CN106080002A - A kind of ceramic tile manufacturing process having 3D decorative pattern - Google Patents
A kind of ceramic tile manufacturing process having 3D decorative pattern Download PDFInfo
- Publication number
- CN106080002A CN106080002A CN201610424310.5A CN201610424310A CN106080002A CN 106080002 A CN106080002 A CN 106080002A CN 201610424310 A CN201610424310 A CN 201610424310A CN 106080002 A CN106080002 A CN 106080002A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- temperature
- enamel
- thin film
- picture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of ceramic tile manufacturing process having 3D decorative pattern, its step through ceramic tile its surface spraying viscose glue water, rolling thin film, frost condense glue, thaw, print 3D picture, hot blast drying ink, spraying enamel, drying enamel, cooling, finally cutting, chamfered edge, packaging, complete；The ceramic tile of this technique and film bond are firm, difficult drop-off, are covered by 3D picture with enamel, are so possible to prevent long rear surface to go bad variable color, convenient for cleaning, smear and wash, and do not seep water, have waterproof effect；3D picture is more life-like simultaneously, is more nearly nature, makes decorative effect more conform to the demand of people.
Description
Technical field
The present invention relates to a kind of ceramic tile, a kind of ceramic tile manufacturing process having 3D decorative pattern.
Background technology
Existing ceramic tile surface pattern is all plane pattern or has concave-convex sense to emulate pattern, and these pattern decorative effects are
Seeing used, without what special feature, the most also can only be that pattern is different, using method have become the way of industry universal, it is difficult to inhale
Drawing consumer to like, along with the raising of quality of life, the style of its required product, intention also require that wants characteristic and individual character.
Summary of the invention
In order to solve above-mentioned technical problem, the present invention provides a kind of can make ceramic tile surface have the ceramic tile system of 3D decorative pattern
Make technique.
The scheme solving above-mentioned technical problem is:
A kind of ceramic tile manufacturing process having 3D decorative pattern, is completed by following step:
Step 1: utilize existing ganoid ceramic tile at its surface spraying viscose glue water, and uniform spraying；
Step 2: at one layer of high-temperature resistant membrane of surface rolling of ceramic tile, rolled smooth by cylinder, makes thin film glue with ceramic tile
Tightly；
Step 3: the ceramic tile gluing thin film is put into the freezer between 1 DEG C-5 DEG C and freezes 1 hour-2 hours, makes glue coagulate
Knot is firm, difficult drop-off；
Step 4: take out, thaw at normal temperatures, makes ceramic tile body recover room temperature airing moisture at normal temperatures；
Step 5: at the picture of the surface printing 3D effect of thin film；
Step 6: by printing ink hot blast drying, the hot blast temperature dried up is: 40 DEG C-50 DEG C；
Step 7: after drying up, at surface spraying enamel；
Step 8: ceramic tile is placed in baking oven, by temperature be: enamel is dried by the hot temperature of 35 DEG C-50 DEG C, during baking
Between be: 1 hour-2 hours；
Step 9: take out, at normal temperatures temperature is reduced to room temperature；
Step 10: cutting, chamfered edge, packaging, completes.
The invention have the benefit that ceramic tile is firm with film bond, difficult drop-off, with enamel, 3D picture is covered, this
Sample is possible to prevent long rear surface to go bad variable color, convenient for cleaning, smear and wash, and does not seeps water, has waterproof effect；3D picture is more forced simultaneously
Very, it is more nearly nature, makes decorative effect more conform to the demand of people.
Detailed description of the invention
A kind of ceramic tile manufacturing process having 3D decorative pattern, is completed by following step:
Step 1: utilize existing ganoid ceramic tile at its surface spraying viscose glue water, and uniform spraying；
Step 2: at one layer of high-temperature resistant membrane of surface rolling of ceramic tile, rolled smooth by cylinder, makes thin film glue with ceramic tile
Tightly, the fusing point of thin film is 200 DEG C.
Step 3: the ceramic tile gluing thin film is put into the freezer between 1 DEG C-5 DEG C and freezes 1 hour-2 hours, makes glue coagulate
Knot is firm, difficult drop-off；
Step 4: take out, thaw at normal temperatures, makes ceramic tile body recover room temperature airing moisture, thawing time at normal temperatures
Being 2 hours-3 hours, the airing time is 2 hours-3 hours；
Step 5: be placed in printing, at the picture of the surface printing 3D effect of thin film；
Step 6: by printing ink hot blast drying, the hot blast temperature dried up is: 40 DEG C-50 DEG C, and the time dried up is 15 points
Clock-45 minutes；
Step 7: after drying up, forms the glaze layer of layer of transparent after surface spraying enamel, spraying uniformly on surface；
Step 8: ceramic tile is placed in baking oven, by temperature be: enamel is dried by the hot temperature of 35 DEG C-50 DEG C, during baking
Between be: 1 hour-2 hours；
Step 9: take out, at normal temperatures temperature is reduced to room temperature；
Step 10: cutting, chamfered edge, packaging, completes, and can sell or for home decoration.
Claims (1)
1. the ceramic tile manufacturing process having 3D decorative pattern, it is characterised in that completed by following step:
Step 1: utilize existing ganoid ceramic tile at its surface spraying viscose glue water, and uniform spraying；
Step 2: at one layer of high-temperature resistant membrane of surface rolling of ceramic tile, rolled by cylinder smooth, make thin film cling with ceramic tile；
Step 3: the ceramic tile gluing thin film is put into the freezer between 1 DEG C-5 DEG C and freezes 1 hour-2 hours, makes glue condense jail
Gu, difficult drop-off；
Step 4: take out, thaw at normal temperatures, makes ceramic tile body recover room temperature airing moisture at normal temperatures；
Step 5: at the picture of the surface printing 3D effect of thin film；
Step 6: by printing ink hot blast drying, the hot blast temperature dried up is: 40 DEG C-50 DEG C；
Step 7: after drying up, at surface spraying enamel；
Step 8: ceramic tile is placed in baking oven, by temperature be: enamel is dried by the hot temperature of 35 DEG C-50 DEG C, and baking time is:
1 hour-2 hours；
Step 9: take out, at normal temperatures temperature is reduced to room temperature；
Step 10: cutting, chamfered edge, packaging, completes.