CN105272374B - The Nano ceramic tea can of tea leaf fermentation speed can be accelerated - Google Patents

The Nano ceramic tea can of tea leaf fermentation speed can be accelerated Download PDF

Info

Publication number
CN105272374B
CN105272374B CN201510673326.5A CN201510673326A CN105272374B CN 105272374 B CN105272374 B CN 105272374B CN 201510673326 A CN201510673326 A CN 201510673326A CN 105272374 B CN105272374 B CN 105272374B
Authority
CN
China
Prior art keywords
parts
tea
nano ceramic
nano
leaf fermentation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510673326.5A
Other languages
Chinese (zh)
Other versions
CN105272374A (en
Inventor
徐海燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dehua Rootslife Culture Co Ltd
Original Assignee
Dehua Rootslife Culture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dehua Rootslife Culture Co Ltd filed Critical Dehua Rootslife Culture Co Ltd
Priority to CN201510673326.5A priority Critical patent/CN105272374B/en
Publication of CN105272374A publication Critical patent/CN105272374A/en
Application granted granted Critical
Publication of CN105272374B publication Critical patent/CN105272374B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to ceramic technology field, is specifically related to a kind of Nano ceramic tea can for accelerating tea leaf fermentation speed.The Nano ceramic tea can of tea leaf fermentation speed, including tea can base substrate can be accelerated, the tea can base substrate nexine and/or outer layer are provided with nano ceramics glaze layer, and the raw material that the nano ceramic enamel includes following parts by weight is prepared:5 10 parts of iron oxide, 15 parts of manganese oxide, 35 45 parts of feldspar, 10 30 parts of calcium carbonate, 5 10 parts of kaolin, nanometer water 10 20.The above-mentioned Nano ceramic tea can for accelerating tea leaf fermentation speed, the gas in tea can be kept to circulate, make moisture that tealeaves can be suitably in absorption air, accelerate the film by wet hot oxidation process of tea body, also moisture and oxygen are provided for microbial metabolism, and nano level hole can filter out the peculiar smell in air, avoid tealeaves from being mixed with peculiar smell;In addition the glaze paint of this nanometer of glaze layer of this kind is smooth, is tightly combined with base substrate, is difficult for drop-off, having unique artistic effect.

Description

The Nano ceramic tea can of tea leaf fermentation speed can be accelerated
Technical field
The present invention relates to ceramic technology field, is specifically related to a kind of Nano ceramic tea making leaf for accelerating tea leaf fermentation speed Tank.
Background technology
It is well known that its more long taste of time of the full fermentation tea such as the Pu'er tea of black tea, six fort tea storage is more mellow, sweet Refreshing, Chen Xiang, over time, the time it is more long black tea its economic value it is higher.But process is being deposited and collected to black tea In notably environmental factor influence, the shadow that especially external cause such as the humidity of room air and excitant peculiar smell is deposited to black tea Ring, deposit the bad quality that can influence black tea.
Existing porcelain tea can is all not suitable for depositing black tea, and reason is the glaze layer that has of porcelain tea can top layer by base substrate On hole completely enclose, and then separated contacting for tealeaves and the external world, and full fermentation tea is to influence its hair with extraneous contacting An important factor for ferment speed, therefore the tea can of existing porcelain is not appropriate for depositing black tea.
The content of the invention
To overcome deficiency of the prior art, the present invention provides a kind of Nano ceramic tea making leaf for accelerating tea leaf fermentation speed Tank.
To achieve the above object, the technical solution adopted by the present invention is as follows:The Nano ceramic system of tea leaf fermentation speed can be accelerated Tea can, including tea can base substrate, it is characterised in that the tea can base substrate nexine and/or outer layer are provided with nano ceramics glaze layer, The raw material that the nano ceramic enamel includes following parts by weight is prepared:Iron oxide 5-10 parts, manganese oxide 1-5 parts, feldspar 35-45 Part, calcium carbonate 10-30 parts, kaolin 5-10 parts, nanometer water 10-20.
Optimization, the raw material that nano ceramic enamel includes following parts by weight is prepared:6 parts of iron oxide, 4 parts of manganese oxide, length 38 parts of stone, 30 parts of calcium carbonate, 8 parts of kaolin, nanometer water 14.
Optimization, the raw material that nano ceramic enamel includes following parts by weight is prepared:9 parts of iron oxide, 3 parts of manganese oxide, length 42 parts of stone, 28 parts of calcium carbonate, 6 parts of kaolin, nanometer water 12.
Optimization, the raw material that nano ceramic enamel includes following parts by weight is prepared:7 parts of iron oxide, 3 parts of manganese oxide, length 40 parts of stone, 20 parts of calcium carbonate, 10 parts of kaolin, nanometer water 20.
Optimization, ZnO, SiO are included in nanometer water2、TiO2、NiO、Fe2O3, MgO and in one or more nanometers Grain.
Optimization, ZnO, SiO in nanometer water2、TiO2、NiO、Fe2O3, MgO weight ratio be 0.3-0.4:0.05-0.1: 0.3-0.5:0.05-0.1:0.1-0.2:0.01-0.05.
Optimization, SiO in nanometer water2、TiO2、Al2O3、Fe2O3Weight ratio with zeolite is 0.32:0.05:0.4:0.08: 0.12:0.03.
Optimization, SiO in nanometer water2、TiO2、Al2O3、Fe2O3Weight ratio with zeolite is 0.35:0.08:0.32:0.1: 0.1:0.05。
Optimization, ZnO, SiO in nanometer water2、TiO2、NiO、Fe2O3, MgO weight ratio be 0.36:0.07:0.35: 0.05:0.15:0.02.
Optimization, sealed shell of tank is made in tea can.
From the above-mentioned description of this invention, the Nano ceramic tea making leaf provided by the invention for accelerating tea leaf fermentation speed Tank, porous nano glaze layer of the tea can outer layer burnt out formed with one layer of good permeability, can keep the gas in tea can Body circulates, and makes moisture, the film by wet hot oxidation process of acceleration tea body that tealeaves can be suitably in absorption air, is also provided for microbial metabolism Moisture and oxygen, and nano level hole can filter out the peculiar smell in air, avoid tealeaves from being mixed with peculiar smell, be especially suitable for Deposit the full fermentation tealeaves such as Pu'er tea, six fort tea;In addition the glaze paint of this nanometer of glaze layer of this kind is smooth, is tightly combined, no with base substrate Artistic effect easy to fall off, that there is uniqueness.
Embodiment
Below by way of embodiment, the invention will be further described.
The Nano ceramic tea can of tea leaf fermentation speed can be accelerated, including sealed shell of tank is made in tea can base substrate, tea can, The tea can base substrate nexine and/or outer layer are provided with nano ceramics glaze layer, and the nano ceramic enamel includes the raw material of following parts by weight It is prepared:Iron oxide 5-10 parts, manganese oxide 1-5 parts, feldspar 35-45 parts, calcium carbonate 10-30 parts, kaolin 5-10 parts, nanometer Water 10-20;ZnO, SiO are included in nanometer water2、TiO2、NiO、Fe2O3, MgO and in one or more nano particles.
Specific embodiment one:
The Nano ceramic tea can of tea leaf fermentation speed, including tea can base substrate, the tea can base substrate nexine can be accelerated Provided with nano ceramics glaze layer,
The raw material that nano ceramic enamel includes following parts by weight is prepared:6 parts of iron oxide, 4 parts of manganese oxide, 38 parts of feldspar, 30 parts of calcium carbonate, 8 parts of kaolin, nanometer water 14;
Wherein, SiO in nanometer water2、TiO2、Al2O3、Fe2O3Weight ratio with zeolite is 0.32:0.05:0.4:0.08: 0.12:0.03.
Specific embodiment two:
The Nano ceramic tea can of tea leaf fermentation speed, including tea can base substrate, the tea can base substrate outer layer can be accelerated Provided with nano ceramics glaze layer,
The raw material that nano ceramic enamel includes following parts by weight is prepared:9 parts of iron oxide, 3 parts of manganese oxide, 42 parts of feldspar, 28 parts of calcium carbonate, 6 parts of kaolin, nanometer water 12;
Wherein, SiO in nanometer water2、TiO2、Al2O3、Fe2O3Weight ratio with zeolite is 0.35:0.08:0.32:0.1: 0.1:0.05。
Specific embodiment three,
The Nano ceramic tea can of tea leaf fermentation speed, including tea can base substrate, the tea can base substrate nexine can be accelerated Nano ceramics glaze layer is respectively equipped with outer layer,
The raw material that nano ceramic enamel includes following parts by weight is prepared:7 parts of iron oxide, 3 parts of manganese oxide, 40 parts of feldspar, 20 parts of calcium carbonate, 10 parts of kaolin, nanometer water 20;
Wherein, ZnO, SiO in nanometer water2、TiO2、NiO、Fe2O3, MgO weight ratio be 0.36:0.07:0.35:0.05: 0.15:0.02.
Some embodiments of the present invention are above are only, but the design concept of the present invention is not limited thereto, all profits The change of unsubstantiality is carried out to the present invention with this design, the behavior for invading the scope of the present invention all should be belonged to.

Claims (8)

1. the Nano ceramic tea can of tea leaf fermentation speed can be accelerated, including tea can base substrate, it is characterised in that the tea can Base substrate nexine and/or outer layer are provided with nano ceramics glaze layer,
The nano ceramic enamel is prepared by the raw material of following parts by weight:Iron oxide 5-10 parts, manganese oxide 1-5 parts, feldspar 35-45 Part, calcium carbonate 10-30 parts, kaolin 5-10 parts, nanometer water 10-20 parts;
ZnO, SiO are included in the nanometer water2、TiO2、NiO、Fe2O3, one or more nano particles in MgO;
ZnO, SiO in the nanometer water2、TiO2、NiO、Fe2O3, MgO weight ratio be 0.3-0.4:0.05-0.1:0.3-0.5: 0.05-0.1:0.1-0.2:0.01-0.05.
2. the Nano ceramic tea can of tea leaf fermentation speed can be accelerated, including tea can base substrate, it is characterised in that the tea can Base substrate nexine and/or outer layer are provided with nano ceramics glaze layer,
The nano ceramic enamel is prepared by the raw material of following parts by weight:Iron oxide 5-10 parts, manganese oxide 1-5 parts, feldspar 35-45 Part, calcium carbonate 10-30 parts, kaolin 5-10 parts, nanometer water 10-20 parts;SiO in the nanometer water2、TiO2、Al2O3、Fe2O3With The weight ratio of zeolite is 0.32:0.05:0.4:0.08:0.12:0.03.
3. the Nano ceramic tea can of tea leaf fermentation speed can be accelerated, including tea can base substrate, it is characterised in that the tea can Base substrate nexine and/or outer layer are provided with nano ceramics glaze layer,
The nano ceramic enamel is prepared by the raw material of following parts by weight:Iron oxide 5-10 parts, manganese oxide 1-5 parts, feldspar 35-45 Part, calcium carbonate 10-30 parts, kaolin 5-10 parts, nanometer water 10-20 parts;SiO in the nanometer water2、TiO2、Al2O3、Fe2O3With The weight ratio of zeolite is 0.35:0.08:0.32:0.1:0.1:0.05.
4. the Nano ceramic tea can for accelerating tea leaf fermentation speed according to claim 1 or 2 or 3, it is characterised in that The raw material that the nano ceramic enamel includes following parts by weight is prepared:6 parts of iron oxide, 4 parts of manganese oxide, 38 parts of feldspar, carbonic acid 30 parts of calcium, 8 parts of kaolin, 14 parts of nanometer water.
5. the Nano ceramic tea can for accelerating tea leaf fermentation speed according to claim 1 or 2 or 3, it is characterised in that The raw material that the nano ceramic enamel includes following parts by weight is prepared:9 parts of iron oxide, 3 parts of manganese oxide, 42 parts of feldspar, carbonic acid 28 parts of calcium, 6 parts of kaolin, 12 parts of nanometer water.
6. the Nano ceramic tea can for accelerating tea leaf fermentation speed according to claim 1 or 2 or 3, it is characterised in that The raw material that the nano ceramic enamel includes following parts by weight is prepared:7 parts of iron oxide, 3 parts of manganese oxide, 40 parts of feldspar, carbonic acid 20 parts of calcium, 10 parts of kaolin, 20 parts of nanometer water.
7. the Nano ceramic tea can according to claim 1 for accelerating tea leaf fermentation speed, it is characterised in that:It is described to receive Meter Shui Zhong ZnO, SiO2、TiO2、NiO、Fe2O3, MgO weight ratio be 0.36:0.07:0.35:0.05:0.15:0.02.
8. the Nano ceramic tea can for accelerating tea leaf fermentation speed according to claim 1 or 2 or 3, it is characterised in that: Sealed shell of tank is made in the tea can.
CN201510673326.5A 2015-10-16 2015-10-16 The Nano ceramic tea can of tea leaf fermentation speed can be accelerated Active CN105272374B (en)