CN104231597A - Heat conductive and corrosion-resistant plastic floor - Google Patents
Heat conductive and corrosion-resistant plastic floor Download PDFInfo
- Publication number
- CN104231597A CN104231597A CN201410449396.8A CN201410449396A CN104231597A CN 104231597 A CN104231597 A CN 104231597A CN 201410449396 A CN201410449396 A CN 201410449396A CN 104231597 A CN104231597 A CN 104231597A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- heat
- resistant plastic
- conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat conducive and corrosion-resistant plastic floor. The heat conducive and corrosion-resistant plastic floor is formed by compounding heat conductive and corrosion-resistant plastic and a base material, and the heat conductive and corrosion-resistant plastic comprises the following components in parts by weight: 85-105 parts of polyether polyol, 40-55 parts of diisocyanate, 0.1-1.5 parts of catalyst, 3-6 parts of cross-linking agent, 5-15 parts of heat conductive filler, 2-6 parts of corrosion-resistant agent, 3-8 parts of plasticizer, 10-15 parts of paraffin and 5-15 parts of color paste. The heat conducive and corrosion-resistant plastic floor disclosed by the invention has simple components and good mechanical comprehensive performances, as well as excellent heat conductivity and corrosion resistance.
Description
Technical field
The present invention relates to plastic floor technical field, particularly relate to a kind of heat-conducting and corrosion-resistant plastic floor.
Background technology
In traditional concept, indoor generally use wood floors, as solid wooden floor board, solid wooden compound floor, bamboo-wood floor or cork flooring.But, in the use procedure of timber floor, it is found that timber floor not only yielding, cracking, also need regularly to maintain, be heated after making moist and can produce various problem of appearance, also having the carcinogenic substances such as methyl alcohol is in addition release, and therefore people start sight to turn to plastic floor.Plastic floor has good elasticity, and also have heat insulation, sound insulation, the advantage such as warming, plastic floor is more and more extensive in the application in the fields such as daily life, communications and transportation, building trade.Then, along with the raising of people's living standard and the transformation of consumption idea, common plastic floor can not meet the life requirement of people, therefore, more advanced, high-grade, environmental protection and the various functional plastic floor of tool studied obtained.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of heat-conducting and corrosion-resistant plastic floor, has good heat conductivility and corrosion resistance nature.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is:
A kind of heat-conducting and corrosion-resistant plastic floor is provided, be be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 85 ~ 105 parts, vulcabond 40 ~ 55 parts, catalyzer 0.1 ~ 1.5 part, linking agent 3 ~ 6 parts, heat conductive filler 5 ~ 15 parts, corrosion-resistant agent 2 ~ 6 parts, 3 ~ 8 parts, softening agent, 10 ~ 15 parts, paraffin and mill base 5 ~ 15 parts.
In a preferred embodiment of the present invention, described heat conductive filler is magnesium hydroxide, aluminium hydroxide or both mixtures.
In a preferred embodiment of the present invention, be be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 95 parts, vulcabond 45 parts, catalyzer 0.8 part, linking agent 4.5 parts, heat conductive filler 12 parts, corrosion-resistant agent 5 parts, 5 parts, softening agent, 12 parts, paraffin and mill base 10 parts.
The invention has the beneficial effects as follows: a kind of heat-conducting and corrosion-resistant plastic floor of the present invention, composition is simple, has good mechanical property, has again excellent heat conductivility and erosion resistance simultaneously.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
Embodiment 1:
This heat-conducting and corrosion-resistant plastic floor, be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 95 parts, vulcabond 45 parts, catalyzer 0.8 part, linking agent 4.5 parts, heat conductive filler 12 parts, corrosion-resistant agent 5 parts, 5 parts, softening agent, 12 parts, paraffin and mill base 10 parts.Wherein, heat conductive filler is magnesium hydroxide.
Embodiment 2:
This heat-conducting and corrosion-resistant plastic floor, be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 100 parts, vulcabond 50 parts, catalyzer 1.2 parts, linking agent 5.5 parts, heat conductive filler 15 parts, corrosion-resistant agent 5 parts, 7.0 parts, softening agent, 12 parts, paraffin and mill base 8 parts.Wherein, heat conductive filler is aluminium hydroxide.
Embodiment 3:
This heat-conducting and corrosion-resistant plastic floor, be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 85 parts, vulcabond 40 parts, catalyzer 0.5 part, linking agent 5 parts, heat conductive filler 8 parts, corrosion-resistant agent 3 parts, 4 parts, softening agent, 12 parts, paraffin and mill base 10 parts.Wherein, heat conductive filler is the mixture for magnesium hydroxide and aluminium hydroxide, and the ratio of weight and number of magnesium hydroxide and aluminium hydroxide is 2:3.
Heat-conducting and corrosion-resistant plastic floor in above-mentioned three embodiments, is prepared from by following step:
1) drying aids, puts into loft drier respectively by catalyzer, linking agent, heat conductive filler, softening agent and paraffin, dry 2h under the condition of 80 ~ 90 DEG C;
2) pre-mixing, puts into reactor by polyether glycol, open stir, add vulcabond and linking agent gradually under stirring, after be warming up to 120 DEG C, insulation 2h, formed premix;
3) mix, open and stir, in premix, add catalyzer, corrosion-resistant agent, softening agent, heat conductive filler and paraffin, stirring velocity is controlled at 500 ~ 800r/min, add mill base after stirring 30min, then stir 30min, form work in-process plastic cement;
4) filter, extruding, work in-process plastic cement step 3) made filters, and obtains liquid heat-conducting and corrosion-resistant plastic cement, then again on base material, coated technique, then through rolling, extruding, extrude or mould shape explained hereafter becomes the plastic floor of finished product.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a heat-conducting and corrosion-resistant plastic floor, it is characterized in that, be be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 85 ~ 105 parts, vulcabond 40 ~ 55 parts, catalyzer 0.1 ~ 1.5 part, linking agent 3 ~ 6 parts, heat conductive filler 5 ~ 15 parts, corrosion-resistant agent 2 ~ 6 parts, 3 ~ 8 parts, softening agent, 10 ~ 15 parts, paraffin and mill base 5 ~ 15 parts.
2. heat-conducting and corrosion-resistant plastic floor according to claim 1, is characterized in that, described heat conductive filler is magnesium hydroxide, aluminium hydroxide or both mixtures.
3. heat-conducting and corrosion-resistant plastic floor according to claim 1, it is characterized in that, be be composited by heat-conducting and corrosion-resistant plastic cement and base material, described heat-conducting and corrosion-resistant plastic cement is grouped into by the one-tenth of following mass fraction: polyether glycol 95 parts, vulcabond 45 parts, catalyzer 0.8 part, linking agent 4.5 parts, heat conductive filler 12 parts, corrosion-resistant agent 5 parts, 5 parts, softening agent, 12 parts, paraffin and mill base 10 parts.