CN102653210A - Wood and clay embossed decorative board and manufacturing process thereof - Google Patents
Wood and clay embossed decorative board and manufacturing process thereof Download PDFInfo
- Publication number
- CN102653210A CN102653210A CN2012101031898A CN201210103189A CN102653210A CN 102653210 A CN102653210 A CN 102653210A CN 2012101031898 A CN2012101031898 A CN 2012101031898A CN 201210103189 A CN201210103189 A CN 201210103189A CN 102653210 A CN102653210 A CN 102653210A
- Authority
- CN
- China
- Prior art keywords
- plate
- wood
- convex
- clay
- relief sculpture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wood and clay embossed decorative board and a manufacturing process thereof. The manufacturing process comprises the following steps of: (1) carrying out cleaning treatment such as surface dedusting on a substrate of the wood and clay embossed decorative board; (2) paving wood and clay in a certain thickness on the surface of the substrate treated in the step (1); (3) rolling wood and clay on one surface of the substrate undergoing the step (2) under a certain temperature and pressure with a roller with various carved convex-concave space patterns so that the surface of the substrate is provided with convex-concave space patterns corresponding to the roller; and (4) finally carrying out painting, coloring and dry molding, thus preparing the wood and clay embossed decorative board. The wood and clay embossed decorative board has a simple processing process, high production efficiency and low cost, and compared with the prior art which only uses logs with limited varieties, the wood and clay embossed decorative board saves wood, is beneficial to environmental protection and does not cause secondary pollution.
Description
Technical field
The present invention relates to artificial decoration plate field, especially belong to a kind of wooden mud decoration plate with relief sculpture and manufacturing process thereof.
Background technology
Present raised table mainly is that the surface has scraggly wooden cubic texture pattern, and mainly is to utilize soft with the hard different wood grain of the plank natural quality in surface, mills brush, polishing on the plank surface through wire roller; Touch soft wooden of surface texturisation, make the harder wood grain of quality protruding, make original even curface produce stereo decoration panel according to the convex-concave shape of wood grain; Said method can only obtain the imitative body effect of standing motionless; And processing technology is complicated, and production efficiency is low, and cost is high; And receive the restriction of timber variety, do not utilize environmental protection.
Summary of the invention
The objective of the invention is; In order to overcome the shortcomings and deficiencies of prior art, provide a kind of log that do not need not only can manufacture imitative wood effect, and can process the stereoeffect of various convex-concave patterns as required; And processing technology is simple; Production efficiency is high, and stereoeffect is good, the wooden mud decoration plate with relief sculpture and the manufacturing process thereof of low cost of manufacture.
The object of the invention can reach through taking following technical scheme:
A kind of manufacturing process of wooden mud decoration plate with relief sculpture is characterised in that may further comprise the steps:
(1) backing material plate with wooden mud decoration plate with relief sculpture carries out clean such as dedusting;
(2) a kind of mixture that is used to make wooden mud decoration plate with relief sculpture of allotment, this mixture is composed of the following components by weight percentage: timber is milled into the wood powder of powdery: 40-70%; Resin: 10-25%; Vegetable oil: 5-20%; Industrial alcohol: 5-10%; Calcium carbonate: surplus.
(3) mixture that certain thickness step (2) modulation forms is gone up in the backing material plate one surface tiling that will carry out after step (1) is handled;
(4) will carry out backing material plate one lip-deep mixture after the step (3) is rolled into the surface through the roller that is carved with various Convex and concave stereoscopic patterns and has with pair of rollers and answer the Convex and concave stereoscopic pattern under certain pressure;
(5) the wooden mud plate spraying NC paint bottoming with Convex and concave stereoscopic pattern that will carry out after the step (4) is changed colour;
(6) dry processing and the transparent UV glue of roller coating more once;
(7) then the UV transfer film of transfer printing different color and solidify after, make that NC prime coat and UV transfer film combine on the plate face Convex and concave stereoscopic pattern salient point position;
(8) again after the facial mask rolling with transfer film, plate face Convex and concave stereoscopic pattern forms the color that there is the NC prime coat concave point position, and there is the color of transfer printing rete the salient point position, forms the color stereovision of whole plate complexion;
(9) last roller coating UV dull finishing coat baffle face damage resistant is difficult for wear surface.
The wooden mud decoration plate with relief sculpture that adopts above-mentioned technology to be made; Comprise the base material flaggy, have the mixture layer and the skin of paint of Convex and concave stereoscopic pattern; On the backing material plate laminar surface, described skin of paint comprises and is sprayed on UV transfer printing rete with transparent UV glue-line on prime coat of NC paint prime coat, roller coating on the Convex and concave stereoscopic pattern wood mud layer, the transparent UV glue-line of protruding space pattern transfer printing different color and the UV dull finishing coat layer that plays the baffle face described mixture layer in the roller roll extrusion through being carved with various Convex and concave stereoscopic patterns under high temperature, the high pressure.
Compared with prior art, the present invention has the following advantages:
(1) owing to this employing environmental protection mixture layer, its plastic performance is good, and convenient formation therefore can be processed into various Convex and concave stereoscopic patterns as required, and processing technology is simple, and production efficiency is high.
(2) demolding performace is good, is difficult for sticking on rolling wheel;
(3) be prone to drying, only need about 30 minutes drying time, can enhance productivity greatly like this;
(4) flexility is good, and is not easy to crack, can carry very big impulsive force;
(5) as substrate, therefore, cost is low, and can only compare with the limited log of kind with prior art, has practiced thrift timber, helps environmental protection with high-density plate in invention.
(6) the present invention's wood mud decoration plate with relief sculpture is used for indoor furniture, door, hall's finishing, KTV finishing, wall decoration, and is not only attractive in appearance, and do not have any harmful material, is the decorative panel of a kind of health, environmental protection therefore, reduces the secondary pollution of interior decoration.
Description of drawings
Fig. 1 is a structural representation of the present invention;
The specific embodiment
Describe in detail below in conjunction with the accompanying drawing specific embodiments of the invention.
A kind of manufacturing process of wooden mud decoration plate with relief sculpture may further comprise the steps:
(1) backing material plate with wooden mud decoration plate with relief sculpture carries out clean such as surperficial dedusting;
(2) a kind of mixture that is used to make wooden mud decoration plate with relief sculpture of allotment, this mixture is composed of the following components by weight percentage: timber is milled into the wood powder of powdery: 40-70%; Resin: 10-25%; Vegetable oil: 5-20%; Industrial alcohol: 5-10%; Calcium carbonate: surplus.
(3) the surperficial above-mentioned steps (2) that goes up 1-2mm thickness that tiles of backing material plate that will carry out after step (1) is handled is allocated the mixture that forms;
The backing material plate wood mud that (4) will carry out after the step (3) is that 60 deg.c and pressure are under 2 tons/square metre in temperature, is rolled into the surface through the roller that is carved with various Convex and concave stereoscopic patterns and has with pair of rollers and answer the Convex and concave stereoscopic pattern;
(5) the wooden mud plate spraying NC paint bottoming with Convex and concave stereoscopic pattern that will carry out after the step (4) is changed colour;
(6) again temperature 60-100 degree centigrade carry out 4-20 minute baking drying dry handle and the transparent UV glue of roller coating once;
(7) then the UV transfer film of transfer printing different color and use 8-14 kilowatt hour UV ultraviolet lamp to solidify after, make that NC prime coat and UV transfer film combine on the plate face Convex and concave stereoscopic pattern salient point position;
(8) again after the facial mask rolling with transfer film, plate face Convex and concave stereoscopic pattern forms the color that there is the NC prime coat concave point position, and there is the color of transfer printing rete the salient point position, forms the color stereovision of whole plate complexion;
(9) last roller coating 20 degree UV dull finishing coat baffle face damage resistants are difficult for wear surface, form product at last.
Wooden mud decoration plate with relief sculpture through above-mentioned technology is processed comprises base material flaggy 1, has the mixture layer 2 and the skin of paint 3 of Convex and concave stereoscopic pattern, and described mixture is composed of the following components by weight percentage: timber is milled into the wood powder of powdery: 40-70%; Resin: 10-25%; Vegetable oil: 5-20%; Industrial alcohol: 5-10%; Calcium carbonate: surplus.Layer 2 of the said mixture at a temperature of 60 ° C, pressure of 2 tons / square punch through the various dimensional pattern engraved roller rolling on the surface of the base sheet layer 1, layer 2 is a mixture of three-dimensional design pattern roll punch After compression molding, spray paint layer 3-1 NC bottoming change color, and then at a temperature of 80 degrees Celsius for about 6 minutes after drying baking, roll UV transparent layer 3-2 once, then transfer different colors UV transfer film Layer 3-3 with 12 kilowatts Kou UV ultraviolet light curing, making three-dimensional decorative pattern punch bump bit NC primer layer 3-1 and 3-3 combined with UV coating transfer, then the transfer film mask after winding , forming a concave pattern plate surface point the NC layer 3-1 colors, bump-bit transfer layer 3-3 colors, form the entire plate surface color layering relatively strong, the last roll of 20 degrees UV matte surface 3-4 paint protection plate surface scratch resistance, easy to wear surface, and finally the formation of product.
Through the wooden mud decoration plate with relief sculpture that above-mentioned technology is processed, its plastic performance is good, and demolding performace is good, strong adhesion, and convenient formation therefore can be processed into various Convex and concave stereoscopic patterns as required, and processing technology is simple, and production efficiency is high; The present invention's wood mud decoration plate with relief sculpture is used for interior decoration, and is not only attractive in appearance, and do not have any harmful material, is the decorative panel of a kind of health, environmental protection therefore; As substrate, therefore, cost is low with high-density plate, and can only compare with the limited log of kind with prior art, has practiced thrift timber, helps environmental protection.
Above disclosedly be merely preferred embodiment of the present invention, can not limit the present invention's interest field certainly with this, the equivalent variations of therefore doing according to claim of the present invention still belongs to the scope that the present invention is contained.
Claims (6)
1. the manufacturing process of a wooden mud decoration plate with relief sculpture is characterised in that may further comprise the steps:
(1) backing material plate with wooden mud decoration plate with relief sculpture carries out clean such as dedusting;
(2) a kind of mixture that is used to make wooden mud decoration plate with relief sculpture of allotment, this mixture is composed of the following components by weight percentage: timber is milled into the wood powder of powdery: 40-70%; Resin: 10-25%; Vegetable oil: 5-20%; Industrial alcohol: 5-10%; Calcium carbonate: surplus;
(3) mixture that certain thickness step (2) modulation forms is gone up in the backing material plate one surface tiling that will carry out after step (1) is handled;
(4) will carry out backing material plate one lip-deep mixture after the step (3) is rolled into the surface through the roller that is carved with various Convex and concave stereoscopic patterns and has with pair of rollers and answer the Convex and concave stereoscopic pattern under certain pressure;
(5) the wooden mud plate spraying NC paint bottoming with Convex and concave stereoscopic pattern that will carry out after the step (4) is changed colour;
(6) dry processing and the transparent UV glue of roller coating more once;
(7) then the UV transfer film of transfer printing different color and solidify after, make that NC prime coat and UV transfer film combine on the plate face Convex and concave stereoscopic pattern salient point position;
(8) again after the facial mask rolling with transfer film, plate face Convex and concave stereoscopic pattern forms the color that there is the NC prime coat concave point position, and there is the color of transfer printing rete the salient point position, forms the color stereovision of whole plate complexion;
(9) last roller coating UV dull finishing coat baffle face damage resistant is difficult for wear surface.
2. the manufacturing process of wooden mud decoration plate with relief sculpture as claimed in claim 1; It is characterized in that: said step (6) is under temperature 60-100 degree centigrade, to carry out 4-20 minute baking drying; Described step (7) is to use 8-14 kilowatt hour UV ultraviolet lamp to solidify, and said step (9) is to be coated with 20 degree UV dull finishing coats.
3. the manufacturing process of wooden mud decoration plate with relief sculpture as claimed in claim 1 is characterized in that: the backing material plate of said wooden mud decoration plate with relief sculpture is a wood-based plate.
4. the manufacturing process of wooden mud decoration plate with relief sculpture as claimed in claim 3 is characterized in that: the artificial backing material plate of said wooden mud decoration plate with relief sculpture is a high-density plate.
5. the manufacturing process of wooden mud decoration plate with relief sculpture as claimed in claim 1 is characterized in that: the pressure in the described step (4) be the 1-3 ton/square metre pressure under carry out roll extrusion.
6. one kind adds the wooden mud decoration plate with relief sculpture that cover process is made like the described wooden mud decoration plate with relief sculpture of claim 1-5; It is characterized in that: comprise the base material flaggy, have the mixture layer and the skin of paint of Convex and concave stereoscopic pattern; On the backing material plate laminar surface, described skin of paint comprises and is sprayed on UV transfer printing rete with transparent UV glue-line on prime coat of NC paint prime coat, roller coating on the Convex and concave stereoscopic pattern wood mud layer, the transparent UV glue-line of protruding space pattern transfer printing different color and the UV dull finishing coat layer that plays the baffle face described mixture layer in the roller roll extrusion through being carved with various Convex and concave stereoscopic patterns under high temperature, the high pressure.