CN105964017A - Industrial solid defoaming agent and preparation method thereof - Google Patents
Industrial solid defoaming agent and preparation method thereof Download PDFInfo
- Publication number
- CN105964017A CN105964017A CN201610498441.8A CN201610498441A CN105964017A CN 105964017 A CN105964017 A CN 105964017A CN 201610498441 A CN201610498441 A CN 201610498441A CN 105964017 A CN105964017 A CN 105964017A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- industrial solid
- defoaming agent
- solid defoaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an industrial solid defoaming agent. The industrial solid defoaming agent consists of the following raw materials in parts by weight: 5-15 parts of hydrophobic silica, 3-13 parts of calcium chloride, 2-8 parts of fatty alcohol, 2-8 parts of polyvalent metal salt, 3-9 parts of a surface active agent, 2-8 parts of oil thickener, 1-7 parts of amino silicon oil, 3-13 parts of glycerinum, 4-16 parts of oxalic acid activated carbon, and 2-8 parts of white mineral oil. The industrial solid defoaming agent has the advantages of good defoaming effect, convenience in manufacturing and the like.
Description
Technical field
The present invention relates to defoamer field, particularly relate to the preparation method of a kind of industrial solid defoaming agent.
Background technology
At present, along with the development of science and technology, every field is all in fast development, and defoamer can be made in some goods
For compounding ingredient, absorb these goods moisture that filler used and foaming agent are brought in process of production, thus reach dry
Purpose, but existing defoamer selects the problem such as unreasonable because of its material, can not play the mesh preferably absorbing moisture
, bring the biggest problem to the processing of people.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide the system of a kind of industrial solid defoaming agent
Preparation Method.
The present invention takes techniques below scheme to realize: a kind of industrial solid defoaming agent, by following according to weight
The raw material composition of number: hydrophobic silica 5-15 part, calcium chloride 3-13 part, fatty alcohol 2-8 part, multivalent metal salt 2-8 part, table
Face activating agent 3-9 part, oil thickening agent 2-8 part, amido silicon oil 1-7 part, glycerol 3-13 part, oxalic acid activated carbon 4-16 part, white edge oil
2-8 part.
The industrial solid defoaming agent of above-mentioned one, is made up of according to the raw material of parts by weight following: hydrophobic silica
5-12 part, calcium chloride 3-11 part, fatty alcohol 2-6 part, multivalent metal salt 2-6 part, surfactant 3-7 part, oil thickening agent 2-6
Part, amido silicon oil 1-5 part, glycerol 3-11 part, oxalic acid activated carbon 4-14 part, white edge oil 2-6 part.
The industrial solid defoaming agent of above-mentioned one, is made up of according to the raw material of parts by weight following: hydrophobic silica
10 parts, 8 parts of calcium chloride, fatty alcohol 5 parts, multivalent metal salt 5 parts, 6 parts of surfactant, oil thickening agent 5 parts, amido silicon oil 4 parts,
Glycerol 8 parts, oxalic acid activated carbon 10 parts, white edge oil 5 parts.
The preparation method of above-mentioned a kind of industrial solid defoaming agent, comprises the steps of:
(1) the material number in claim 3 is chosen, by hydrophobic silica, calcium chloride, fatty alcohol, multivalent metal salt, glycerol
Using agitating device to mix with white edge oil, mixing time is 20min, obtains mixture A；
(2) surfactant, oil thickening agent, amido silicon oil and oxalic acid activated carbon being carried out heat treated, heat time heating time is
30min, is then stirred the material after heating, and mixing time is 15min, obtains mixture B；
(3) mixture A and mixture B is carried out mixed processing, then mixed material is put in exsiccator and dry, obtain
Finished product.
The method have the advantages that the present invention has the advantages such as defoaming effect is good and easy to make in sum,
Effectively facilitate the use of staff.
Detailed description of the invention
A kind of industrial solid defoaming agent, is made up of according to the raw material of parts by weight following: hydrophobic silica 5-15 part,
Calcium chloride 3-13 part, fatty alcohol 2-8 part, multivalent metal salt 2-8 part, surfactant 3-9 part, oil thickening agent 2-8 part, amino silicone
Oil 1-7 part, glycerol 3-13 part, oxalic acid activated carbon 4-16 part, white edge oil 2-8 part.
The industrial solid defoaming agent of above-mentioned one, is made up of according to the raw material of parts by weight following: hydrophobic silica
5-12 part, calcium chloride 3-11 part, fatty alcohol 2-6 part, multivalent metal salt 2-6 part, surfactant 3-7 part, oil thickening agent 2-6
Part, amido silicon oil 1-5 part, glycerol 3-11 part, oxalic acid activated carbon 4-14 part, white edge oil 2-6 part.
The industrial solid defoaming agent of above-mentioned one, is made up of according to the raw material of parts by weight following: hydrophobic silica
10 parts, 8 parts of calcium chloride, fatty alcohol 5 parts, multivalent metal salt 5 parts, 6 parts of surfactant, oil thickening agent 5 parts, amido silicon oil 4 parts,
Glycerol 8 parts, oxalic acid activated carbon 10 parts, white edge oil 5 parts.
The preparation method of above-mentioned a kind of industrial solid defoaming agent, comprises the steps of:
(1) the material number in claim 3 is chosen, by hydrophobic silica, calcium chloride, fatty alcohol, multivalent metal salt, glycerol
Using agitating device to mix with white edge oil, mixing time is 20min, obtains mixture A；
(2) surfactant, oil thickening agent, amido silicon oil and oxalic acid activated carbon being carried out heat treated, heat time heating time is
30min, is then stirred the material after heating, and mixing time is 15min, obtains mixture B；
(3) mixture A and mixture B is carried out mixed processing, then mixed material is put in exsiccator and dry, obtain
Finished product.
The present invention has the advantages such as defoaming effect is good and easy to make, effectively facilitates the use of staff.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute
The equivalence change done or modification, in the range of being all included in present patent application.
Claims (4)
1. an industrial solid defoaming agent, it is characterised in that be made up of according to the raw material of parts by weight following: hydrophobic titanium dioxide
Silicon 5-15 part, calcium chloride 3-13 part, fatty alcohol 2-8 part, multivalent metal salt 2-8 part, surfactant 3-9 part, oil thickening agent 2-8
Part, amido silicon oil 1-7 part, glycerol 3-13 part, oxalic acid activated carbon 4-16 part, white edge oil 2-8 part.
One the most according to claim 1 industrial solid defoaming agent, it is characterised in that by following according to parts by weight
Raw material forms: hydrophobic silica 5-12 part, calcium chloride 3-11 part, fatty alcohol 2-6 part, multivalent metal salt 2-6 part, surface activity
Agent 3-7 part, oil thickening agent 2-6 part, amido silicon oil 1-5 part, glycerol 3-11 part, oxalic acid activated carbon 4-14 part, white edge oil 2-6 part.
One the most according to claim 1 industrial solid defoaming agent, it is characterised in that by following according to parts by weight
Raw material forms: hydrophobic silica 10 parts, 8 parts of calcium chloride, fatty alcohol 5 parts, multivalent metal salt 5 parts, 6 parts of surfactant, oil
Thickening agent 5 parts, amido silicon oil 4 parts, glycerol 8 parts, oxalic acid activated carbon 10 parts, white edge oil 5 parts.
4. according to the preparation method of a kind of industrial solid defoaming agent described in claim 1-3, it is characterised in that by following step
Rapid composition:
(1) the material number in claim 3 is chosen, by hydrophobic silica, calcium chloride, fatty alcohol, multivalent metal salt, glycerol
Using agitating device to mix with white edge oil, mixing time is 20min, obtains mixture A；
(2) surfactant, oil thickening agent, amido silicon oil and oxalic acid activated carbon being carried out heat treated, heat time heating time is
30min, is then stirred the material after heating, and mixing time is 15min, obtains mixture B；
(3) mixture A and mixture B is carried out mixed processing, then mixed material is put in exsiccator and dry, obtain
Finished product.