CN104386999A - Fireproof acoustic panel - Google Patents
Fireproof acoustic panel Download PDFInfo
- Publication number
- CN104386999A CN104386999A CN201410525437.7A CN201410525437A CN104386999A CN 104386999 A CN104386999 A CN 104386999A CN 201410525437 A CN201410525437 A CN 201410525437A CN 104386999 A CN104386999 A CN 104386999A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- fireproof acoustic
- acoustic panel
- gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a fireproof acoustic panel. The fireproof acoustic panel comprises, by weight, 32-36 parts of wood fibers, 50-55 parts of dihydrate gypsum, 4-6 parts of glass fibers, 5-8 parts of an acrylic acid emulsion, 3-5 parts of an inorganic aluminum salt waterfroof agent and 50-60 parts of industrial waste water. A preparation method of the fireproof acoustic panel comprises the followings steps. The fireproof acoustic panel utilizes the wear-resistant components, guarantees plasterboard strength and hardness and has good wear resistance.
Description
Technical field
The present invention relates to a kind of building material field for interior decoration, specifically belong to fireproof acoustic plate.
Background technology
Plasterboard because having light weight, intensity is high, sound insulation is adiabatic, prevent fires, be convenient to the advantages such as processing and be widely used in constructional ornamental material.The wear resisting property of plasterboard is general, a direction of the research in building materials, but its range of application still needs developing.
Summary of the invention
The object of this invention is to provide a kind of fireproof acoustic plate, in composition, increase wear-resisting formula, the while of ensure that intensity and the hardness of plasterboard, there is good wear resistance.
Technical scheme of the present invention is as follows:
Fireproof acoustic plate, be made up of following raw material: 32 ~ 36 parts of wood fibres, the dihydrate gypsum of 50 ~ 55 parts, 4 ~ 6 parts of glass fibers, 5 ~ 8 parts of ACRYLIC EMULSION, 3 ~ 5 parts of inorganic aluminate water-proof agents, 50-60 part trade effluents, the concrete preparation method of fibrous plaster is as follows:
1), the preparation of wood fibre, be 1:2-3 cocoanut tree skin by weight ratio, to be ground into particle diameter be that the bark of 0.5-1.5mm is broken to Cortex Pini pulverizer cuts, again broken for above bark cutting is put into the fermentation vat that weakly acid soln is housed and soaked 2-4 hour, after reciprocal 2-4 time, the immersion liquid after suction filtration is merged and distill process together, to obtain final product;
2), by step 1) obtain wood fibre and mix with dihydrate gypsum, glass fiber the trade effluent simultaneously adding gypsum weight 40-60%, the ageing of ageing storehouse is inputted after stirring 6 ~ 10h, raw material after ageing is carried out secondary mixing, stirring velocity is 900-1000rpm, churning time is 8 ~ 10h, obtains major ingredient;
3), in step 2) add ACRYLIC EMULSION, inorganic aluminate water-proof agent, remaining trade effluent in the major ingredient that obtains, mix and blend 3 ~ 4h, obtains compound, and compound carries out shaping, solidification treatment, obtains plasterboard.
The present invention is with Chinese scholartree charcoal, gypsum, ceramic powder for main raw material, and redispersibility latex powder, realizes the resource reutilization of gypsum, ceramic powder, turn waste into wealth, decrease environmental pollution, simultaneously, it is hard that sheet material of the present invention has quality, do not absorb water, anti-pollution, acid and alkali-resistance, anti-aging, environmental protection, the advantages such as "dead" murder by poisoning, can be widely used in building decoration.
Embodiment
Fireproof acoustic plate, be made up of following raw material: 32 ~ 36 parts of wood fibres, the dihydrate gypsum of 50 ~ 55 parts, 4 ~ 6 parts of glass fibers, 5 ~ 8 parts of ACRYLIC EMULSION, 3 ~ 5 parts of inorganic aluminate water-proof agents, 50-60 part trade effluents, the concrete preparation method of fibrous plaster is as follows:
1), the preparation of wood fibre, be 1:2-3 cocoanut tree skin by weight ratio, to be ground into particle diameter be that the bark of 0.5-1.5mm is broken to Cortex Pini pulverizer cuts, again broken for above bark cutting is put into the fermentation vat that weakly acid soln is housed and soaked 2-4 hour, after reciprocal 2-4 time, the immersion liquid after suction filtration is merged and distill process together, to obtain final product;
2), by step 1) obtain wood fibre and mix with dihydrate gypsum, glass fiber the trade effluent simultaneously adding gypsum weight 40-60%, the ageing of ageing storehouse is inputted after stirring 6 ~ 10h, raw material after ageing is carried out secondary mixing, stirring velocity is 900-1000rpm, churning time is 8 ~ 10h, obtains major ingredient;
3), in step 2) add ACRYLIC EMULSION, inorganic aluminate water-proof agent, remaining trade effluent in the major ingredient that obtains, mix and blend 3 ~ 4h, obtains compound, and compound carries out shaping, solidification treatment, obtains plasterboard.
Claims (1)
1. fireproof acoustic plate, it is characterized in that: be made up of following raw material: 12 ~ 16 parts of wood fibres, 4 ~ 5 parts cement, 20-25 part gypsum, 4 ~ 6 parts of glass fibers, 12 ~ 18 parts of diatomite, 3 ~ 5 parts of aluminum oxide, 10-12 part asbestos powder, 8-10 part sound absorbent material, 3.5-5.5 part inorganic gel, 50-60 part trade effluents, its concrete preparation method is as follows:
1), the preparation of wood fibre, be 1:2-3 cocoanut tree skin by weight ratio, to be ground into particle diameter be that the bark of 0.5-1.5mm is broken to Cortex Pini pulverizer cuts, again broken for above bark cutting is put into the fermentation vat that weakly acid soln is housed and soaked 2-4 hour, after reciprocal 2-4 time, the immersion liquid after suction filtration is merged and distill process together, to obtain final product;
2), by the glass fiber of above-mentioned weight part, wood fibre 12-15% salt acid soak 3-4 hour, use deionized water wash again, 3-4 hour is soaked afterwards with 10-12% sodium hydroxide solution, extremely neutral with deionized water wash again, particulate state is become with after cement, gypsum Homogeneous phase mixing after filtering, roasting 1-1.5 hour, maturing temperature 700-800 DEG C; Drop into pulverizer pulverizing after roasting and obtain substrate material;
3), substrate material is put in homogenizer together with aluminum oxide, asbestos powder, sound absorbent material, inorganic gel, trade effluent, rotating speed remains on 1200-1300r/min, constantly to be uniformly mixed and after being warmed up to 400 DEG C with 20 DEG C/h, 2-3 hour is left standstill after cool to room temperature, finally carry out extrusion molding in base substrate mould, obtained shaping blank.