CN106042230A - 一种橡胶脱模剂 - Google Patents
一种橡胶脱模剂 Download PDFInfo
- Publication number
- CN106042230A CN106042230A CN201610427608.1A CN201610427608A CN106042230A CN 106042230 A CN106042230 A CN 106042230A CN 201610427608 A CN201610427608 A CN 201610427608A CN 106042230 A CN106042230 A CN 106042230A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- releasing agent
- ether
- mould release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种橡胶脱模剂，包括以下重量份的原料：聚四氟乙烯120‑200份、甲基硅油25‑60份、聚丙烯酰胺15‑40份、脂肪醇10‑30份、聚乙二醇醚15‑40份、肪醇醚硫酸钠80‑150份、酞酸正丁酯12‑36份、二甲苯磺酸钠16‑28份、云母粉20‑50份、甲苯10‑25份、异构醇聚氧乙烯醚5‑15份、去离子水150‑300份、交联剂15‑30份、触媒5‑15份。本发明生产的橡胶脱模剂为白色乳液，PH值为6.5‑8，具有长达6个月的稳定性，用于橡胶制品脱模时，将脱模剂涂布与橡胶制品的模具上，经硫化后可形成牢固均匀的隔离涂膜，使得模具变得光亮、润滑，具有良好的脱模效果，而且该产品不腐蚀也不容易沾污模具，具有很好的水性环保且隔离效果显著。
Description
技术领域
本发明涉及脱模剂技术领域，尤其涉及一种橡胶脱模剂。
背景技术
脱模剂是一种介于模具和成品之间的功能性物质。脱模剂有耐化学性，在与不同树脂的化学成份(特别是苯乙烯和胺类)接触时不被溶解。脱模剂还具有耐热及应力性能，不易分解或磨损；脱模剂粘合到模具上而不转移到被加工的制件上，不妨碍喷漆或其他二次加工操作。由于注塑、挤出、压延、模压、层压等工艺的迅速发展，脱模剂的用量也大幅度地提高，目前粉末脱模剂使用得较多。粉末脱模剂涉及颗粒或粉料，如碳酸钙、滑石粉等。颗粒或粉料能够在橡胶制品与模具表面形成阻隔层，从而实现橡胶制品从模具上顺利脱离下来。但是，颗粒或粉料使用量较大，易漂浮在空气中，容易造成空气污染或成为过敏源，同时也会对橡胶制品和模具造成一定的污染。因此，粉末脱模剂不是理想的脱模剂。良好的橡胶脱模剂应该是既能实现橡胶制品的顺利脱模，又不污染橡胶制品和模具，对环境友好。
发明内容
基于背景技术存在的技术问题，本发明提出了一种橡胶脱模剂及其制备方法。本发明橡胶脱模剂的成品为白色乳液，PH值为6.5-8，具有长达6个月的稳定性，用于橡胶制品脱模时，将脱模剂涂布与橡胶制品的模具上，经硫化后可形成牢固均匀的隔离涂膜，使得模具变得光亮、润滑，具有良好的脱模效果，而且该产品不腐蚀也不容易沾污模具，具有很好的水性环保且隔离效果显著。
本发明提出的一种橡胶脱模剂，包括以下重量份的原料：聚四氟乙烯120-200份、甲基硅油25-60份、聚丙烯酰胺15-40份、脂肪醇10-30份、聚乙二醇醚15-40份、肪醇醚硫酸钠80-150份、酞酸正丁酯12-36份、二甲苯磺酸钠16-28份、云母粉20-50份、甲苯10-25份、异构醇聚氧乙烯醚5-15份、去离子水150-300份、交联剂15-30份、触媒5-15份。
优选地，包括以下重量份的原料：聚四氟乙烯150-180份、甲基硅油30-40份、聚丙烯酰胺18-35份、脂肪醇15-28份、聚乙二醇醚17-33份、肪醇醚硫酸钠100-135份、酞酸正丁酯19-34份、二甲苯磺酸钠20-27份、云母粉25-48份、甲苯13-22份、异构醇聚氧乙烯醚7-13份、去离子水190-280份、交联剂16-26份、触媒6-10份。
优选地，包括以下重量份的原料：聚四氟乙烯150份、甲基硅油49份、聚丙烯酰胺31份、脂肪醇20份、聚乙二醇醚33份、肪醇醚硫酸钠120份、酞酸正丁酯27份、二甲苯磺酸钠25份、云母粉40份、甲苯19份、异构醇聚氧乙烯醚10份、去离子水230份、交联剂20份、触媒10份。
优选地，所述聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇的重量比为150-180：35-55：22-38：15-28。
优选地，所述聚乙二醇醚、肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠的重量比为20-36：90-130：19-33：21-26。
优选地，所述云母粉、甲苯、异构醇聚氧乙烯醚、去离子水的重量比为25-40：13-24：7-12：180-270。
优选地，所述交联剂为过氧化苯酰或氨基甲酸乙酯。
优选地，所述脱模剂的制备方法包括以下步骤：
S1，按照份量配比称聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇、聚乙二醇醚、甲苯，将上述原料混合后放入搅拌机中，在40-85℃的温度下，持续搅拌30-60min；
S2，按照份量配比称取肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠、异构醇聚氧乙烯醚，将上述原料混合后放入S1中的搅拌机中，在50-90℃的温度下，持续搅拌35-55min；
S3，向S2中的搅拌机中加入去离子水，充分搅拌20-30min后，添加交联剂和触媒，继续搅拌15-30min，即可得到一种橡胶脱模剂。
本发明中，该脱模剂的成品为白色乳液，PH值为6.5-8，具有长达6个月的稳定性，用于橡胶制品脱模时，将脱模剂涂布与橡胶制品的模具上，经硫化后可形成牢固均匀的隔离涂膜，使得模具变得光亮、润滑，具有良好的脱模效果，而且该产品不腐蚀也不容易沾污模具，具有很好的水性环保且隔离效果显著。
具体实施方式
下面结合具体实施例对本发明作进一步解说。
实施例一
本发明提出的一种橡胶脱模剂，包括以下重量份的原料：聚四氟乙烯130份、甲基硅油30份、聚丙烯酰胺25份、脂肪醇15份、聚乙二醇醚22份、肪醇醚硫酸钠100份、酞酸正丁酯18份、二甲苯磺酸钠20份、云母粉30份、甲苯15份、异构醇聚氧乙烯醚7份、去离子水170份、交联剂20份、触媒7份。
其制备方法包括以下步骤：
S1，按照份量配比称聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇、聚乙二醇醚、甲苯，将上述原料混合后放入搅拌机中，在45℃的温度下，持续搅拌35min；
S2，按照份量配比称取肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠、异构醇聚氧乙烯醚，将上述原料混合后放入S1中的搅拌机中，在55℃的温度下，持续搅拌40min；
S3，向S2中的搅拌机中加入去离子水，充分搅拌23min后，添加交联剂和触媒，继续搅拌18min，即可得到一种橡胶脱模剂。
实施例二
本发明提出的一种橡胶脱模剂，包括以下重量份的原料：聚四氟乙烯180份、甲基硅油40份、聚丙烯酰胺30份、脂肪醇20份、聚乙二醇醚30份、肪醇醚硫酸钠120份、酞酸正丁酯24份、二甲苯磺酸钠23份、云母粉35份、甲苯18份、异构醇聚氧乙烯醚11份、去离子水230份、交联剂22份、触媒10份。
其制备方法包括以下步骤：
S1，按照份量配比称聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇、聚乙二醇醚、甲苯，将上述原料混合后放入搅拌机中，在60℃的温度下，持续搅拌45min；
S2，按照份量配比称取肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠、异构醇聚氧乙烯醚，将上述原料混合后放入S1中的搅拌机中，在65℃的温度下，持续搅拌45min；
S3，向S2中的搅拌机中加入去离子水，充分搅拌26min后，添加交联剂和触媒，继续搅拌22min，即可得到一种橡胶脱模剂。
实施例三
本发明提出的一种橡胶脱模剂，包括以下重量份的原料：聚四氟乙烯190份、甲基硅油55份、聚丙烯酰胺38份、脂肪醇29份、聚乙二醇醚37份、肪醇醚硫酸钠140份、酞酸正丁酯35份、二甲苯磺酸钠27份、云母粉48份、甲苯23份、异构醇聚氧乙烯醚14份、去离子水280份、交联剂28份、触媒13份。
其制备方法包括以下步骤：
S1，按照份量配比称聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇、聚乙二醇醚、甲苯，将上述原料混合后放入搅拌机中，在75℃的温度下，持续搅拌55min；
S2，按照份量配比称取肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠、异构醇聚氧乙烯醚，将上述原料混合后放入S1中的搅拌机中，在80℃的温度下，持续搅拌50min；
S3，向S2中的搅拌机中加入去离子水，充分搅拌30min后，添加交联剂和触媒，继续搅拌28min，即可得到一种橡胶脱模剂。
为了对实施例中的脱模剂脱模效果进行验证，本发明进行了隔离脱模实验，使用效果如下表所示，
由上表可知，本发明中生产的橡胶脱模剂具有较强的稳定性，脱模隔离持久性好，使用中大大节约了成本和人力资源，大大的提高了生产效率。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种橡胶脱模剂，其特征在于，包括以下重量份的原料：聚四氟乙烯120-200份、甲基硅油25-60份、聚丙烯酰胺15-40份、脂肪醇10-30份、聚乙二醇醚15-40份、肪醇醚硫酸钠80-150份、酞酸正丁酯12-36份、二甲苯磺酸钠16-28份、云母粉20-50份、甲苯10-25份、异构醇聚氧乙烯醚5-15份、去离子水150-300份、交联剂15-30份、触媒5-15份。
2.根据权利要求1所述的一种橡胶脱模剂，其特征在于，包括以下重量份的原料：聚四氟乙烯150-180份、甲基硅油30-40份、聚丙烯酰胺18-35份、脂肪醇15-28份、聚乙二醇醚17-33份、肪醇醚硫酸钠100-135份、酞酸正丁酯19-34份、二甲苯磺酸钠20-27份、云母粉25-48份、甲苯13-22份、异构醇聚氧乙烯醚7-13份、去离子水190-280份、交联剂16-26份、触媒6-10份。
3.根据权利要求1所述的一种橡胶脱模剂，其特征在于，包括以下重量份的原料：聚四氟乙烯150份、甲基硅油49份、聚丙烯酰胺31份、脂肪醇20份、聚乙二醇醚33份、肪醇醚硫酸钠120份、酞酸正丁酯27份、二甲苯磺酸钠25份、云母粉40份、甲苯19份、异构醇聚氧乙烯醚10份、去离子水230份、交联剂20份、触媒10份。
4.根据权利要求1所述的一种橡胶脱模剂，其特征在于，所述聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇的重量比为150-180：35-55：22-38：15-28。
5.根据权利要求1所述的一种橡胶脱模剂，其特征在于，所述聚乙二醇醚、肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠的重量比为20-36：90-130：19-33：21-26。
6.根据权利要求1所述的一种橡胶脱模剂，其特征在于，所述云母粉、甲苯、异构醇聚氧乙烯醚、去离子水的重量比为25-40：13-24：7-12：180-270。
7.根据权利要求1所述的一种橡胶脱模剂，其特征在于，所述交联剂为过氧化苯酰或氨基甲酸乙酯。
8.根据权利要求1所述的一种橡胶脱模剂，其特征在于，所述脱模剂的制备方法包括以下步骤：
S1，按照份量配比称聚四氟乙烯、甲基硅油、聚丙烯酰胺、脂肪醇、聚乙二醇醚、甲苯，将上述原料混合后放入搅拌机中，在40-85℃的温度下，持续搅拌30-60min；
S2，按照份量配比称取肪醇醚硫酸钠、酞酸正丁酯、二甲苯磺酸钠、异构醇聚氧乙烯醚，将上述原料混合后放入S1中的搅拌机中，在50-90℃的温度下，持续搅拌35-55min；
S3，向S2中的搅拌机中加入去离子水，充分搅拌20-30min后，添加交联剂和触媒，继续搅拌15-30min，即可得到一种橡胶脱模剂。