CN109111115A - transmutation crack glaze and preparation method thereof - Google Patents
transmutation crack glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109111115A CN109111115A CN201811077113.6A CN201811077113A CN109111115A CN 109111115 A CN109111115 A CN 109111115A CN 201811077113 A CN201811077113 A CN 201811077113A CN 109111115 A CN109111115 A CN 109111115A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- transmutation
- component
- crack
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of transmutation crack glaze and preparation method thereof, the component and each component mass parts contained in glaze used in transmutation crack glaze is as follows: 20-30 parts of potassium feldspar；20-30 parts of albite；10-20 parts of calcite；10-15 parts of barium carbonate；It is 10-20 parts quartzy；5-8 parts of lithium carbonate；It is scholar 5-7 parts viscous；8-10 parts of titanium dioxide；3-5 parts of borax；20-30 parts of glass powder；3-5 parts of toner.Glaze image surface jade fan of the invention is emerald green the same, pseudo-classic to return very, gives people a kind of feeling to go through the veil of time.
Description
Technical field
The present invention relates to a kind of transmutation crack glazes and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
It is colorful.The porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer, that is as beautiful
Glaze paint as stone fan is emerald green can make porcelain give people a kind of feeling to go through the veil of time, this is also a kind of fashion of current porcelain industry.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of transmutation crack glaze is provided, it
Glaze image surface jade fan is emerald green the same, pseudo-classic to return very, gives people a kind of feeling to go through the veil of time.
In order to solve the above technical problems, the technical scheme is that a kind of transmutation crack glaze, glaze used in it
In the component that contains and each component mass parts it is as follows:
20-30 parts of potassium feldspar；
20-30 parts of albite；
10-20 parts of calcite；
10-15 parts of barium carbonate；
It is 10-20 parts quartzy；
5-8 parts of lithium carbonate；
It is scholar 5-7 parts viscous；
8-10 parts of titanium dioxide；
3-5 parts of borax；
20-30 parts of glass powder；
3-5 parts of toner.
The present invention also provides a kind of preparation method of transmutation crack glaze, the step of method in contain:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 12~16 hours, the glaze after ball milling crossed 325
After mesh, it is stand-by to be modulated into the glaze slip that specific gravity is 1.6~1.8；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
After above-mentioned technical proposal, the glaze image surface jade fan of transmutation crack glaze of the invention is emerald green the same, pseudo-classic to return very,
Give people a kind of feeling to go through the veil of time.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of transmutation crack glaze, the component and each component mass parts contained in glaze used in it are as follows:
20 parts of potassium feldspar；
20 parts of albite；
10 parts of calcite；
10 parts of barium carbonate；
10 parts of quartz；
5 parts of lithium carbonate；
Viscous 5 parts of scholar；
8 parts of titanium dioxide；
3 parts of borax；
20 parts of glass powder；
3 parts of toner.
Contain in the step of preparation method of the transmutation crack glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 12 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.6~1.8；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
Embodiment two
A kind of transmutation crack glaze, the component and each component mass parts contained in glaze used in it are as follows:
30 parts of potassium feldspar；
30 parts of albite；
20 parts of calcite；
15 parts of barium carbonate；
20 parts of quartz；
8 parts of lithium carbonate；
Viscous 7 parts of scholar；
10 parts of titanium dioxide；
5 parts of borax；
30 parts of glass powder；
5 parts of toner.
Contain in the step of preparation method of the transmutation crack glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 16 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.6~1.8；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
Embodiment three
A kind of transmutation crack glaze, the component and each component mass parts contained in glaze used in it are as follows:
25 parts of potassium feldspar；
25 parts of albite；
15 parts of calcite；
12 parts of barium carbonate；
15 parts of quartz；
6 parts of lithium carbonate；
Viscous 6 parts of scholar；
9 parts of titanium dioxide；
4 parts of borax；
25 parts of glass powder；
4 parts of toner.
Contain in the step of preparation method of the transmutation crack glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 14 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.6~1.8；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
The transmutation crack glaze that three above embodiment is prepared, as it has been observed that its glaze image surface jade fan is emerald green,
It is pseudo-classic to return very, it gives people a kind of feeling to go through the veil of time, meets design requirement.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. a kind of transmutation crack glaze, it is characterised in that the component and each component mass parts contained in glaze used in it is as follows:
20-30 parts of potassium feldspar；
20-30 parts of albite；
10-20 parts of calcite；
10-15 parts of barium carbonate；
It is 10-20 parts quartzy；
5-8 parts of lithium carbonate；
It is scholar 5-7 parts viscous；
8-10 parts of titanium dioxide；
3-5 parts of borax；
20-30 parts of glass powder；
3-5 parts of toner.
2. a kind of preparation method of transmutation crack glaze as described in claim 1, it is characterised in that contain in the step of method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 12~16 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.6~1.8；
S3: taking clean green body, glaze or bubble glaze or leaching glaze is soaked directly on green body using glaze slip, then at 1160 DEG C -1230 DEG C
Temperature environment under fire.