CN105891915A - 一种新型uv420镜片的制造方法 - Google Patents
一种新型uv420镜片的制造方法 Download PDFInfo
- Publication number
- CN105891915A CN105891915A CN201610332384.6A CN201610332384A CN105891915A CN 105891915 A CN105891915 A CN 105891915A CN 201610332384 A CN201610332384 A CN 201610332384A CN 105891915 A CN105891915 A CN 105891915A
- Authority
- CN
- China
- Prior art keywords
- eyeglass
- novel
- stiffened
- manufacture method
- lens
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型UV420镜片的制造方法，区别于传统UV380、UV420镜片有明显的优势，可以将阻断波长上限提至420nm。主要步骤：镜片处理、溶液配制、固化、镀膜和检测。该工艺将添加剂（UV420）加入加硬液中，实现镜片UV加硬，这样不仅可以缩短工艺链，降低生产成本，而且该工艺生产的镜片可以有效将紫外阻断波长上限提至420nm，可以更好的保护眼睛。
Description
技术领域
本发明涉及镜片制造技术领域，特别是涉及一种阻断特定波长UV420镜片的制造方法。
背景技术
树脂镜片是目前全球最常见的镜片，具有出色的光学性能、耐冲击和不易碎、质轻等优良特点。由于树脂镜片本身的特点，除了PC镜片，其它的树脂镜片不能够阻挡全部的紫外线，而紫外线对人体的伤害不容忽视，目前镜片通过添加相应UV粉和镀膜只能对下面几个波长段进行阻挡：UVC（短波紫外线）辐射的波长最短（100-280纳米）；UVB（中波紫外线）辐射的波长为280-320纳米。少量的UVB能穿透臭氧层，10%甚至更低的UVB辐射可以达到地表。UVB是造成皮肤老化、日晒伤、免疫抑制、DNA损伤和皮肤癌的原因之一。
UVA（长波紫外线）辐射的波长为320-400纳米，90%以上的UVA辐射可以达到地表。UVA对皮肤的晒伤性和破坏性强度虽然不如UVB，但是也同样会造成日晒伤，并且较大程度地抑制了皮肤的免疫系统机能。就目前而言，UV 400 镜片只能将紫外阻断上限提至400nm，而420nm左右的蓝紫光处于高能量带，会引起人眼黄斑病变，而420nm左右的波长普遍的存在与手机、电视和电脑等的显示屏上，蓝紫光对人眼的伤害不容小觑。
发明内容
为了克服上述现有技术的不足，本发明提供了一种阻断特定波长UV420树脂镜片制造工艺，主要解决高能量带蓝紫光阻断问题，通过合理的制造方法将镜片的防紫外功能提升至UV420。
本发明所采用的技术方案是：一种新型UV420镜片的制造方法，该工艺包括以下步骤：
步骤一：镜片处理：将镜片分类放入待加硬区，并对镜片进行外观检查，预处理清洗干净，并上夹具；
步骤二：溶液配制：在浸涂加硬机所用的加硬底涂、顶涂溶液中或旋涂机加硬液中加入特定剂量的UV粉添加剂，并充分搅拌混匀；
步骤三：加硬固化：将镜片用浸涂方式或旋涂方式对镜片进行表面加硬固化；
步骤四：镜片镀膜：在完成步骤三后，将已经进行加硬固化的镜片转入真空镀膜机进行加镀膜层；
步骤五：检查：终检进行镜片检查，镜片质检按照镜片质检ISO标准和美国FDA标准进行检测。
本发明的进一步改进在于：在所述步骤一中的镜片为CR-39、KOC 1.56、MR(1.60、1.67和1.74)系列树脂镜片。
本发明的进一步改进在于：在所述步骤二中所述UV粉添加剂为可以阻断上限为420nm的紫外吸收剂，所述紫外吸收剂的用量为0.1%-5%，所述紫外吸收剂可以起到防止镜片老化、变黄的作用。
本发明的进一步改进在于：在所述步骤二中所述浸涂加硬机和所述旋涂机其循环滤芯为1~10μm。
本发明的进一步改进在于：所述步骤三中的浸涂方式为将镜片通过超声波KOH刻蚀、清洗和烘干后，浸入B所配溶液中，提拉速度设定底涂为0.5~1.5mm/s，顶涂为1.0~2.5mm/s，提拉结束后放入烘箱中固化。
本发明的进一步改进在于：所述步骤三中的旋涂方式其旋涂速度为300~600r/min，UV固化1800~2200r/min，UV固化时间为15~35s；。
本发明的进一步改进在于：所述步骤四的镜片镀膜所用的真空镀膜机是劳尔或莱宝真空镀膜机。
本发明的有益效果：该工艺对镜片原料没有太大限制，所有折射率镜片都可以应用该工艺实现镜片紫外线阻断，而且可以起到防止镜片老化、变黄的作用，在镜片表面加硬层添加UV粉，有效降低了变色镜片成本、减少工艺链、增加生产效率密切工艺更加简单、容易控制。
附图说明
图1为；为该发明的示意图
其中：1为加硬层、2为树脂镜片 、3为镀膜层。
具体实施方式
下面结合附图对本发明进一步说明,下面的实施例只是对本发明进行举例说明，本发明不局限于该实施例的范围。
实施例 1
本实施例所采用的技术方案是：一种新型UV420镜片的制造方法，该工艺包括以下步骤：
步骤一：镜片处理：将CR-39、KOC 1.56、MR(1.60、1.67和1.74)系列树脂镜片2分类放入待加硬区，并对镜片进行外观检查，预处理清洗干净，并上夹具；
步骤二：溶液配制：在浸涂加硬机所用的加硬底涂、顶涂溶液中或旋涂机加硬液中加入可以阻断上限为420nm的紫外吸收剂，所述紫外吸收剂的用量为1%，并充分搅拌混匀，之后加入浸涂加硬机用5μm的滤芯循环24h；
步骤三：加硬固化：将镜片用浸涂方式对镜片进行表面加硬固化，形成加硬层1，将镜片通过超声波KOH刻蚀、清洗和烘干后，浸入步骤二所配溶液中，提拉速度设定底涂为1.0mm/s，顶涂为1.8mm/s，提拉结束后放入烘箱中进行固化；
步骤四：镜片镀膜：在完成步骤三后，将已经进行加硬固化的镜片转入莱宝真空镀膜机进行加镀膜层3；
步骤五：检查：将镜片按照镜片质检ISO标准和美国FDA标准进行检测，具体结果如下：
本实施例的有益效果：该工艺对镜片原料没有太大限制，所有折射率镜片都可以应用该工艺实现镜片紫外线阻断，在镜片表面加硬层添加UV粉，有效降低了变色镜片成本、减少工艺链、增加生产效率密切工艺更加简单、容易控制。
实施例 2
本实施例所采用的技术方案是：一种新型UV420镜片的制造方法，该工艺包括以下步骤：
步骤一：镜片处理：将CR-39、KOC 1.56、MR(1.60、1.67和1.74)系列树脂镜片2分类放入待加硬区，并对镜片进行外观检查，预处理清洗干净，并上夹具；
步骤二：溶液配制：在浸涂加硬机所用的加硬底涂、顶涂溶液中或旋涂机加硬液中加入可以阻断上限为420nm的紫外吸收剂，所述紫外吸收剂的用量为1.2%，并充分搅拌混匀，之后加入浸涂加硬机用5μm的滤芯循环24h；
步骤三：加硬固化：将镜片用浸涂方式对镜片进行表面加硬固化，形成加硬层1，将镜片通过超声波KOH刻蚀、清洗和烘干后，浸入步骤二所配溶液中，提拉速度设定底涂为1.0mm/s，顶涂为1.8mm/s，提拉结束后放入烘箱中进行固化；
步骤四：镜片镀膜：在完成步骤三后，将已经进行加硬固化的镜片转入莱宝真空镀膜机进行加镀膜层3；
步骤五：检查：将镜片按照镜片质检ISO标准和美国FDA标准进行检测，具体结果如下：
实施例 3
本实施例所采用的技术方案是：一种新型UV420镜片的制造方法，该工艺包括以下步骤：
步骤一：镜片处理：对树脂镜2进行外观检查、预处理；
步骤二：溶液配制：将旋涂机所用加硬液中加入可以阻断上限为420nm的紫外吸收剂，所述紫外吸收剂的用量为1%，并充分搅拌混匀，之后加入旋涂机用5μm的滤芯循环2h；
步骤三：加硬固化：将镜片用旋涂方式对镜片进行表面加硬固化，形成加硬层1，将镜片通过超声波KOH刻蚀、清洗和烘干后，将旋涂速度调为400r/min，UV固化调为2200r/min，并UV固化20s；
步骤四：镜片镀膜：在完成步骤三后，将已经进行加硬固化的镜片转入莱宝真空镀膜机进行加镀膜层3；
步骤五：检查：将镜片按照镜片质检ISO标准和美国FDA标准进行检测，具体结果如下：
以上仅为本专利实施例的较佳实施例而已，并不用以限制本专利实施例，凡在本专利实施例的使用和原则之内，所作的任何修改、等同替换、改善等，均应包含在本专利实施例的保护范围之内。
Claims (7)
1.一种新型UV420镜片的制造方法，其特征在于：该工艺包括以下步骤：
步骤一：镜片处理：将镜片分类放入待加硬区，并对镜片进行外观检查，预处理清洗干净，并上夹具；
步骤二：溶液配制：在浸涂加硬机所用的加硬底涂、顶涂溶液中或旋涂机加硬液中加入特定剂量的UV粉添加剂，并充分搅拌混匀；
步骤三：加硬固化：将镜片用浸涂方式或旋涂方式对镜片进行表面加硬固化；
步骤四：镜片镀膜：在完成步骤三后，将已经进行加硬固化的镜片转入真空镀膜机进行加镀膜层；
步骤五：检查：终检进行镜片检查，镜片质检按照镜片质检ISO标准和美国FDA标准进行检测。
2.根据权利要求1所述的一种新型UV420镜片的制造方法，其特征在于：在所述步骤一中的镜片为CR-39、KOC 1.56、MR(1.60、1.67和1.74)系列树脂镜片。
3.根据权利要求1所述的一种新型UV420镜片的制造方法，其特征在于：在所述步骤二中所述UV粉添加剂为可以阻断上限为420nm的紫外吸收剂，所述紫外吸收剂的用量为0.1%-5%。
4.根据权利要求1所述的一种新型UV420镜片的制造方法，其特征在于：在所述步骤二中所述浸涂加硬机和所述旋涂机其循环滤芯为1~10μm。
5.根据权利要求1所述的一种新型UV420镜片的制造方法，其特征在于：所述步骤三中的浸涂方式为将镜片通过超声波KOH刻蚀、清洗和烘干后，浸入B所配溶液中，提拉速度设定底涂为0.5~1.5mm/s，顶涂为1.0~2.5mm/s，提拉结束后放入烘箱中固化。
6.根据权利要求1所述的一种新型UV420镜片的制造方法，其特征在于：所述步骤三中的旋涂方式其旋涂速度为300~600r/min，UV固化1800~2200r/min，UV固化时间为15~35s；。
7.根据权利要求1所述的一种新型UV420镜片的制造方法，其特征在于：所述步骤四的镜片镀膜所用的真空镀膜机是劳尔或莱宝真空镀膜机。