CN105200863A - Low-temperature-hot-stamped gold-stamped type tipping paper for cigarettes and preparation method of tipping paper - Google Patents
Low-temperature-hot-stamped gold-stamped type tipping paper for cigarettes and preparation method of tipping paper Download PDFInfo
- Publication number
- CN105200863A CN105200863A CN201510572619.4A CN201510572619A CN105200863A CN 105200863 A CN105200863 A CN 105200863A CN 201510572619 A CN201510572619 A CN 201510572619A CN 105200863 A CN105200863 A CN 105200863A
- Authority
- CN
- China
- Prior art keywords
- tipping paper
- environment
- friendly type
- ink
- stamping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides low-temperature-hot-stamped gold-stamped type tipping paper for cigarettes and a preparation method of the tipping paper. The low-temperature-hot-stamped gold-stamped type tipping paper for the cigarettes and the preparation method of the tipping paper are used for overcoming the disadvantages in existing high-temperature hot-stamping that the energy consumption is high, and that the rate of finished products is low and the cold hot-stamping effect is poor. The gold-stamped type tipping paper for the cigarettes, provided by the invention, is prepared through firstly printing environment-friendly alcohol-soluble white ink and printing ink on a base paper layer, then, additionally printing a layer of an adhesion-assisting glue material on the environment-friendly alcohol-soluble ink layer, then, carrying out low-temperature hot-stamping at the temperature of 85-100 DEG C, and carrying out laser boring, slitting and rewinding. According to the low-temperature-hot-stamped gold-stamped type tipping paper for the cigarettes, provided by the invention, an adhesion-assisting layer is additionally printed on the ink layer and has the functions of protecting the ink layer, enhancing the hydrophobicity of the ink layer and improving the adherence with a gold-stamped layer and the fastness of adhering of winding-adhesive glue, and special electrochemical aluminum hot-stamping foil for low-temperature hot-stamping is used in a matched manner, so that a low-temperature hot-stamping procedure can be completed at the temperature of 85-100 DEG C, and the energy consumption of a gold-stamping process is greatly lowered, and the service efficiency of a gold-stamping plate is increased, and thus the cost of gold-stamping is reduced.
Description
Technical field
The present invention relates to cigarette tipping paper technical field, gold stamping type cigarette tipping paper being specifically related to a kind of low temperature thermoprint and preparation method thereof.
Background technology
Cigarette tipping paper is a kind of cigarette packaging material, Main Function be cigarette filter is hinged with cigarette together with, belong to a kind of special industrial paper using of cigarette industry.At present, tipping paper has had larger innovation in purposes, is not only confined to simple packaging, and more focus on ornamental, antifalsification and health environment-friendly, its production and processing technology is also updated, through printing, gold stamping, punch, the operation such as to cut after make.
Gold stamping is a kind of special typography without the need to ink, and it gives thermoprint base material strong metal-like, and obviously, in recent years, the continuous release of high-grade cigarette made the application of thermoprint type tipping paper increasingly extensive, and in rising trend for its decoration and antifalse effect.Gilding technology divides hot stamping and cold-hot stamping, and alumite thermoprinting foil is main raw material, hot stamping effects with by thermoprint material and alumite thermoprinting foil relation comparatively tight.
Hot stamping utilizes hot pressing principle, namely by heating gold stamping version, then to have exerted pressure transfer printing through silica gel pressure roller.Existing most cigarette tipping paper adopts this thermoprint mode, but hot stamping carries out usually under the hot conditions of 160-200 DEG C, not only consume a large amount of energy, and under the high temperature conditions, serious and the gold stamping version expanded by heating of moisture loss in thermoprint material thin paper, causes register trouble during polychrome thermoprint, produces a large amount of waste products, thus affect production efficiency, increase the cost of product.
Cold-hot stamping utilizes uv adhesive stamping systems to be transferred to method on printable fabric.Its main technological steps is as follows: (1) prints cationic uv adhesive on printable fabric; (2) uv adhesive is cured; (3) by pressure roll, cold-hot stamping paper tinsel and printable fabric are combined with each other; (4) unnecessary stamping systems is stripped down from printable fabric, only leave required thermoprint picture and text at the position scribbling adhesive.This technique possesses the feature of energy-conserving and environment-protective, but because UV adhesive flow levelling is poor, there is out-of-flatness phenomenon in dried surface, make the stamping systems surface brightness that is transferred to above it poor, there is diffuse reflection phenomenon, effect is not as traditional hot stamping, and this technique also needs special equipment and corresponding material.Therefore, limit it to apply on a large scale.
Summary of the invention
There is energy resource consumption greatly in the high-temperature hot thermoprint that the object of the invention is to improve prior art, yield rate is low, cold-hot stamping energy-conserving and environment-protective, but the drawback that also there is hot stamping effects difference, gold stamping type cigarette tipping paper that a kind of low temperature thermoprint is provided and preparation method thereof.
For achieving the above object, present invention employs following technological means: a kind of gold stamping type cigarette tipping paper of low temperature thermoprint, printing environment-friendly type alcohol dissolubility chalk and environment-friendly type alcohol-soluble printing ink on base paper for tipping paper layer successively, then in environment-friendly type alcohol-soluble printing layer of ink, one adhesion promoting layer sizing material is printed additional, again through 85-100 DEG C of low temperature thermoprint, laser boring and cutting and rewinding are made.
Described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 5-20 part, nitrocotton 1-5 part, nano titanium oxide 1-10 part, precipitated calcium carbonate 5-20 part, wax powder 0.5-2 part, ethanol 40-85 part.Preferably, environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 10-15 part, nitrocotton 2-3 part, nano titanium oxide 1-5 part, precipitated calcium carbonate 10-15 part, wax powder 0.5-1 part, ethanol 60-75 part.
Described environment-friendly type alcohol-soluble printing ink is prepared from by the raw material of following weight portion: polyvinyl butyral resin 5-20 part, nitrocotton 1-5 part, nano titanium oxide 1-10 part, precipitated calcium carbonate 5-20 part, wax powder 0.5-2 part, iron oxide pigment 5-30 part, ethanol 30-80 part.Preferably, environment-friendly type alcohol-soluble printing ink is prepared from by the raw material of following weight portion: polyvinyl butyral resin 10-15 part, nitrocotton 2-3 part, nano titanium oxide 1-5 part, precipitated calcium carbonate 10-15 part, wax powder 0.5-1%, iron oxide pigment 10-25 part, ethanol 35-65 part.
Described adhesion promoting layer sizing material is prepared from by the raw material of following weight portion: low softening point rosin ester or modified rosin resin 10-30 part, nitrocotton 1-5 part, ethyl acetate 65-90 part.Preferably, low softening point rosin ester or modified rosin resin 15-20 part, nitrocotton 1-2 part, ethyl acetate 78-84 part.
Described low softening point rosin ester or modified rosin resin by eating ester gum, hydrogenated rosin glyceride, pentalyn, any one changing in surname phenolic resins of rosin form.
The preparation method of the gold stamping type cigarette tipping paper of a kind of low temperature of the present invention thermoprint, comprises the following steps:
(1) environment-friendly type alcohol dissolubility chalk is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, obtains compound A;
C, the compound A obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol dissolubility chalk.
(2) environment-friendly type alcohol-soluble printing ink is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder, iron oxide pigment respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, must mix colorant C;
C, the mixing colorant C obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol-soluble printing ink.
(3) adhesion promoting layer sizing material is prepared
A, adding in container by the load weighted solvent ethyl acetate of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted low softening point rosin ester of formula rate or modified rosin resin, nitrocotton respectively;
B, treat that resin adds after, dispersion machine is adjusted to 1200-1500 to turn/rotating speed of min fully stirs 40-60min, obtain adhesion promoting layer sizing material.
(4) print: be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-95 ± 5 DEG C.
(5) low temperature thermoprint: will be placed on polychrome gilding press through printing and the cigarette tipping paper semi-finished product point to cut and low temperature thermoprint Special electric aluminium stamping systems, heat first group of gold stamping version temperature to 85-95 DEG C, second group of 90-100 DEG C, with the pressure of 3.0-5.0Pa, the machine speed of 100-120m/min completes low temperature thermoprint operation.
(6) punch: cut gold stamping cigarette tipping paper semi-finished product by required specification, be placed on laser-beam drilling machine, air permeability, pore area (hole line) and distance hem width degree, the air permeability coefficient of variation etc., by product technology requirement, carry out laser boring with the machine speed of 150-180m/min.
(7) cutting and rewinding: as required cutting and rewinding, packaging are carried out to cigarette tipping paper.
When needing, the ink colors of printing is darker, when one-step print can not meet strategic point, twice printing is adopted during step (4) printing-ink, namely be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-145 ± 5 DEG C-95 ± 5 DEG C.
beneficial effect of the present invention is:1. the gold stamping type cigarette tipping paper of a kind of low temperature thermoprint of the present invention, intaglio printing environment-friendly type alcohol-soluble printing layer of ink is coated with transparent low softening point rosin ester or the gluing adhesion promoting layer of modified rosin resin, be equipped with the special alumite thermoprinting foil of low temperature thermoprint again, realize 85-100 DEG C and can complete hot stamping process, the effective Yin Gaowen of improvement thermoprint makes paper distortion or gold stamping version expanded by heating causes thermoprint to be forbidden and alumite thermoprinting foil variable color tarnishes and causes waste, improve the service efficiency of gold stamping version, thus saved gold stamping cost, and its effect and high temperature thermoprint are consistent.
2. the gold stamping type cigarette tipping paper of a kind of low temperature thermoprint of the present invention, low temperature hot stamping process ensure that moisture certain in the expansion rate of gold stamping version and tipping base paper, and paper distortion is little, and when two looks or polychrome thermoprint, alignment is accurate, eliminates the generation of waste product.In addition, low temperature thermoprint prolonged process service life of gold stamping version, greatly enhance productivity.
3. the gold stamping type cigarette tipping paper of a kind of low temperature thermoprint of the present invention; intaglio printing environment-friendly type alcohol-soluble printing layer of ink is coated with transparent low softening point rosin ester or the gluing adhesion promoting layer of modified rosin resin; possess protection ink layer, strengthen layer of ink hydrophobicity; improve the cigarette adaptability of cigarette tipping paper, solve the open defect problem such as alice, gas leakage, bubble wrinkle connecing because interface is gluing and loosely cause.
4. production technology of the present invention is simple, and original working condition can meet production requirement, without the need to investments such as extra increase equipment.
Detailed description of the invention
Below in conjunction with specific embodiment, the specific embodiment of the present invention is described further.
embodiment 1
A kind of gold stamping type cigarette tipping paper of low temperature thermoprint, printing environment-friendly type alcohol dissolubility chalk and environment-friendly type alcohol-soluble printing ink on base paper for tipping paper layer successively, then in environment-friendly type alcohol-soluble printing layer of ink, one adhesion promoting layer sizing material is printed additional, again through 85-100 DEG C of low temperature thermoprint, laser boring and cutting and rewinding are made.
Described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 10 parts, nitrocotton 3 parts, nano titanium oxide 2 parts, precipitated calcium carbonate 15 parts, 0.5 part, wax powder, ethanol 85 parts.
Described environment-friendly type alcohol-soluble printing ink is prepared from by the raw material of following weight portion: polyvinyl butyral resin 10 parts, nitrocotton 3 parts, nano titanium oxide 2 parts, precipitated calcium carbonate 15 parts, 0.5 part, wax powder, iron oxide pigment 25 parts, ethanol 45 parts.
Described adhesion promoting layer sizing material is prepared from by the raw material of following weight portion: edible ester gum 15 parts, nitrocotton 1 part, 84 parts, ethyl acetate.
A preparation method for the gold stamping type cigarette tipping paper of low temperature thermoprint, comprises the following steps:
(1) environment-friendly type alcohol dissolubility chalk is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, obtains compound A;
C, the compound A obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol dissolubility chalk.
(2) environment-friendly type alcohol-soluble printing ink is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder, iron oxide pigment respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, must mix colorant C;
C, the mixing colorant C obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol-soluble printing ink.
(3) adhesion promoting layer sizing material is prepared
A, adding in container by the load weighted solvent ethyl acetate of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted low softening point rosin ester of formula rate or modified rosin resin, nitrocotton respectively;
B, treat that resin adds after, dispersion machine is adjusted to 1200-1500 to turn/rotating speed of min fully stirs 40-60min, obtain adhesion promoting layer sizing material.
(4) print: be under the environment of 60-80% in humidity, by intaglio plate anilox roll by sequentially printing base paper for tipping paper successively by chalk-ink-help viscose material, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-95 ± 5 DEG C;
(5) low temperature thermoprint: will be placed on dichromatism gilding press through printing and the cigarette tipping paper semi-finished product point to cut and low temperature thermoprint Special electric aluminium stamping systems, heat first group of gold stamping version temperature to 85-95 DEG C, second group of 90-100 DEG C, with the pressure of 3.0-5.0Pa, the machine speed of 100-120m/min completes low temperature thermoprint operation.
(6) punch: cut gold stamping cigarette tipping paper semi-finished product by required specification, be placed on laser-beam drilling machine, air permeability, pore area (hole line) and distance hem width degree, the air permeability coefficient of variation etc., by product technology requirement, carry out laser boring with the machine speed of 150-180m/min.
(7) cutting and rewinding: as required cutting and rewinding, packaging are carried out to cigarette tipping paper.
The gold stamping type cigarette tipping paper of a kind of low temperature thermoprint prepared by the present invention, intaglio printing environment-friendly type alcohol-soluble printing layer of ink is coated with the transparent gluing adhesion promoting layer of low softening point rosin ester, be equipped with the special alumite thermoprinting foil of low temperature thermoprint again, realize 85-100 DEG C and can complete hot stamping process, significantly reduce the consumption of the energy, and its effect and high temperature thermoprint are consistent.
embodiment 2
A kind of gold stamping type cigarette tipping paper of low temperature thermoprint, printing environment-friendly type alcohol dissolubility chalk and environment-friendly type alcohol-soluble printing ink on base paper for tipping paper layer successively, then in environment-friendly type alcohol-soluble printing layer of ink, one adhesion promoting layer sizing material is printed additional, again through 85-100 DEG C of low temperature thermoprint, laser boring and cutting and rewinding are made.
Described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 12 parts, nitrocotton 2 parts, nano titanium oxide 3 parts, precipitated calcium carbonate 13 parts, 0.7 part, wax powder, ethanol 70 parts.
Described environment-friendly type alcohol-soluble printing ink is prepared from by the raw material of following weight portion: polyvinyl butyral resin 12 parts, nitrocotton 2 parts, nano titanium oxide 3 parts, precipitated calcium carbonate 13 parts, 0.7 part, wax powder, iron oxide pigment 20 parts, ethanol 50 parts.
Described adhesion promoting layer sizing material is prepared from by following raw materials in part by weight: hydrogenated rosin glyceride 17 parts, nitrocotton 2 parts, 81 parts, ethyl acetate.
A preparation method for the gold stamping type cigarette tipping paper of low temperature thermoprint, comprises the following steps:
(1) environment-friendly type alcohol dissolubility chalk is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, obtains compound A;
C, the compound A obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol dissolubility chalk.
(2) environment-friendly type alcohol-soluble printing ink is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder, iron oxide pigment respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, must mix colorant C;
C, the mixing colorant C obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol-soluble printing ink.
(3) adhesion promoting layer sizing material is prepared
A, adding in container by the load weighted solvent ethyl acetate of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted low softening point rosin ester of formula rate or modified rosin resin, nitrocotton respectively;
B, treat that resin adds after, dispersion machine is adjusted to 1200-1500 to turn/rotating speed of min fully stirs 40-60min, obtain adhesion promoting layer sizing material.
(4) print: be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-145 ± 5 DEG C-95 ± 5 DEG C.
(5) low temperature thermoprint: will be placed on 2 look gilding press through printing and the cigarette tipping paper semi-finished product point to cut and low temperature thermoprint Special electric aluminium stamping systems, heat first group of gold stamping version temperature to 85-95 DEG C, second group of 90-100 DEG C, with the pressure of 3.0-5.0Pa, the machine speed of 100-120m/min completes low temperature thermoprint operation.
(6) punch: cut gold stamping cigarette tipping paper semi-finished product by required specification, be placed on laser-beam drilling machine, air permeability, pore area (hole line) and distance hem width degree, the air permeability coefficient of variation etc., by product technology requirement, carry out laser boring with the machine speed of 150-180m/min.
(7) cutting and rewinding: as required cutting and rewinding, packaging are carried out to cigarette tipping paper.
The gold stamping type cigarette tipping paper of a kind of low temperature thermoprint of the present invention, low temperature hot stamping process ensure that moisture certain in the expansion rate of gold stamping version and tipping base paper, and paper distortion is little, and during two look thermoprints, alignment is accurate, eliminates the generation of waste product.In addition, low temperature thermoprint prolonged process service life of gold stamping version, greatly enhance productivity.
embodiment 3
A kind of gold stamping type cigarette tipping paper of low temperature thermoprint, printing environment-friendly type alcohol dissolubility chalk and environment-friendly type alcohol-soluble printing ink on base paper for tipping paper layer successively, then in environment-friendly type alcohol-soluble printing layer of ink, one adhesion promoting layer sizing material is printed additional, again through 85-100 DEG C of low temperature thermoprint, laser boring and cutting and rewinding are made.
Described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 13 parts, nitrocotton 3 parts, nano titanium oxide 4 parts, precipitated calcium carbonate 12 parts, 0.9 part, wax powder, ethanol 68 parts.
Described environment-friendly type alcohol-soluble printing ink is prepared from by following raw materials in part by weight: polyvinyl butyral resin 13 parts, nitrocotton 3 parts, nano titanium oxide 4 parts, precipitated calcium carbonate 12 parts, 0.9 part, wax powder, iron oxide pigment 15 parts, ethanol 53 parts.
Described adhesion promoting layer sizing material is prepared from by following raw materials in part by weight: pentalyn 19 parts, nitrocotton 2 parts, 79 parts, ethyl acetate.
A preparation method for the gold stamping type cigarette tipping paper of low temperature thermoprint, comprises the following steps:
(1) environment-friendly type alcohol dissolubility chalk is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, obtains compound A;
C, the compound A obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol dissolubility chalk.
(2) environment-friendly type alcohol-soluble printing ink is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder, iron oxide pigment respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, must mix colorant C;
C, the mixing colorant C obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains ink.
(3) adhesion promoting layer sizing material is prepared
A, adding in container by the load weighted solvent ethyl acetate of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted low softening point rosin ester of formula rate or modified rosin resin, nitrocotton respectively;
B, treat that resin adds after, dispersion machine is adjusted to 1200-1500 to turn/rotating speed of min fully stirs 40-60min, obtain adhesion promoting layer sizing material.
(4) print: be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-95 ± 5 DEG C.
(5) low temperature thermoprint: will be placed on 2 look gilding press through printing and the cigarette tipping paper semi-finished product point to cut and low temperature thermoprint Special electric aluminium stamping systems, heat first group of gold stamping version temperature to 85-95 DEG C, second group of 90-100 DEG C, with the pressure of 3.0-5.0Pa, the machine speed of 100-120m/min completes low temperature thermoprint operation.
(6) punch: cut gold stamping cigarette tipping paper semi-finished product by required specification, be placed on laser-beam drilling machine, air permeability, pore area (hole line) and distance hem width degree, the air permeability coefficient of variation etc., by product technology requirement, carry out laser boring with the machine speed of 150-180m/min.
(7) cutting and rewinding: as required cutting and rewinding, packaging are carried out to cigarette tipping paper.
The gold stamping type cigarette tipping paper of a kind of low temperature thermoprint of the present invention, improves the cigarette adaptability of cigarette tipping paper, solves the open defect problem such as alice, gas leakage, bubble wrinkle connecing because interface is gluing and loosely cause.
embodiment 4
A kind of gold stamping type cigarette tipping paper of low temperature thermoprint, printing environment-friendly type alcohol dissolubility chalk and environment-friendly type alcohol-soluble printing ink on base paper for tipping paper layer successively, then in environment-friendly type alcohol-soluble printing layer of ink, one adhesion promoting layer sizing material is printed additional, again through 85-100 DEG C of low temperature thermoprint, laser boring and cutting and rewinding are made.
Described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 15 parts, nitrocotton 2 parts, nano titanium oxide 5 parts, precipitated calcium carbonate 10 parts, 1 part, wax powder, ethanol 67 parts.
Described environment-friendly type alcohol-soluble printing ink is prepared from by following raw materials in part by weight: polyvinyl butyral resin 15 parts, nitrocotton 2 parts, nano titanium oxide 5 parts, precipitated calcium carbonate 10 parts, 1 part, wax powder, iron oxide pigment 10 parts, ethanol 57 parts.
Described adhesion promoting layer sizing material is prepared from by following raw materials in part by weight: rosin modified phenolic resin 20 parts, nitrocotton 3 parts, 77 parts, ethyl acetate.
A preparation method for the gold stamping type cigarette tipping paper of low temperature thermoprint, comprises the following steps:
(1) environment-friendly type alcohol dissolubility chalk is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, obtains compound A;
C, the compound A obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol dissolubility chalk.
(2) environment-friendly type alcohol-soluble printing ink is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder, iron oxide pigment respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, must mix colorant C;
C, the mixing colorant C obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol-soluble printing ink.
(3) adhesion promoting layer sizing material is prepared
A, adding in container by the load weighted solvent ethyl acetate of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted low softening point rosin ester of formula rate or modified rosin resin, nitrocotton respectively;
B, treat that resin adds after, dispersion machine is adjusted to 1200-1500 to turn/rotating speed of min fully stirs 40-60min, obtain adhesion promoting layer sizing material.
(4) print: be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-145 ± 5 DEG C-95 ± 5 DEG C;
(5) low temperature thermoprint: will be placed on 2 look gilding press through printing and the cigarette tipping paper semi-finished product point to cut and low temperature thermoprint Special electric aluminium stamping systems, heat first group of gold stamping version temperature to 85-95 DEG C, second group of 90-100 DEG C, with the pressure of 3.0-5.0Pa, the machine speed of 100-120m/min completes low temperature thermoprint operation;
(6) punch: cut gold stamping cigarette tipping paper semi-finished product by required specification, be placed on laser-beam drilling machine, air permeability, pore area (hole line) and distance hem width degree, the air permeability coefficient of variation etc., by product technology requirement, carry out laser boring with the machine speed of 150-180m/min;
(7) cutting and rewinding: as required cutting and rewinding, packaging are carried out to cigarette tipping paper.
Production technology of the present invention is simple, and original working condition can meet production requirement, without the need to investments such as extra increase equipment.
Claims (5)
1. the gold stamping type cigarette tipping paper of a low temperature thermoprint, it is characterized in that, printing environment-friendly type alcohol dissolubility chalk and environment-friendly type alcohol-soluble printing ink on base paper for tipping paper layer successively, then in environment-friendly type alcohol-soluble printing layer of ink, one adhesion promoting layer sizing material is printed additional, again through 85-100 DEG C of low temperature thermoprint, laser boring and cutting and rewinding are made;
Described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 5-20 part, nitrocotton 1-5 part, nano titanium oxide 1-10 part, precipitated calcium carbonate 5-20 part, wax powder 0.5-2 part, ethanol 40-85 part;
Described environment-friendly type alcohol-soluble printing ink is prepared from by following raw materials in part by weight: polyvinyl butyral resin 5-20 part, nitrocotton 1-5 part, nano titanium oxide 1-10 part, precipitated calcium carbonate 5-20 part, wax powder 0.5-2%, iron oxide pigment 5-30 part, ethanol 30-80 part;
Described adhesion promoting layer sizing material is prepared from by following raw materials in part by weight: low softening point rosin ester or modified rosin resin 10-30 part, nitrocotton 1-5 part, ethyl acetate 65-90 part.
2. the gold stamping type cigarette tipping paper of a kind of low temperature thermoprint according to claim 1, it is characterized in that, described environment-friendly type alcohol dissolubility chalk is prepared from by following raw materials in part by weight: polyvinyl butyral resin 10-15 part, nitrocotton 2-3 part, nano titanium oxide 1-5 part, precipitated calcium carbonate 10-15 part, wax powder 0.5-1 part, ethanol 60-75 part;
Described environment-friendly type alcohol-soluble printing ink is prepared from by following raw materials in part by weight: polyvinyl butyral resin 10-15 part, nitrocotton 2-3 part, nano titanium oxide 1-5 part, precipitated calcium carbonate 10-15 part, wax powder 0.5-1 part, iron oxide pigment 10-25 part, ethanol 35-65 part;
Described adhesion promoting layer sizing material is prepared from by following raw materials in part by weight: low softening point rosin ester or modified rosin resin 15-20 part, nitrocotton 1-2 part, ethyl acetate 78-84 part.
3. the gold stamping type cigarette tipping paper of a kind of low temperature thermoprint according to claim 1 and 2, it is characterized in that, described low softening point rosin ester or modified rosin resin are edible ester gums, hydrogenated rosin glyceride, pentalyn, rosin change in surname phenolic resins any one.
4. prepare a method for the gold stamping type cigarette tipping paper of the low temperature thermoprint according to any one of claims 1 to 3, it is characterized in that, comprise the following steps:
(1) environment-friendly type alcohol dissolubility chalk is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, obtains compound A;
C, the compound A obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol dissolubility chalk;
(2) environment-friendly type alcohol-soluble printing ink is prepared
A, first adding in container by the load weighted ethanol of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted polyvinyl butyral resin of formula rate, nitrocotton, nano titanium oxide, precipitated calcium carbonate, wax powder, iron oxide pigment respectively;
B, dispersion machine be adjusted to 1200-1500 turn/rotating speed of min stirs 60-80min, must mix colorant C;
C, the mixing colorant C obtained by step b join grinding in ball grinder 2-4 time, and fineness of grind reaches less than 15 μm and namely obtains environment-friendly type alcohol-soluble printing ink;
(3) adhesion promoting layer sizing material is prepared
A, adding in container by the load weighted solvent ethyl acetate of formula rate, 300-400 turn/rotating speed of min under slowly add by the load weighted low softening point rosin ester of formula rate or modified rosin resin, nitrocotton respectively;
B, treat that resin adds after, dispersion machine is adjusted to 1200-1500 to turn/rotating speed of min fully stirs 40-60min, obtain adhesion promoting layer sizing material;
(4) print: be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-95 ± 5 DEG C;
(5) low temperature thermoprint: will be placed on 2 look gilding press through printing and the cigarette tipping paper semi-finished product point to cut and low temperature thermoprint Special electric aluminium stamping systems, heat first group of gold stamping version temperature to 85-95 DEG C, second group of 90-100 DEG C, with the pressure of 3.0-5.0Pa, the machine speed of 100-120m/min completes low temperature thermoprint operation;
(6) punch: cut gold stamping cigarette tipping paper semi-finished product by required specification, be placed on laser-beam drilling machine, air permeability, pore area (hole line) and distance hem width degree, the air permeability coefficient of variation etc., by product technology requirement, carry out laser boring with the machine speed of 150-180m/min;
(7) cutting and rewinding: as required cutting and rewinding, packaging are carried out to cigarette tipping paper.
5. the preparation method of the gold stamping type cigarette tipping paper of low temperature thermoprint according to claim 4, it is characterized in that, twice printing is adopted during step (4) printing-ink, namely be under the environment of 60-80% in humidity, by the successively order of intaglio plate anilox roll by chalk-ink-ink-help viscose material, base paper for tipping paper is printed, controlling the dry-coated amount of coating is 4-6g/ ㎡, machine speed 160-180m/min, drying tunnel bake out temperature 135 ± 5 DEG C-140 ± 5 DEG C-145 ± 5 DEG C-95 ± 5 DEG C.