CN105082855B - The production method and ceramic bakeware of a kind of ceramic bakeware - Google Patents
The production method and ceramic bakeware of a kind of ceramic bakeware Download PDFInfo
- Publication number
- CN105082855B CN105082855B CN201510406319.9A CN201510406319A CN105082855B CN 105082855 B CN105082855 B CN 105082855B CN 201510406319 A CN201510406319 A CN 201510406319A CN 105082855 B CN105082855 B CN 105082855B
- Authority
- CN
- China
- Prior art keywords
- baking tray
- marble paper
- line piece
- time
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The production method of ceramic bakeware disclosed by the invention, includes the following steps：1) the baking tray green body without glaze paint is made；2) baking tray marble paper is made；3) it pastes baking tray marble paper and the ceramics of the figure line piece posted in baking tray marble paper is put into heating furnace and carry out decoration firing, 1~2 hour decoration firing time, ceramic bakeware is made in 1250 DEG C~1350 DEG C of temperature.Water transfer marble paper, as base material, with special decal method is attached on the baking tray green body of no glaze paint using the baking tray green body of special no glaze paint, obtains ceramic bakeware by 1250 DEG C~1350 DEG C, have the feel for commonly having glaze ceramics incomparable by the present invention.
Description
Technical field
The present invention relates to ceramic bakeware manufacture technology field, the production method and ceramic bakeware of especially a kind of ceramic bakeware.
Background technology
With social economy, culture develop by leaps and bounds, people life just from it is simply having adequate food and clothing step into it is fairly well-off, advocate human nature and when
Still, individual character and glamour are constantly moulded, it has also become the pursuit of people, nowadays clock and watch have not been singly a kind of tool for showing the time, and
It is more that it is used as a kind of ornament, therefore, it will be ornaments from now on to research and develop novel clock and watch ornament
The hot spot in field.Dial plate currently on the market generally using plastics or metal material, is easily deformed and is difficult to using plastics dial plate
The class of clock and watch is improved, using metal dial, then scale mark, dial plate pattern etc. are typically necessary by welding, bonding, inlaying
Etc. techniques could be combined with metal dial, assembly technology is complicated, takes time and effort, and dial plate pattern, color be difficult to obtain compared with
Quantum jump.Therefore, method used in dial plate decoration seriously constrains the development speed of horological industry at present, it is impossible to meet people
Growing consumption demand.
Invention content
The first technical problem to be solved by the present invention is to provide a kind of pottery for the problems of prior art
The production method of porcelain baking tray.
The second technical problem to be solved by the present invention is to provide made by the production method using above-mentioned ceramic bakeware
Ceramic bakeware.
The production method of ceramic bakeware as the first invention of the present invention, includes the following steps：
1) the baking tray green body without glaze paint is made；
2) baking tray marble paper is made, is specifically comprised the following steps
2.1) inorganic pigment first pass is printed on water transfer base stock using full-automatic screen printer；
2.2) water transfer base stock is put into drying box for the first time and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock；
2.3) inorganic pigment is printed on water transfer base stock for second time using full-automatic screen printer；
2.4) water transfer base stock is put into for the second time in drying box and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock, the silk-screen printing of finishing patterns；
2.5) cover mimeograph brush
By cover oil covering step 2.4 by the way of the silk-screen printing) on the decorative pattern of silk-screen printing completed, it is made
Baking tray marble paper；
The inorganic pigment is prepared by the raw material of following mass parts：32-38 parts of potassium oxide, 30-36 parts of oxidation
Calcium, 12-18 parts of barium monoxide, 9-15 parts of zinc oxide and 2-8 parts of chromophore compound；
3) baking tray marble paper is pasted, is included the following steps：
The 3.1 baking tray marble papers that step 2) is taken to prepare are soaked in 40~50 DEG C of warm water, and soaking time is 10~30 seconds, is allowed roasting
Figure line piece and the packing paper of baking tray marble paper in disc floret paper come off；
3.2) the figure line piece correspondence in baking tray marble paper is placed in the baking tray green body of no glaze paint needs applique position；
3.3) seal closure enclosed hood tightly baking tray green body institute's applique position without glaze paint is taken, water vapour is inputted into seal closure,
Water vapor pressure be 1~2 atmospheric pressure, 40~50 DEG C of temperature, 5~15 seconds reaction time；The water vapour with pressure can be wet at this time
Moisten the figure line piece in baking tray marble paper, and the figure line piece in baking tray marble paper is made uniformly to be tightly attached to the baking tray billet surface of no glaze paint,
Under the action of water vapour and pressure, the figure line piece in baking tray marble paper generates slight extension, smoothes away wrinkles；
3.4) after water vapour stops input, then hot-air is inputted into seal closure, 55~60 DEG C of hot air temperature, during reaction
Between be 20~30 seconds；This step dries marble paper figure line piece using hot-air, to remove moisture content, and makes marble paper figure line piece and vessel
It is close on surface；
3.5) stop input hot-air, remove seal closure, the ceramics of the figure line piece posted in baking tray marble paper are put into heating
Decoration firing, 1~2 hour decoration firing time are carried out in stove, ceramic bakeware is made in 1250 DEG C~1350 DEG C of temperature.
As the ceramic bakeware of second aspect of the present invention, it is made by the production method of above-mentioned ceramic bakeware.
The present invention, as base material, is pasted water transfer marble paper with special decal method using the baking tray green body of special no glaze paint
On the baking tray green body of no glaze paint, ceramic bakeware is obtained by 1250 DEG C~1350 DEG C, having commonly there are glaze ceramics that can not compare
The feel of plan.
Specific embodiment
Embodiment 1
The production method of ceramic bakeware, includes the following steps：
1) the baking tray green body without glaze paint is made；
2) baking tray marble paper is made, is specifically comprised the following steps
2.1) inorganic pigment first pass is printed on water transfer base stock using full-automatic screen printer；
2.2) water transfer base stock is put into drying box for the first time and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock；
2.3) inorganic pigment is printed on water transfer base stock for second time using full-automatic screen printer；
2.4) water transfer base stock is put into for the second time in drying box and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock, the silk-screen printing of finishing patterns；
2.5) cover mimeograph brush
By cover oil covering step 4 by the way of the silk-screen printing) on the decorative pattern of silk-screen printing completed, it is made roasting
Disc floret paper；
The inorganic pigment is prepared by the raw material of following mass parts：35 parts of potassium oxide, 33 parts of calcium oxide, 15 parts
Barium monoxide, 12 parts of zinc oxide and 1 part of magnesia, 4 parts of strontium carbonate.
3) baking tray marble paper is pasted, is included the following steps：
3.1) baking tray marble paper prepared by step 2) is taken to be soaked in 40~50 DEG C of warm water, soaking time is 10~30 seconds, is allowed
Figure line piece and the packing paper of baking tray marble paper in baking tray marble paper come off；
3.2) the figure line piece correspondence in baking tray marble paper is placed in the baking tray green body of no glaze paint needs applique position；
3.3) seal closure enclosed hood tightly baking tray green body institute's applique position without glaze paint is taken, water vapour is inputted into seal closure,
Water vapor pressure be 1~2 atmospheric pressure, 40~50 DEG C of temperature, 5~15 seconds reaction time；The water vapour with pressure can be wet at this time
Moisten the figure line piece in baking tray marble paper, and the figure line piece in baking tray marble paper is made uniformly to be tightly attached to the baking tray billet surface of no glaze paint,
Under the action of water vapour and pressure, the figure line piece in baking tray marble paper generates slight extension, smoothes away wrinkles；
3.4) after water vapour stops input, then hot-air is inputted into seal closure, 55~60 DEG C of hot air temperature, during reaction
Between be 20~30 seconds；This step dries marble paper figure line piece using hot-air, to remove moisture content, and makes marble paper figure line piece and vessel
It is close on surface；
3.5) stop input hot-air, remove seal closure, the ceramics of the figure line piece posted in baking tray marble paper are put into heating
Decoration firing, 1~2 hour decoration firing time are carried out in stove, ceramic bakeware is made in 1250 DEG C~1350 DEG C of temperature.
Embodiment 2
The production method of ceramic bakeware, includes the following steps：
1) the baking tray green body without glaze paint is made；
2) baking tray marble paper is made, is specifically comprised the following steps
2.1) inorganic pigment first pass is printed on water transfer base stock using full-automatic screen printer；
2.2) water transfer base stock is put into drying box for the first time and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock；
2.3) inorganic pigment is printed on water transfer base stock for second time using full-automatic screen printer；
2.4) water transfer base stock is put into for the second time in drying box and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock, the silk-screen printing of finishing patterns；
2.5) cover mimeograph brush
By cover oil covering step 4 by the way of the silk-screen printing) on the decorative pattern of silk-screen printing completed, it is made roasting
Disc floret paper；
The inorganic pigment is prepared by the raw material of following mass parts：33 parts of potassium oxide, 35 parts of calcium oxide, 17 parts
Barium monoxide, 10 parts of zinc oxide and 1 part of magnesia, 2 parts of strontium carbonate, 2 parts of copper oxide.
3) baking tray marble paper is pasted, is included the following steps：
3.1) baking tray marble paper prepared by step 2) is taken to be soaked in 40~50 DEG C of warm water, soaking time is 10~30 seconds, is allowed
Figure line piece and the packing paper of baking tray marble paper in baking tray marble paper come off；
3.2) the figure line piece correspondence in baking tray marble paper is placed in the baking tray green body of no glaze paint needs applique position；
3.3) seal closure enclosed hood tightly baking tray green body institute's applique position without glaze paint is taken, water vapour is inputted into seal closure,
Water vapor pressure be 1~2 atmospheric pressure, 40~50 DEG C of temperature, 5~15 seconds reaction time；The water vapour with pressure can be wet at this time
Moisten the figure line piece in baking tray marble paper, and the figure line piece in baking tray marble paper is made uniformly to be tightly attached to the baking tray billet surface of no glaze paint,
Under the action of water vapour and pressure, the figure line piece in baking tray marble paper generates slight extension, smoothes away wrinkles；
3.4) after water vapour stops input, then hot-air is inputted into seal closure, 55~60 DEG C of hot air temperature, during reaction
Between be 20~30 seconds；This step dries marble paper figure line piece using hot-air, to remove moisture content, and makes marble paper figure line piece and vessel
It is close on surface；
3.5) stop input hot-air, remove seal closure, the ceramics of the figure line piece posted in baking tray marble paper are put into heating
Decoration firing, 1~2 hour decoration firing time are carried out in stove, ceramic bakeware is made in 1250 DEG C~1350 DEG C of temperature.
Embodiment 3
The production method of ceramic bakeware, includes the following steps：
1) the baking tray green body without glaze paint is made；
2) baking tray marble paper is made, is specifically comprised the following steps
2.1) inorganic pigment first pass is printed on water transfer base stock using full-automatic screen printer；
2.2) water transfer base stock is put into drying box for the first time and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock；
2.3) inorganic pigment is printed on water transfer base stock for second time using full-automatic screen printer；
2.4) water transfer base stock is put into for the second time in drying box and dried, drying temperature is 35 DEG C, and drying time is 60 points
Clock, the silk-screen printing of finishing patterns；
2.5) cover mimeograph brush
By cover oil covering step 4 by the way of the silk-screen printing) on the decorative pattern of silk-screen printing completed, it is made roasting
Disc floret paper；
The inorganic pigment is prepared by the raw material of following mass parts：38 parts of potassium oxide, 36 parts of calcium oxide, 17 parts
Barium monoxide, 10 parts of zinc oxide and 1 part of magnesia, 2 parts of strontium carbonate, 2 parts of copper oxide.
3) baking tray marble paper is pasted, is included the following steps：
3.1) baking tray marble paper prepared by step 2) is taken to be soaked in 40~50 DEG C of warm water, soaking time is 10~30 seconds, is allowed
Figure line piece and the packing paper of baking tray marble paper in baking tray marble paper come off；
3.2) the figure line piece correspondence in baking tray marble paper is placed in the baking tray green body of no glaze paint needs applique position；
3.3) seal closure enclosed hood tightly baking tray green body institute's applique position without glaze paint is taken, water vapour is inputted into seal closure,
Water vapor pressure be 1~2 atmospheric pressure, 40~50 DEG C of temperature, 5~15 seconds reaction time；The water vapour with pressure can be wet at this time
Moisten the figure line piece in baking tray marble paper, and the figure line piece in baking tray marble paper is made uniformly to be tightly attached to the baking tray billet surface of no glaze paint,
Under the action of water vapour and pressure, the figure line piece in baking tray marble paper generates slight extension, smoothes away wrinkles；
3.4) after water vapour stops input, then hot-air is inputted into seal closure, 55~60 DEG C of hot air temperature, during reaction
Between be 20~30 seconds；This step dries marble paper figure line piece using hot-air, to remove moisture content, and makes marble paper figure line piece and vessel
It is close on surface；
3.5) stop input hot-air, remove seal closure, the ceramics of the figure line piece posted in baking tray marble paper are put into heating
Decoration firing, 1~2 hour decoration firing time are carried out in stove, ceramic bakeware is made in 1250 DEG C~1350 DEG C of temperature.
Claims (2)
1. the production method of ceramic bakeware, which is characterized in that include the following steps：
1) the baking tray green body without glaze paint is made；
2) baking tray marble paper is made, is specifically comprised the following steps
2.1) inorganic pigment first pass is printed on water transfer base stock using full-automatic screen printer；
2.2) water transfer base stock is put into drying box for the first time and dried, drying temperature is 35 DEG C, and drying time is 60 minutes；
2.3) inorganic pigment is printed on water transfer base stock for second time using full-automatic screen printer；
2.4) water transfer base stock is put into for the second time in drying box and dried, drying temperature is 35 DEG C, and drying time is 60 minutes, complete
Into the silk-screen printing of pattern；
2.5) cover mimeograph brush
By cover oil covering step 2.4 by the way of the silk-screen printing) on the decorative pattern of silk-screen printing completed, baking tray is made
Marble paper；
The inorganic pigment is prepared by the raw material of following mass parts：32-38 parts of potassium oxide, 30-36 parts of calcium oxide,
12-18 parts of barium monoxide, 9-15 parts of zinc oxide and 2-8 parts of chromophore compound；
3) baking tray marble paper is pasted, is included the following steps：
The 3.1 baking tray marble papers that step 2) is taken to prepare are soaked in 40~50 DEG C of warm water, and soaking time is 10~30 seconds, and baking tray is allowed to spend
Figure line piece and the packing paper of baking tray marble paper in paper come off；
3.2) the figure line piece correspondence in baking tray marble paper is placed in the baking tray green body of no glaze paint needs applique position；
3.3) seal closure enclosed hood tightly baking tray green body institute's applique position without glaze paint is taken, water vapour is inputted into seal closure, water steams
Steam pressure be 1~2 atmospheric pressure, 40~50 DEG C of temperature, 5~15 seconds reaction time；The water vapour with pressure can moisten roasting at this time
Figure line piece in disc floret paper, and the figure line piece in baking tray marble paper is made uniformly to be tightly attached to the baking tray billet surface of no glaze paint, it is steamed in water
Under the action of vapour and pressure, the figure line piece in baking tray marble paper generates slight extension, smoothes away wrinkles；
3.4) after water vapour stops input, then hot-air is inputted into seal closure, 55~60 DEG C of hot air temperature, the reaction time is
20~30 seconds；This step dries marble paper figure line piece using hot-air, to remove moisture content, and makes marble paper figure line piece and vessel surface
It is close to；
3.5) stop input hot-air, remove seal closure, the ceramics of the figure line piece posted in baking tray marble paper are put into heating furnace
Decoration firing, 1~2 hour decoration firing time are carried out, ceramic bakeware is made in 1250 DEG C~1350 DEG C of temperature.
2. ceramic bakeware, which is characterized in that be made by the production method of ceramic bakeware described in claim 1.