CN108274911A - The method that water at low temperature transfers radium-shine marble paper - Google Patents
The method that water at low temperature transfers radium-shine marble paper Download PDFInfo
- Publication number
- CN108274911A CN108274911A CN201810054461.5A CN201810054461A CN108274911A CN 108274911 A CN108274911 A CN 108274911A CN 201810054461 A CN201810054461 A CN 201810054461A CN 108274911 A CN108274911 A CN 108274911A
- Authority
- CN
- China
- Prior art keywords
- water
- base stock
- radium
- shine
- marble paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of methods that water at low temperature transfers radium-shine marble paper, including:1) one layer of gold stamping base oil is printed on membranelle base stock, is carried out dry for the first time;2) gold stamping marble paper on the membranelle base stock made from step 1) obtains the membranelle base stock with radium-shine part;3) water-soluble environment-friendly ink is stamped on the radium-shine part for the membranelle base stock that step 2) obtains;4) one layer of isolation oil of the membranelle base stock printing after step 3) completion, carries out second of drying;5) the membranelle base stock after step 4) completion print one layer can dyestripping, it is dry to carry out third time;6) step 5) completion after, by membranelle base stock carry out water at low temperature turn separation after, be attached on radium-shine pasted objects, removing can dyestripping, baking, you can.It is that low temperature thermal transfer and high-temperature water transfer, and format surface is single compared with the existing technology;The technology of the present invention is water at low temperature transfer, reduces cost, improves efficiency, abundant expression forms are various, energy conservation and environmental protection.
Description
Technical field
The present invention relates to a kind of methods that water at low temperature transfers radium-shine marble paper, belong to printing technology.
Technical background
Laser effect in existing goods packaging is that pattern zone is independently separated with laser effect area, the flower with laser effect
Line yet there are no in the market, and the technique of existing laser label, is first upper labelled in packaging, is then needing to locate gold stamping, scalding
Layer gold can will be completely covered at corresponding label.Traditional high temperature marble paper needs to burn to 700-900 degree, and 9-10 hours, the energy consumed
Fei Duo, long time period, and be ceramic idiosome etc. in face of radium-shine object, the high temperature of baking can also change the structure of radium-shine object
And shape, and prior art format surface in terms of Colour selection is relatively simple.For this purpose, the present invention comes into being.
Invention content
In view of the above technical problems, the present invention provides a kind of methods that water at low temperature transfers radium-shine marble paper, wherein including with
Lower step:
1) one layer of gold stamping base oil is printed with the mode of silk-screen printing and/or offset printing on membranelle base stock, carried out dry for the first time
It is dry;
2) the gold stamping marble paper of gilding press is used on the membranelle base stock made from step 1), is made membranelle base stock that there is laser effect, is obtained
To the membranelle base stock with radium-shine part;
3) on the radium-shine part for the membranelle base stock that step 2) obtains water-soluble environment-friendly is stamped with silk-screen or the method for offset printing
Ink;
4) one layer of isolation oil of membranelle base stock printing after step 3) is completed, carries out second of drying;
5) the membranelle base stock after step 4) is completed print one layer can dyestripping, carry out obtaining water at low temperature after third time is dry turning
Print radium-shine marble paper;
6) after step 5) is completed, water at low temperature is transferred into radium-shine marble paper water and is turned after detaching, is attached on radium-shine pasted objects,
Tear off can dyestripping, toast to get the marble paper finished product with laser effect.
In the method that above-mentioned water at low temperature transfers radium-shine marble paper, the specification of membranelle base stock is neatly formula in the step 1)
Transfer paper.Preferably scheme Li Shi paper industry, dimensions 500*700mm, 540*390mm or 350*500mm, gold stamping base oil are excellent
Select nine ACE Semi, product identification 026, thickness 0.1-0.2mm, the dry time be air drying for 24 hours more than.
In the method that above-mentioned water at low temperature transfers radium-shine marble paper, the gold stamping marble paper temperature of step 2) is 120~150 DEG C.
Water-soluble environment-friendly ink is spot color or four in the method that above-mentioned water at low temperature transfers radium-shine marble paper, the step 3)
Color water-soluble environment-friendly ink.
The color of water-soluble environment-friendly ink turns for water in the method that above-mentioned water at low temperature transfers radium-shine marble paper, the step 3)
Bright red, water turns former yellow, high covering white and water turns one or more of goth black combination.It is preferably the letter environmental protection of Shenzhen U.S.
Materials Co., Ltd, SW-1807Z water turn bright red, SW-1802A water and turn former yellow, SW-1801A high coverings white, SW-1815A water
Turn one or more of goth black combination, it is environmentally friendly, nontoxic, tasteless, to no damage to human body.Print thickness:It can cover in
Background color reaches effect, non-discolouring;Temperature control and whether dry directly affect product firing after, the firmness of marble paper prevents
Glutinous version.Its advantage is that printing is at transparent or semitransparent water-soluble ink, the radium-shine Jin Qu of bottom will not be covered, there can be laser effect
It appears;Printing is that can hide the radium-shine Jin Qu of bottom lid, no laser effect appears at opaque water-soluble ink.
It is 0.05- in the thickness of the method that above-mentioned water at low temperature transfers radium-shine marble paper, step 4) the isolation oil
0.1mm, drying temperature are 30-35 DEG C, drying time >=for 24 hours.The specification ACE Semi number of wherein described step 4) the isolation oil
813.Further, the preferred silk-screen printing of mode of printing isolation oil.
In the method that above-mentioned water at low temperature transfers radium-shine marble paper, described in the step 5) can dyestripping drying temperature be 30-
35 DEG C, drying time >=12h.The dry specification of the step 5) is 30-35 DEG C and is more than or equal to 12 hours, if drying time is less than
12 hours, marble paper cannot parch, can the separation of dyestripping difficulty.Wherein, printing can dyestripping the preferred silk-screen printing of mode.
Water at low temperature turns separating step and includes in the method that above-mentioned water at low temperature transfers radium-shine marble paper, the step 6):It will print
The membranelle base stock finished is brushed, is entirely immersed in normal-temperature water 3-5 minutes, membranelle base stock is removed, pattern layer marble paper is taken out viscous
It is attached on ceramics, glass, metal or plastic preform, 0.5-2h is toasted at 150-175 DEG C.Preferably, operating personnel exist
When feel membranelle base stock can be detached from pattern layer, i.e., the taking-up of pattern layer marble paper is pasted onto ceramic/glass/metal/plastic etc.
On green body, and membranelle base stock is removed.Toast specification:0.5-2h is toasted at 150-175 DEG C, can be reinforced secured after toasting
Degree is resistant to 3M adhesive tapes and glues the tests such as drawing, ethanol-tolerant, heat resisting water soaking friction.The wherein described radium-shine object is ceramic/glass/gold
Category/plastics etc..
In the method that above-mentioned water at low temperature transfers radium-shine marble paper, in step 5) plus print can dyestripping, be detached from it in membranelle base stock
Afterwards, pattern can be made to be attached to surface can be transferred on the green bodies such as ceramics on dyestripping, then again with the effective quick separating of marble paper pattern
.
Marble paper firmness test method:Before room temperature does not impregnate, garland paper is continuously glued three times with 3M adhesive tapes, marble paper is without falling off;
Airing after marble paper is impregnated 2 hours in 55%vol white wine, 3M adhesive tapes glue garland paper, and marble paper is without falling off;By marble paper in 50 DEG C of heat
After being impregnated 30 minutes in water, bottle phase mutual friction in water is picked up for 20 times, marble paper without it is damaged, fall off;By marble paper in 50 DEG C of hot water
It is middle impregnate 30 minutes after, cooling 15 minutes to room temperature, drawn with 3M adhesive tapes are viscous, marble paper is without falling off.
The step of step 2 and step 4 are most critical of the present invention in the present invention, the effect of step 2 are to make marble paper with radium-shine
Effect, step 4 are to play the role of protecting marble paper pattern.
Water at low temperature provided by the invention, which transfers radium-shine marble paper, can make the commodity packagings such as ceramic/glass/metal/plastic have flower
There is laser effect again while colored pattern.
Advantage:For the technology of the present invention instead of traditional high temperature marble paper (700-900 degree, 9-10h), advantage is to save energy
Source, cost-effective, environmental protection, raising production efficiency, traditional high temperature marble paper need to burn to 700-900 degree, and 9-10 hours, the energy consumed
Fei Duo, long time period.And low temperature marble paper of the present invention, it is only necessary to fire 150-175 degree, toast 0.5-2 hours, significantly
The energy and time are saved.It can flash back and recycle again, be 700- on the ceramic body after being attached to glaze firing due to marble paper
Under 900 degree of conditions of high temperature, glaze is initially located in molten condition, and glaze will certainly be destroyed by being fired again such as high temperature marble paper, and low temperature
Marble paper is since baking temperature is low, and only 150-175 degree does not interfere with glaze quality, therefore can flash back and recycle again at this time.Make
It obtains the radium-shine marble paper of the invention prepared to have a wide range of application, overcomes the single defect of high temperature marble paper color, decorative colour is abundant.
The present invention will be further described for following embodiment, but the protection model that the embodiment is not intended to limit the invention
It encloses.
Specific implementation mode
Embodiment 1
Step 1):One layer of gold stamping base oil is printed with the mode that silk-screen printing or offset printing are combined on membranelle base stock, then
Under room temperature more than drying for 24 hours;
Step 2):Gilding press gold stamping marble paper at 120 DEG C is used on the membranelle base stock made from step 1), and membranelle base stock is made to have
There is laser effect;
Step 3):On the radium-shine part of membranelle base stock that step 2) obtains spot color or four are stamped with the method for silk-screen or offset printing
Color water-soluble environment-friendly ink, the marble paper are made of transparent part and opaque section, and opaque section is completely covered by radium-shine area,
Radium-shine area is appeared from transparent part at transparent part, and the pattern of transparent part is made to have in various degree radium-shine according to its transparency
Effect.
Step 4):After the completion of the step 3), one layer of isolation oil of silk-screen printing, room temperature 30-35 degree is dried for 24 hours.
Step 5):On the basis of step 4) one layer of silk-screen printing can dyestripping, 30-35 degree dries 12h or more under room temperature.
Step 6):By membranelle base stock made from step 5), water at low temperature transfers radium-shine marble paper water and turns after detaching, and is attached to pottery
Porcelain/glass/metal/plastics etc. above, can dyestripping tear.Water at low temperature will be posted transfer later the ceramic/glass of radium-shine marble paper/
Metal/plastic etc. toasts 2h to get to finished product at 150 DEG C.
Products obtained therefrom is subjected to marble paper firmness test:Before room temperature does not impregnate, garland paper, flower are continuously glued three times with 3M adhesive tapes
Paper is without falling off;Airing after marble paper is impregnated 2 hours in 55%vol white wine, 3M adhesive tapes glue garland paper, and marble paper is without falling off;It will spend
After paper impregnates 30 minutes in 50 DEG C of hot water, bottle phase mutual friction in water is picked up for 20 times, marble paper without it is damaged, fall off;By marble paper
It after being impregnated 30 minutes in 50 DEG C of hot water, cooling 15 minutes to room temperature, is drawn with 3M adhesive tapes are viscous, marble paper is without falling off.
Embodiment 2
Step 1):One layer of gold stamping base oil is printed with the mode that silk-screen printing or offset printing are combined on membranelle base stock, then
Under room temperature more than drying for 24 hours;
Step 2):Gilding press gold stamping marble paper at 140 DEG C is used on the membranelle base stock made from step 1), and membranelle base stock is made to have
There is laser effect;
Step 3):On the radium-shine part of membranelle base stock that step 2) obtains spot color or four are stamped with the method for silk-screen or offset printing
Color water-soluble environment-friendly ink, the marble paper are made of transparent part and opaque section, and opaque section is completely covered by radium-shine area,
Radium-shine area is appeared from transparent part at transparent part, and the pattern of transparent part is made to have in various degree radium-shine according to its transparency
Effect.
Step 4):After the completion of the step 3), one layer of isolation oil of silk-screen printing, room temperature 30-35 degree is dried for 24 hours.
Step 5):On the basis of step 4) one layer of silk-screen printing can dyestripping, 30-35 degree dries 12h or more under room temperature.
Step 6):Water at low temperature made from step 5) is transferred radium-shine marble paper water to turn after detaching, is attached to ceramic/glass/gold
Category/plastics etc. above, can dyestripping tear.Ceramic/glass/metal/plastic of radium-shine marble paper water at low temperature will be posted transferred later
1.5h is toasted to get to finished product Deng at 160 DEG C.
Products obtained therefrom is subjected to marble paper firmness test:Before room temperature does not impregnate, garland paper, flower are continuously glued three times with 3M adhesive tapes
Paper is without falling off;Airing after marble paper is impregnated 2 hours in 55%vol white wine, 3M adhesive tapes glue garland paper, and marble paper is without falling off;It will spend
After paper impregnates 30 minutes in 50 DEG C of hot water, bottle phase mutual friction in water is picked up for 20 times, marble paper without it is damaged, fall off;By marble paper
It after being impregnated 30 minutes in 50 DEG C of hot water, cooling 15 minutes to room temperature, is drawn with 3M adhesive tapes are viscous, marble paper is without falling off.
Embodiment 3
Step 1):One layer of gold stamping base oil is printed with the mode that silk-screen printing or offset printing are combined on membranelle base stock, then
Under room temperature more than drying for 24 hours;
Step 2):Gilding press gold stamping marble paper at 150 DEG C is used on the membranelle base stock made from step 1), and membranelle base stock is made to have
There is laser effect;
Step 3):On the radium-shine part of membranelle base stock that step 2) obtains spot color or four are stamped with the method for silk-screen or offset printing
Color water-soluble environment-friendly ink, the marble paper are made of transparent part and opaque section, and opaque section is completely covered by radium-shine area,
Radium-shine area is appeared from transparent part at transparent part, and the pattern of transparent part is made to have in various degree radium-shine according to its transparency
Effect.
Step 4):After the completion of the step 3), one layer of isolation oil of silk-screen printing, room temperature 30-35 degree is dried for 24 hours.
Step 5):On the basis of step 4) one layer of silk-screen printing can dyestripping, 30-35 degree dries 12h or more under room temperature.
Step 6):Water at low temperature made from step 5) is transferred radium-shine marble paper water to turn after detaching, is attached to ceramic/glass/gold
Category/plastics etc. above, can dyestripping tear.Ceramic/glass/metal/plastic of radium-shine marble paper water at low temperature will be posted transferred later
0.5h is toasted to get to finished product Deng at 175 DEG C.
Above-described embodiment membranelle base stock selects figure Li Shi paper industry (Korean Utility Model Laid), 500*700mm, 540*390mm, 350*
500mm。
Gold stamping base oil selects nine ACE Semi's number 813, thickness 0.05-0.1mm.
Products obtained therefrom is subjected to marble paper firmness test:Before room temperature does not impregnate, garland paper, flower are continuously glued three times with 3M adhesive tapes
Paper is without falling off;Airing after marble paper is impregnated 2 hours in 55%vol white wine, 3M adhesive tapes glue garland paper, and marble paper is without falling off;It will spend
After paper impregnates 30 minutes in 50 DEG C of hot water, bottle phase mutual friction in water is picked up for 20 times, marble paper without it is damaged, fall off;By marble paper
It after being impregnated 30 minutes in 50 DEG C of hot water, cooling 15 minutes to room temperature, is drawn with 3M adhesive tapes are viscous, marble paper is without falling off.
The above technical scheme, beneficial effects of the present invention is taken to be:
One, marble paper product produced by the present invention is tested by stringent firmness, and for marble paper without obscission, product is whole
Body is stable, weather-proof, service life is long.
Two, technology of the invention is instead of traditional high temperature marble paper (700-900 degree, 9-10h), advantage be it is energy saving,
It is cost-effective, environmental protection, raising production efficiency, traditional high temperature marble paper needs burning to 700-900 degree, 9-10 hours, energy consumption
More, long time period.And low temperature marble paper of the present invention, it is only necessary to fire 150-175 degree, toast 0.5-2 hours, save significantly
The about energy and time.It can flash back and recycle again, be 700-900 on the ceramic body after being attached to glaze firing due to marble paper
It spends under the condition of high temperature, glaze is initially located in molten condition, and glaze will certainly be destroyed by being fired again such as high temperature marble paper, for radium-shine right
It is then more sensitive to temperature as plastics idiosome.And low temperature marble paper is since baking temperature is low, only 150-175 degree, at this time
Glaze quality is not interfered with, therefore can flash back and recycle again.So that radium-shine marble paper prepared by the present invention has a wide range of application, overcome
High temperature marble paper color single defect, decorative colour are abundant.
Several embodiments of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
Cannot the limitation to the scope of the claims of the present invention therefore be interpreted as, it is noted that for those skilled in the art,
Without departing from the inventive concept of the premise, several deformations and transformation can also be made, these belong to the protection model of the present invention
It encloses, therefore, the protection domain of patent of the present invention is determined by the appended claims.
Claims (8)
1. a kind of method that water at low temperature transfers radium-shine marble paper, which is characterized in that include the following steps:
1) one layer of gold stamping base oil is printed with the mode of silk-screen printing and/or offset printing on membranelle base stock, carried out dry for the first time;
2) the gold stamping marble paper of gilding press is used on the membranelle base stock made from step 1), makes membranelle base stock that there is laser effect, is had
There is the membranelle base stock of radium-shine part;
3) on the radium-shine part for the membranelle base stock that step 2) obtains water-soluble environment-friendly ink is stamped with the method for silk-screen or offset printing;
4) one layer of isolation oil of the membranelle base stock printing after step 3) completion, carries out second of drying;
5) the membranelle base stock after step 4) completion print one layer can dyestripping, carry out obtaining water at low temperature transfer after third time is dry
Radium-shine marble paper;
6) after step 5) completion, water at low temperature is transferred into radium-shine marble paper water and is turned after detaching, is attached on radium-shine pasted objects, tears
Go can dyestripping, toast to get the marble paper finished product with laser effect.
2. according to the method described in claim 1, it is characterized in that, the specification of membranelle base stock turns for neatly formula in the step 1)
Printing paper.
3. according to the method described in claim 1, it is characterized in that, the temperature of gold stamping marble paper is 120~150 in the step 2)
℃。
4. according to the method described in claim 1, it is characterized in that, in the step 3) water-soluble environment-friendly ink be spot color or
Four color water-soluble environment-friendly ink.
5. according to the method described in claim 4, it is characterized in that, the color of water-soluble environment-friendly ink is water in the step 3)
Turn former yellow, the high combination for covering white and water and turning one or more of goth black of bright red, water turn.
6. according to the method described in claim 1, it is characterized in that, the thickness of the step 4) the isolation oil is 0.05-
0.1mm, drying temperature are 30-35 DEG C, drying time >=for 24 hours.
7. according to the method described in claim 1, it is characterized in that, described in the step 5) can the drying temperature of dyestripping be
30-35 DEG C, drying time >=12h.
8. according to the method described in claim 1, it is characterized in that, water at low temperature transfers radium-shine marble paper water turn point in the step 6)
Include from step:The membranelle base stock that will be finished printing entirely is immersed in normal-temperature water 3-5 minutes, membranelle base stock is removed, will scheme
The taking-up of pattern layer marble paper is pasted onto on ceramics, glass, metal or plastic preform, and 0.5-2h is toasted at 150-175 DEG C.