KR20120078375A - Method for embossing on sheet and surface material embossed - Google Patents

Method for embossing on sheet and surface material embossed Download PDF

Info

Publication number
KR20120078375A
KR20120078375A KR1020100140658A KR20100140658A KR20120078375A KR 20120078375 A KR20120078375 A KR 20120078375A KR 1020100140658 A KR1020100140658 A KR 1020100140658A KR 20100140658 A KR20100140658 A KR 20100140658A KR 20120078375 A KR20120078375 A KR 20120078375A
Authority
KR
South Korea
Prior art keywords
coating
agent
sheet
embossing
coating layer
Prior art date
Application number
KR1020100140658A
Other languages
Korean (ko)
Other versions
KR101223099B1 (en
Inventor
신동원
손기용
이장섭
Original Assignee
주식회사 한샘
엔에프씨 주식회사
(주)원진우드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 한샘, 엔에프씨 주식회사, (주)원진우드 filed Critical 주식회사 한샘
Priority to KR1020100140658A priority Critical patent/KR101223099B1/en
Publication of KR20120078375A publication Critical patent/KR20120078375A/en
Application granted granted Critical
Publication of KR101223099B1 publication Critical patent/KR101223099B1/en

Abstract

PURPOSE: An embossing forming method on sheets is provided to improve productivity by facilitating formation of embossing patterns. CONSTITUTION: An embossing forming method on sheets comprises the following steps: providing a sheet(10); printing patterns on the provided sheet; forming a coating layer(30) by spreading a coating agent on the sheet; drying the coated sheet; and reeling the dried sheet. In the coating layer, embossing(33) is formed according to viscosity of the coating agent. A coating stage comprises the following steps: forming a flat first coating layer by using a first coating agent; temporarily drying the first coating layer; and forming a second coating layer(32) in which embossing is formed on top of the first coating layer by using a second coating agent.

Description

시트에 엠보싱을 형성하는 방법 및 엠보싱이 형성된 표면재 { METHOD FOR EMBOSSING ON SHEET AND SURFACE MATERIAL EMBOSSED }METHOD FOR EMBOSSING ON SHEET AND SURFACE MATERIAL EMBOSSED}

본 발명은 시트에 엠보싱을 형성하는 방법 및 엠보싱이 형성된 표면재에 관한 것으로서, 특히 가압방법이 아닌 코팅제의 점도를 이용하여 엠보싱을 형성함으로써, 표면재의 내마모성 및 내스크래치성 등을 향상시킬 수 있는 시트에 엠보싱을 형성하는 방법 및 엠보싱이 형성된 표면재에 관한 것이다.The present invention relates to a method of forming an embossing on the sheet and to a surface material on which the embossing is formed. In particular, the present invention relates to a sheet capable of improving wear resistance and scratch resistance of the surface material by forming an embossing using a viscosity of a coating agent rather than a pressing method. A method of forming embossing and a surface material on which embossing is formed.

우리 주변에서 생활용품으로 사용되는 각종 가구들은 전통적으로 원목을 사용하여 주로 제작되어 왔다. Various furniture used as daily necessities around us have traditionally been mainly made of solid wood.

원목 가구는 견고하고, 원목 고유의 무늬를 그대로 살릴 수 있는 장점은 있으나, 장기간 사용하면 가구의 형태가 뒤틀리거나 표면에 균열이 생기는 등의 단점이 있다. Solid wood furniture has the advantage of being solid and keeping the original pattern of wood as it is, but there are disadvantages such as distorting the shape of the furniture or cracking the surface when used for a long time.

이러한 원목 가구의 단점을 보완하기 위하여 최근에는 인조합판이 가구용 재료로 널리 사용되고 있다.In order to make up for the shortcomings of such wooden furniture, in recent years, combined plates are widely used as furniture materials.

인조합판은 소위 베니어합판과, 집성목재, 인조목재 등으로 분류할 수 있다.The composite board can be classified into so-called veneer plywood, aggregate wood, artificial wood, and the like.

이들 중 인조목재는 원목을 분쇄한 목재 파편에다 아교를 섞어서 중간 정도의 밀도를 갖도록 평판 형태로 압착시킨 중밀도 섬유판(MDF; medium density fiberboard)와, 목재 등 섬유질 소편(particle)에다 합성수지 접착제를 스프레이로 도포하여 고밀도로 열압 성형 시킨 파티클 보드(particle board)로 분류된다. Among them, artificial wood is sprayed with synthetic resin adhesives on medium-density fiberboard (MDF), which is compressed in a flat plate form to have a medium density by mixing glue with wood crushed wood fragments, and a medium density. It is classified into particle boards which are coated with a high pressure thermoformed.

이러한 인조합판은 평면 내에서 강도나 수축 또는 팽창력이 균일하고, 균열이 잘 생기지 않으며, 가공이 용이한 등의 장점이 있으나, 표면 무늬가 단조롭고, 내수성이 약한 등의 단점이 있다.Such phosphorescent plate has advantages such as uniform strength, shrinkage or expansion force in a plane, hardly cracking, and easy processing, but has a disadvantage of monotonous surface pattern and weak water resistance.

이와 같이 목재가구들은 여러 가지 원인으로 인하여 표면을 재가공할 필요성이 있고, 이에 따라 목재가구의 표면에 다양한 색상의 도료를 도포하거나, 또는 여러 무늬가 인쇄된 합성수지 표면재를 부착하는 등 여러 가지 방법들이 개발되어 있다.As such, wooden furniture needs to be reworked for various reasons. Therefore, various methods have been developed, such as applying various colors of paint to the surface of wooden furniture, or attaching synthetic resin surface materials printed with various patterns. It is.

그 중에서 최근에 제안된 한가지 방법을 예로 들어 보면, 국내 특허공개 제2005-91690호(공개일자; 2005.09.15.)에서는 '목재 표면에 천연무늬를 형성하는 방법'이 소재되어 있다. 상기 특허방법은 표면에 무늬를 형성할 목재 생활용품을 준비하는 단계와, 상기 목재 생활용품의 표면상에 천연무늬를 형성하기 위한 천연재료를 준비하는 단계와, 준비된 천연재료를 상기 목재 생활용품의 표면상에 위치시키는 단계와, 그 위에다 합성수지 필름을 소정의 두께로 도포하는 단계와, 상기 합성수지 필름이 도포 된 생활용품을 가압하는 단계로 이루어지는 것을 특징으로 한다.For example, one method recently proposed is Korean Patent Publication No. 2005-91690 (published date: September 15, 2005), which describes a method of forming a natural pattern on a surface of wood. The patent method comprises the steps of preparing a wooden dairy product to form a pattern on the surface, preparing a natural material for forming a natural pattern on the surface of the wooden dairy product, and the prepared natural material of the wooden household product Positioning on a surface, applying a synthetic film on the surface to a predetermined thickness, and pressing the household article to which the synthetic resin film is applied.

그러나 이러한 종래의 방법들은 목재가구의 표면에 형성되는 무늬가 전체적으로 평면구조이기 때문에 그 질감을 표현하는데 한계가 있고, 특히 상기 특허방법의 경우에는 가구 표면에 각종 꽃잎이나 나뭇잎과 같은 천연재료를 부착하기 때문에 오랜 시간이 경과 하면, 이들 천연재료들이 가구표면에서 이탈될 가능성이 매우 높다는 문제점이 있었다.However, these conventional methods have a limitation in expressing the texture because the pattern formed on the surface of the wooden furniture as a whole is a flat structure, in particular, in the case of the patent method to attach natural materials such as petals and leaves to the furniture surface Therefore, after a long time, there is a problem that these natural materials are very likely to fall off the furniture surface.

또한, 종래에는 이와 같은 문제점을 해결하기 위해 엠보싱을 형성하는 경우도 있었으나, 이는 모두 합성수지필름을 물리적으로 가압하여 엠보싱을 형성하는 것으로써, 종이시트을 사용하는 경우에는 위와 같은 엠보싱을 형성할 수가 없었다.In addition, in order to solve such problems in the prior art, there was a case of forming embossing, all of which is embossed by physically pressing the synthetic resin film, when using a paper sheet could not form the above embossing.

본 발명은 종이 등을 포함하는 시트에 가압방식이 아닌 코팅제의 점도를 이용하여 용이하게 엠보싱을 형성하고, 이로 인해 내마모성 및 내스크래치성을 향상시킬 수 있는 시트에 엠보싱을 형성하는 방법 및 엠보싱이 형성된 표면재를 제공하는데 그 목적이 있다.The present invention is easily embossed by using a viscosity of the coating agent in a sheet including a paper, etc., thereby forming a method of embossing on the sheet that can improve the wear resistance and scratch resistance and embossing is formed The purpose is to provide a surface material.

상기 목적을 달성하기 위하여 본 발명의 시트에 엠보싱을 형성하는 방법은, 시트을 공급하는 공급단계와; 공급된 시트에 문양을 인쇄하는 인쇄단계와; 문양이 인쇄된 시트에 코팅제를 도포하여 코팅층을 형성하는 코팅단계와; 코팅된 시트을 건조하는 건조단계와; 건조된 시트을 권취하는 권취단계로 이루어지되, 상기 코팅단계에서는 문양이 인쇄된 시트에 상기 코팅제의 점도에 의해 엠보싱이 형성된 코팅층을 형성하는 것을 특징으로 한다.In order to achieve the above object, a method of forming an embossing on a sheet of the present invention includes a supplying step of supplying a sheet; A printing step of printing a pattern on the supplied sheet; A coating step of forming a coating layer by applying a coating agent to the printed sheet; A drying step of drying the coated sheet; It is made of a winding step of winding the dried sheet, the coating step is characterized in that for forming the coating layer embossed by the viscosity of the coating agent on the sheet printed pattern.

상기 코팅단계는, 제1코팅제를 이용하여 평평한 제1코팅층을 형성하는 제1코팅단계와; 상기 제1코팅층을 가건조하는 가건조단계와; 가건조된 상기 제1코팅층의 상부에 제2코팅제를 이용하여 엠보싱이 형성된 제2코팅층을 형성하는 제2코팅단계로 이루어진다.The coating step may include a first coating step of forming a flat first coating layer using a first coating agent; A temporary drying step of temporarily drying the first coating layer; And a second coating step of forming a second coating layer on which the embossing is formed by using a second coating agent on the temporarily dried first coating layer.

상기 제2코팅제의 고형분의 중량%는 상기 제1코팅제의 고형분의 중량%보다 높아 상기 제2코팅제의 점도가 상기 제1코팅제의 점도보다 높다.The weight percent of the solids of the second coating agent is higher than the weight percent of the solids of the first coating agent, the viscosity of the second coating agent is higher than the viscosity of the first coating agent.

상기 제1코팅제는 고형분이 25 ~ 40 중량%를 갖는 폴리에스테르 오버코팅제, 폴리우레탄 오버코팅제, 아크릴폴리오 오버코팅제 및 에폭시 오버코팅제 중 어느 하나로 이루어지고, 상기 제2코팅제는 고형분이 50 ~ 70 중량%를 갖는 폴리에스테르 오버코팅제, 폴리우레탄 오버코팅제, 아크릴폴리오 오버코팅제 및 에폭시 오버코팅제 중 어느 하나로 이루어지며, 상기 제1코팅제와 제2코팅제의 용제는 톨루엔, MEK(Methyl Ethyl Ketone), 아세톤, 이소프로필알코올(IPA), EA(Ethyl Acetate) 중 어느 하나이다.The first coating agent is made of any one of a polyester overcoat agent having a solid content of 25 to 40% by weight, a polyurethane overcoat agent, an acrylic overcoat agent and an epoxy overcoat agent, and the second coating agent has a solid content of 50 to 70 wt% It is made of any one of a polyester overcoat agent, a polyurethane overcoat agent, an acrylic overcoat agent and an epoxy overcoat agent, the solvent of the first coating agent and the second coating agent toluene, MEK (Methyl Ethyl Ketone), acetone, isopropyl Alcohol (IPA) or EA (Ethyl Acetate).

상기 제1코팅단계에서는 제1롤러를 이용하여 제1코팅층을 형성하고, 상기 제2코팅단계에서는 제2롤러를 이용하여 제2코팅층을 형성한다.In the first coating step, a first coating layer is formed using a first roller, and in the second coating step, a second coating layer is formed using a second roller.

상기 인쇄단계에서는 목무늬를 인쇄하고, 상기 제1코팅제는 투명한 유광제를 사용하며, 상기 제2코팅제는 투명한 무광제를 사용하되, 상기 제2코팅단계에서는 상기 목무늬의 라인을 따라 엠보싱을 형성한다.In the printing step, the wood pattern is printed, the first coating agent uses a transparent matting agent, and the second coating agent uses a transparent matting agent, and in the second coating step, embossing is formed along the line of the wood pattern. do.

상기 제2롤러에는 상기 엠보싱을 형성하기 위한 요홈에 형성되되, 상기 요홈의 깊이는 상기 엠보싱의 돌출 높이보다 크다.The second roller is formed in the groove for forming the embossing, the depth of the groove is greater than the projecting height of the embossing.

또한, 상기 목적을 달성하기 위하여 본 발명의 엠보싱이 형성된 표면재는, 시트과; 상기 시트의 상부에 적층된 인쇄층과; 상기 인쇄층의 상부에 적층된 코팅층으로 이루어지되, 상기 코팅층은 코팅제의 점도에 의해 엠보싱이 형성된 것을 특징으로 한다.In addition, in order to achieve the above object, the embossed surface material is formed of a sheet; A printed layer laminated on the sheet; Consists of a coating layer laminated on top of the printing layer, the coating layer is characterized in that the embossing is formed by the viscosity of the coating agent.

상기 코팅층은, 상기 인쇄층의 상부에 적층되고, 투명한 재질로 이루어지며, 평평한 면을 갖는 제1코팅층과; 상기 제1코팅층의 상부에 적층되고, 투명한 재질로 이루어지며, 상기 엠보싱이 형성된 제2코팅층으로 이루어진다.The coating layer is laminated on top of the printing layer, the first coating layer made of a transparent material and having a flat surface; It is laminated on top of the first coating layer, made of a transparent material, and made of a second coating layer formed with the embossing.

이상에서 설명한 바와 같은 본 발명의 시트에 엠보싱을 형성하는 방법 및 엠보싱이 형성된 표면재에 따르면, 가압방식이 아닌 코팅제의 점도에 의해 시트에 용이하게 엠보싱을 형성할 수 있으며, 이로 인해 내마모성 및 내스크래치성을 향상시킬 수 있고, 제조 등이 용이하여 생산성을 향상시킬 수 있다.According to the method of forming the embossing on the sheet of the present invention as described above and the surface material on which the embossing is formed, it is possible to easily form the embossing on the sheet by the viscosity of the coating agent, not the pressure method, thereby abrasion resistance and scratch resistance The productivity can be improved, and the production can be easily performed.

도 1은 본 발명의 실시예에 따른 엠보싱을 형성하는 방법의 순서도,
도 2는 본 발명의 실시예에 따른 표면재의 구조도,1 is a flow chart of a method of forming embossing according to an embodiment of the present invention;
2 is a structural diagram of a surface material according to an embodiment of the present invention;

도 1은 본 발명의 실시예에 따른 엠보싱을 형성하는 방법의 순서도이고, 도 2는 본 발명의 실시예에 따른 표면재의 구조도이다.1 is a flowchart of a method of forming an embossing according to an embodiment of the present invention, Figure 2 is a structural diagram of a surface material according to an embodiment of the present invention.

본 발명의 시트에 엠보싱을 형성하는 방법은 도 1에 도시된 바와 같이, 공급단계(S10)와, 인쇄단계(S20)와, 코팅단계(S30)와, 건조단계(S40)와, 권취단계(S50)로 이루어진다.The method of forming the embossing on the sheet of the present invention, as shown in Figure 1, the supplying step (S10), printing step (S20), coating step (S30), drying step (S40), winding step ( S50).

상기 공급단계(S10)는 시트(10,Sheet)을 공급하는 단계로써, 원통형으로 권취되어 있는 시트(10)을 회전시켜 상기 시트(10)을 다음 단계로 공급하는 것이다.The supply step (S10) is a step of supplying the sheet (10, Sheet), by rotating the sheet 10 wound in a cylindrical shape to supply the sheet 10 to the next step.

상기 시트(10)은 종이, PET, PP 등을 포함한다.The sheet 10 includes paper, PET, PP, and the like.

상기 인쇄단계(S20)는 상기 공급단계(S10)로부터 공급된 시트(10)에 문양을 인쇄하는 단계이다.The printing step S20 is a step of printing a pattern on the sheet 10 supplied from the supply step (S10).

상기 인쇄단계(S20)는, 프라이머인쇄(S21), 베다인쇄(S22) 및 문양인쇄(S23)로 이루어지고, 각각의 인쇄공정의 사이사이에는 가건조를 수행하도록 한다.The printing step (S20) is composed of primer printing (S21), veda printing (S22) and pattern printing (S23), and to perform the temporary drying between each printing process.

상기 프라이머인쇄(S21)와 베다인쇄(S22)는 시트(10) 전체에 인쇄를 수행하여 도 2에 도시된 바와 같이 프라이머인쇄층(21)과 베다인쇄층(22)을 형성하도록 하고, 상기 문양인쇄(S23)는 시트(10)의 전체가 아닌 문양을 내고자 하는 특정부위에만 인쇄를 수행하여 문양인쇄층(23)을 형성하도록 한다.The primer printing (S21) and the Veda printing (S22) to perform the printing on the entire sheet 10 to form a primer printing layer 21 and the Vedic printing layer 22 as shown in Figure 2, the pattern In the printing S23, the pattern printing layer 23 is formed by performing printing only on a specific portion of the sheet 10 to be printed.

상기 프라이머인쇄층(21)은 우레탄, 아크릴 및 폴리에스테르로 이루어진 군에서 선택된 어느 하나를 도포하여 형성된다.The primer printing layer 21 is formed by applying any one selected from the group consisting of urethane, acrylic and polyester.

상기 코팅단계(S30)는 상기 인쇄단계(S20)에 의해 문양이 인쇄된 시트(10)에 코팅제를 도포하여 코팅층(30)을 형성하는 단계이다.The coating step (S30) is a step of forming a coating layer 30 by applying a coating agent to the sheet 10, the pattern is printed by the printing step (S20).

이러한 상기 코팅단계(S30)에서는 문양이 인쇄된 시트(10)에 엠보싱(33)이 형성된 코팅층(30)을 형성하도록 한다.In the coating step (S30) to form a coating layer 30, the embossing 33 is formed on the sheet 10, the pattern is printed.

상기 코팅층(30)에 엠보싱(33)이 형성되도록 하는 방법으로는 상기 코팅제의 점도에 의해 상기 엠보싱(33)이 형성되도록 한다.The embossing 33 is formed on the coating layer 30 so that the embossing 33 is formed by the viscosity of the coating agent.

즉, 상기 코팅제의 점도를 높게 하여 코팅제가 옆으로 펴짐이 없이 작은 물방울과 같이 올록볼록한 엠보싱(33)을 형성하도록 한다.That is, by increasing the viscosity of the coating agent to form a convex embossing 33, such as droplets without the coating unfolded sideways.

이러한 상기 코팅단계(S30)는, 제1코팅제를 이용하여 평평한 제1코팅층(31)을 형성하는 제1코팅단계(S31)와, 상기 제1코팅층(31)을 가건조하는 가건조단계(S32)와, 가건조된 상기 제1코팅층(31)의 상부에 제2코팅제를 이용하여 엠보싱(33)이 형성된 제2코팅층(32)을 형성하는 제2코팅단계(S33)로 이루어진다.The coating step (S30), the first coating step (S31) to form a flat first coating layer 31 using a first coating agent, and the temporary drying step (S32) to temporarily dry the first coating layer (31). ) And a second coating step S33 of forming a second coating layer 32 on which an embossing 33 is formed by using a second coating agent on the temporarily dried first coating layer 31.

상기 제1코팅단계(S31)에서는 제1코팅층(31)을 평평하게 형성하여 상기 제1코팅층(31)이 상기 인쇄층(20)과 잘 결합되도록 한다.In the first coating step S31, the first coating layer 31 is formed to be flat so that the first coating layer 31 is well bonded to the printing layer 20.

상기 가건조단계(S32)에서는 상기 제2코팅단계(S33)를 수행하기 이전에 상기 제1코팅층(31)을 가건조시킴으로써, 상기 제1코팅제와 제2코팅제가 상호 혼합되는 것을 방지한다.In the temporary drying step S32, the first coating layer 31 is temporarily dried before the second coating step S33 is performed to prevent mixing of the first coating agent and the second coating agent.

상기 제2코팅단계(S33)에서는 상기 제2코팅제를 상기 제1코팅층(31)의 상부에 도포하면서 상기 제2코팅제로 하여금 상기 엠보싱(33)이 형성된 상기 제2코팅층(32)을 형성한다.In the second coating step S33, the second coating agent is applied to the upper portion of the first coating layer 31 to form the second coating layer 32 having the embossing 33 formed thereon.

이때, 상기 제2코팅제의 고형분의 중량%는 상기 제1코팅제의 고형분의 중량%보다 높아 상기 제2코팅제의 점도가 상기 제1코팅제의 점도보다 높도록 함으로써, 상기 제2코팅단계(S33)에서 코팅제의 점도의 차이에 의해 엠보싱(33)이 용이하게 형성되도록 한다.At this time, the weight percent of the solids of the second coating agent is higher than the weight percent of the solids of the first coating agent so that the viscosity of the second coating agent is higher than the viscosity of the first coating agent, in the second coating step (S33) The embossing 33 is easily formed by the difference in the viscosity of the coating agent.

상기 제1코팅제는 고형분이 25 ~ 40 중량%를 갖는 폴리에스테르 오버코팅제, 폴리우레탄 오버코팅제, 아크릴폴리오 오버코팅제 및 에폭시 오버코팅제 중 어느 하나로 이루어지고, 상기 제2코팅제는 고형분이 50 ~ 70 중량%를 갖는 폴리에스테르 오버코팅제, 폴리우레탄 오버코팅제, 아크릴폴리오 오버코팅제 및 에폭시 오버코팅제 중 어느 하나로 이루어진다.The first coating agent is made of any one of a polyester overcoat agent having a solid content of 25 to 40% by weight, a polyurethane overcoat agent, an acrylic overcoat agent and an epoxy overcoat agent, and the second coating agent has a solid content of 50 to 70 wt% It consists of any one of a polyester overcoat agent, a polyurethane overcoat agent, an acrylic overcoat agent and an epoxy overcoat agent.

그리고, 상기 제1코팅제와 제2코팅제의 용제는 톨루엔, MEK(Methyl Ethyl Ketone), 아세톤, 이소프로필알코올(IPA), EA(Ethyl Acetate) 중 어느 하나를 사용함이 바람직하다.In addition, the solvent of the first coating agent and the second coating agent is preferably any one of toluene, MEK (Methyl Ethyl Ketone), acetone, isopropyl alcohol (IPA), EA (Ethyl Acetate).

위와 같은, 상기 제1코팅단계(S31)에서는 제1롤러를 이용하여 제1코팅층(31)을 형성하고, 상기 제2코팅단계(S33)에서는 제2롤러를 이용하여 제2코팅층(32)을 형성한다.As described above, in the first coating step S31, the first coating layer 31 is formed using the first roller, and in the second coating step S33, the second coating layer 32 is formed using the second roller. Form.

상기 제1코팅단계(S31)와 제2코팅단계(S33)에서 상기 시트(10)이 동일한 속도로 이동되도록 한다.In the first coating step S31 and the second coating step S33, the sheet 10 is moved at the same speed.

또한, 상기 제2롤러에는 상기 엠보싱(33)을 형성하기 위한 요홈이 형성되고, 상기 요홈의 깊이는 상기 엠보싱(33)의 돌출 높이보다 크도록 한다.In addition, a groove for forming the embossing 33 is formed in the second roller, and the depth of the groove is greater than the protruding height of the embossing 33.

이로 인해, 상기 요홈에 수용되어 있던 상기 제2코팅제는 상기 제2롤러의 회전시, 상기 제1코팅층(31)이 형성된 상기 시트(10)과 접하면서 상기 제1코팅층(31)에 접착되어 엠보싱(33)을 형성된 제2코팅층(32)을 형성하게 된다.Therefore, the second coating agent accommodated in the groove is bonded to the first coating layer 31 and embossed while being in contact with the sheet 10 on which the first coating layer 31 is formed when the second roller is rotated. A second coating layer 32 on which 33 is formed is formed.

이때, 상기 요홈의 깊이를 상기 엠보싱(33)을 돌출 높이보다 크게 함으로써, 상기 제2롤러의 회전시 상기 요홈에 수용되어 있던 제2코팅제 중 일부가 상기 요홈에 잔존하고 있어도 상기 엠보싱(33)을 형성할 수 있게 된다.In this case, the depth of the groove is greater than the height of the embossing 33 so that the embossing 33 may be removed even if some of the second coating agent accommodated in the groove is left in the groove during the rotation of the second roller. It can be formed.

또한, 상기 요홈에 수용되어 있던 제2코팅제가 상기 제1코팅층(31)이 형성된 시트(10)에 접하였을 때, 상기 제2롤러가 제1롤러보다 빠르게 회전하기 때문에, 상기 제2롤러에 부착되어 있던 상기 제2코팅제가 상기 제1코팅층(31)과 접하면서 옆으로 퍼지거나 다시 상기 제2롤러로 부착됨이 없이 상기 제2롤러로부터 이탈되어 상기 제1코팅층(31)의 상부에 엠보싱(33)을 잘 형성할 수 있게 된다.In addition, since the second roller rotates faster than the first roller when the second coating agent accommodated in the groove contacts the sheet 10 on which the first coating layer 31 is formed, the second coating agent adheres to the second roller. The second coating agent, which is not in contact with the first coating layer 31 and spreads laterally or is attached to the second roller, is separated from the second roller and is embossed on the first coating layer 31. 33) can be formed well.

물론, 상기 코팅단계(S30)에서는 상기 제1코팅단계(S31) 및 가건조단계(S32)없이 엠보싱(33)을 형성하는 상기 제2코팅단계(S33)만으로 이루어질 수도 있다.Of course, the coating step (S30) may be made of only the second coating step (S33) to form the embossing 33 without the first coating step (S31) and the temporary drying step (S32).

상기 건조단계(S40)는 코팅된 시트(10)을 건조하는 건조단계(S40)이다.The drying step (S40) is a drying step (S40) for drying the coated sheet 10.

건조하는 방법으로는 UV경화 또는 열경화를 한다.As a method of drying, UV curing or thermosetting is performed.

상기 권취단계(S50)는 상기 건조단계(S40)에 의해 건조된 시트(10)을 롤 등을 이용하여 권취하는 단계이다.The winding step (S50) is a step of winding the sheet 10 dried by the drying step (S40) using a roll or the like.

한편, 상기 인쇄단계(S20)에서 목무늬를 인쇄할 경우, 상기 제1코팅제는 투명한 유광제를 사용하고 상기 제2코팅제는 투명한 무광제를 사용하도록 한다.On the other hand, when printing the wood pattern in the printing step (S20), the first coating agent to use a transparent glaze agent and the second coating agent to use a transparent matte agent.

이때, 상기 제2코팅단계(S33)에서는 상기 목무늬의 라인을 따라 엠보싱(33)을 형성하도록 한다.At this time, in the second coating step (S33) to form an embossing 33 along the line of the neck pattern.

위와 같이, 상기 제1코팅제로 투명한 유광제를 사용하고, 엠보싱(33)을 형성하는 상기 제2코팅제로 투명한 무광제를 사용함으로써, 상기 인쇄단계(S20)에서 상기 시트(10)에 인쇄한 목무늬가 외부로 잘 표현되도록 할 수 있다.As described above, by using a transparent matting agent as the first coating agent, and by using a transparent matting agent as the second coating agent to form the embossing 33, the neck printed on the sheet 10 in the printing step (S20) The pattern can be displayed well to the outside.

위와 같은 방법으로 생산된 엠보싱(33)이 형성된 표면재는, 도 2에 도시된 바와 같이, 시트(10)과, 상기 시트(10)의 상부에 적층된 인쇄층(20)과, 상기 인쇄층(20)의 상부에 적층된 코팅층(30)으로 이루어지게 된다.As shown in FIG. 2, the surface material on which the embossing 33 produced by the above method is formed includes a sheet 10, a printed layer 20 stacked on top of the sheet 10, and the printed layer ( 20 is made of a coating layer 30 laminated on the top.

상기 시트(10)은 상술한 바와 같이, 종이, PET, PP 등으로 이루어진다.As described above, the sheet 10 is made of paper, PET, PP, or the like.

상기 코팅층(30)은 코팅제의 점도에 의해 엠보싱(33)이 형성되게 된다.The coating layer 30 is embossed 33 is formed by the viscosity of the coating agent.

상기 코팅층(30)은, 상기 인쇄층(20)의 상부에 적층되고 투명한 재질로 이루어지며 평평한 면을 갖는 제1코팅층(31)과, 상기 제1코팅층(31)의 상부에 적층되고 투명한 재질로 이루어지며 상기 엠보싱(33)이 형성된 제2코팅층(32)으로 이루어진다.The coating layer 30 is made of a transparent material laminated on the upper portion of the printing layer 20 and has a flat surface and a transparent material laminated on the upper portion of the first coating layer 31. And a second coating layer 32 having the embossing 33 formed thereon.

위와 같이, 코팅제의 점도에 의해 시트(10)에 엠보싱(33)을 형성함으로써, 표면재의 표면물성 즉 내마모성 및 내스크래치성 등을 향상시킬 수 있다.As described above, by forming the embossed 33 on the sheet 10 by the viscosity of the coating agent, it is possible to improve the surface physical properties of the surface material, that is, wear resistance and scratch resistance.

본 발명인 시트에 엠보싱을 형성하는 방법 및 엠보싱이 형성된 표면재는 전술한 실시예에 국한하지 않고, 본 발명의 기술 사상이 허용되는 범위 내에서 다양하게 변형하여 실시할 수 있다.The method of forming the embossing on the sheet of the present invention and the surface material on which the embossing is formed are not limited to the above-described embodiments, and may be variously modified within the range in which the technical idea of the present invention is permitted.

S10 : 공급단계, S20 : 인쇄단계, S21 : 프라이머인쇄, S22 : 베다인쇄, S23 : 문양인쇄, S30 : 코팅단계, S31 : 제1코팅단계, S32 : 가건조단계, S33 : 제2코팅단계, S40 : 건조단계, S50 : 권취단계
10 : 시트, 20 : 인쇄층, 21 : 프라이머인쇄층, 22 : 베다인쇄층, 23 : 문양인쇄층, 30 : 코팅층, 31 : 제1코팅층, 32 : 제2코팅층, 33 : 엠보싱,S10: supplying step, S20: printing step, S21: primer printing, S22: veda printing, S23: pattern printing, S30: coating step, S31: first coating step, S32: temporary drying step, S33: second coating step, S40: drying step, S50: winding step
10: sheet, 20: printing layer, 21: primer printing layer, 22: veda printing layer, 23: pattern printing layer, 30: coating layer, 31: first coating layer, 32: second coating layer, 33: embossing,

Claims (9)

시트을 공급하는 공급단계와;
공급된 시트에 문양을 인쇄하는 인쇄단계와;
문양이 인쇄된 시트에 코팅제를 도포하여 코팅층을 형성하는 코팅단계와;
코팅된 시트을 건조하는 건조단계와;
건조된 시트을 권취하는 권취단계로 이루어지되,
상기 코팅단계에서는 문양이 인쇄된 시트에 상기 코팅제의 점도에 의해 엠보싱이 형성된 코팅층을 형성하는 것을 특징으로 하는 시트에 엠보싱을 형성하는 방법.A feeding step of feeding the sheet;
A printing step of printing a pattern on the supplied sheet;
A coating step of forming a coating layer by applying a coating agent to the printed sheet;
A drying step of drying the coated sheet;
It consists of a winding step of winding the dried sheet,
In the coating step, the embossed to form a sheet, characterized in that to form a coating layer embossed by the viscosity of the coating on the sheet printed pattern. 제 1항에 있어서,
상기 코팅단계는,
제1코팅제를 이용하여 평평한 제1코팅층을 형성하는 제1코팅단계와;
상기 제1코팅층을 가건조하는 가건조단계와;
가건조된 상기 제1코팅층의 상부에 제2코팅제를 이용하여 엠보싱이 형성된 제2코팅층을 형성하는 제2코팅단계로 이루어진 것을 특징으로 하는 시트에 엠보싱을 형성하는 방법.The method of claim 1,
The coating step,
A first coating step of forming a flat first coating layer using a first coating agent;
A temporary drying step of temporarily drying the first coating layer;
And a second coating step of forming a second coating layer on which the embossing is formed by using a second coating agent on top of the temporarily dried first coating layer. 제 2항에 있어서,
상기 제2코팅제의 고형분의 중량%는 상기 제1코팅제의 고형분의 중량%보다 높아 상기 제2코팅제의 점도가 상기 제1코팅제의 점도보다 높은 것을 특징으로 하는 시트에 엠보싱을 형성하는 방법.The method of claim 2,
The weight percent of the solids of the second coating agent is higher than the weight percent of the solids of the first coating agent The method of forming the embossing on the sheet, characterized in that the viscosity of the second coating agent is higher than the viscosity of the first coating agent. 제 3항에 있어서,
상기 제1코팅제는 고형분이 25 ~ 40 중량%를 갖는 폴리에스테르 오버코팅제, 폴리우레탄 오버코팅제, 아크릴폴리오 오버코팅제 및 에폭시 오버코팅제 중 어느 하나로 이루어지고,
상기 제2코팅제는 고형분이 50 ~ 70 중량%를 갖는 폴리에스테르 오버코팅제, 폴리우레탄 오버코팅제, 아크릴폴리오 오버코팅제 및 에폭시 오버코팅제 중 어느 하나로 이루어지며,
상기 제1코팅제와 제2코팅제의 용제는 톨루엔, MEK(Methyl Ethyl Ketone), 아세톤, 이소프로필알코올(IPA), EA(Ethyl Acetate) 중 어느 하나인 것을 특징으로 하는 시트에 엠보싱을 형성하는 방법.The method of claim 3, wherein
The first coating agent is made of any one of a polyester overcoat agent having a solid content of 25 to 40% by weight, a polyurethane overcoat agent, an acrylic overcoat agent and an epoxy overcoat agent,
The second coating agent is made of any one of a polyester overcoat agent, a polyurethane overcoat agent, an acrylic overcoat agent and an epoxy overcoat agent having a solid content of 50 to 70% by weight,
The solvent of the first coating agent and the second coating agent is emulsified to the sheet, characterized in that any one of toluene, MEK (Methyl Ethyl Ketone), acetone, isopropyl alcohol (IPA), EA (Ethyl Acetate). 제 2항 내지 제 4항 중 어느 한 항에 있어서,
상기 제1코팅단계에서는 제1롤러를 이용하여 제1코팅층을 형성하고,
상기 제2코팅단계에서는 제2롤러를 이용하여 제2코팅층을 형성하는 것을 특징으로 하는 시트에 엠보싱을 형성하는 방법.The method according to any one of claims 2 to 4,
In the first coating step, to form a first coating layer using a first roller,
And in the second coating step, forming a second coating layer using a second roller. 제 2항 내지 제 4항 중 어느 한 항에 있어서,
상기 인쇄단계에서는 목무늬를 인쇄하고,
상기 제1코팅제는 투명한 유광제를 사용하며, 상기 제2코팅제는 투명한 무광제를 사용하되,
상기 제2코팅단계에서는 상기 목무늬의 라인을 따라 엠보싱을 형성하는 것을 특징으로 하는 시트에 엠보싱을 형성하는 방법.The method according to any one of claims 2 to 4,
In the printing step, the wood pattern is printed,
The first coating agent uses a transparent glaze agent, the second coating agent uses a transparent matte agent,
In the second coating step embossing is formed on a sheet, characterized in that for forming embossing along the line of the neck pattern. 제 5항에 있어서,
상기 제2롤러에는 상기 엠보싱을 형성하기 위한 요홈에 형성되되,
상기 요홈의 깊이는 상기 엠보싱의 돌출 높이보다 큰 것을 특징으로 하는 엠보싱을 형성하는 방법.6. The method of claim 5,
The second roller is formed in the groove for forming the embossing,
And the depth of the recess is greater than the projecting height of the embossing. 시트과;
상기 시트의 상부에 적층된 인쇄층과;
상기 인쇄층의 상부에 적층된 코팅층으로 이루어지되,
상기 코팅층은 코팅제의 점도에 의해 엠보싱이 형성된 것을 특징으로 하는 엠보싱이 형성된 표면재.Sheets;
A printed layer laminated on the sheet;
Consists of a coating layer laminated on top of the printed layer,
The coating layer is embossed surface material, characterized in that the embossing is formed by the viscosity of the coating agent. 제 8항에 있어서,
상기 코팅층은,
상기 인쇄층의 상부에 적층되고, 투명한 재질로 이루어지며, 평평한 면을 갖는 제1코팅층과;
상기 제1코팅층의 상부에 적층되고, 투명한 재질로 이루어지며, 상기 엠보싱이 형성된 제2코팅층으로 이루어진 것을 특징으로 하는 엠보싱이 형성된 표면재.
The method of claim 8,
The coating layer,
A first coating layer laminated on top of the printing layer, made of a transparent material, and having a flat surface;
An embossed surface material laminated on top of the first coating layer, made of a transparent material, and formed of a second coating layer on which the embossing is formed.
KR1020100140658A 2010-12-31 2010-12-31 Method for embossing on sheet KR101223099B1 (en)