight portion as follows:
Silica 15 ~ 25 parts, cullet 10 ~ 35 parts, calcium oxide 10 ~ 20 parts, quartz sand 30 ~ 45 parts, magnesium oxide 2 ~ 4 parts, aluminium oxide 5
~ 12 parts, potassium nitrate 5 ~ 10 parts, 2 ~ 8 parts of sodium sulfate, barium chloride 2 ~ 5 parts, 2 ~ 5 parts of fluorite, Matrii Sulfas Exsiccatus 1 ~ 6 part, selenium powder 0.1 ~ 0.3
Part, clarifier 0.1 ~ 0.5 part and stabilizer 1 ~ 4 part.
As the preferred version of the present invention, porcelain white glass is by forming according to the raw material of weight portion as follows: silica 18 ~ 22
Part, cullet 15 ~ 30 parts, calcium oxide 14 ~ 18 parts, quartz sand 34 ~ 40 parts, magnesium oxide 2.2 ~ 3 parts, aluminium oxide 6 ~ 9 parts, potassium nitrate
7 ~ 8.6 parts, 4 ~ 7 parts of sodium sulfate, barium chloride 3 ~ 4 parts, 3 ~ 4.3 parts of fluorite, Matrii Sulfas Exsiccatus 2 ~ 5 parts, selenium powder 0.1 ~ 0.2 part, clarifier
0.2 ~ 0.4 part and stabilizer 2 ~ 4 parts.
As the preferred version of the present invention, porcelain white glass is by forming according to the raw material of weight portion as follows: silicon dioxide 20 parts,
Cullet 25 parts, calcium oxide 15 parts, quartz sand 38 parts, magnesium oxide 2.7 parts, aluminium oxide 8 parts, potassium nitrate 8.2 parts, 5 parts of sodium sulfate,
Barium chloride 3.6 parts, 3.3 parts of fluorite, Matrii Sulfas Exsiccatus 3 parts, selenium powder 0.1 part, clarifier 0.2 part and stabilizer 2.4 parts.
This kind of porcelain white glass fusion temperature is relatively low, while reducing energy consumption, has saved raw material, has decreased the wasting of resources,
Reduce production cost, there is even particle size distribution, environmentally safe, the feature of length in service life, the glass of production
Appearance good, it is adaptable to processing technology goods and bottle for cosmetics.
The preferred embodiment of the present invention described in detail above.Should be appreciated that those of ordinary skill in the art without
Need creative work just can make many modifications and variations according to the design of the present invention.Therefore, all technology in the art
Personnel are available by logical analysis, reasoning, or a limited experiment the most on the basis of existing technology
Technical scheme, all should be in the protection domain being defined in the patent claims.
Claims (3)
1. a porcelain white glass, it is characterised in that by forming according to the raw material of weight portion as follows: silica 15 ~ 25 parts, broken glass
Glass 10 ~ 35 parts, calcium oxide 10 ~ 20 parts, quartz sand 30 ~ 45 parts, magnesium oxide 2 ~ 4 parts, aluminium oxide 5 ~ 12 parts, potassium nitrate 5 ~ 10 parts,
2 ~ 8 parts of sodium sulfate, barium chloride 2 ~ 5 parts, 2 ~ 5 parts of fluorite, Matrii Sulfas Exsiccatus 1 ~ 6 part, selenium powder 0.1 ~ 0.3 part, clarifier 0.1 ~ 0.5 part and
Stabilizer 1 ~ 4 part.
Porcelain white glass the most according to claim 1, it is characterised in that by forming according to the raw material of weight portion as follows: dioxy
SiClx 18 ~ 22 parts, cullet 15 ~ 30 parts, calcium oxide 14 ~ 18 parts, quartz sand 34 ~ 40 parts, magnesium oxide 2.2 ~ 3 parts, aluminium oxide 6 ~ 9
Part, potassium nitrate 7 ~ 8.6 parts, 4 ~ 7 parts of sodium sulfate, barium chloride 3 ~ 4 parts, 3 ~ 4.3 parts of fluorite, Matrii Sulfas Exsiccatus 2 ~ 5 parts, selenium powder 0.1 ~ 0.2
Part, clarifier 0.2 ~ 0.4 part and stabilizer 2 ~ 4 parts.
Porcelain white glass the most according to claim 1, it is characterised in that by forming according to the raw material of weight portion as follows: dioxy
SiClx 20 parts, cullet 25 parts, calcium oxide 15 parts, quartz sand 38 parts, magnesium oxide 2.7 parts, aluminium oxide 8 parts, potassium nitrate 8.2 parts,
5 parts of sodium sulfate, barium chloride 3.6 parts, 3.3 parts of fluorite, Matrii Sulfas Exsiccatus 3 parts, selenium powder 0.1 part, clarifier 0.2 part and stabilizer 2.4 parts.