CN105946430A - Relief decoration firing process - Google Patents
Relief decoration firing process Download PDFInfo
- Publication number
- CN105946430A CN105946430A CN201510656755.1A CN201510656755A CN105946430A CN 105946430 A CN105946430 A CN 105946430A CN 201510656755 A CN201510656755 A CN 201510656755A CN 105946430 A CN105946430 A CN 105946430A
- Authority
- CN
- China
- Prior art keywords
- embossment
- product
- relief
- firing process
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a relief decoration firing process comprising the following steps: 1) preparation of a relief pigment: uniformly mixing a relief powder and varnish, grinding the mixture for 3-4 times into paste to prepare the relief pigment for later use; 2) printing: printing the surface of a to-be-fired product with the relief pigment, and allowing the printed product in a ventilated and dry place for 24 h, and applying surface oil to the product; 3) labeling the product and air-drying the product in a ventilated and dry place for 20 h; and 4) firing the product in a furnace at 590-615 DEG C to obtain a relief decoration firing product. The relief decoration firing product has stereoscopic relief patterns thereon, wherein the patterns are not liable to discolor and strip and has strong adhesion force. The product satisfies high demand on elegance of glass and ceramic products by people who want high-grade life.
Description
Technical field
The present invention relates to a kind of enamel firing process, particularly relate to a kind of embossment enamel firing process, belong to enamel firing process field.
Background technology
The product that embossment is sculpture to be combined with drawing, processes object by the way of compression, by perspective etc. because usually showing three
Dimension space, and watch only for one or both sides.Embossment is usually attached in another plane, therefore in architectural use more
Many, on apparatus implements also often it can be seen that.The characteristic compressed due to it, is taken up space less, so being applicable to multiple environment
Decoration.In recent years, embossment account for increasingly consequence in urban beautification environment.Embossment is in content, form and material
Upper rich and varied as circular engravure.Decoration firing is then the common process needed for a lot of glass, ceramic, will bake by various patterns
Glass, the surface of ceramic.At present, market does not the most have the glass of embossment decoration firing, ceramic, it is difficult to meet height
The people of quality life is to glass, the high request of the exquisite degree of ceramic.
Summary of the invention
[purpose of the present invention is that provides a kind of embossment decoration firing that can process embossment decoration firing finished product to solve the problems referred to above
Technique.
In order to achieve the above object, present invention employs techniques below scheme:
Embossment enamel firing process of the present invention, comprises the following steps:
(1) preparation embossment pigment: by embossment powder and varnish mix homogeneously, and grind 3-4 time, becomes paste, prepares embossment
Pigment is stand-by；
(2) printing: by described embossment color-printed on product surface to be roasted；
(3) soil face oil after drying in the air at aeration-drying 24 hours is put；
(4) labeling, puts and dries in the air at aeration-drying 20 hours；
(5) enter stove barbecue, furnace temperature 590 DEG C-615 DEG C, roasted and i.e. obtained embossment decoration firing finished product.
As preferably, in described step (1), described embossment powder includes 19220 embossment powder and H31005 embossment powder；Institute
Stating varnish is 80820 varnish.
In described step (2), print 2 times continuously with 75 DEG C of ink knifes.
In described step (4), during labeling, moisture to be scraped dry completely.
In described step (5), the barbecue time is 1-2 hour.
The beneficial effects of the present invention is:
The embossment decoration firing finished product processed by the present invention, its pattern is three-dimensional embossing pattern, and pattern invariant color, peeling, and attachment is insisted on
For a long time, the people of high-quality life is met to glass, the high request of the exquisite degree of ceramic.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further described in detail:
Embodiment 1:
Use following methods to treat baked goods (such as glass or ceramic) to be processed:
(1) preparation embossment pigment: by 19220 embossment powder, H31005 embossment powder and 80820 varnish mix homogeneously, and grind
3-4 time, become paste, prepare embossment pigment stand-by；
(2) printing: by described embossment color-printed on product surface to be roasted, print 2 times continuously with 75 DEG C of ink knifes；
(3) put after drying in the air at aeration-drying 24 hours the most oily；
(4) labeling, during labeling, moisture to be scraped dry completely, then puts and dries in the air at aeration-drying 20 hours；
(5) entering stove barbecue, furnace temperature 600 DEG C, the barbecue time is 1.5 hours, has roasted and has i.e. obtained embossment decoration firing finished product.
Embodiment 2:
Use following methods to treat baked goods (such as glass or ceramic) to be processed:
(1) preparation embossment pigment: by 19220 embossment powder, H31005 embossment powder and 80820 varnish mix homogeneously, and grind
3-4 time, become paste, prepare embossment pigment stand-by；
(2) printing: by described embossment color-printed on product surface to be roasted, print 2 times continuously with 75 DEG C of ink knifes；
(3) put after drying in the air at aeration-drying 24 hours the most oily；
(4) labeling, during labeling, moisture to be scraped dry completely, then puts and dries in the air at aeration-drying 20 hours；
(5) entering stove barbecue, furnace temperature 590 DEG C, the barbecue time is 2 hours, has roasted and has i.e. obtained floating Ju decoration firing finished product.
Embodiment 3:
Use following methods to treat baked goods (such as glass or ceramic) to be processed:
(1) preparation embossment pigment: by 19220 embossment powder, H31005 embossment powder and 80820 varnish mix homogeneously, and grind
3-4 time, become paste, prepare embossment pigment stand-by；
(2) printing: by described embossment color-printed on product surface to be roasted, print 2 times continuously with 75 DEG C of ink knifes；
(3) put after drying in the air at aeration-drying 24 hours the most oily；
(4) labeling, during labeling, moisture to be scraped dry completely, then puts and dries in the air at aeration-drying 20 hours；
(5) entering stove barbecue, furnace temperature 615 DEG C, the barbecue time is 1 hour, has roasted and has i.e. obtained embossment decoration firing finished product.
Claims (5)
1. an embossment enamel firing process, it is characterised in that: comprise the following steps:
Preparation embossment pigment: by embossment powder and varnish mix homogeneously, and grind 3-4 time, becomes paste, prepares embossment pigment and treats
With；
Printing: by described embossment color-printed on product surface to be roasted；
Put after drying in the air at aeration-drying 24 hours the most oily；
Labeling, puts and dries in the air at aeration-drying 20 hours；
Enter stove barbecue, furnace temperature 590 DEG C-615 DEG C, roasted and i.e. obtained embossment decoration firing finished product.
Embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (1), described embossment powder includes
19220 embossment powder and H31005 embossment powder；Described varnish is 80820 varnish.
Embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (2), continuous with 75 DEG C of ink knifes
Print 2 times.
Embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (4), during labeling, moisture is complete
Entirely scrape dry.
Embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (5), the barbecue time is 1-2
Hour.