CN107034734A - A kind of ventilative cigarette tipping paper of constant humidity and its manufacturing process - Google Patents
A kind of ventilative cigarette tipping paper of constant humidity and its manufacturing process Download PDFInfo
- Publication number
- CN107034734A CN107034734A CN201710284094.3A CN201710284094A CN107034734A CN 107034734 A CN107034734 A CN 107034734A CN 201710284094 A CN201710284094 A CN 201710284094A CN 107034734 A CN107034734 A CN 107034734A
- Authority
- CN
- China
- Prior art keywords
- layer
- constant humidity
- original paper
- thermoprint
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ventilative cigarette tipping paper of constant humidity, including original paper layer, wherein:The upper surface of the original paper layer is disposed with printing layer and thermoprint layer from the inside to the outside, and the lower surface of the original paper layer is provided with constant humidity air-permeable layer.Wherein, the constant humidity air-permeable layer is ceramic powder layer or high molecular polymer powder bed.The manufacturing step of the cigarette tipping paper includes:1) printing layer is formed in the upper surface of original paper layer by way of intaglio printing;2) surface of electrochemical aluminum foil material thermoprint to the printing layer is formed into thermoprint layer by way of thermoprint;3) constant humidity gas permeable material is printed to the lower surface formation constant humidity air-permeable layer of the original paper layer by way of intaglio printing.The cigarette tipping paper of the present invention, by the setting of constant humidity air-permeable layer, the demand of cigarette product air permeability can be met on the basis of productivity ratio, reduction production cost is improved, the water balance of cigarette product can also be played a part of aiding in simultaneously, the quality of cigarette product is kept.
Description
Technical field
The present invention relates to a kind of paper product and its manufacturing process, and in particular to it is a kind of for cigarette package, with constant humidity, thoroughly
The cigarette tipping paper of airway dysfunction and its corresponding manufacturing process, belong to pulp technology for making paper.
Background technology
Cigarette tipping paper is as the supplementary material of cigarette package, and it is the connection function for playing cigarette and filter stick, mesh that it, which is acted on,
The conventional cigarette tipping paper of preceding in the market is broadly divided into common tipping paper and the major class of perforated tipping paper two.Wherein, perforated tipping paper
Because it can meet the demand of cigarette high-air-permeability, thus with high market prospects.However, existing perforated tipping paper
Productivity ratio is relatively low, production cost remains high always, causes the coverage rate in its market relatively low.
The content of the invention
Connect it is an object of the invention to overcome the deficiencies of the prior art and provide a kind of cigarette with constant humidity, airing function
Fill paper.In addition, another object of the present invention is to provide a kind of manufacturing process of the cigarette tipping paper.
To achieve the above object, the present invention uses following technical scheme:
A kind of constant humidity is breathed freely cigarette tipping paper, including original paper layer, wherein:The upper surface of the original paper layer is from the inside to the outside successively
Printing layer and thermoprint layer are provided with, the lower surface of the original paper layer is provided with constant humidity air-permeable layer.
Preferably:The constant humidity air-permeable layer is ceramic powder layer or high molecular polymer powder bed.
Preferably:The particle diameter of ceramic powder or the high molecular polymer powder is 1 μm -100 μm, specific surface area
For 30-2000g/m2。
Preferably:The surface of ceramic powder or the high molecular polymer powder has micropore, and the micropore
Aperture be less than 1nm.
Preferably:The original paper layer is cork paper original paper layer.
Another object of the present invention, a kind of manufacturing process of cigarette tipping paper as described above, it includes following manufacture step
Suddenly:
1) printing layer is formed in the upper surface of original paper layer by way of intaglio printing;
2) surface of electrochemical aluminum foil material thermoprint to the printing layer is formed into thermoprint layer by way of thermoprint;
3) by way of intaglio printing by constant humidity gas permeable material print to the original paper layer lower surface formation constant humidity it is saturating
Gas-bearing formation.
Preferably:Step 3) described in constant humidity gas permeable material be ceramic powder or high molecular polymer powder,
And its particle diameter is 1 μm -100 μm, specific surface area is 30-2000g/m2。
Preferably:The surface of ceramic powder or the high molecular polymer powder has micropore, and the micropore
Aperture be less than 1nm.
Preferably:Step 2) described in intaglio printing employed in intaglio plate pit depth be 30 μm -80 μm, its consolidate
It is 80 DEG C -120 DEG C to change temperature.
Preferably:Step 3) described in intaglio printing employed in intaglio plate pit depth be 30 μm -80 μm, solidification
Temperature is 80 DEG C -120 DEG C, and the dry-coated amount of the constant humidity air-permeable layer is 1g/m2-5g/m2。
The beneficial effects of the present invention are cigarette tipping paper of the invention, by the setting of constant humidity air-permeable layer, can improved
On the basis of productivity ratio, reduction production cost, the demand of cigarette product air permeability can be met, while auxiliary cigarette production can also be played
The effect of the water balance of product, keeps the quality of cigarette product.
Brief description of the drawings
Fig. 1 shows the structural representation of the ventilative cigarette tipping paper of constant humidity of the present invention.
Embodiment
The embodiment to the present invention is described further below in conjunction with the accompanying drawings.
The cigarette tipping paper as shown in figure 1, constant humidity of the present invention is breathed freely, including original paper layer 1, the original paper layer 1 it is upper
Surface is cascading from the inside to the outside printing layer 2 and thermoprint layer 3, and the lower surface of the original paper layer 1 is additionally provided with constant humidity
Air-permeable layer 4.
Specifically, in the present invention, the original paper layer 1 can use cork paper original paper layer;By way of intaglio printing,
The surface intaglio printing of the original paper layer 1 forms printing layer 2, wherein, the intaglio plate pit depth employed in gravure printing process
For 30 μm -80 μm, its solidification temperature is 80 DEG C -120 DEG C.Then, by electrochemical aluminum foil material thermoprint to print by way of thermoprint
The surface of brush layer 2 forms thermoprint layer 3.
The constant humidity air-permeable layer 4 is ceramic powder or high molecular polymer powder bed, and it passes through the side of intaglio printing
Formula is formed at the lower surface of the original paper layer 1.Wherein, the intaglio plate pit depth employed in the gravure printing process is 30 μ
M-80 μm, solidification temperature is 80 DEG C -120 DEG C, and the dry-coated amount of the constant humidity air-permeable layer 4 is 1g/m2-5g/m2.The ceramic material
The particle diameter of powder or high molecular polymer powder is 1 μm -100 μm, and specific surface area is 30-2000g/m2, also, the ceramic material
Feed powder end or the surface of high molecular polymer powder have micropore, and the aperture of the micropore is less than 1nm, to meet cigarette product
The demand and auxiliary of air permeability reach the water balance of cigarette product.
Embodiment 1
A kind of constant humidity breathes freely cigarette tipping paper, its structure as shown in figure 1, including cork paper original paper layer 1 and from the inside to the outside
The printing layer 2 and thermoprint layer 3 of the upper surface of the original paper layer 1 are set in turn in, the lower surface of the original paper layer 1 is also formed with perseverance
Drenched gas-bearing formation 4.The manufacturing step of the tipping paper includes:
1) printing layer 2 is formed in the upper surface of the cork paper original paper layer 1 by way of intaglio printing, wherein, it is described
Intaglio plate pit depth employed in gravure printing process is 30 μm, and solidification temperature is 80 DEG C;
2) surface of electrochemical aluminum foil material thermoprint to the printing layer 2 is formed into thermoprint layer 3 by way of thermoprint;
3) be 10 μm by particle diameter by way of intaglio printing, specific surface area be 50g/m2, surface micropore aperture be less than 1nm
Ceramic powder print to the lower surface formation constant humidity air-permeable layer 4 of the cork paper original paper layer 1, wherein, the intaglio process
Intaglio plate pit depth employed in swiped through journey is 80 μm, and solidification temperature is 120 DEG C, and dry-coated amount is 5g/m2。
Embodiment 2
A kind of constant humidity breathes freely cigarette tipping paper, its structure as shown in figure 1, including cork paper original paper layer 1 and from the inside to the outside
The printing layer 2 and thermoprint layer 3 of the upper surface of the original paper layer 1 are set in turn in, the lower surface of the original paper layer 1 is also formed with perseverance
Drenched gas-bearing formation 4.The manufacturing step of the tipping paper includes:
1) printing layer 2 is formed in the upper surface of the cork paper original paper layer 1 by way of intaglio printing, wherein, it is described
Intaglio plate pit depth employed in gravure printing process is 80 μm, and solidification temperature is 120 DEG C;
2) surface of electrochemical aluminum foil material thermoprint to the printing layer 2 is formed into thermoprint layer 3 by way of thermoprint;
3) be 100 μm by particle diameter by way of intaglio printing, specific surface area be 2000g/m2, surface micropore aperture is less than
1nm high molecular polymer powder is printed to the lower surface formation constant humidity air-permeable layer 4 of the cork paper original paper layer 1, wherein, it is described
Intaglio plate pit depth employed in gravure printing process is 30 μm, and solidification temperature is 80 DEG C, and dry-coated amount is 1g/m2。
The present invention is by preferred embodiment having carried out detailed explanation.However, by studying carefully above, to each
The change and increase of embodiment are also apparent to those of ordinary skill in the art.It is intended that it is all this
A little changes and increase fall in the protection domain of the claims in the present invention.Term used herein is only to specific implementation
Example is illustrated, and it, which is not intended to, limits the invention.Unless otherwise defined, all terms used herein (including
Technical term and scientific terminology) it is identical with the understanding of those skilled in the art of the art.It is any that this product is entered
Capable modification and improvement, the replacement of similar in the scope of the claims or category or close material belongs to patent of the present invention with using
Protection domain.
Claims (10)
- The cigarette tipping paper 1. a kind of constant humidity is breathed freely, including original paper layer, it is characterised in that:The upper surface of the original paper layer is from the inside to the outside Printing layer and thermoprint layer are disposed with, the lower surface of the original paper layer is provided with constant humidity air-permeable layer.
- 2. cigarette tipping paper according to claim 1, it is characterised in that:The constant humidity air-permeable layer is ceramic powder layer Or high molecular polymer powder bed.
- 3. cigarette tipping paper according to claim 2, it is characterised in that:The ceramic powder or high molecular polymer The particle diameter of powder is 1 μm -100 μm, and specific surface area is 30-2000g/m2。
- 4. the cigarette tipping paper according to Claims 2 or 3, it is characterised in that:The ceramic powder or polyphosphazene polymer The surface of compound powder has micropore, and the aperture of the micropore is less than 1nm.
- 5. the cigarette tipping paper according to any one in claim 1-3, it is characterised in that:The original paper layer is cork paper Original paper layer.
- 6. the manufacturing process of the cigarette tipping paper as described in any one in claim 1-3, it is characterised in that:Including following system Make step:1) printing layer is formed in the upper surface of original paper layer by way of intaglio printing;2) surface of electrochemical aluminum foil material thermoprint to the printing layer is formed into thermoprint layer by way of thermoprint;3) constant humidity gas permeable material is printed to the lower surface formation constant humidity air-permeable layer of the original paper layer by way of intaglio printing.
- 7. manufacturing process according to claim 6, it is characterised in that:Step 3) described in constant humidity gas permeable material for ceramics Material powder or high molecular polymer powder, and its particle diameter is 1 μm -100 μm, specific surface area is 30-2000g/m2。
- 8. manufacturing process according to claim 7, it is characterised in that:Ceramic powder or the high molecular polymer powder The surface at end has micropore, and the aperture of the micropore is less than 1nm.
- 9. manufacturing process according to claim 6, it is characterised in that:Step 2) described in intaglio printing employed in Intaglio plate pit depth is 30 μm -80 μm, and its solidification temperature is 80 DEG C -120 DEG C.
- 10. manufacturing process according to claim 6, it is characterised in that:Step 3) described in intaglio printing employed in Intaglio plate pit depth be 30 μm -80 μm, solidification temperature is 80 DEG C -120 DEG C, and the dry-coated amount of the constant humidity air-permeable layer is 1g/m2- 5g/m2。