WO2016134556A1 - Manufacturing process for plate surface pattern as well as plate and furniture manufactured by same - Google Patents

Manufacturing process for plate surface pattern as well as plate and furniture manufactured by same Download PDF

Info

Publication number
WO2016134556A1
WO2016134556A1 PCT/CN2015/073917 CN2015073917W WO2016134556A1 WO 2016134556 A1 WO2016134556 A1 WO 2016134556A1 CN 2015073917 W CN2015073917 W CN 2015073917W WO 2016134556 A1 WO2016134556 A1 WO 2016134556A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
sheet
layer
transfer
process according
Prior art date
Application number
PCT/CN2015/073917
Other languages
French (fr)
Chinese (zh)
Inventor
马留生
Original Assignee
苏州帅马金属制品有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 苏州帅马金属制品有限公司 filed Critical 苏州帅马金属制品有限公司
Publication of WO2016134556A1 publication Critical patent/WO2016134556A1/en

Abstract

A manufacturing process for a plate surface pattern, comprising the following steps: (1) primarily treating a surface of a plate blank; (2) applying a powder material on the surface of the plate to form a paint layer; (3) treating the surface of the paint layer; and (4) adhering a transfer paper to the surface of the paint layer of the plate, roasting at the temperature of 160-180 DEG C for a controlled time of 40-50min, and then stripping the transfer paper to obtain a product. By means of the process, the surface pattern of the product is firm in adhesion, does not have chromatic aberration and is not easy to discolor.

Description

板材表面图案制作工艺及其所制板材和家具Plate surface pattern making process and its made plates and furniture 技术领域Technical field
本发明涉及一种家装板材表面处理工艺及相关成品板材和家具。The invention relates to a surface treatment process for home improvement plates and related finished plates and furniture.
背景技术Background technique
在家装领域，常常需要于板材表面转印图案来达到一定的视觉效果，但是现有转印工艺基于板材厚度、大小、生产区域室内外环境温度等的影响存在温控技术不足，容易造成产品出现色差、图案附着不牢，易变色的问题，影响产品质量。In the field of home decoration, it is often necessary to transfer the pattern on the surface of the board to achieve a certain visual effect. However, the existing transfer process is based on the thickness and size of the sheet, the temperature of the indoor and outdoor environment in the production area, and the temperature control technology is insufficient, which easily causes the product to appear. The problem of color difference, pattern adhesion is not strong, and it is easy to change color, which affects product quality.
发明内容Summary of the invention
一种板材表面图案制作工艺，其特征是，包括如下步骤：A sheet surface patterning process, characterized in that the method comprises the following steps:
(1)板材毛坯表面初步处理；(1) preliminary treatment of the surface of the blank of the sheet;
(2)板材表面上粉末材料，形成油漆层；(2) powder material on the surface of the sheet to form a paint layer;
(3)对油漆层表面处理；(3) surface treatment of the paint layer;
(4)转印纸贴在板材的油漆层表面，160～180℃烘烤40～50分钟，之后剥离转印纸，即得到产品；(4) The transfer paper is attached to the surface of the paint layer of the board, baked at 160 to 180 ° C for 40 to 50 minutes, and then the transfer paper is peeled off to obtain the product;
所述转印纸包括基材纸，涂覆于所述基材纸表面的印刷层，以及设于所述印刷层上表面的胶层，所述胶层由转印胶构成，步骤(4)将转印纸的胶层一侧贴合在板材的油漆层表面进行转印。The transfer paper comprises a substrate paper, a printing layer coated on the surface of the substrate paper, and a glue layer disposed on the upper surface of the printing layer, the glue layer is composed of a transfer adhesive, and step (4) The adhesive layer side of the transfer paper is attached to the surface of the paint layer of the sheet for transfer.
优选的，所述板材为金属板。Preferably, the sheet material is a metal sheet.
优选的，所述板材为钢板。Preferably, the sheet material is a steel sheet.
优选的，所述转印胶包括按重量份比例计的以下组分：醋酸乙烯酯42-47份，聚乙烯醇4-7份，邻苯二甲酸二丁酯3-5份，辛醇0.9-1.1份，过硫酸铵0.08-0.12份，和水44.8-45.0份。Preferably, the transfer adhesive comprises the following components in parts by weight: vinyl acetate 42-47 parts, polyvinyl alcohol 4-7 parts, dibutyl phthalate 3-5 parts, octanol 0.9 - 1.1 parts, 0.08-0.12 parts of ammonium persulfate, and 44.8-45.0 parts of water.
优选的，所述印刷层包括按重量份比例计的以下组分：异丁醇48-52份、甲醇19-21份、分散染料19-21份、聚乙烯缩丁醛9-11份。Preferably, the printing layer comprises the following components in parts by weight: 48-52 parts of isobutanol, 19-21 parts of methanol, 19-21 parts of disperse dye, and 9-11 parts of polyvinyl butyral.
优选的，所述印刷层为木纹印刷层。 Preferably, the printed layer is a wood grain printed layer.
优选的，所述粉末材料包括按重量份比例计的以下组分：聚酯树脂27-29份、环氧树脂27-29份、填充料37-39份、助剂2.7-2.9份、钛白粉2.4-2.6份、和颜料0.65-0.75份。Preferably, the powder material comprises the following components in parts by weight: 27-29 parts of polyester resin, 27-29 parts of epoxy resin, 37-39 parts of filler, 2.7-2.9 parts of auxiliary agent, titanium dioxide 2.4-2.6 parts, and pigments 0.65-0.75 parts.
一种板材，采用上述任一技术方案的工艺制得。A sheet material obtained by the process of any of the above technical solutions.
一种家具，由若干上述板材围合而成。A piece of furniture that is enclosed by a plurality of the above-mentioned sheets.
本发明所达到的有益效果：The beneficial effects achieved by the invention:
1.本发明板材表面图案制作工艺，通过毛坯面初处理、毛坯面上油漆、油漆面处理和转印的工序，尤其是控制转印时烘烤温度和时间来获得高质的产品，使得产品表面图案附着牢固，无色差，不易变色。1. The surface patterning process of the board of the invention obtains a high quality product through the initial processing of the blank surface, the paint on the blank surface, the surface treatment of the paint surface, and the transfer process, in particular to control the baking temperature and time during the transfer, so that the product The surface pattern adheres firmly, has no color difference, and is not easily discolored.
2.本发明工艺尤其适合金属板表面制作图案，而金属板中又尤以刚板为最佳。2. The process of the invention is especially suitable for making patterns on the surface of metal plates, and in the metal plates, especially rigid plates are preferred.
3.本发明工艺中转印纸的转印胶采用自有的特别配方，可进一步达到加强转印图案牢固度，避免变色的目的，提高转印效果。3. The transfer adhesive of the transfer paper in the process of the invention adopts its own special formula, and can further enhance the firmness of the transfer pattern, avoid the purpose of discoloration, and improve the transfer effect.
4.本发明工艺中转印纸的印刷层也采用自有的特别配方，可更进一步的增强转印效果。4. The printing layer of the transfer paper in the process of the invention also adopts its own special formula, which can further enhance the transfer effect.
5.本发明工艺尤其适合在板材表面制作木纹图案，也即印刷层采用木纹印刷层。而采用自有特别配方的粉末材料形成油漆层则能够与木纹印刷层最佳的适配，更有利于色牢和颜色效果。5. The process of the invention is particularly suitable for making a wood grain pattern on the surface of the board, that is, the printed layer is printed with a wood grain. The use of a powder material with its own special formula to form a paint layer can be optimally matched with the wood grain printing layer, which is more conducive to color fastness and color effect.
6.各种板材家具其板材的表面均可使用本发明工艺进行图案制作，获得图案附着牢固，无色差，不易变色的有益效果，而特别的，钢板表面转印木纹图案，不仅能够具备优质、仿真的木质效果，而且相对于传统木质板材更加的环保、耐用，还有不易燃烧的优点，有十分广阔的推广前景。尤其适合用来制作家具。6. All kinds of sheet furniture The surface of the board can be patterned by using the process of the invention, and the pattern is firmly adhered, no color difference, no discoloration is beneficial, and in particular, the wood surface transfer wood pattern can not only have high quality. The wooden effect of the simulation is more environmentally friendly and durable than the traditional wooden board, and has the advantage of being non-flammable, and has a very broad promotion prospect. Especially suitable for making furniture.
具体实施方式detailed description
下面结合实施例对本发明作进一步描述。The invention is further described below in conjunction with the embodiments.
实施例1Example 1
一种板材表面图案制作工艺，用于制作表面带有图案的板材产品，包括如下步骤： A sheet surface patterning process for producing a sheet product having a pattern on a surface, comprising the following steps:
(1)对作为板材毛坯的钢板，表面去渣、打磨光滑。(1) For the steel sheet as the blank of the sheet, the surface is slag-free and smooth.
(2)在打磨光滑的板材表面高温静电喷塑适配木纹图案印刷材料的粉末材料，从而在板材表面形成油漆层，得到半成品。(2) High-temperature electrostatic spraying on the surface of the polished plate to match the powder material of the wood grain pattern printing material, thereby forming a paint layer on the surface of the plate to obtain a semi-finished product.
其中粉末材料由按重量份比例计的以下组分组成：聚酯树脂28份、环氧树脂28份、填充料38份、助剂2.8份、钛白粉2.5份、和颜料0.7份。The powder material was composed of the following components in terms of parts by weight: 28 parts of polyester resin, 28 parts of epoxy resin, 38 parts of filler, 2.8 parts of auxiliary agent, 2.5 parts of titanium dioxide, and 0.7 part of pigment.
(3)对半成品的油漆层表面用细沙皮进行轻微打磨，然后用干净的抹布擦拭干净。(3) The surface of the semi-finished paint layer is slightly sanded with fine sand and then wiped clean with a clean rag.
(4)将转印纸贴在打磨过的板材油漆层表面，160～180℃烘烤，时间控制在40～50分钟，由于转印纸的印刷层油墨和转印胶的热升华性能，转印纸上印刷的木纹图案被转印到产品的油漆层表面，之后剥离转印纸，即得到产品。(4) Paste the transfer paper on the surface of the polished paint layer, bake at 160-180 °C, and control the time between 40 and 50 minutes. Due to the thermal sublimation performance of the printing layer ink and transfer adhesive of the transfer paper, The wood grain pattern printed on the printing paper is transferred to the surface of the paint layer of the product, and then the transfer paper is peeled off to obtain the product.
其中转印纸包括基材纸，涂覆于基材纸表面的印刷层，以及设于印刷层上表面的胶层，胶层由转印胶构成，步骤(4)将转印纸的胶层一侧贴合在板材的油漆层表面进行转印。The transfer paper comprises a substrate paper, a printing layer coated on the surface of the substrate paper, and a glue layer disposed on the upper surface of the printing layer, the glue layer is composed of a transfer adhesive, and the glue layer of the transfer paper is carried out in the step (4). One side is attached to the surface of the paint layer of the sheet for transfer.
转印胶由按重量份比例计的以下组分组成：醋酸乙烯酯45份，聚乙烯醇5份，邻苯二甲酸二丁酯4份，辛醇1份，过硫酸铵0.1份，和水44.9份。The transfer adhesive consists of the following components in parts by weight: 45 parts of vinyl acetate, 5 parts of polyvinyl alcohol, 4 parts of dibutyl phthalate, 1 part of octanol, 0.1 part of ammonium persulfate, and water. 44.9 parts.
印刷层为木纹印刷层，由按重量份比例计的以下组分组成：异丁醇50份、甲醇20份、分散染料20份、聚乙烯缩丁醛10份。The printed layer was a wood grain printed layer composed of the following components in parts by weight: 50 parts of isobutanol, 20 parts of methanol, 20 parts of disperse dye, and 10 parts of polyvinyl butyral.
转印时，在转印纸贴到油漆层表面后、烘烤前，需用刮板把转印纸和产品油漆层表面间的空气刮出，刮平，以提高转印质量。烘烤出来以后，可用清水在转印纸进行表面湿润，方便剥离转印纸，之后再用抹布擦拭产品表面多余的转印胶，即得到本发明实施例1的板材成品。During transfer, after the transfer paper is applied to the surface of the paint layer and before baking, the air between the transfer paper and the surface of the product paint layer is scraped off and smoothed to improve the transfer quality. After baking, the surface of the transfer paper can be wetted with water to facilitate the peeling of the transfer paper, and then the excess transfer adhesive on the surface of the product is wiped with a rag to obtain the finished product of the first embodiment of the present invention.
实施例2Example 2
一种板材表面图案制作工艺，制得实施例2的板材成品，与实施例1的区别在于：A sheet surface patterning process for producing the finished sheet product of Example 2, which differs from Embodiment 1 in that:
转印纸中，转印胶由按重量份比例计的以下组分组成：醋酸乙烯酯42份，聚乙烯醇4份，邻苯二甲酸二丁酯3份，辛醇0.9份，过硫酸铵0.08份，和水44.8份。印刷层由按重量份比例计的以下组分组成：异丁醇48份、甲醇19份、分散染料19份、聚乙烯缩丁醛9份。 In the transfer paper, the transfer adhesive consists of the following components in parts by weight: vinyl acetate 42 parts, polyvinyl alcohol 4 parts, dibutyl phthalate 3 parts, octanol 0.9 parts, ammonium persulfate 0.08 parts, and 44.8 parts of water. The printed layer was composed of the following components in terms of parts by weight: 48 parts of isobutanol, 19 parts of methanol, 19 parts of disperse dye, and 9 parts of polyvinyl butyral.
粉末材料由按重量份比例计的以下组分组成：聚酯树脂27份、环氧树脂27份、填充料37份、助剂2.7份、钛白粉2.4份、和颜料0.65份。The powder material was composed of the following components in terms of parts by weight: 27 parts of polyester resin, 27 parts of epoxy resin, 37 parts of filler, 2.7 parts of auxiliary agent, 2.4 parts of titanium dioxide, and 0.65 parts of pigment.
实施例3Example 3
一种板材表面图案制作工艺，制得实施例3的板材成品，与实施例1的区别在于：A sheet surface patterning process for producing the finished sheet product of Example 3, which differs from Embodiment 1 in that:
转印纸中，转印胶由按重量份比例计的以下组分组成：由按重量份比例计的以下组分组成：醋酸乙烯酯47份，聚乙烯醇7份，邻苯二甲酸二丁酯5份，辛醇1.1份，过硫酸铵0.12份，和水45.0份。印刷层由按重量份比例计的以下组分组成：异丁醇52份、甲醇21份、分散染料21份、聚乙烯缩丁醛11份。In the transfer paper, the transfer adhesive consists of the following components in parts by weight: consisting of the following components in parts by weight: 47 parts of vinyl acetate, 7 parts of polyvinyl alcohol, dibutyl phthalate 5 parts of ester, 1.1 parts of octanol, 0.12 parts of ammonium persulfate, and 45.0 parts of water. The printed layer was composed of the following components in terms of parts by weight: 52 parts of isobutanol, 21 parts of methanol, 21 parts of disperse dye, and 11 parts of polyvinyl butyral.
粉末材料由按重量份比例计的以下组分组成：聚酯树脂29份、环氧树脂29份、填充料39份、助剂2.9份、钛白粉2.6份、和颜料0.75份。The powder material was composed of the following components in terms of parts by weight: 29 parts of polyester resin, 29 parts of epoxy resin, 39 parts of filler, 2.9 parts of auxiliary agent, 2.6 parts of titanium dioxide, and 0.75 parts of pigment.
实施例4-6Example 4-6
一种家具制作工艺，家具具体为箱柜，包括如下步骤：A furniture making process, the furniture is specifically a cabinet, comprising the following steps:
(1)大张的钢板通过剪板机裁切成需要的小块钢板作为板材毛坯。(1) A large sheet of steel is cut into a required small piece of steel as a sheet blank by a shearing machine.
(2)把板材毛坯利用同行业通用的设备和方法加工出箱柜所需的各种组件。(2) The various components required for the processing of the cabinet blanks using the equipment and methods common to the industry.
(3)把成型的各种组件通过焊接围成一个带门的箱体。(3) The molded various components are welded into a box with a door.
(4)在箱体的各组件板材表面通过实施例1工艺加工木纹图案，或通过实施例2工艺加工木纹图案或通过实施例3工艺加工木纹图案。(4) The wood grain pattern is processed by the process of the first embodiment on the surface of each component plate of the casing, or the wood grain pattern is processed by the process of the embodiment 2 or the wood grain pattern is processed by the process of the third embodiment.
(5)对步骤(4)加工完图案的箱体装配各种附件即可得到完整的箱柜，附件例如可以是锁具、脚轮、操作面板、后盖、抽屉、隔板。(5) A complete cabinet can be obtained by assembling various accessories to the box in which the pattern is processed in step (4), and the accessories can be, for example, a lock, a caster, an operation panel, a back cover, a drawer, and a partition.
(6)产品表面打蜡。(6) Wax on the surface of the product.
本实施例4-6工艺制得的家具，由于采用钢板作为板材，同时辅以木纹图案，不仅能够具备优质、仿真的木质家具效果，图案附着牢固，无色差，不易变色而且相对于传统木质家具更加的环保、耐用，还有不易燃烧的优点，有十分广阔的推广前景。The furniture made in the process of the present embodiment 4-6, because the steel plate is used as the plate material, and supplemented by the wood grain pattern, can not only have the high-quality, simulated wooden furniture effect, the pattern is firmly attached, no color difference, no discoloration and relative to the traditional wood. The furniture is more environmentally friendly, durable, and has the advantage of being non-flammable, and has a very broad promotion prospect.
需要说明的是，本发明中分散染料、填充料、助剂分别可以采用本行业通用的材料。填充料例如硫酸钡，助剂例如砂纹剂、蜡。 It should be noted that, in the present invention, the disperse dye, the filler, and the auxiliary agent may each be a material commonly used in the industry. Fillers such as barium sulfate, auxiliaries such as sanding agents, waxes.
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变形，这些改进和变形也应视为本发明的保护范围。 The above is only a preferred embodiment of the present invention, and it should be noted that those skilled in the art can make several improvements and modifications without departing from the technical principles of the present invention. It should also be considered as the scope of protection of the present invention.

Claims (9)

  1. 一种板材表面图案制作工艺，其特征是，包括如下步骤：A sheet surface patterning process, characterized in that the method comprises the following steps:
    (1)板材毛坯表面初步处理；(1) preliminary treatment of the surface of the blank of the sheet;
    (2)板材表面上粉末材料，形成油漆层；(2) powder material on the surface of the sheet to form a paint layer;
    (3)对油漆层表面处理；(3) surface treatment of the paint layer;
    (4)转印纸贴在板材的油漆层表面，160～180℃烘烤40～50分钟，之后剥离转印纸，即得到产品；(4) The transfer paper is attached to the surface of the paint layer of the board, baked at 160 to 180 ° C for 40 to 50 minutes, and then the transfer paper is peeled off to obtain the product;
    所述转印纸包括基材纸，涂覆于所述基材纸表面的印刷层，以及设于所述印刷层上表面的胶层，所述胶层由转印胶构成，步骤(4)将转印纸的胶层一侧贴合在板材的油漆层表面进行转印。The transfer paper comprises a substrate paper, a printing layer coated on the surface of the substrate paper, and a glue layer disposed on the upper surface of the printing layer, the glue layer is composed of a transfer adhesive, and step (4) The adhesive layer side of the transfer paper is attached to the surface of the paint layer of the sheet for transfer.
  2. 根据权利要求1所述的一种板材表面图案制作工艺，其特征是，所述板材为金属板。A sheet surface patterning process according to claim 1, wherein the sheet material is a metal sheet.
  3. 根据权利要求2所述的一种板材表面图案制作工艺，其特征是，所述板材为钢板。A sheet surface patterning process according to claim 2, wherein the sheet material is a steel sheet.
  4. 根据权利要求1-3任一项所述的一种板材表面图案制作工艺，其特征是，所述转印胶包括按重量份比例计的以下组分：醋酸乙烯酯42-47份，聚乙烯醇4-7份，邻苯二甲酸二丁酯3-5份，辛醇0.9-1.1份，过硫酸铵0.08-0.12份，和水44.8-45.0份。A sheet surface pattern forming process according to any one of claims 1 to 3, wherein the transfer adhesive comprises the following components in parts by weight: vinyl acetate 42-47 parts, polyethylene 4-7 parts of alcohol, 3-5 parts of dibutyl phthalate, 0.9-1.1 parts of octanol, 0.08-0.12 parts of ammonium persulfate, and 44.8-45.0 parts of water.
  5. 根据权利要求4所述的一种板材表面图案制作工艺，其特征是，所述印刷层包括按重量份比例计的以下组分：异丁醇48-52份、甲醇19-21份、分散染料19-21份、聚乙烯缩丁醛9-11份。A sheet surface patterning process according to claim 4, wherein the printing layer comprises the following components in parts by weight: isobutyl alcohol 48-52 parts, methanol 19-21 parts, disperse dye 19-21 parts, polyvinyl butyral 9-11 parts.
  6. 根据权利要求1-3、5任一项所述的一种板材表面图案制作工艺，其特征是，所述印刷层为木纹印刷层。A sheet surface patterning process according to any one of claims 1-3, 5, wherein the printing layer is a wood grain printing layer.
  7. 根据权利要求6所述的一种板材表面图案制作工艺，其特征是，所述粉末材料包括按重量份比例计的以下组分：聚酯树脂27-29份、环氧树脂27-29份、填充料37-39份、助剂2.7-2.9份、钛白粉2.4-2.6份、和颜料0.65-0.75份。A sheet surface pattern forming process according to claim 6, wherein the powder material comprises the following components in parts by weight: 27-29 parts of polyester resin, 27-29 parts of epoxy resin, 37-39 parts of filler, 2.7-2.9 parts of auxiliary agent, 2.4-2.6 parts of titanium dioxide, and 0.65-0.75 parts of pigment.
  8. 一种板材，其特征是，由权利要求1-7任一项工艺制得。 A sheet material produced by the process of any of claims 1-7.
  9. 一种家具，其特征是，由若干权利要求8所述板材围合而成。 A piece of furniture characterized in that it is enclosed by a plurality of sheets of claim 8.
PCT/CN2015/073917 2015-02-28 2015-03-10 Manufacturing process for plate surface pattern as well as plate and furniture manufactured by same WO2016134556A1 (en)