KR101547777B1

KR101547777B1 - Lacquer plate manufacturing method

Info

Publication number: KR101547777B1
Application number: KR1020140173561A
Authority: KR
Inventors: 전종선
Original assignee: 전종선
Priority date: 2014-05-09
Filing date: 2014-12-05
Publication date: 2015-08-26

Abstract

The present invention relates to a manufacturing method of a lacquer plank, which is capable of producing a product lacquered on the surface by attaching the lacquer plank manufactured with the method of the present invention with an adhesive on the desired region, forming a lacquer layer by lacquering to be overlapped on a thin frame plate composed of a thin plank such as aluminum foil with a applying and drying step for 2-6 times, and providing a method for obtaining a lacquer plank by breaking and removing the thin frame plate from the lacquer layer composed of the overlapped lacquer, without forming a lacquer layer by lacquering a product, respectively.

Description

[0001] Lacquer plate manufacturing method [0002]

본 발명은 옻칠 판재의 제조 방법에 관한 것이며 나아가 고서의 표지에 돌출되게 형성된 돌출 문양을 복사하여서 되는 옻칠 판체의 제조 방법에 관한 것이다.The present invention relates to a method for manufacturing a lacquered plate, and more particularly, to a method for manufacturing a lacquered plate by copying a protruding pattern protruding from a cover of a book.

옻칠은 그 미려함에 있어서 모든 다른 칠 재료를 능가한다. 이러한 옻칠은 칠하기의 대상이 되는 물품에 직접 도포하는 방법으로 사용되어 왔다. 따라서 종래의 옻칠 방법은, 칠하기 대상 물품 재료의 특성 상 및 칠하기 대상 물품의 제작 시간과 장소 상의 특성으로 인하여 옻칠의 대상이 되기에 적합하지 아니한 물품에는 사용이 곤란한 결점이 있다.Lacquer exceeds all other plaster materials in its beauty. Such lacquer has been used as a method of applying directly to the article to be painted. Therefore, the conventional lacquer method has drawbacks that it is difficult to use the lacquer for articles that are not suitable for being subject to lacquer due to the characteristics of the article to be painted and the characteristics of the article to be painted at the time and place of production.

즉, 옻칠은 이를 상하전후좌우의 모든 면에 동시에 칠하여 모든 면이 동일한 질감을 가지게 하는 일은 극히 어려우며, 옻칠은 적어도 2회 이상 다수 회 도포와 건조를 반복하여야 할 뿐 아니라 매회 도포 후의 건조 시간도 매회 상온에서 24시간 정도가 걸리게 되니 각각의 물품에 각각 옻칠을 하여 옻칠층을 형성시키는 일은 결코 용이한 일이 아닌 것이다. That is, it is extremely difficult to apply the lacquer to all sides of the top and bottom, right and left sides simultaneously so that all the sides have the same texture. In addition, the lacquer has to repeatedly apply and dry a plurality of times at least twice, It takes about 24 hours at room temperature, so it is not easy to lacquer each of the articles to form a lacquer layer.

이에 본 발명은 옻칠 판재를 제공할 수 있게 함으로서 사용자는 필요로 하는 부위에 본 발명의 방법으로 제조되는 옻칠 판재를 접착제로 부착하기만 함으로서 표면이 옻칠로 되는 물품을 생산할 수 있게 하여야 한다는 과제를 해결하고자 한다.Accordingly, the present invention can provide a lacquered plate, so that a user merely attaches a lacquered plate manufactured by the method of the present invention to a necessary portion with an adhesive, thereby making it possible to produce an article whose surface is lacquered I want to.

또한 본 발명은, 한국의 고서는 그 표지에 꽃모양(능화) 등으로 되는 요철 문양이 형성되어 있는 바, 이와 같은 요철 모양을 복사 등의 방법으로 재현시켜 상기의 옻칠 판재가 상기의 요철 문양을 가지게 하여야 한다는 과제를 해결하고자 한다. In the present invention, a Korean embroidery pattern is formed with a pattern of irregularities such as a flower shape (nitrification) on its cover. Such a pattern of irregularities is reproduced by a method such as copying, so that the above- And to solve this problem.

위와 같은 과제를 해결하기 위하여, 본 발명은, 알루미늄 호일(foil)과 같은 얇은 판재로 되는 얇은형틀판에 2회 내지 6회에 걸치는 도포와 건조단계로, 겹치게 옻칠을 하여 옻칠층을 형성시키고, 겹쳐진 옻칠로 이루어진 옻칠층으로부터 상기 얇은형틀판을 파손 제거함으로서 옻칠 판재를 얻게 하는 방법을 제공한다.In order to solve the above problems, the present invention provides a method for producing a lacquer layer, comprising laminating a thin laminating plate made of a thin plate material such as an aluminum foil by two or six times of application and drying steps, A method for obtaining a lacquered plate by breaking and removing the thin plate from a lacquer layer made of lacquer overlapped.

나아가, 본 발명은 상기 얇은형틀판에 요철문양을 압인 형성시키고, 요철문양이 압인된 얇은형틀판에 옻칠층을 형성시키며, 옻칠층으로부터 얇은형틀판을 파손 제거함으로서 요철문양을 가진 옻칠 판재를 제조하는 방법을 제공하며, 또한 상기 요철 문양이 한국 고서의 꽃모양을 복제하여서 된 것임을 특징으로 하는 옻칠 판재 제조 방법을 제공한다. Further, according to the present invention, a concave-convex pattern is formed on the thin plate-shaped plate, a lacquer layer is formed on the thin plate-shaped plate in which the concave-convex pattern is stamped, and a thin plate- The present invention also provides a method of manufacturing a lacquered plate characterized in that the uneven pattern is formed by replicating the flower shape of Korean paper.

위와 같은 본 발명은, 표면에 옻칠 장식을 하고자 하는 사용자가 본 발명의 방법으로 제조되는 옻칠 판재를 임의의 물품에 접착제로 부착함으로서, 각개 물품에 각각 옻칠 작업을 하지 아니하고서도, 옻칠 표면을 가지는 물품을 제조할 수 있게 되는 효과가 있다.According to the present invention as described above, a user who wants to decorate a lacquer on the surface can attach a lacquered plate manufactured by the method of the present invention to an arbitrary article with an adhesive, so that the article having a lacquer surface Can be produced.

또한 본 발명은, 고서의 표지를 손상시키지 아니하고서도 고서 표지의 문양을 복사하여 장식판으로 사용할 수 있게 되는 효과가 있으며, 나아가, 본 발명의 방법으로 제조된 고서 표지 복사 문양 옻칠 판재는 이를 복사용의 능화형틀판으로 사용하여 고서 문양을 다량 복제할 수 있게 되는 효과가 있다.In addition, the present invention has an effect that it can be used as a decorative plate by copying the pattern of the old book cover without damaging the cover of the old book, and further, the old book cover copy lacquer plate manufactured by the method of the present invention is used for copying It is possible to replicate a large number of ancient calligraphy patterns by using it as an active form frame.

본 발명자는 옻칠 판재를 얻기 위하여 평평한 형틀판에 옻칠을 하고 건조하는 과정을 수회 반복하여 형틀판에 옻칠층을 형성시킨 후, 옻칠층을 분리하였던 바, 옻칠층이 극히 쉽게 찢어져 형틀판으로부터의 분리가 불가능하였다. 그리하여 형틀판에 이형제를 도포하고 옻칠을 하였더니 이제는 옻칠 상태가 평활하지 못하게 되는 결점이 있었다.In order to obtain a lacquered plate, the present inventor repeatedly lacquered and dried the flat plate to form a lacquer layer on the plate, and then separated the lacquer layer. The lacquer layer was extremely easily torn and separated from the plate Was impossible. Thus, when the release agent was applied to the plate and the lacquer was applied, there was a drawback that the lacquer state was not smooth.

이에 본 발명자는, 쉽게 구부러지거나 쉽게 찢어지는 얇은 판체로 얇은형틀판을 형성시키고, 형틀판으로부터 옻칠층을 박리하는 것이 아니라 옻칠층으로부터 얇은형틀판을 박리하는 방법으로 박리 방법을 변경하였던 바, 옻칠층의 파손 없이 옻칠층으로부터 얇은형틀판을 분리하여 양질의 옻칠 판체를 얻을 수 있음을 알았다.The inventors of the present invention have changed the peeling method by forming a thin plate with a thin plate easily bent or easily torn and peeling the thin plate from the lacquer layer instead of peeling the lacquer layer from the plate. It was found that a thin lacquer plate can be obtained by separating the thin plate from the lacquer layer without damaging the layer.

상기 얇은형틀판은 곡물풀(찹쌀풀)이나 합성수지필름 또는 알루미늄 호일(foil) 중에서 선택되는 하나로 된 것일 수 있다.The thin flat plate may be one selected from a grain paste (glutinous rice paste), a synthetic resin film or an aluminum foil.

요철 문양을 가지는 얇은형틀판은 알루미늄 호일로 형성되는 것이 가장 적합하다. 요철문양을 형성시킴에 있어서, 알루미늄 호일은 압인의 방법으로 극히 용이하게 문양을 형성시킬 수 있으며, 알루미늄 호일의 표면에 옻칠을 하면 옻칠이 고르게 또 쉽게 도포될 뿐 아니라, 건조 형성된 옻칠판으로부터 옻칠 판재의 손상 없이 알루미늄으로 된 얇은형틀판을 뜯어 내어 용이하게 분리할 수 있기 때문이다. It is most preferable that the thin plate having the irregular pattern is formed of aluminum foil. In forming the uneven pattern, the aluminum foil can extremely easily form the pattern by the method of stamping, and when the lacquer is applied to the surface of the aluminum foil, the lacquer is uniformly and easily applied, and the lacquered plate The thin flat plate made of aluminum can be easily peeled off without being damaged.

찹쌀풀과 같은 곡물풀로 얇은형틀판을 형성시킨 경우에는 물에 장시간 침지하여 얇은형틀판을 제거할 수 있다. When a thin template plate is formed of a grain paste such as a glutinous rice paste, the thin template plate can be removed by dipping in water for a long time.

이와 같은 본 발명을 상세히 설명하면 다음과 같다. Hereinafter, the present invention will be described in detail.

본 발명은, According to the present invention,

얇은형틀판 마련단계와,A thin flat plate preparing step,

테레핀유에 희석된 옻칠 마련단계와, A lacquer preparation step diluted in terpine oil,

상기 얇은형틀판에 상기 옻칠을 도포와 건조를 반복하면서 2~6회 바람직하게는 3~5회 도포하여 옻칠판을 형성시키는 옻칠판 형성 단계와, Forming a lacquer plate by repeating application and drying of the lacquer on the thin plate with a coating of 2 to 6 times, preferably 3 to 5 times,

최종으로 도포된 옻칠이 건조되어 옻칠판의 형성이 완료된 후 옻칠판으로부터 얇은형틀판을 제거하여 박리하는 얇은형틀판제거단계로 구성됨을 특징으로 하는 옻칠 판체 제조 방법을 제공한다. And removing the thin plate from the lacquer plate after the lacquer is dried to complete the formation of the lacquered plate, and removing the thin plate from the lacquer plate to remove the thin lacquer plate.

상기 얇은형틀판마련단계에 있어서의 얇은형틀판은 위에서 본 바와 같이 알루미늄 호일로 된 것임이 바람직하다. It is preferable that the thin flat plate in the thin flat plate preparing step is made of aluminum foil as shown above.

상기 얇은형틀판 마련 단계는, 상기 얇은형틀판에 요철문양을 압인 형성시키는 요철 문양 형성단계를 포함하는 것이 바람직하며, 요철문양 형성단계는 고서 표지 표면을 평판 위에 올려놓고 표지 뒷면 요철이 있는 부분에 알루미늄 호일을 대고 압인하여 문양이 압인된 알루미늄 호일 판체로 되는 얇은형틀판을 얻는 단계인 것이 바람직하다. Preferably, the step of forming the thin plate includes a step of forming a concave-convex pattern on the concave and convex patterns on the thin plate. In the step of forming the concave and the convex pattern, the surface of the paper is placed on a flat plate, It is preferable that the aluminum foil is pressed and pressed to obtain a thin plate having an embossed aluminum foil plate.

또한, 본 발명은, 상기 옻칠 판체를, 나무판, 합성수지판, 포지 또는 판지(두꺼운 종이)와 같은 바닥판체에 부착하여 보강된 옻칠 판체를 얻는 보강 옻칠 판체 제조 단계를 더 포함할 수 있다. The present invention may further include a step of preparing a reinforced lacquer plate by attaching the lacquer plate to a bottom plate such as a wooden plate, a synthetic resin plate, a forge or a cardboard (thick paper) to obtain a reinforced lacquered plate.

상기 얇은형틀판 마련 단계에서 행하는 압인 작업은 알루미늄 호일이나 고서 표지의 돌출 문양이 훼손되지 않아야 한다. 따라서, 미세한 요철에 따라 압인되게 하는 누름기구, 예컨대 얇은 합성수지 판체로 된 풍선과 같은 누름기구로 알루미늄 호일 표면을 눌러서 알루미늄 호일이 오목하게 형성된 문양 홈 속으로 눌리워 들어가게 하는 것이 바람직하다. 그러나 이러한 누름기구에 갈음하여 알루미늄 호일 위에 맨 발로 올라가 체중으로 압인하는 것이 더욱 바람직하다. The stamping operation performed in the step of forming the thin plate must not damage the protruding pattern of the aluminum foil or the book mark. Therefore, it is preferable to press the surface of the aluminum foil with a pressing mechanism such as a balloon, which is made of a thin synthetic resin plate, so that the aluminum foil is pressed into the recessed concave groove. However, it is more preferable that the pushing mechanism is replaced with a weight on the bare foot on the aluminum foil.

압인된 얇은형틀판에 도포하기 위한 옷칠은, 옻나무에서 채취되는 수액으로, 가공되지 않은 상태일 때 생칠(生漆)이라고 부르며, 표면발색에 따라 주합(朱合), 주칠(朱漆), 흑칠(黑漆) 등으로 불리우고, 주로 목가구나 그릇 등에 도포되어 자연친화적이고 독성을 중화시키고 내구성을 강화시켜주는 재료로 인식되어 왔다. 본 발명에 있어서의 옻칠 마련 단계는 정제옻 100부량(중량비)에 테레핀유 30~100부량(중량비)을 혼합 교반하여 도포할 희석된 옻칠을 마련하는 단계인 것이 바람직하다. The lacquer to be applied to the stamped thin plate is a sap collected from the lacquer tree. It is called raw lacquer when it is not processed. It is made of red lacquer, black lacquer, black lacquer, Lacquer), and it has been recognized as a natural-friendly, neutralizing toxic substance and strengthening durability, mainly applied to a wooden box or a vessel. The lacquer preparation step in the present invention is preferably a step of providing diluted lacquer to be applied by mixing and stirring 30 to 100 parts by weight (weight ratio) of terfenafine to 100 parts by weight of purified lacquer (weight ratio).

고서의 문양이 압인된 상기 얇은형틀판에 옻칠을 함에 있어서는 고서의 표지에 형성된 요홈의 깊이에 따라 옻칠을 도포하는 횟수가 정해진다. 즉, 옻칠은 칠해진 표면이 상술한 바와 같이 평평해 질 때 까지 행하는 것이 바람직하다. When lacquering the thin plate with the embossed pattern, the number of times the lacquer is applied depends on the depth of the groove formed on the cover of the book. That is, it is preferable that the lacquer is performed until the painted surface is flattened as described above.

고서 표지에 형성된 홈부의 깊이는 1mm 이하로서 각 홈은 그 깊이의 차이가 크지 아니하다. 따라서 옻칠의 두께가 두꺼워지면 문양이 잘 보이지 아니하며, 표면이 평평하지 아니하면 상기와 같은 바닥판체에 부착된 문양 옻칠 판재의 외향 돌출부가 눌리워져 손상될 수 있다. 따라서 홈의 깊이에 따라 도포와 건조를 반복하면서 3~5회 도포하여 문양 옻칠판의 표면이 평평하게 하는 것이 바람직하다. 옻칠의 도포 후 차기 도포를 위한 건조 시간은 기온이 섭씨 25도이고 습도가 80%인 경우(여름철) 24시간의 건조시간이 필요하다. The depth of the grooves formed on the book cover is 1 mm or less, and the difference in the depth of each groove is not large. Therefore, if the thickness of the lacquer is increased, the pattern is not easily seen. If the surface is not flat, the outward protrusion of the pattern lacquer plate attached to the bottom plate body may be crushed and damaged. Therefore, it is preferable that the surface of the patterned lacquer plate is flattened by applying 3 to 5 times while repeating application and drying according to the depth of the groove. Drying time for next application after application of lacquer requires 24 hours of drying time when the temperature is 25 ° C and humidity is 80% (in summer).

최종으로 도포된 옻칠이 건조되어 문양 옻칠판의 형성이 완료된 후 옻칠판으로부터 얇은형틀판을 떼어내는 알루미늄판체로부터 옻칠판을 떼어내는 얇은형틀판제거단계에서는, 유리판에 물을 뿌리고, 그 위에 문양 옻칠판을 접착시키고 알루미늄 호일을 찢으면서 떼어 내는 것이 바람직하다. 옻칠판이나 알루미늄 호일은 강도가 약하므로 옻칠판으로부터 알루미늄호일을 떼어내는 과정에서 옻칠판이 훼손되는 일이 흔할 수 있기 때문이다. In the step of removing the lacquer plate from the aluminum plate which removes the thin plate from the lacquer plate after the finally coated lacquer is dried to complete the formation of the pattern lacquer plate, water is sprayed on the glass plate, It is preferable to bond the lacquered plate and tear off the aluminum foil. Because lacquer plates and aluminum foil are weak in strength, it is common that lacquer plates are damaged during peeling of aluminum foil from lacquer plates.

문양 옻칠판을 바닥판체에 부착하여 소기의 고서 표지 문양 복사 판체를 얻는 보강 옻칠 판체 제조단계에서, 바닥판체에 옻칠판을 부착하는 공정은 바닥판체에 옻칠을 하고 칠해진 옻칠 위에 문양 옻칠판을 올려놓고 롤러로 눌러 문양 옻칠판과 바닥판체 사이의 공기를 빼어 내는 공정으로 되는 것이 바람직하다. The process of attaching the lacquer plate to the bottom plate in the step of preparing the reinforced lacquer plate by attaching the pattern lacquer plate to the bottom plate is to lacquer the bottom plate and place the pattern lacquer on the lacquered lacquer It is preferable to be a step of extracting air between the patterned lacquered plate and the bottom plate by pressing with a roller.

이와 같은 본 발명의 방법으로 제조된 고서 표지 문양 복사 판체는 문양 선이 선명하게 표출되어 장식품으로서의 효과가 크며, 다른 얇은형틀판 제조를 위한 성형틀인 능화판으로의 사용 또한 가능하게 되는 효과가 있는 것이다. The present invention provides a method for producing a laminated plate for an embossed plate, which is capable of using the laminated plate as a mold for manufacturing a thin plate, will be.

Claims

A thin flat plate preparing step,
A lacquer preparation step diluted in terpine oil,
A lacquer plate forming step of forming a lacquered plate by applying the lacquer to the thin flat plate twice or six times while repeating application and drying,
And a thin plate removing step of removing the thin plate from the lacquer plate after the lacquer is dried to complete the formation of the lacquered plate,

The thin flat plate is made of aluminum foil,

The thin flat plate preparing step
And a step of forming a concave-convex pattern to obtain a thin plate having a pattern stamped by pressing an aluminum foil against a portion of the back surface of the cover with the aluminum foil placed on the flat plate.

delete

The method of manufacturing a lacquer plate according to claim 1, further comprising a step of laminating a lacquer plate from which a thin flat plate is removed, and laminating the lacquer plate on the bottom plate, and laminating the lacquer on the lacquer.