CN105033418A - 一种q690d高强钢焊接工艺 - Google Patents

一种q690d高强钢焊接工艺 Download PDF

Info

Publication number
CN105033418A
CN105033418A CN201510399450.7A CN201510399450A CN105033418A CN 105033418 A CN105033418 A CN 105033418A CN 201510399450 A CN201510399450 A CN 201510399450A CN 105033418 A CN105033418 A CN 105033418A
Authority
CN
China
Prior art keywords
welding
weld
welds
strength steel
weldingvoltage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510399450.7A
Other languages
English (en)
Inventor
章阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd
Original Assignee
ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd filed Critical ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd
Priority to CN201510399450.7A priority Critical patent/CN105033418A/zh
Publication of CN105033418A publication Critical patent/CN105033418A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种Q690D高强钢焊接工艺，涉及钢焊接技术领域，主要包括焊前准备、焊接、焊后热处理等步骤。本发明的Q690D高强钢焊接工艺焊缝美观均匀，成型良好，无气孔、裂纹等缺陷，不存在夹渣、未熔合等问题，焊缝焊根以及余高均符合标准。

Description

一种Q690D高强钢焊接工艺
技术领域
本发明涉及钢焊接技术领域，更具体地说是一种Q690D高强钢焊接工艺。
背景技术
Q690高强度钢是低碳调质钢中的一种。低碳调质钢的含碳量较低,在设计的合金系统中加入多种能提高洋透性的元素,以取得强化和较高韧性的目的,同时也兼顾了焊接的要求。这类钢一般是在调质状态下直接焊接,焊后不再做调质热处理。尽管综合力学性能比较优越,但其焊接性却比碳钢差得多。对于Q690D高强度钢的焊接,预热温度、焊后保温温度及时间如何选择,经过焊接热循环后的焊缝、热影响区组织性能如何分析,焊接接头的强度、韧性能否达到目标要求,冷、热裂纹的倾向如何,与之相匹配的焊接材料如何确定和焊接工艺参数如何优化,这些都是Q690高强钢焊接存在的难题。
发明内容
本发明的目的是为了弥补现有技术的不足，提供一种Q690D高强钢焊接工艺。
本发明的目的是通过以下技术方案实现的：
一种Q690D高强钢焊接工艺，其中母材厚度为25mm，其特征在于：包括以下步骤：
（1）焊前准备：
第一，焊接方式和焊接材料的选择：采用熔化极气体保护焊进行焊接，20%CO2+80%Ar气体保护，焊接材料为JM-110焊丝，焊丝规格为φ1.2；
第二，采用火焰切割的方式对Q690D钢板开X型坡口，根部间隙为4mm，钝边1-2mm，坡口角度60°；
第三，对母材进行预热，预热温度为130-150℃；
（2）焊接：
第一，打底层焊接，采用熔化极气体保护焊以300-350mm/min的速度进行焊接，焊接电流180-210A，焊接电压25-27V；
第二，填充层焊接，采用熔化极气体保护焊以250-300mm/min的速度进行焊接，焊接电流210-240A，焊接电压27-28V；
第三，盖面层焊接，采用熔化极气体保护焊以350-400mm/min的速度进行焊接，焊接电流210-250A，焊接电压27-28V；
（3）焊后热处理：
焊接完毕后立即对焊接接头进行保温，保温温度为200-250℃，保温时间为75-90分钟。
本发明的优点在于：本发明的Q690D高强钢焊接工艺焊缝美观均匀，成型良好，无气孔、裂纹等缺陷，不存在夹渣、未熔合等问题，焊缝焊根以及余高均符合标准。
具体实施方式
一种Q690D高强钢焊接工艺，其中母材厚度为25mm，包括以下步骤：
（1）焊前准备：
第一，焊接方式和焊接材料的选择：采用熔化极气体保护焊进行焊接，20%CO2+80%Ar气体保护，焊接材料为JM-110焊丝，焊丝规格为φ1.2；
第二，采用火焰切割的方式对Q690D钢板开X型坡口，根部间隙为4mm，钝边1-2mm，坡口角度60°；
第三，对母材进行预热，预热温度为130℃；
（2）焊接：
第一，打底层焊接，采用熔化极气体保护焊以300mm/min的速度进行焊接，焊接电流180A，焊接电压25V；
第二，填充层焊接，采用熔化极气体保护焊以250mm/min的速度进行焊接，焊接电流210A，焊接电压27V；
第三，盖面层焊接，采用熔化极气体保护焊以350mm/min的速度进行焊接，焊接电流210A，焊接电压27V；
（3）焊后热处理：
焊接完毕后立即对焊接接头进行保温，保温温度为200℃，保温时间为90分钟。

Claims (1)

1.一种Q690D高强钢焊接工艺，其中母材厚度为25mm，其特征在于：包括以下步骤：
（1）焊前准备：
第一，焊接方式和焊接材料的选择：采用熔化极气体保护焊进行焊接，20%CO2+80%Ar气体保护，焊接材料为JM-110焊丝，焊丝规格为φ1.2；
第二，采用火焰切割的方式对Q690D钢板开X型坡口，根部间隙为4mm，钝边1-2mm，坡口角度60°；
第三，对母材进行预热，预热温度为130-150℃；
（2）焊接：
第一，打底层焊接，采用熔化极气体保护焊以300-350mm/min的速度进行焊接，焊接电流180-210A，焊接电压25-27V；
第二，填充层焊接，采用熔化极气体保护焊以250-300mm/min的速度进行焊接，焊接电流210-240A，焊接电压27-28V；
第三，盖面层焊接，采用熔化极气体保护焊以350-400mm/min的速度进行焊接，焊接电流210-250A，焊接电压27-28V；
（3）焊后热处理：
焊接完毕后立即对焊接接头进行保温，保温温度为200-250℃，保温时间为75-90分钟。
CN201510399450.7A 2015-07-09 2015-07-09 一种q690d高强钢焊接工艺 Pending CN105033418A (zh)