CN105946427A - Transparent relief decoration firing process - Google Patents
Transparent relief decoration firing process Download PDFInfo
- Publication number
- CN105946427A CN105946427A CN201510649591.XA CN201510649591A CN105946427A CN 105946427 A CN105946427 A CN 105946427A CN 201510649591 A CN201510649591 A CN 201510649591A CN 105946427 A CN105946427 A CN 105946427A
- Authority
- CN
- China
- Prior art keywords
- transparent
- embossment
- product
- pattern
- firing process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a transparent relief decoration firing process including the steps of: 1) printing a pattern on the surface of a to-be-fired product with varnish; 2) uniformly spreading a transparent relief powder onto the pattern, and coating the pattern with surface oil when the relief powder is fully dried; 3) labeling the product and allowing the product to stand for more than 12 h in a ventilated and dry place; and 4) firing the product in a furnace at 580-600 DEG C to produce the transparent relief decoration firing product. The pattern has an irregular transparent crystal granular appearance and has an uneven feel, is not liable to discolor and strip off, has durable adhesion force. The product satisfies high demand on elegance of glass products by people who want high-grade life.
Description
Technical field
The present invention relates to a kind of enamel firing process, particularly relate to a kind of transparent embossment enamel firing process, belong to enamel firing process field.
Background technology
The product that embossment is sculpture to be combined with drawing, processes object by the way of compression, by perspective etc. because usually showing three
Dimension space, and watch only for one or both sides.Embossment is usually attached in another plane, therefore in architectural use more
Many, on apparatus implements also often it can be seen that.The characteristic compressed due to it, is taken up space less, so being applicable to multiple environment
Decoration.In recent years, embossment account for increasingly consequence in urban beautification environment.Embossment is in content, form and material
Upper rich and varied as circular engravure.Embossing techniques is applied on transparent article such as glass then for transparent embossment.Decoration firing is then
Common process needed for a lot of glass, ceramics, will bake on glass, the surface of ceramic by various patterns.At present, city
The most not there is the glass of transparent embossment decoration firing, it is difficult to meet the people of high-quality life to the exquisite degree of glass on field
High request.
Summary of the invention
The purpose of the present invention is that providing a kind of to solve the problems referred to above can process the transparent of transparent embossment decoration firing finished product
Embossment enamel firing process.
In order to achieve the above object, present invention employs techniques below scheme:
Transparent embossment enamel firing process of the present invention comprises the following steps:
(1) with varnish at product surface printing pattern to be roasted；
(2) transparent embossment powder is uniformly spread on pattern；
(3) the fully dried front cover oil of embossment powder is treated；
(4) make a gift of mark, put and dry in the air at aeration-drying more than 12 hours；
(5) enter stove barbecue, furnace temperature 580 DEG C-600 DEG C, roasted and i.e. obtained transparent embossment decoration firing finished product.
As preferably, in described step (1), described varnish is 80820 varnish.
In described step (3), described oil is 5088 oil.
In described step (3), during front cover oil, the pressure between ink knife and forme being transferred to minimum, ink knife temperature is 75
℃。
The beneficial effects of the present invention is:
The transparent embossment decoration firing finished product processed by the present invention, the pattern after baking is irregular pebble graininess, has concave-convex sense,
Not fading, peel off, adhesive force is lasting, meets the people of the high-quality life high request to the exquisite degree of glass.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further described in detail:
Embodiment 1:
Use following methods to treat baked goods (such as glass) to be processed:
(1) with 80820 varnish at product surface printing pattern to be roasted；
(2) transparent embossment powder is uniformly spread on pattern；
(3) treat that embossment powder seals 5088 oil the most after drying, during front cover oil, the pressure between ink knife and forme is transferred to minimum, ink
Cutter temperature is 75 DEG C；
(4) labeling, puts and dries in the air at aeration-drying more than 12 hours；
(5) enter stove barbecue, furnace temperature 590 DEG C, roasted and i.e. obtained transparent embossment decoration firing finished product.
Embodiment 2:
Use following methods to treat baked goods (such as glass) to be processed:
(1) with 80820 varnish at product surface printing pattern to be roasted；
(2) transparent embossment powder is uniformly spread on pattern；
(3) treat that embossment powder seals 5088 oil the most after drying, during front cover oil, the pressure between ink knife and forme is transferred to minimum, ink
Cutter temperature is 75 DEG C；
(4) labeling, puts and dries in the air at aeration-drying more than 12 hours；
(5) enter stove barbecue, furnace temperature 580 DEG C, roasted and i.e. obtained transparent embossment decoration firing finished product.
Embodiment 3:
Use following methods to treat baked goods (such as glass) to be processed:
(1) with 80820 varnish at product surface printing pattern to be roasted；
(2) transparent embossment powder is uniformly spread on pattern；
(3) treat that embossment powder seals 5088 oil the most after drying, during front cover oil, the pressure between ink knife and forme is transferred to minimum, ink
Cutter temperature is 75c；
(4) labeling, puts and dries in the air at aeration-drying more than 12 hours；
(5) enter stove barbecue, furnace temperature 600 DEG C, roasted and i.e. obtained transparent embossment decoration firing finished product.
Claims (4)
1. a transparent embossment enamel firing process, it is characterised in that: comprise the following steps:
With varnish at product surface printing pattern to be roasted；
Transparent embossment powder is uniformly spread on pattern；
Treat the fully dried front cover oil of embossment powder；
Labeling, puts and dries in the air at aeration-drying more than 12 hours；
Enter stove barbecue, furnace temperature 580 DEG C-600 DEG C, roasted and i.e. obtained transparent embossment decoration firing finished product.
Transparent embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (1), described varnish
It is 80820 varnish.
Transparent embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (3), described oil is
5088 oil.
Transparent embossment enamel firing process the most according to claim 1, it is characterised in that: in described step (3), during front cover oil,
Pressure between ink knife and forme is transferred to minimum, and ink knife temperature is 75 DEG C.