CN105969271A - 一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶及制作方法 - Google Patents
一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶及制作方法 Download PDFInfo
- Publication number
- CN105969271A CN105969271A CN201610486555.0A CN201610486555A CN105969271A CN 105969271 A CN105969271 A CN 105969271A CN 201610486555 A CN201610486555 A CN 201610486555A CN 105969271 A CN105969271 A CN 105969271A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- alcohol ester
- antioxidant
- storage battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶及制作方法,包括A组分和B组分;所述A组分由甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,纳米碳化硅,补强性填料,抗氧剂,氯磺化聚乙烯组成;B组分由甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,辛酸铋,BYK‑065,增粘剂组成;本发明通过将A、B两个组份的胶黏剂分别通过密闭搅拌,负压干燥,以及控温混合的方式,制成两个不同组份的胶黏剂。本发明的有益效果:本发明相较于一般的其他胶黏剂具有良好的高弹性,耐热性,耐水性,导热性,粘接性,无污染等优点,能够在使用过程中良好的粘结,并且密封效果好,内部空气少等效果。
Description
技术领域
本发明涉及化工技术领域,特别涉及对蓄电池起到密封作用的一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶
及制作方法
。
背景技术
现有的蓄电池密封胶水的胺类固化剂存在易结晶且胶水可使用时间(胶水在一定温度下粘度升高至两倍的时间)短的问题,可使用时间体现了胶水的反应速度,决定客户配胶后胶水能使用和操作时间的长短,固化剂生产出来后在保质期内的结晶致使客户不能使用该产品。对蓄电池密封胶,固化剂中各原材料的比例不当及固化剂的原生产工艺下,就容易产生上述问题。
随着蓄电池市场需求的逐年上升,对废旧电池的处理与蓄电池的维修越来越受到重视,而蓄电池维修的关键是即要打开密封盖又不能损坏蓄电池外壳,现有的一些密封胶如果是粘接强度高的,在打开密封盖时由于密封胶难于剥离会损坏蓄电池外壳,而易于剥离的粘接强度高均比较低,如何暨保证良好的粘接强度又在打开密封盖时不损坏蓄电池外壳是急待解决的一个难题。
发明内容
本发明的目的是提供
一种具有良好的
高弹性
,
耐热性
,
耐水性
,
导热性
,
粘接性
,
无污染的一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶
及制作方法
,解决蓄电池密封胶的使用需求问题。
为了达到上述目的,本发明提供如下技术方案:
一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:包括
A
组分和
B
组分;所述
A
组分由甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,纳米碳化硅,补强性填料,抗氧剂,氯磺化聚乙烯组成;
B
组分由甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,辛酸铋,
BYK-065
,增粘剂组成;其中所述
A
组分中,包括:
50-70
份的甲基丙烯酸正丁酯,
15-35
份的溶剂,
2-15
份的邻苯二甲酸二环己酯,
10-15
份的纳米碳化硅,
5-15
份的补强性填料,
5-20
份的抗氧剂,
25-35
份的氯磺化聚乙烯组成;所述
B
组分中,包括:
60-80
份的甲基丙烯醸四氢糠醇酯,
30-35
份的聚醚橡胶,
5-15
份的有机膨润土,
3-15
份的辛酸铋,
10-25
份的
BYK-065
,
10-15
份的增粘剂。
所述
A
组分中,甲基丙烯酸正丁酯的平均分子量为
8000-10000
,所述
B
组分中,甲基丙烯醸四氢糠醇酯的平均分子量为
10000-14000
。
所述
A
组分中,包括:
60
份的甲基丙烯酸正丁酯,
25
份的溶剂,
10
份的邻苯二甲酸二环己酯,
12
份的纳米碳化硅,
10
份的补强性填料,
12
份的抗氧剂,
30
份的氯磺化聚乙烯组成;所述
B
组分中,包括:
70
份的甲基丙烯醸四氢糠醇酯,
32
份的聚醚橡胶,
10
份的有机膨润土,
10
份的辛酸铋,
18
份的
BYK-065
,
12
份的增粘剂。
所述溶剂为丙酮、三氯甲烷、二氯乙烷、尼龙酸二甲酯、乙酸乙酯、甲苯或二甲苯中的一种或几种的混合;补强性填料为气相法白炭黑、沉淀法白炭黑和表面处理白炭黑中的一种或几种的混合;抗氧剂为
IrgastabPUR68
、抗氧剂
1010
和
Irganox5057
中的一种或几种的混合;增粘剂为钛酸异丙酯、钛酸丁酯、
r-
氨基丙基三乙氧基硅烷
,
1
、
2-
环氧乙氧基三甲氧基硅烷、碳酸酯的乙酰乙酸乙酯螯合物中的一种或几种的混合。
具体步骤为:
A
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,氯磺化聚乙烯,搅拌升温,温度控制在
80
℃
~110
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比纳米碳化硅,补强性填料,抗氧剂,温度控制在
65
~
75
℃
,混合均匀,即得
A
组分密封胶。
B
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,搅拌升温,温度控制在
80
℃
~110
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比的辛酸铋,
BYK-065
,增粘剂,温度控制在
65
~
75
℃,
混合均匀,即得
B
组分密封胶。
本发明的有益效果:本发明相较于一般的
其他胶黏剂具有良好的
高弹性
,
耐热性
,
耐水性
,
导热性
,
粘接性
,
无污染
等优点,能够在使用过程中良好的粘结,并且密封效果好,内部空气少等效果
。
具体实施方式
下面将结合实施例,对本发明的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例
1
:
一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:包括
A
组分和
B
组分;所述
A
组分由甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,纳米碳化硅,补强性填料,抗氧剂,氯磺化聚乙烯组成;
B
组分由甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,辛酸铋,
BYK-065
,增粘剂组成;其中所述
A
组分中,包括:
50-70
份的甲基丙烯酸正丁酯,
15-35
份的溶剂,
2-15
份的邻苯二甲酸二环己酯,
10-15
份的纳米碳化硅,
5-15
份的补强性填料,
5-20
份的抗氧剂,
25-35
份的氯磺化聚乙烯组成;所述
B
组分中,包括:
60-80
份的甲基丙烯醸四氢糠醇酯,
30-35
份的聚醚橡胶,
5-15
份的有机膨润土,
3-15
份的辛酸铋,
10-25
份的
BYK-065
,
10-15
份的增粘剂。
所述
A
组分中,甲基丙烯酸正丁酯的平均分子量为
8000-10000
,所述
B
组分中,甲基丙烯醸四氢糠醇酯的平均分子量为
10000-14000
。
所述
A
组分中,包括:
60
份的甲基丙烯酸正丁酯,
25
份的溶剂,
10
份的邻苯二甲酸二环己酯,
12
份的纳米碳化硅,
10
份的补强性填料,
12
份的抗氧剂,
30
份的氯磺化聚乙烯组成;所述
B
组分中,包括:
70
份的甲基丙烯醸四氢糠醇酯,
32
份的聚醚橡胶,
10
份的有机膨润土,
10
份的辛酸铋,
18
份的
BYK-065
,
12
份的增粘剂。
所述溶剂为丙酮、三氯甲烷、二氯乙烷、尼龙酸二甲酯、乙酸乙酯、甲苯或二甲苯中的一种或几种的混合;补强性填料为气相法白炭黑、沉淀法白炭黑和表面处理白炭黑中的一种或几种的混合;抗氧剂为
IrgastabPUR68
、抗氧剂
1010
和
Irganox5057
中的一种或几种的混合;增粘剂为钛酸异丙酯、钛酸丁酯、
r-
氨基丙基三乙氧基硅烷
,
1
、
2-
环氧乙氧基三甲氧基硅烷、碳酸酯的乙酰乙酸乙酯螯合物中的一种或几种的混合。
具体步骤为:
A
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,氯磺化聚乙烯,搅拌升温,温度控制在
80
℃
~110
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比纳米碳化硅,补强性填料,抗氧剂,温度控制在
65
~
75
℃
,混合均匀,即得
A
组分密封胶。
B
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,搅拌升温,温度控制在
80
℃
~110
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比的辛酸铋,
BYK-065
,增粘剂,温度控制在
65
~
75
℃,
混合均匀,即得
B
组分密封胶。
实施例
2
:
一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:包括
A
组分和
B
组分;所述
A
组分由甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,纳米碳化硅,补强性填料,抗氧剂,氯磺化聚乙烯组成;
B
组分由甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,辛酸铋,
BYK-065
,增粘剂组成;其中所述
A
组分中,包括:
50-70
份的甲基丙烯酸正丁酯,
15-35
份的溶剂,
2-15
份的邻苯二甲酸二环己酯,
10-15
份的纳米碳化硅,
5-15
份的补强性填料,
5-20
份的抗氧剂,
25-35
份的氯磺化聚乙烯组成;所述
B
组分中,包括:
60-80
份的甲基丙烯醸四氢糠醇酯,
30-35
份的聚醚橡胶,
5-15
份的有机膨润土,
3-15
份的辛酸铋,
10-25
份的
BYK-065
,
10-15
份的增粘剂。
具体
生产加工
步骤为:
A
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,氯磺化聚乙烯,搅拌升温,温度控制在
80
℃
~110
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比纳米碳化硅,补强性填料,抗氧剂,温度控制在
65
~
75
℃
,混合均匀,即得
A
组分密封胶。
B
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,搅拌升温,温度控制在
80
℃
~110
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比的辛酸铋,
BYK-065
,增粘剂,温度控制在
65
~
75
℃,
混合均匀,即得
B
组分密封胶。
A
组分
和
B
组分
分别
静置分装,使用时直接将
A
组分、
B
组分按照重量比混合均匀后即可进行灌封操作。
下表为本发明与其他类产品的数据对比:
上表表明本发明的各项性能优于同类产品,可满足蓄电池密封的工艺需求。
实施例
3
:
本发明中,优选配比为:
A
组分中:
60
份的甲基丙烯酸正丁酯,
25
份的溶剂,
10
份的邻苯二甲酸二环己酯,
12
份的纳米碳化硅,
10
份的补强性填料,
12
份的抗氧剂,
30
份的氯磺化聚乙烯组成;
B
组分中
:
70
份的甲基丙烯醸四氢糠醇酯,
32
份的聚醚橡胶,
10
份的有机膨润土,
10
份的辛酸铋,
18
份的
BYK-065
,
12
份的增粘剂。
优选生产加工
步骤为:
A
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,氯磺化聚乙烯,搅拌升温,温度控制在
90
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比纳米碳化硅,补强性填料,抗氧剂,温度控制在
70
℃
,混合均匀,即得
A
组分密封胶。
B
组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,搅拌升温,温度控制在
90
℃
,开启真空泵抽负压,压力控制在
-
0.1MPa
以下;然后降温到
65
℃
以下,通入干燥氮气解除真空,加入上述重量份数比的辛酸铋,
BYK-065
,增粘剂,温度控制在
70
℃,
混合均匀,即得
B
组分密封胶。
A
组分
和
B
组分
分别
静置分装,使用时直接将
A
组分、
B
组分按照重量比混合均匀后即可进行灌封操作。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应所述以权利要求的保护范围为准。
Claims (5)
1.一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:包括A组分和B组分;所述A组分由甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,纳米碳化硅,补强性填料,抗氧剂,氯磺化聚乙烯组成;B组分由甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,辛酸铋,消泡剂,增粘剂组成;其中所述A组分中,包括:50-70份的甲基丙烯酸正丁酯,15-35份的溶剂,2-15份的邻苯二甲酸二环己酯,10-15份的纳米碳化硅,5-15份的补强性填料,5-20份的抗氧剂,25-35份的氯磺化聚乙烯组成;所述B组分中,包括:60-80份的甲基丙烯醸四氢糠醇酯,30-35份的聚醚橡胶,5-15份的有机膨润土,3-15份的辛酸铋,10-25份的消泡剂,10-15份的增粘剂。
2.根据权利要求1所述的一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:所述A组分中,甲基丙烯酸正丁酯的平均分子量为8000-10000,所述B组分中,甲基丙烯醸四氢糠醇酯的平均分子量为10000-14000。
3.根据权利要求1所述的一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:所述A组分中,包括:60份的甲基丙烯酸正丁酯,25份的溶剂,10份的邻苯二甲酸二环己酯,12份的纳米碳化硅,10份的补强性填料,12份的抗氧剂,30份的氯磺化聚乙烯组成;所述B组分中,包括:70份的甲基丙烯醸四氢糠醇酯,32份的聚醚橡胶,10份的有机膨润土,10份的辛酸铋,18份的消泡剂,12份的增粘剂。
4.根据权利要求1所述的一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶,其特征在于:所述溶剂为丙酮、三氯甲烷、二氯乙烷、尼龙酸二甲酯、乙酸乙酯、甲苯或二甲苯中的一种或几种的混合;补强性填料为气相法白炭黑、沉淀法白炭黑和表面处理白炭黑中的一种或几种的混合;抗氧剂为IrgastabPUR68、抗氧剂1010和Irganox5057中的一种或几种的混合;增粘剂为钛酸异丙酯、钛酸丁酯、r-氨基丙基三乙氧基硅烷,1、2-环氧乙氧基三甲氧基硅烷、碳酸酯的乙酰乙酸乙酯螯合物中的一种或几种的混合。
5.根据权利要求1-4中任一项所述的一种基于正丁酯和糠醇酯的高弹性蓄电池密封胶的制作方法,其特征在于:具体步骤为:
A组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯酸正丁酯,溶剂,邻苯二甲酸二环己酯,氯磺化聚乙烯,搅拌升温,温度控制在80℃~110℃,开启真空泵抽负压,压力控制在-0.1MPa以下;然后降温到65℃以下,通入干燥氮气解除真空,加入上述重量份数比纳米碳化硅,补强性填料,抗氧剂,温度控制在65~75℃,混合均匀,即得A组分密封胶;
B组分包括步骤:在密闭反应釜中,加入上述重量份数比的甲基丙烯醸四氢糠醇酯,聚醚橡胶,有机膨润土,搅拌升温,温度控制在80℃~110℃,开启真空泵抽负压,压力控制在-0.1MPa以下;然后降温到65℃以下,通入干燥氮气解除真空,加入上述重量份数比的辛酸铋,消泡剂,增粘剂,温度控制在65~75℃,混合均匀,即得B组分密封胶。