CN108821796A - Color decoration technology on a kind of ceramic glaze - Google Patents

Color decoration technology on a kind of ceramic glaze Download PDF

Info

Publication number
CN108821796A
CN108821796A CN201810649610.2A CN201810649610A CN108821796A CN 108821796 A CN108821796 A CN 108821796A CN 201810649610 A CN201810649610 A CN 201810649610A CN 108821796 A CN108821796 A CN 108821796A
Authority
CN
China
Prior art keywords
finished product
semi
time
dried
color
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810649610.2A
Other languages
Chinese (zh)
Inventor
陈行
陈行一
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810649610.2A priority Critical patent/CN108821796A/en
Publication of CN108821796A publication Critical patent/CN108821796A/en
Pending legal-status Critical Current

Abstract

The invention discloses decoration technologies color on a kind of ceramic glaze, it is comprised the following steps:One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 10-16 hours, and semi-finished product are made, and forms oil colour layer on the outer surface of semi-finished product at this time;Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out, required pattern is drawn;Three, it is dried, flash-off time is one day or a couple of days;Four, kiln-firing is fired 4-6 hours under 780 DEG C of -830 DEG C of environment, and after soaking time 10-20 minutes, natural cooling is come out of the stove, finished product;Color decoration technology on a kind of ceramic glaze of the present invention, technique is unique, and pattern and color can be with changeable multiplicity.

Description

Color decoration technology on a kind of ceramic glaze
Technical field
The present invention relates to ceramic glazing technical fields, and in particular to color decoration technology on a kind of ceramic glaze.
Background technique
Porcelain is that one kind is made of porcelain stone, kaolin etc., and outer top application has the sundries of glaze or colored drawing.The forming of porcelain will pass through Pass through high temperature in kiln(About 1280 DEG C -1400 DEG C)Fire, come across Shang dynasty middle and advanced stage earliest, the glaze colours on porcelain surface can because The difference of temperature is to occur various chemical changes.The porcelain tire of sintering generally contain only 3% less than ferro element, and it is waterproof, because The common people of its more cheap cost and wear-resisting fluid-tight characteristic widely all over the world are used.The high porcelain of raw material degree of purity Device can issue the clear and melodious sound of metalloid collision in mutual collision.Advanced porcelain possesses the production much higher than general porcelain Technology difficulty, therefore also it is no lack of the collection of exquisite porcelain in imperial family in ancient times.
Glazing is exactly so-called in fire porcelain, should fire blank first, glazing is taken out after burned, is then reburned A kind of mode.It is applied on the blank baked and is covered with one layer of vitreous glaze layer, primarily serve protection and decorative effect.Tradition Glazing method be that Freehandhand-drawing is carried out after the completion of blank biscuiting, pattern obtained and color fidelity be not high, and is difficult to changeable.
Summary of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide decoration technologies color on a kind of ceramic glaze.
To achieve the above object, the technical solution adopted by the present invention is that:It is comprised the following steps:
One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 10- 16 hours, semi-finished product are made, form oil colour layer on the outer surface of semi-finished product at this time;
Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out, Draw required pattern;
Three, it is dried, flash-off time is one day or a couple of days;
Four, kiln-firing is fired 4-6 hours under 780 DEG C of -830 DEG C of environment, after soaking time 10-20 minutes, natural cooling, It comes out of the stove, finished product.
After adopting the above scheme, the present invention has the beneficial effect that:Color decoration technology, work on a kind of ceramic glaze of the present invention Skill is unique, and pattern and color can be with changeable multiplicity.
Specific embodiment
The present invention is further illustrated below.
Embodiment:Color decoration technology on a kind of ceramic glaze, it is comprised the following steps:
One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 14 Hour, semi-finished product are made, form oil colour layer on the outer surface of semi-finished product at this time;
Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out, Draw required pattern;
Three, it is dried, flash-off time is one day or a couple of days;
Four, kiln-firing is fired 5 hours under 780 DEG C of -830 DEG C of environment, and soaking time after twenty minutes, come out of the stove by natural cooling, Finished product.
Porcelain floral disc made from the scheme of the present embodiment, technique is unique and simple, beautiful and generous.
The above is merely illustrative of the technical solution of the present invention, rather than limits those of ordinary skill in the art to this hair The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention, It is intended to be within the scope of the claims of the invention.

Claims (1)

1. color decoration technology on a kind of ceramic glaze, it is characterised in that it is comprised the following steps:
One, on burned pottery, one layer of oiliness overglaze color pigment is smeared, and it is half-dried to dry in the air, the half-dried process time that dries in the air is 10- 16 hours, semi-finished product are made, form oil colour layer on the outer surface of semi-finished product at this time;
Two, on semi-finished product, with writing brush, hairbrush or other painting tools, the oil colour layer being coated on pottery is smeared out, Draw required pattern;
Three, it is dried, flash-off time is one day or a couple of days;
Four, kiln-firing is fired 4-6 hours under 780 DEG C of -830 DEG C of environment, after soaking time 10-20 minutes, natural cooling, It comes out of the stove, finished product.
CN201810649610.2A 2018-06-22 2018-06-22 Color decoration technology on a kind of ceramic glaze Pending CN108821796A (en)