CN105968930A - 一种环保耐水内墙腻子 - Google Patents
一种环保耐水内墙腻子 Download PDFInfo
- Publication number
- CN105968930A CN105968930A CN201610446995.3A CN201610446995A CN105968930A CN 105968930 A CN105968930 A CN 105968930A CN 201610446995 A CN201610446995 A CN 201610446995A CN 105968930 A CN105968930 A CN 105968930A
- Authority
- CN
- China
- Prior art keywords
- water
- powder
- parts
- putty
- bentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种建筑装饰材料,具体来说,是涉及一种环保耐水内墙腻子粉,包括以下组分:白水泥50‑85份,GR复合钛白颜料15‑25份,羧甲基纤维素4‑10份,膨润土0.5‑1.5份,负离子粉2‑8份,保水稠化剂2‑5份,高分子聚丙氨4‑‑8份,防腐剂0.1‑1份。该环保耐水内墙腻子配料简单、绿色环保、优化环境、耐水性好、易施工、成本低。
Description
技术领域
本发明涉及一种建筑装饰材料,具体来说,是涉及一种环保耐水内墙腻子粉。
背景技术
众所周知,建筑涂料已成为建筑物室内外墙体装饰的首选材料,与之配套使用的建筑腻子也就成为建筑物墙体装饰必不可少的重要辅助材料,以前腻子的使用采用的是利用液体胶现场调配使用,这样由于配置的条件及调配人员的不同,导致调配的腻子质量差异较大,易带来腻子质量的不稳定,涂装后,普遍存在耐水性差、粘结强度低、附着力差、易脱皮、粉化等问题。现在,人们使用的是大多是粉末腻子,只需要按一定的比例用水将粉末腻子调制成膏状即可使用,这种粉末腻子这既保持了水性腻子环保性特点,又很好地解决了利用液体胶在施工现场临时配制的随意性问题。然而目前也存在大量使用不耐水干粉腻子导致墙面出现的脱皮、粉化等现象,给用户带来很多麻烦和金钱的浪费。
发明内容
本发明的目的是针对目前腻子存在的问题,提供一种具有配料简单、绿色环保、优化环境、耐水性好、易施工、成本低的环保型耐水内墙腻子。
为实现该发明目的,本发明的技术方案如下:一种环保耐水内墙腻子,按照重量份数计,包括以下组分:
进一步地,所述的膨润土为钠基膨润土、钙基膨润土和氢基膨润土中的一种。
更进一步地,所述的保水稠化剂的成分包含5%改性纤维素醚、40%高岭土、30%蒙脱石、25%皂土、1%酒石酸。
较佳地,所述的防腐剂为异噻唑啉酮类化合物、山梨酸钾、丙酸钙中的一种。
本发明中的保水稠化剂添加后,能得到均匀细腻、粘度适宜的腻子浆料,且在施工后不开裂,静置状态稳定。
本发明还涉及一种制备上述环保耐水内墙腻子的方法,采取的技术手段为:直接将水和腻子粉按照一定的质量比进行调配成膏状腻子。
较佳地,所述的膏状腻子的配置过程如下,先将水加入搅拌罐中,再加入腻子粉,用电动搅拌器在转速1000r/min下搅拌30分钟,使充分搅拌均匀,静置10-15分钟再次搅拌3-5分钟,根据施工人员的施工喜好,可适当加水重复上述操作。
施工前应先将基体表面的油渍、浮灰、污垢等物质清除掉,确保基体表面的洁净,为避免基体表面太干燥导致对批刮上的腻子造成吸水,在批刮前应用水性界面材料简单处理或用水将基体表面润湿,然后再将腻子涂刮到基体表面。
施工技术要求:腻子批刮厚度超过2mm的,应分次批刮,每次批刮厚度应保持0.5—1mm,—次批刮过厚易出现干缩开裂。腻子应在2h内用完,待表干后实干前即可打磨。
与现有技术相比,本发明的有益效果为:
GR复合钛白颜料对紫外光有很强的吸收屏蔽作用,能够帮助吸收室内的紫外线,负离子粉能有效持续释放负离子,提高室内负氧离子浓度,特制的保水稠化剂,使得浆料均匀细腻、粘度适宜,且在施工后不开裂,静置状态稳定,高分子聚丙胺在碱性条件下释放一种胶体,该胶体能有效的起到憎水作用解决掉粉抗粉化,增加强度耐水浇,水越冲越硬,有效提高腻子施工后墙体的硬度,添加防腐剂增加墙体抗菌防霉能力。
总的来说,本发明得到的环保耐水腻子,具有良好的保水、增稠、抗掉粉儿、抗开裂、打磨性能佳、且使用方法简单、对环境友好等优点,具有良好的市场应用前景。
具体实施方式
为了使本领域的技术人员能够更好地理解本发明的技术方案,下面结合具体实施例对本发明的内容做进一步的详细说明。
实施例1
一种环保耐水内墙腻子,包含以下重量份组分:
白水泥50份,GR复合钛白颜料25份,羧甲基纤维素8份,钠基膨润土0.8份,负离子粉4份,保水稠化剂4份,高分子聚丙氨8份,异噻唑啉酮类化合物0.2份。其中保水稠化剂的成分包含5%改性纤维素醚、40%高岭土、30%蒙脱石、25%皂土、1%酒石酸。
将50份水加入搅拌罐中,再加入80份腻子粉,用电动搅拌器在转速1000r/min下搅拌30分钟,使充分搅拌均匀,静置10-15分钟再次搅拌3-5分钟,根据施工人员的施工喜好,可适当增加加水或增加腻子粉量重复上述操作。
实施例2
一种环保耐水内墙腻子,包含以下重量份组分:
白水泥60份,GR复合钛白颜料20份,羧甲基纤维素4份,钠基膨润土0.6份,负离子粉8份,保水稠化剂3份,高分子聚丙氨4份,异噻唑啉酮类化合物0.4份。其中保水稠化剂的成分包含5%改性纤维素醚、40%高岭土、30%蒙脱石、25%皂土、1%酒石酸。
将60份水加入搅拌罐中,再加入90份腻子粉,用电动搅拌器在转速1000r/min下搅拌30分钟,使充分搅拌均匀,静置10-15分钟再次搅拌3-5分钟,根据施工人员的施工喜好,可适当增加加水或增加腻子粉量重复上述操作。
实施例3
一种环保耐水内墙腻子,包含以下重量份组分:
白水泥72份,GR复合钛白颜料15份,羧甲基纤维素4份,钠基膨润土0.5份,负离子粉2份,保水稠化剂2份,高分子聚丙氨4份,异噻唑啉酮类化合物0.5份。其中保水稠化剂的成分包含5%改性纤维素醚、40%高岭土、30%蒙脱石、25%皂土、1%酒石酸。
将80份水加入搅拌罐中,再加入100份腻子粉,用电动搅拌器在转速1000r/min下搅拌30分钟,使充分搅拌均匀,静置10-15分钟再次搅拌3-5分钟,根据施工人员的施工喜好,可适当增加加水或增加腻子粉量重复上述操作。
施工前应先将基体表面的油渍、浮灰、污垢等物质清除掉,确保基体表面的洁净,为避免基体表面太干燥导致对批刮上的腻子造成吸水,在批刮前应用水性界面材料简单处理或用水将基体表面润湿,含水率<8%,PH值<10,然后再将腻子涂刮到基体表面,施工温度5℃以上,35℃以下,空气相对湿度小于75%。
施工技术要求:腻子批刮厚度超过2mm的,应分次批刮,每次批刮厚度应保持0.5—1mm,—次批刮过厚易出现干缩开裂。腻子应在2h内用完,应在表干后实干前进行打磨。
内墙耐水性腻子的性能
上述技术方案仅体现了本发明的优选实施方式,不能理解为对本发明准许范围的限制,凡根据本发明内容做出的变形和改进,均属于本发明保护范围。
Claims (6)
1.一种环保耐水内墙腻子,由各成分按照比例混合而成,其特征在于:按照重量份数计,包括以下组分:
白水泥 50-85份
GR复合钛白颜料 15-25份
羧甲基纤维素 4-10份
膨润土 0.5-1.5份
负离子粉 2-8份
保水稠化剂 2-5份
高分子聚丙胺 4--8份
防腐剂 0.1-1份。
2.根据权利要求1所述的一种环保耐水内墙腻子粉,其特征在于:所述的膨润土为钠基膨润土、钙基膨润土和氢基膨润土中的一种。
3.根据权利要求1所述的一种环保耐水内墙腻子粉,其特征在于:所述的保水稠化剂的成分包含5%改性纤维素醚、40%高岭土、30%蒙脱石、25%皂土、1%酒石酸。
4.根据权利要求1所述的一种环保耐水内墙腻子粉,其特征在于:所述的防腐剂为异噻唑啉酮类化合物、山梨酸钾、丙酸钙中的一种。
5.制备如权利要求1所述的一种环保耐水内墙腻子粉的方法,其特征在于:直接将水和腻子粉按照一定的质量比进行调配成膏状腻子。
6.根据权利要求5所述的制备环保耐水内墙腻子粉的方法,其特征在于:所述的膏状腻子的配置过程如下,先将水加入搅拌罐中,再加入腻子粉,用电动搅拌器在转速1000r/min下搅拌30分钟,使充分搅拌均匀,静置10-15分钟再次搅拌3-5分钟,根据施工人员的施工喜好,可适当加水重复上述操作。