CN101092098A - Laser transfer printing method without printing plate - Google Patents
Laser transfer printing method without printing plate Download PDFInfo
- Publication number
- CN101092098A CN101092098A CN 200610017988 CN200610017988A CN101092098A CN 101092098 A CN101092098 A CN 101092098A CN 200610017988 CN200610017988 CN 200610017988 CN 200610017988 A CN200610017988 A CN 200610017988A CN 101092098 A CN101092098 A CN 101092098A
- Authority
- CN
- China
- Prior art keywords
- paper
- transfer printing
- printing
- membranelle
- literal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a laser transfer printing method without ruling film. It takes transfer printing on ceramic and glass. The method includes the following steps: printing image and text on small film paper or large film paper through laser printer; covering cover glue on the small film paper or large film paper, drying; while printing, dipping small film paper or large film paper in warm water until the small paper mesophragm separated from bottom paper; putting the small paper on the printing object, removing bottom paper, and remaining image and text on the object; drying to gain the product. The invention does not need ruling film and the color is natural and vivid. It has the advantages of rapid printing speed, high efficiency, etc.
Description
Technical field
The present invention relates to a kind of printing process, especially relate to a kind of laser transfer printing method without printing plate.
Background technology
At present, transfer technique has water transfer printing and hot transfer technique, water transfer printing, heat-transferring method commonly used both at home and abroad is with the pictograph of the institute's transfer printing method with silk screen seal, offset printing, inkjet printing, and pictograph is imprinted on transfer paper or the transfer film, transfers to then on the article of required printing.Wherein, the advantage of silk screen seal is black bed thickness, advantage such as bright in luster, be the most frequently used hectographic printing mode at present, but the trapping printing colour picture need be made a plurality of versions, and color transition is poor, and needs repeatedly printing, and operation is numerous and diverse, strict to printing environment.The offset printing transfer printing has realized colored printing, natural color transition perfection, can not satisfy as pottery, glass applique for the specific (special) requirements of some article but the China ink layer is thin, and need a plurality of versions of system, and the seal amount is had certain requirement.The inkjet printing transfer technique, be that Weak solvent ink or hot transfer printing ink are added to Epson ink-jet printer cartridge, or on special transfer paper, print external the company in the ink supply box, need not plate-making with the method, bright in luster, but the article for need high temperature stamps such as some article such as potteries can't be realized, and speed is slow, cost is high, ink is very big to the printer head damage, can't realize producing in batches.
Summary of the invention
Purpose of the present invention just be at above-mentioned shortcoming provide a kind of do not have version, personalization, fashion, efficient and convenient, color transition good, bright in colour, cost is low, the laser transfer printing method without printing plate that can produce in batches, can remedy the deficiencies in the prior art.
Purpose of the present invention can realize by following measure:
Laser transfer printing method without printing plate of the present invention:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, during printing membranelle paper or big film paper is soaked in warm water, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, baking gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, baking gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
The present invention is for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, and described soak time is 5-30 kind second.For the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃.For the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃.For the transfer printing of yarn fabric, the hot pressure time is 10-60 second.Laser printer is color laser printer or monochrome laser printer.
The present invention is owing to the employing said method, thus the shortcoming of several prior aries more than having overcome.This method need not plate-making (going out film sheet), and the natural color transition of colored printing is gorgeous true to nature.Can realize water rotation printing on any article, print speed printing speed is fast, and the production efficiency height can be produced in batches.
The specific embodiment
The present invention does with detailed description below in conjunction with drawings and Examples:
Embodiment 1,
Laser transfer printing method without printing plate of the present invention:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, will membranelle paper during printing or big film paper warm water in soak, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, oven dry gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, oven dry gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
The present invention is for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, and described soak time is 5-30 kind second, and soak time is for being preferably 5 seconds kinds.For the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃, and bake out temperature is preferably 50 ℃.For the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃, is preferably 160 ℃.For the transfer printing of yarn fabric, the hot pressure time is 10-60 second, is preferably 10 seconds.Laser printer is color laser printer or monochrome laser printer.
Embodiment 2,
Laser transfer printing method without printing plate of the present invention:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, will membranelle paper during printing or big film paper warm water in soak, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, oven dry gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, oven dry gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
The present invention is for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, and described soak time is 5-30 kind second.Soak time is for being preferably 10 seconds kinds.For the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃, and bake out temperature is preferably 200 ℃.For the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃, is preferably 180 ℃.For the transfer printing of yarn fabric, the hot pressure time is 10-60 second, is preferably 30 seconds.Laser printer is color laser printer or monochrome laser printer.
Embodiment 3,
Laser transfer printing method without printing plate of the present invention:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, will membranelle paper during printing or big film paper warm water in soak, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, oven dry gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, oven dry gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
The present invention is for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, and described soak time is 5-30 kind second.Soak time is for being preferably 20 seconds kinds.For the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃, and bake out temperature is preferably 600 ℃.For the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃, is preferably 200 ℃.For the transfer printing of yarn fabric, the hot pressure time is 10-60 second, is preferably 40 seconds.Laser printer is color laser printer or monochrome laser printer.
Embodiment 4,
Laser transfer printing method without printing plate of the present invention:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, will membranelle paper during printing or big film paper warm water in soak, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, oven dry gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, oven dry gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
The present invention is for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, and described soak time is 5-30 kind second.Soak time is for being preferably 25 seconds kinds.For the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃, and bake out temperature is preferably 1000 ℃.For the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃, is preferably 210 ℃.For the transfer printing of yarn fabric, the hot pressure time is 10-60 second, is preferably 50 seconds.Laser printer is color laser printer or monochrome laser printer.
Embodiment 5,
Laser transfer printing method without printing plate of the present invention:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, will membranelle paper during printing or big film paper warm water in soak, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, oven dry gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, oven dry gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
The present invention is for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, and described soak time is 5-30 kind second.Soak time is for being preferably 30 seconds kinds.For the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃, and bake out temperature is preferably 1350 ℃.For the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃, is preferably 220 ℃.For the transfer printing of yarn fabric, the hot pressure time is 10-60 second, is preferably 60 seconds.Laser printer is color laser printer or monochrome laser printer.
Certainly, also each concrete point value of choose reasonable in its scope as required of each parameter among the present invention.
Claims (7)
1, a kind of laser transfer printing method without printing plate is characterized in that:
Transfer printing for pottery, the high temperature resistant article of glass, be figure, literal to be imprinted on membranelle paper or the big film paper by laser printer, front cover glue on membranelle paper or the big film paper dries then, will membranelle paper during printing or big film paper warm water in soak, soak time is as the criterion so that film and base stock are broken away from, membranelle paper is placed on the printed material product, take out base stock, figure, literal are retained on the printed material product, dry then, oven dry gets final product;
Transfer printing for the non-high-temperature resistant article, figure, the literal of required printing should be printed on the membranelle paper with laser printer, printing protection gloss oil on membranelle paper is gone up dyestripping glue then then, the membranelle paper that will be printed on figure, literal places warm water to soak, soak time is as the criterion so that film and base stock are broken away from, and membranelle paper is placed on the printed material product, takes out base stock, figure, literal are retained on the printed material product, dry then, tear dyestripping glue off, oven dry gets final product;
Transfer printing for yarn fabric, be figure, literal to be printed on the release liners by minute surface by laser printer, on needed figure, text profile, print hot melt adhesive then, dry, when transfer printing on yarn fabric, earlier yarn fabric is placed on the Pyrograph machine, the release liners figure that will be printed on pattern, hot melt adhesive faces down and is placed on the yarn fabric, Pyrograph machine depressed carry out hot pressure, raise Pyrograph machine then, tear release liners off, will obtain high light face pattern, tear release liners after the cooling off and obtain mute light face pattern.
2, laser transfer printing method without printing plate according to claim 1 is characterized in that: for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described soak time is 5-30 kind second.
3, laser transfer printing method without printing plate according to claim 1 is characterized in that: for the transfer printing of pottery, the high temperature resistant article of glass and non-high-temperature resistant article, described bake out temperature is 50 ℃-1350 ℃.
4, according to claim 1 or 2 or 3 described laser transfer printing method without printing plate, it is characterized in that: for the transfer printing of yarn fabric, the hot pressure temperature is 160 ℃-220 ℃.
5, according to claim 1 or 2 or 3 described laser transfer printing method without printing plate, it is characterized in that: for the transfer printing of yarn fabric, the hot pressure time is 10-60 second.
6, according to claim 1 or 2 or 3 described laser transfer printing method without printing plate, it is characterized in that: described laser printer is a color laser printer.
7, according to claim 1 or 2 or 3 described laser transfer printing method without printing plate, it is characterized in that: described laser printer is a monochrome laser printer.