CN105149742A - 一种t23钢管焊接工艺 - Google Patents

一种t23钢管焊接工艺 Download PDF

Info

Publication number
CN105149742A
CN105149742A CN201510399408.5A CN201510399408A CN105149742A CN 105149742 A CN105149742 A CN 105149742A CN 201510399408 A CN201510399408 A CN 201510399408A CN 105149742 A CN105149742 A CN 105149742A
Authority
CN
China
Prior art keywords
welding
steel
weld
pipe
welds
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510399408.5A
Other languages
English (en)
Inventor
章阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd
Original Assignee
ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd filed Critical ANHUI KINGYOUNG STRUCTURAL METAL WORK Co Ltd
Priority to CN201510399408.5A priority Critical patent/CN105149742A/zh
Publication of CN105149742A publication Critical patent/CN105149742A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种T23钢管焊接工艺，涉及钢材焊接技术领域，主要由焊前准备、焊接两个步骤组成。本发明的一种T23钢管焊接工艺焊缝美观，无未焊透、未熔融等缺陷，焊缝韧性和塑形优良，力学性能好，无裂纹及过烧组织。

Description

一种T23钢管焊接工艺
技术领域
本发明涉及钢材焊接技术领域，更具体地说是一种T23钢管焊接工艺。
背景技术
T23钢是贝氏体耐热钢，该钢具有良好的力学性能及持久塑性，适于制造工作温度在600℃以下的高温过热器、再热器部件及锅炉集箱、蒸汽导管等。由于T23钢中含有较多的Cr、W、V、Nb等高熔点元素，致使该钢的液态金属的粘度较大，焊接时容易产生未焊透、未熔合等缺陷。
发明内容
本发明的目的是为了弥补现有技术的不足，提供一种T23钢管焊接工艺。
本发明的目的是通过以下技术方案实现的：
一种T23钢管焊接工艺，其中钢管规格为φ55×6mm，其特征在于：包括以下步骤：
（1）焊前准备
第一，焊接方式和焊接材料的选择，采用钨极氩弧焊的方式焊接，焊接材料为TGS-2CW焊丝，焊丝规格为φ2.4mm；
第二，对焊接钢管开V型坡口，对口间隙为2mm，钝边大小为1mm，单边坡角为30°；
第三，对焊接件进行预热，预热温度为100-150℃；
（2）焊接
第一，打底层焊接，采用钨极氩弧焊以75-85mm/min的速度进行焊接，焊接电流为90-110A，焊接电压为10-15V；
第二，填充层焊接，采用钨极氩弧焊以70-85mm/min的速度进行焊接，焊接电流为100-120A，焊接电压为10-16V；
第三，盖面层焊接，采用钨极氩弧焊以70-80mm/min的速度进行焊接，焊接电流为100-120A，焊接电压为10-15V。
所述的一种T23钢管焊接工艺，其特征在于：焊接过程中的层间温度保持在150-250℃。
所述的一种T23钢管焊接工艺，其特征在于：焊接过程中需要进行管内充氩保护，氩气流量为6-8L/min。
本发明的优点在于：
本发明的一种T23钢管焊接工艺焊缝美观，无未焊透、未熔融等缺陷，焊缝韧性和塑形优良，力学性能好，无裂纹及过烧组织。
具体实施方式
一种T23钢管焊接工艺，其中钢管规格为φ55×6mm，其特征在于：包括以下步骤：
（1）焊前准备
第一，焊接方式和焊接材料的选择，采用钨极氩弧焊的方式焊接，焊接材料为TGS-2CW焊丝，焊丝规格为φ2.4mm；
第二，对焊接钢管开V型坡口，对口间隙为2mm，钝边大小为1mm，单边坡角为30°；
第三，对焊接件进行预热，预热温度为100℃；
（2）焊接
第一，打底层焊接，采用钨极氩弧焊以75mm/min的速度进行焊接，焊接电流为90A，焊接电压为10V；
第二，填充层焊接，采用钨极氩弧焊以70mm/min的速度进行焊接，焊接电流为100A，焊接电压为10V；
第三，盖面层焊接，采用钨极氩弧焊以70mm/min的速度进行焊接，焊接电流为100A，焊接电压为10V。
焊接过程中的层间温度保持在150℃。
焊接过程中需要进行管内充氩保护，氩气流量为8L/min。

Claims (3)

1.一种T23钢管焊接工艺，其中钢管规格为φ55×6mm，其特征在于：包括以下步骤：
（1）焊前准备
第一，焊接方式和焊接材料的选择，采用钨极氩弧焊的方式焊接，焊接材料为TGS-2CW焊丝，焊丝规格为φ2.4mm；
第二，对焊接钢管开V型坡口，对口间隙为2mm，钝边大小为1mm，单边坡角为30°；
第三，对焊接件进行预热，预热温度为100-150℃；
（2）焊接
第一，打底层焊接，采用钨极氩弧焊以75-85mm/min的速度进行焊接，焊接电流为90-110A，焊接电压为10-15V；
第二，填充层焊接，采用钨极氩弧焊以70-85mm/min的速度进行焊接，焊接电流为100-120A，焊接电压为10-16V；
第三，盖面层焊接，采用钨极氩弧焊以70-80mm/min的速度进行焊接，焊接电流为100-120A，焊接电压为10-15V。
2.根据权利要求1所述的一种T23钢管焊接工艺，其特征在于：焊接过程中的层间温度保持在150-250℃。
3.根据权利要求1所述的一种T23钢管焊接工艺，其特征在于：焊接过程中需要进行管内充氩保护，氩气流量为6-8L/min。
CN201510399408.5A 2015-07-09 2015-07-09 一种t23钢管焊接工艺 Pending CN105149742A (zh)