CN106040968A - 一种铸造用水玻璃废砂再生处理方法 - Google Patents
一种铸造用水玻璃废砂再生处理方法 Download PDFInfo
- Publication number
- CN106040968A CN106040968A CN201610354783.2A CN201610354783A CN106040968A CN 106040968 A CN106040968 A CN 106040968A CN 201610354783 A CN201610354783 A CN 201610354783A CN 106040968 A CN106040968 A CN 106040968A
- Authority
- CN
- China
- Prior art keywords
- sand
- treatment
- water glass
- magnetic separation
- antiquated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种铸造用水玻璃废砂再生处理方法，包括以下步骤：（1）、废砂预处理；(2)、将步骤（1）处理好的预处理砂放入高温炉，在523‑525℃下处理10‑15min，处理过程中，向高温炉中通入氮气与氧气的混合气，混合气的通入速度为0.85‑0.9 m3/min，得到二次处理砂；（3）、将二次处理砂使用磁选机进行磁选，将磁选处理后的二次处理砂破碎，过60目筛，然后进行水洗，将水洗后的二次处理砂在55℃下烘干，得到再生砂。经过本发明方法处理后的Na2O的残留量降低至0.05%左右，处理后的废砂可以重新用作新砂使用，而且本发明处理后的废液可以循环使用，降低了处理的成本。
Description
技术领域
本发明属于铸造领域，具体涉及一种铸造用水玻璃废砂再生处理方法。
背景技术
我国是铸造大国，在铸造时，每铸造一吨铸件约产生1.5吨铸造废砂，我国每年的铸造废砂产量达到5000万吨以上，很多采用掩埋的方式进行处理，现在虽然有一些水玻璃废砂回收方法，但是回收利用率低，而且水玻璃废砂中的钠盐成分极难出去，容易造成再生砂耐火度及粘结性下降，造成铸件粘砂等现象。现在的脱膜方法也有几种，但是脱膜率不高。
发明内容
本发明的目的是提供一种铸造用水玻璃废砂再生处理方法，可以提升废砂的脱膜率。
本发明通过以下技术方案实现：
一种铸造用水玻璃废砂再生处理方法，包括以下步骤：
（1）、将100kg废砂进行破碎，过40目筛，将废砂放入洗涤池，使用300L质量分数为2%的柠檬酸钠溶液洗涤，洗涤过程中使用超声波进行处理，超声波频率为25-28KHz，震荡10min后，按2.5-3m3/h的流量加入质量分数为6.2%的盐酸溶液，盐酸溶液加入量为120-150L，在25℃下搅拌处理12-15min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂放入高温炉，在523-525℃下处理10-15min，处理过程中，向高温炉中通入氮气与氧气的混合气，氮气与氧气的体积比为12.2：1，混合气的通入速度为0.85-0.9 m3/min，得到二次处理砂；
（3）、将二次处理砂使用磁选机进行磁选，将磁选处理后的二次处理砂破碎，过60目筛，然后进行水洗，将水洗后的二次处理砂在55℃下烘干，得到再生砂。
本发明的有益效果：本发明提供的铸造用水玻璃废砂的再生处理方法针对水玻璃废砂难以脱膜的特性，改变传统先磁选、高温处理、再洗涤的方式，采用先使用酸液洗涤，然后高温处理，再进行磁选，并精确控制各步骤的温度及处理时间，可以明显提升水玻璃膜的去除率，在进行高温处理时使用通入混合气体，可以使废砂脱膜率提升15%，经过本发明方法处理后的Na2O的残留量降低至0.05%左右，处理后的废砂可以重新用作新砂使用，而且本发明处理后的废液可以循环使用，降低了处理的成本。
具体实施方式
实施例1
一种铸造用水玻璃废砂再生处理方法，包括以下步骤：
（1）、将100kg废砂进行破碎，过40目筛，将废砂放入洗涤池，使用300L质量分数为2%的柠檬酸钠溶液洗涤，洗涤过程中使用超声波进行处理，超声波频率为25-28KHz，震荡10min后，按2.6m3/h的流量加入质量分数为6.2%的盐酸溶液，盐酸溶液加入量为130L，在25℃下搅拌处理15min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂放入高温炉，在524℃下处理10-15min，处理过程中，向高温炉中通入氮气与氧气的混合气，氮气与氧气的体积比为12.2：1，混合气的通入速度为0.88 m3/min，得到二次处理砂；
（3）、将二次处理砂使用磁选机进行磁选，将磁选处理后的二次处理砂破碎，过60目筛，然后进行水洗，将水洗后的二次处理砂在55℃下烘干，得到再生砂。
经过本发明方法处理后的Na2O的残留量降低至0.049%。
实施例2
一种铸造用水玻璃废砂再生处理方法，包括以下步骤：
（1）、将100kg废砂进行破碎，过40目筛，将废砂放入洗涤池，使用300L质量分数为2%的柠檬酸钠溶液洗涤，洗涤过程中使用超声波进行处理，超声波频率为28KHz，震荡10min后，按3m3/h的流量加入质量分数为6.2%的盐酸溶液，盐酸溶液加入量为140L，在25℃下搅拌处理14min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂放入高温炉，在525℃下处理12min，处理过程中，向高温炉中通入氮气与氧气的混合气，氮气与氧气的体积比为12.2：1，混合气的通入速度为0.87m3/min，得到二次处理砂；
（3）、将二次处理砂使用磁选机进行磁选，将磁选处理后的二次处理砂破碎，过60目筛，然后进行水洗，将水洗后的二次处理砂在55℃下烘干，得到再生砂。
经过本发明方法处理后的Na2O的残留量降低至0.051%。
Claims (1)
1.一种铸造用水玻璃废砂再生处理方法，其特征在于，包括以下步骤：
（1）、将100kg废砂进行破碎，过40目筛，将废砂放入洗涤池，使用300L质量分数为2%的柠檬酸钠溶液洗涤，洗涤过程中使用超声波进行处理，超声波频率为25-28KHz，震荡10min后，按2.5-3m3/h的流量加入质量分数为6.2%的盐酸溶液，盐酸溶液加入量为120-150L，在25℃下搅拌处理12-15min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂放入高温炉，在523-525℃下处理10-15min，处理过程中，向高温炉中通入氮气与氧气的混合气，氮气与氧气的体积比为12.2：1，混合气的通入速度为0.85-0.9 m3/min，得到二次处理砂；
（3）、将二次处理砂使用磁选机进行磁选，将磁选处理后的二次处理砂破碎，过60目筛，然后进行水洗，将水洗后的二次处理砂在55℃下烘干，得到再生砂。