CN106739738A - A kind of holographic laser raster picture and text water transfers marble paper preparation method - Google Patents
A kind of holographic laser raster picture and text water transfers marble paper preparation method Download PDFInfo
- Publication number
- CN106739738A CN106739738A CN201710003207.8A CN201710003207A CN106739738A CN 106739738 A CN106739738 A CN 106739738A CN 201710003207 A CN201710003207 A CN 201710003207A CN 106739738 A CN106739738 A CN 106739738A
- Authority
- CN
- China
- Prior art keywords
- parts
- text
- water
- picture
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of holographic laser raster picture and text water transfer marble paper preparation method, equidistant holographic laser raster picture and text anodized aluminium is made first, then by the gold stamping base oil ink of itself and printing, the water at low temperature transfer marble paper that printing method makes is hotly joined into by water-transfer printing paper Zhang Dingwei, not only luxurious fineness, with uniqueness anti-counterfeiting information, and its effective solid picture and text directly perceived, the stereo relief effect of impact vision can be reached.
Description
Technical field
The present invention relates to technical field of packaging and printing, and in particular to a kind of holographic laser raster picture and text water transfer marble paper makes
Method.
Background technology
Water at low temperature transfer marble paper printing method is the water-transfer printing paper and anodized aluminium of the gold stamping base oil ink of printing on current market
The compound printing method of full version blanching is made water at low temperature transfer marble paper, is shifted through water, can toast and be attached to glass surface, ceramic plane, oil
On the product surfaces such as lacquer painting, metal covering, plastic cover, with performances such as ethanol-tolerant, rub resistances, bright color and low-temperature bake is only needed
The characteristics of, product is widely used on the products such as glass, ceramic ornament, if hot with anodized aluminium full version using gold stamping base oil ink is printed
Scald compound printing method and be made water transfer low temperature marble paper, have the following disadvantages：1st, light water transfer marble paper is without holography
Pattern function；2nd, light water transfer marble paper does not reach 3D and four-dimensional effect；3rd, light water transfer marble paper does not have ultra-thin multiple-layer stand
Body picture and text；4th, light water transfer marble paper does not strengthen the visual sense of beauty and class of the ornament of glass, ceramics etc.；5th, light water turns
Calico paper does not reach plastic relief picture and text effect；6th, light water transfer marble paper is stealthy anti-without micro, laser, mole encryption etc.
Puppet effect；7th, anodized aluminium non-refractory, high pressure molding used by light water transfer marble paper.
Because the water-transfer printing paper that Conventional cryogenic water transfer marble paper printing method is the gold stamping base oil ink of printing is expired with anodized aluminium
Version blanching be combined, water at low temperature transfer marble paper to be firmly attached on the surface of decoration such as glass surface, ceramic plane, paint face, it is necessary to
Can just be reached by 150 DEG C~210 DEG C degree bakings, and the holographic grating picture and text layer of existing in the market holographic laser raster anodized aluminium
Be the soft pressure of 110 DEG C~120 DEG C molding machine nickel plates or in it is molded, when baking temperature is more than 120 DEG C of mould temperature, laser is complete
Breath grating picture and text layer will dissipate, and imaging function coating resin layer can not bear 150 DEG C~210 DEG C of temperature baking, so existing
In the market holographic laser raster picture and text anodized aluminium can not meet the baking demand that present common process water at low temperature transfers marble paper.
The content of the invention
In view of this, it is an object of the invention to overcome the shortcomings of above-mentioned prior art, there is provided it is a kind of it is new, be suitable to work
The holographic laser raster picture and text water transfer marble paper preparation method that industry metaplasia is produced.Equidistant holographic laser raster picture and text are made first
Anodized aluminium, then by the gold stamping base oil ink of itself and printing, the water at low temperature that printing method makes is hotly joined into by water-transfer printing paper Zhang Dingwei
Marble paper is transferred, not only luxurious fineness, with uniqueness anti-counterfeiting information, and its effective solid picture and text directly perceived, impact can be reached
The stereo relief effect of vision.
To solve above technical problem, technical solution of the present invention provides a kind of calico paper preparation method, described method bag
Include following steps：
1) holographic laser raster picture and text anodized aluminium, is made；
2), holographic laser raster picture and text anodized aluminium positioning is scalded and is being printed on the water-transfer printing paper of gold stamping base oil ink；
3), printing auxiliary picture and text, printing protection gloss oil, can dyestripping.
Preferably, it is described to make concretely comprising the following steps for holographic laser raster picture and text anodized aluminium：
A), design and produce equidistant holographic laser raster picture and text anodized aluminium and press nickel version firmly,
B), be coated with mould release and functional paint successively on film, form release layer and functional layer, then through it is vacuum aluminum-coated it
Afterwards, aluminium coated is formed, the first prefabricated component is obtained；
First prefabricated component is pressed in nickel plate firmly in the anodized aluminium, temperature is pressed firmly for 220-280 DEG C, will be described
Holographic laser raster picture and text are transferred in the functional layer of first prefabricated component, are coated protective agent, form protective layer, obtain the
Two prefabricated components；
C) second prefabricated component, is drawn into equidistant holographic laser raster picture and text anodized aluminium.
Preferably, described functional layer is made up of the raw material of following mass parts：5 parts~40 parts of cellulose butyrate resin, fibre
Plain 3 parts~25 parts of the resin of dimension, 5 parts~30 parts of ethylene acid resin, 1 part~10 parts of styrene anhydride resin, amino resins 2 parts~10
Part, 3 parts~15 parts of unsaturated polyester (UP), 1 part~10 parts of epoxy resin, 2 parts~10 parts of polyurethane, 1 part~5 parts of auxiliary agent, solvent 50
Part~75 parts.
Preferably, the organic toner in described functional layer adds stirring for 5 parts~35 parts according to organic toner.
Preferably, step 2) the compound temperature of positioning is 110 DEG C~260 DEG C, speed is 3m/s~25m/s.
Preferably, step 3) in be dried treatment after each step, dry auxiliary picture and text ink, dried through drying tunnel
38-42 DEG C of temperature, drying time 1-3h, dry-run protection gloss oil, through 38-42 DEG C of drying tunnel drying temperature, drying time 1-3h is dried
Can dyestripping, 26-30 DEG C of indoor temperature dries 4-6h.
Technical solution of the present invention also provides a kind of printing transferring method of above-mentioned transfer marble paper, and described method includes following step
Suddenly：
1) holographic laser raster picture and text water transfer marble paper, is placed in water immersion, water transfer marble paper is positioned at product
On relevant position, then water-transfer printing paper is extracted out；
2), being removed after low temperature drying can dyestripping；
3) the said goods, are put into baking oven, baking and curing.
Preferably, step 1) soak time is 10-15s in reclaimed water.
Preferably, step 2) in temperature be 40 DEG C~75 DEG C, 20~45min of time, or natural air dry 2h-6h is dried.
Preferably, step 3) in temperature be 150 DEG C~210 DEG C degree, 10~45min of time attachment solidification.
The present invention is described in further detail below：
The invention provides a kind of preparation method of calico paper, the method is by preparing the special holographic laser raster of high temperature resistant
Picture and text anodized aluminium, then it scalded be compounded on water-transfer printing paper with gold stamping base oil ink positioning, and auxiliary view is republished on its surface
Text, protection gloss oil, can dyestripping, specific preparation process is as follows：
1), design and produce equidistant holographic laser raster picture and text anodized aluminium and press nickel version and laser holograph anodized aluminium firmly
The gold stamping base oil ink registration pattern of pattern；
2) holographic laser raster picture and text anodized aluminium, is made；
3), the holographic laser raster picture and text anodized aluminium that will be made with equidistant film drawing device is drawn into equidistant laser
Holographic grating picture and text anodized aluminium；
4) film, printing screen version, are made；
5) commercially available water-soluble water transfer base stock, is taken, base stock is dried；
6) the thin version printing of gold stamping base oil ink, is transferred into base stock to water-soluble water on the printer with the equidistant thin version of printing
On, the gold stamping base oil ink of the thin version of drying；
7) equidistant holographic laser raster picture and text anodized aluminium, is scalded compound with gold stamping base oil ink positioning with positioning bronzing machine
On water-transfer printing paper；
8), dry air dry positioning it is hot after water-soluble water transfer base stock, allow water-soluble water to transfer base stock through high temperature thermal expansion
After reduce；
9), printing auxiliary picture and text, printing protection gloss oil, can dyestripping.
Preferably, the preparation method of holographic laser raster picture and text anodized aluminium is as follows：
A), design and produce equidistant holographic laser raster picture and text anodized aluminium and press nickel version firmly,
B), be coated with mould release and functional paint successively on film, form release layer and functional layer, then through it is vacuum aluminum-coated it
Afterwards, aluminium coated is formed, the first prefabricated component is obtained；
First prefabricated component is pressed in nickel plate firmly in the anodized aluminium, temperature is pressed firmly for 220-280 DEG C, will be described
Holographic laser raster picture and text are transferred in the functional layer of first prefabricated component, are coated protective agent, form protective layer, obtain the
Two prefabricated components；
C) second prefabricated component, is drawn into equidistant holographic laser raster picture and text anodized aluminium.
Preferably, described functional layer is made up of the raw material of following mass parts：5 parts~40 parts of cellulose butyrate resin, fibre
Plain 3 parts~25 parts of the resin of dimension, 5 parts~30 parts of ethylene acid resin, 1 part~10 parts of styrene anhydride resin, amino resins 2 parts~10
Part, 3 parts~15 parts of unsaturated polyester (UP), 1 part~10 parts of epoxy resin, 2 parts~10 parts of polyurethane, 1 part~5 parts of auxiliary agent, solvent 50
Part~75 parts.Preferably, described solvent is the organic solvents such as ketone and esters, it is preferred that organic in described functional layer
Colorant adds stirring for 5 parts~35 parts according to organic toner.
Above-mentioned functions layer is the dope layer with imaging function, and the dope layer passes through specific resin composition, the screening of content
And proportioning, make described dope layer that there is resistant to elevated temperatures technique effect, therefore in the preparation process of anodized aluminium, on film according to
Secondary coating mould release and functional paint, form release layer and functional layer, then through after vacuum aluminum-coated, forming aluminium coated, it is described
The nickel plate that composite bed can bear 220-280 DEG C is pressed firmly, holographic laser raster picture and text is passed through aluminium coated, is transferred to functional layer
In, described laser holograph clearly can be transferred in functional layer, and anodized aluminium used is the above method in the present invention
The special anodized aluminium of high temperature resistant of preparation.
Preferably, step 4) preparation method it is as follows：
Gold stamping base oil ink system is made according to the electrochemical aluminium gold-stamped base oil ink registration pattern of equidistant holographic laser raster picture and text
Make film, it is equidistant to make same printing according to the electrochemical aluminium gold-stamped base oil ink registration pattern film of holographic laser raster picture and text
Print thin version.
Preferably, step 7) in the compound temperature of positioning be 110 DEG C~260 DEG C, speed is 3m/s~25m/s.
Temperature and speed can realize the precise positioning of thermoprint in the boiling hot recombination process of above-mentioned positioning, if temperature is low, no
All the special laser holograph anodized aluminium positioning of high temperature resistant can be ironed on equidistant gold stamping base oil ink, can also the boiling hot upper electricity of full version
Change aluminium, or even cause the phenomenons such as overlap, and speed is fast is just enclosed within equidistant gold stamping base oil ink, or even positioning picture and text occur
Partially, leak boiling hot etc.；
Preferably, step 9) in be dried treatment after each step, dry auxiliary picture and text ink, dried through drying tunnel
38-42 DEG C of temperature, drying time 1-3h, dry-run protection gloss oil, through 38-42 DEG C of drying tunnel drying temperature, drying time 1-3h is dried
Can dyestripping, 26-30 DEG C of indoor temperature dries 4-6h.
Technical solution of the present invention also provides a kind of printing transferring method of above-mentioned calico paper, and described method is comprised the following steps：
1) holographic laser raster picture and text water transfer marble paper, is placed in water immersion, water transfer marble paper is positioned at product
On relevant position, then water-transfer printing paper is extracted out；
2), being taken off after low temperature drying can dyestripping；
3) the said goods, are put into baking oven, baking and curing.
Preferably, step 1) soak time is 10-15s in reclaimed water.
Preferably, step 2) in temperature be 40 DEG C~75 DEG C, 20~45min of time, or natural air dry 2h-6h is dried.
Preferably, step 3) in temperature be 150 DEG C~210 DEG C degree, 10~45min of time attachment solidification.
The invention provides a kind of preparation method of calico paper, the method laser hologram light special by preparing high temperature resistant
Grid picture and text anodized aluminium, then it scalded be compounded on water-transfer printing paper with gold stamping base oil ink positioning, and auxiliary is republished on its surface
Picture and text, protection gloss oil, can dyestripping.First, the method is different from the water-transfer printing paper of traditional anodized aluminium and the gold stamping base oil ink of printing
Edition blanching that is filled is combined the water at low temperature transfer marble paper that system makes, and being scalded by positioning can realize the precise positioning of thermoprint, scald correction
The positioning image of the location division of hot stamping foil, production efficiency is substantially improved, and product quality also increases；Secondly, the present invention
Anodized aluminium preparation process in, by specific resin composition, the screening of content and proportioning prepare functional layer, with high temperature resistant
Effect, therefore the temperature carried out on moulding press when nickel plate is pressed firmly can reach 220 DEG C~280 DEG C, make holographic laser raster
Picture and text are transferred in functional layer, and will not also be dissipated, therefore the above method scalds work by the making and positioning of specific anodized aluminium
Skill realizes the anti-counterfeiting information of paper, and has reached effective intuitively effect.
From above-mentioned technical proposal as can be seen that the invention has the advantages that：
1) functional layer in anodized aluminium preparation process of the invention is the dope layer with imaging function, described dope layer
By specific resin composition, the screening of content and proportioning, obvious resistant to elevated temperatures technique effect is made it have.
2) functional layer in anodized aluminium preparation process of the invention is the dope layer with imaging function, organic toner according to
5 parts~35 parts of organic toner adds stirring, can be according to the actually required imaging work(for preparing required color in production process
Can painting color layer.
3) mould release and functional paint are coated with anodized aluminium preparation process of the invention successively on film, release layer is formed
And functional layer, then through after vacuum aluminum-coated, it is enterprising in the moulding press equipped with holographic laser raster picture and text nickel plate after forming aluminium coated
220 DEG C~280 DEG C nickel plates of row are pressed firmly, during holographic laser raster picture and text can copy to functional layer through aluminium coated, are different from existing
There is the direct embossed holographic security pattern on imaging layer in technology, then aluminize, the method overcome traditional anodized aluminium in baking
When temperature is more than 120 DEG C of mould temperature, the defect that holographic laser raster picture and text layer will dissipate, there is provided it is a kind of it is real at high temperature
Exquisite pattern with laser antifalse effect and containing laser hologram and can be with the laser hologram light of high-quality thermoprint
Grid picture and text anodized aluminium.
4) the holographic laser raster picture and text anodized aluminium that the present invention is used and the gold stamping base oil ink of printing, by water-transfer printing paper Zhang Ding
Position hotly joins into printing method, instead of traditional anodized aluminium and the water-transfer printing paper of printing gold stamping base oil ink and is filled the compound system of edition blanching
The water at low temperature of making transfers marble paper, not only luxurious fineness, with uniqueness anti-counterfeiting information, and its effective stereogram directly perceived
Text, can reach the stereo relief effect of impact vision.
5) the electrochemical aluminium gold-stamped technology of water robin of the invention can be by swashing that user's requirement making multiple color is matched
Light holographic grating picture and text water transfers marble paper, and production process is specialized, is applicable to the multiples such as the gold stamping decoration of lamp decoration, vessel, trade mark
Field, can be applied on the base materials such as glass, ceramics, metal, plastics, woodenware, be that the present invention can decorate anodized aluminium more particularly
The positions such as hard, curved surface, irregular face and corner are applied to, the range of application of electrochemical aluminium gold-stamped technology is greatly expanded.
Specific embodiment
Embodiment 1：
1), design and produce equidistant holographic laser raster picture and text anodized aluminium and press nickel version and laser holograph anodized aluminium firmly
The gold stamping base oil ink registration pattern of pattern；
2) holographic laser raster picture and text anodized aluminium, is made：
21) mould release and functional paint, are coated with successively on film with coating machine, release layer and functional layer, coating is formed
Through 135 DEG C~175 DEG C, 7s~15s baking dryings on machine；
22) it is, vacuum aluminum-coated；
23) vacuum aluminum-coated rear plastic sheeting, is being pressed into the moulding press of nickel version equipped with holographic laser raster picture and text anodized aluminium firmly
On carry out 220 DEG C~280 DEG C nickel plates and press firmly, holographic laser raster picture and text are copied in functional layer；
24), it is molded into coat protective layer in the functional layer as after in holographic grating pattern with coating machine；
Wherein, described high temperature imaging function dope layer is made up of the raw material of following mass parts：5 parts of cellulose butyrate resin
~40 parts, 3 parts~25 parts of celluosic resin, 5 parts~30 parts of ethylene acid resin, 1 part~10 parts of styrene anhydride resin, amino tree
2 parts~10 parts of fat, 3 parts~15 parts of unsaturated polyester (UP), 1 part~10 parts of epoxy resin, 2 parts~10 parts of polyurethane, auxiliary agent 1 part~5
Part, 50 parts~75 parts of solvent, the organic toner of described imaging function painting color layer are added for 5 parts~35 parts according to organic toner
Stirring.
3), the holographic laser raster picture and text anodized aluminium that will be made with equidistant film drawing device is drawn into equidistant laser
Hologram grating anodized aluminium；
4) film, galley, are made, according to the electrochemical aluminium gold-stamped base oil ink positioning of equidistant holographic laser raster picture and text
Pattern makes gold stamping bottom printing ink to manufacture film, according to the electrochemical aluminium gold-stamped base oil ink registration pattern film of holographic laser raster picture and text
Piece makes the equidistant thin version of printing of same printing；
5), water-soluble water transfers base stock and dries base stock, controls drying temperature and time；
6), with the equidistant thin version of printing on the printer by gold stamping base oil ink (purchased from Jiangxi profit monarch's science and technology, model UV750)
Thin version printing is transferred on base stock to water-soluble water；
7), the gold stamping base oil ink of the thin version of drying, controls drying temperature and time；
8), with positioning bronzing machine by equidistant holographic laser raster picture and text anodized aluminium be printed on Bao Mo, thick black gold stamping bottom
The water-soluble water transfer base stock positioning of ink is scalded and is combined, and is combined through 110 DEG C~260 DEG C on positioning bronzing machine, is controlled
Positioning bronzing machine cylinder heating-up temperature, speed 3m/s~25m/s；
9), dry air dry positioning it is hot after water-soluble water transfer base stock, allow water-soluble water to transfer base stock through high temperature thermal expansion
After reduce；
10), by step 4) method for platemaking, holographic laser raster picture and text water transfer marble paper is made respectively, and other aid in picture and text
Galley, other the auxiliary picture and text required for press printing holographic laser raster picture and text, dries other auxiliary picture and text ink, warp
38-42 DEG C of drying tunnel drying temperature, drying time 1-3h；
11) protection gloss oil (being purchased from Chongqing Billiter printing material Co., Ltd, model JX-200), is printed on printing machine,
Dry-run protection gloss oil, through 38-42 DEG C of drying tunnel drying temperature, drying time 1-3h；
12), on printing machine printing can dyestripping, can dyestripping be the tearable front cover film of polystyrene, dry front cover film, indoor temperature
26-30 DEG C, dry 4-6h；
13), check；
14), packaging and storage.
When using, by 10~50 seconds in holographic laser raster picture and text water transfer marble paper soaking water, water transfer marble paper is positioned
The position needed for the surface of decoration of glass, ceramics etc., then slowly extracts water-transfer printing paper out, transfers water with soft spreading knife and spends
The water of paper bottom scrapes discharge.The ornament that glass, the ceramics of holographic laser raster picture and text water transfer marble paper etc. will be adhesive with is put into
40 DEG C~75 DEG C of baking oven toasts 20~45 minutes (can 2 hours~6 hours natural air dry dry), but this film is removed after drying.Swash
After but light holographic grating picture and text water transfer marble paper removes this film, with wet towel by the marble paper table on the ornament of glass, ceramics etc.
Face sassafras is clean, is put into baking oven and toasts 150 DEG C~210 DEG C degree, and constant temperature attachment baking in 10~45 minutes is produced in glass, ceramic ornament etc.
On product surface, decorative pattern is formed.
Embodiment 2：
1) the special holographic laser raster picture and text anodized aluminium of high temperature resistant, is designed and produced, with step in embodiment one；
2) the thick galley of film, 0.2mm~1.2mm, is made.According to equidistant holographic laser raster picture and text electrification
The gold stamping base oil ink registration pattern of aluminium makes gold stamping bottom printing ink to manufacture film, according to the electrochemical aluminium gold-stamped bottom of holographic laser raster picture and text
Ink registration pattern film makes the equidistant thin version of printing of same printing；
3), water-soluble water transfers base stock and dries base stock, controls drying temperature and time；
4), with equidistant embossment galley on the printer by gold stamping base oil ink (purchased from Jiangxi profit monarch's science and technology, model
UV750) it is printed onto on water-soluble water transfer base stock；
5) the gold stamping base oil ink of embossment version, is dried, drying temperature and time is controlled；
6), with positioning bronzing machine by equidistant holographic laser raster picture and text anodized aluminium be printed on Bao Mo, thick black gold stamping bottom
The water-soluble water transfer base stock positioning of ink is scalded and is combined, and is combined through 110 DEG C~260 DEG C on positioning bronzing machine, speed
3m/s~25m/s；
7), dry air dry positioning it is hot after water-soluble water transfer base stock, allow water-soluble water to transfer base stock through high temperature thermal expansion
After reduce；
8), by step 2) method for platemaking, holographic laser raster picture and text water transfer marble paper is made respectively, and other aid in picture and text
Galley, other the auxiliary picture and text required for press printing holographic laser raster picture and text, dries other auxiliary picture and text ink, warp
38-42 DEG C of drying tunnel drying temperature, drying time 1-3h；
9) protection gloss oil (being purchased from Chongqing Billiter printing material Co., Ltd, model JX-200), is printed on printing machine, is done
Dry protection gloss oil, through 38-42 DEG C of drying tunnel drying temperature, drying time 1-3h；
10), on printing machine printing can dyestripping, can dyestripping be the tearable front cover film of polystyrene, dry laminate cover, Indoor Temperature
26-30 DEG C of degree, dries 4-6h；
11), check；
12), packaging and storage.
The above method can produce the holographic laser raster picture and text water transfer marble paper with embossing pattern.
Embodiment 3：
1) the special holographic laser raster picture and text anodized aluminium of high temperature resistant, is designed and produced, with the step of embodiment one；
2), water-soluble water transfers base stock and dries base stock, controls drying temperature and time；
3), press printing white bottoming ink (being purchased from Dongguan Mei Ji printing materials Co., Ltd, model MJ102), does
Dry white bottoming ink, controls drying temperature and time；
4), printing machine prints the color inks of CMYK tetra- (purchased from Hang Hua ink limited company, model UV161 oil respectively
Ink), the color inks of CMYK tetra- are dried, control drying temperature and time；
5), press printing vacation metallic ink, dries vacation metallic ink, controls drying temperature and time；
6), press printing does not scald laser holograph anodized aluminium isolation gloss oil (purchased from the ACE Semi's electronic material of Kunshan nine
Co., Ltd, model 910-51 isolation gloss oil), make to be formed on white bottoming ink, false bronze ink and the color ink patterns of CMYK tetra-
Anodized aluminium isolation oil reservoir is not scalded, drying is not scalded anodized aluminium isolation light oil reservoir, controls drying temperature and time；
7), with the equidistant thin version of printing on the printer by gold stamping base oil ink (purchased from Jiangxi profit monarch's science and technology, model UV750)
Thin version printing is transferred on base stock to water-soluble water；
8), the gold stamping base oil ink of the thin version of drying, controls drying temperature and time；
9) gold stamping base oil ink thickness version printing, is transferred into base stock to water-soluble water on the printer with equidistant embossment galley
On, the thick ink effects of 0.2mm~1.2mm are printed off, the gold stamping base oil ink of embossment version is dried, control drying temperature and time；
10), with positioning bronzing machine by equidistant holographic laser raster picture and text anodized aluminium be printed on Bao Mo, thick black gold stamping bottom
The water-soluble water transfer base stock positioning of ink is scalded and is combined, and is combined through 110 DEG C~260 DEG C on positioning bronzing machine, speed
3m/s~25m/s；
11), dry air dry positioning it is hot after water-soluble water transfer base stock, allow water-soluble water to transfer base stock through high temperature thermal expansion
After reduce；
12) protection gloss oil (being purchased from Chongqing Billiter printing material Co., Ltd, model JX-200), is printed on printing machine,
Dry-run protection gloss oil, through 38-42 DEG C of drying tunnel drying temperature, drying time 1-3h；
13), on printing machine printing can dyestripping, can dyestripping be the tearable front cover film of polystyrene, dry laminate cover, Indoor Temperature
26-30 DEG C of degree, dries 4-6h；
14), check；
15), packaging and storage.
The above is only the preferred embodiment of the present invention, it is noted that it is right that above-mentioned preferred embodiment is not construed as
Limitation of the invention, protection scope of the present invention should be defined by claim limited range.For the art
For those of ordinary skill, without departing from the spirit and scope of the present invention, some improvements and modifications can also be made, these change
Enter and retouch and also should be regarded as protection scope of the present invention.
Claims (10)
1. a kind of calico paper preparation method, it is characterised in that step is as follows：
1) holographic laser raster picture and text anodized aluminium, is made；
2), holographic laser raster picture and text anodized aluminium positioning is scalded and is being printed on the water-transfer printing paper of gold stamping base oil ink；
3), printing auxiliary picture and text, printing protection gloss oil, can dyestripping.
2. calico paper preparation method as claimed in claim 1, it is characterised in that the making holographic laser raster picture and text electrification
Aluminium is concretely comprised the following steps：
A), design and produce equidistant holographic laser raster picture and text anodized aluminium and press nickel version firmly,
B), it is coated with mould release and functional paint successively on film, forms release layer and functional layer, then through after vacuum aluminum-coated,
Aluminium coated is formed, the first prefabricated component is obtained；
First prefabricated component is pressed in nickel plate firmly in the anodized aluminium, temperature is pressed firmly for 220-280 DEG C, make the laser
Holographic grating picture and text are transferred in the functional layer of first prefabricated component, are coated protective agent, form protective layer, obtain second pre-
Product；
C) second prefabricated component, is drawn into equidistant holographic laser raster picture and text anodized aluminium.
3. calico paper preparation method as claimed in claim 2, it is characterised in that described functional layer by following mass parts original
Material is made：5 parts~40 parts of cellulose butyrate resin, 3 parts~25 parts of celluosic resin, 5 parts~30 parts of ethylene acid resin, styrene
It is 1 part~10 parts of anhydride resin, 2 parts~10 parts of amino resins, 3 parts~15 parts of unsaturated polyester (UP), 1 part~10 parts of epoxy resin, poly-
2 parts~10 parts of urethane, 1 part~5 parts of auxiliary agent, 50 parts~75 parts of solvent.
4. calico paper preparation method as claimed in claim 3, it is characterised in that organic toner in described functional layer according to
5 parts~35 parts of organic toner adds stirring.
5. calico paper preparation method as claimed in claim 1, it is characterised in that step 2) in the compound temperature of positioning be 110
DEG C~260 DEG C, speed is 3m/s~25m/s.
6. calico paper preparation method as claimed in claim 1, it is characterised in that step 3) in done after each step
Dry treatment, dries auxiliary picture and text ink, through 38-42 DEG C of drying tunnel drying temperature, drying time 1-3h, dry-run protection gloss oil, through drying
38-42 DEG C of road drying temperature, drying time 1-3h, drying can dyestripping, 26-30 DEG C of indoor temperature dries 4-6h.
7. a kind of printing transferring method of calico paper, it is characterised in that：Including：
1) the holographic laser raster picture and text water transfer marble paper for, preparing claim 1 methods described is placed in water immersion, and water is turned
Calico paper is positioned on the relevant position of decorative product, and then water-transfer printing paper is extracted out；
2), being removed after low temperature drying can dyestripping；
3) the said goods, are put into baking oven, baking and curing.
8. the printing transferring method of calico paper as claimed in claim 7, it is characterised in that step 1) soak time is 10- in reclaimed water
15s。
9. the printing transferring method of calico paper as claimed in claim 7, it is characterised in that step 2) described in low temperature drying it is specific
For：It it is 40 DEG C~75 DEG C in temperature, 20~45min of time is dried；Or natural air dry 2h-6h is dried.
10. the printing transferring method of calico paper as claimed in claim 7, it is characterised in that step 3) described in baking and curing it is specific
For：It is 150 DEG C~210 DEG C degree, 10~45min of time attachment solidifications in temperature.