CN105983771A - 一种钢管的焊前预热工艺 - Google Patents
一种钢管的焊前预热工艺 Download PDFInfo
- Publication number
- CN105983771A CN105983771A CN201510046989.4A CN201510046989A CN105983771A CN 105983771 A CN105983771 A CN 105983771A CN 201510046989 A CN201510046989 A CN 201510046989A CN 105983771 A CN105983771 A CN 105983771A
- Authority
- CN
- China
- Prior art keywords
- wall thickness
- temperature
- welding
- preheating
- pipes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钢管的焊前预热工艺，包括如下步骤：1）、壁厚大于等于6mm的12Cr1MoV管子、壁厚大于等于10mm的15CrMo管子焊前必须进行预热；2）、预热温度：12Cr1MoV为200-300℃；15CrMo为150-250℃；当采用钨极氩弧焊打底时，可按下限温度降低50℃预热；在负温下焊接时以上温度值需提高20-50℃；3）、当环境温度低于0℃时，壁厚小于6㎜的低合金管子及壁厚小于15㎜的碳素钢管子在焊接时也应适当预热，预热宽度从中心开始，每侧不小于焊件壁厚的3倍，且不小于60mm；4）、火焰加热应以焊缝为中心，加热宽度为焊缝两侧各外延不少于50mm；火焰加热的恒温时间按每毫米焊接厚度保温1min计算；加热完毕，应立即使用干燥的保温材料进行保温。本发明工序合理，制造成本低。
Description
技术领域
本发明涉及一种钢管的焊前预热工艺。
背景技术
现有的钢管的焊前预热工艺存在工序安排不合理、工序繁多，对操作者经验要求较高，使得生产成本偏高。
发明内容
有鉴于现有技术的上述缺陷，本发明所要解决的技术问题是提供一种工序合理、制造成本低的钢管的焊前预热工艺。
为实现上述目的，本发明提供了
一种钢管的焊前预热工艺，包括如下步骤：
1）、壁厚大于等于6mm的12Cr1MoV管子、壁厚大于等于10mm的15CrMo管子焊前必须进行预热；
2）、预热温度：12Cr1MoV为200-300℃；15CrMo为150-250℃；当采用钨极氩弧焊打底时，可按下限温度降低50℃预热；在负温下焊接时以上温度值需提高20-50℃；
3）、当环境温度低于0℃时，壁厚小于6㎜的低合金管子及壁厚小于15㎜的碳素钢管子在焊接时也应适当预热，预热宽度从中心开始，每侧不小于焊件壁厚的3倍，且不小于60mm；
4）、火焰加热应以焊缝为中心，加热宽度为焊缝两侧各外延不少于50mm；火焰加热的恒温时间按每毫米焊接厚度保温1min计算；加热完毕，应立即使用干燥的保温材料进行保温。
本发明的有益效果是：本发明工序合理，制造成本低。
具体实施方式
下面结合实施例对本发明作进一步说明：
一种钢管的焊前预热工艺，包括如下步骤：
1）、壁厚大于等于6mm的12Cr1MoV管子、壁厚大于等于10mm的15CrMo管子焊前必须进行预热；
2）、预热温度：12Cr1MoV为200-300℃；15CrMo为150-250℃；当采用钨极氩弧焊打底时，可按下限温度降低50℃预热；在负温下焊接时以上温度值需提高20-50℃；
3）、当环境温度低于0℃时，壁厚小于6㎜的低合金管子及壁厚小于15㎜的碳素钢管子在焊接时也应适当预热，预热宽度从中心开始，每侧不小于焊件壁厚的3倍，且不小于60mm；
4）、火焰加热应以焊缝为中心，加热宽度为焊缝两侧各外延不少于50mm；火焰加热的恒温时间按每毫米焊接厚度保温1min计算；加热完毕，应立即使用干燥的保温材料进行保温。
Claims (1)
1.一种钢管的焊前预热工艺，其特征在于，包括如下步骤：
1）、壁厚大于等于6mm的12Cr1MoV管子、壁厚大于等于10mm的15CrMo管子焊前必须进行预热；
2）、预热温度：12Cr1MoV为200-300℃；15CrMo为150-250℃；当采用钨极氩弧焊打底时，可按下限温度降低50℃预热；在负温下焊接时以上温度值需提高20-50℃；
3）、当环境温度低于0℃时，壁厚小于6㎜的低合金管子及壁厚小于15㎜的碳素钢管子在焊接时也应适当预热，预热宽度从中心开始，每侧不小于焊件壁厚的3倍，且不小于60mm；
4）、火焰加热应以焊缝为中心，加热宽度为焊缝两侧各外延不少于50mm；火焰加热的恒温时间按每毫米焊接厚度保温1min计算；加热完毕，应立即使用干燥的保温材料进行保温。