CN105818456A - Anti-static striped fabric and making process thereof - Google Patents
Anti-static striped fabric and making process thereof Download PDFInfo
- Publication number
- CN105818456A CN105818456A CN201610183470.5A CN201610183470A CN105818456A CN 105818456 A CN105818456 A CN 105818456A CN 201610183470 A CN201610183470 A CN 201610183470A CN 105818456 A CN105818456 A CN 105818456A
- Authority
- CN
- China
- Prior art keywords
- fabric
- sample
- fiber
- wool
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-static striped fabric and a making process thereof.The fabric is characterized by comprising a fabric body, a thin-stripe fabric layer is arranged on the surface of the fabric body and connected with the fabric body with threads, bold-stripe rectangular short cloths are distributed on the thin-stripe fabric layer, arranged in a staggered mode in the horizontal direction, and fixed to the thin-stripe fabric layer with threads, a fluff layer is arranged on the bottom surface of the fabric body, and an anti-static layer is arranged on the bottom surface of the fluff layer.Due to the fact that the short cloths protrude out of the plane where the thin-stripe fabric layer is located, the layering sense of the striped fabric is improved; the fluff layer enables the heat retention property of the striped fabric to be improved, and the anti-static layer enables anti-static property to be improved.
Description
Technical field
The present invention relates to antistatic strip fabric and processing technology thereof, belong to fabric technical field.
Background technology
Traditional fabric is usually single layer structure, and function is the most single.In recent years along with the development of textile industry, occurring in that double-layer fabric, double-layer fabric is three dimensional structure, has solid layer feeling, and abundant degree and intensity are relatively good, but do not possess electrostatic-proof function.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that solid layer feeling preferable antistatic strip fabric and processing technology thereof.
The object of the present invention is achieved like this:
Antistatic strip fabric, including fabric body, described fabric body surface is provided with microgroove precoat, and microgroove precoat is connected with fabric body line, and described microgroove precoat is distributed coarse groove rectangle billet cloth, described billet cloth alternate in the horizontal direction, and be fixed on microgroove precoat with line, the bottom surface of described fabric body is provided with tapetum, and tapetum bottom surface is provided with antistatic backing, offer lower floor's pore on described antistatic backing, described microgroove precoat offers upper strata pore;
The processing technology of antistatic strip fabric is:
1), yarn variety design:
nullSelect wool fiber、Cashmere fiber and aethiops vegetabilis fiber,Described wool fiber is by rabbit fur fibre、Beautiful promise superfine wool、Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form,In described blending rabbit wool fiber fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%,Described beautiful promise superfine wool accounts for 15%-19%,Described Angora goat wool fibre accounts for 26%-30%,Described mercerized wool fiber accounts for 29%-41%,To wool fiber、Cashmere fiber and aethiops vegetabilis fiber carry out anti pilling process、Ferment treatment and soft treatment,Anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent,Phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%,Ferment treatment system uses protease to process,Protease consumption is the 0.1-0.2% of wool fiber weight,The softening agent that soft treatment is selected is water-soluble organic silicon softening agent,Water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight;
2), recombing technique:
Sequentially passing through silver mixing grilling combing grilling becomes bar operation to complete recombing;
3), spinning process:
Using generally known spinning process, sequentially pass through scalp acupuncture two pin three pin four pin rove-deposit spun yarn yarn steaming from winder-doubling-double twisting yarn steaming operation, make the yarn for weaving worsted fabric, spinning process uses compact spinning spun yarn equipment;
4), weaving and repair technology:
Use generally known weaving and repair technology, yarn weaving is become grey cloth, and makes grey cloth nonwoven defect and float by repairing;
5), postfinishing process:
Grey cloth dry through open width braying crabbing of singing-high speed braying-bakings-increase depths and manage and ripe repair middle inspection-bristle-cropping tank steaming-decatizing-shrinking processes, make worsted fabric;
6) test drying property:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the sample of width as test sample;
Step 2: be placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into after sealing in dry-cleaning instrument, takes out, then repeated washing twice after dry-cleaning 30min;
Step 3: sample is flat on temperature 20 ± 2 DEG C, in the environment of humidity 65 ± 3%, is put on balance after balancing 12 hours and weighs, and claims to obtain the front weight of sample leaching;
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent FFA in 499.5ml distilled water), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute;
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, the airer for clothes hanging with sample is placed in temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, sample weight is measured, until sample recovers weight before leaching after 30 minutes;
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Compared with prior art, the invention has the beneficial effects as follows:
In antistatic strip fabric of the present invention and processing technology thereof, billet cloth protrudes the place plane of microgroove precoat, enhances the stereovision of strip fabric, and tapetum enhances the warmth retention property of strip fabric, and antistatic backing improves static electricity resistance simultaneously.
Detailed description of the invention
The present invention relates to antistatic strip fabric and processing technology thereof, including fabric body, described fabric body surface is provided with microgroove precoat, microgroove precoat is connected with fabric body line, coarse groove rectangle billet cloth it is distributed on described microgroove precoat, described billet cloth alternate in the horizontal direction, and be fixed on microgroove precoat with line, the bottom surface of described fabric body is provided with tapetum, tapetum bottom surface is provided with antistatic backing, offer lower floor's pore on described antistatic backing, described microgroove precoat offers upper strata pore.
The process making antistatic strip fabric and processing technology thereof is:
1), yarn variety design:
nullSelect wool fiber、Cashmere fiber and aethiops vegetabilis fiber,Described wool fiber is by rabbit fur fibre、Beautiful promise superfine wool、Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form,In described blending rabbit wool fiber fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%,Described beautiful promise superfine wool accounts for 15%-19%,Described Angora goat wool fibre accounts for 26%-30%,Described mercerized wool fiber accounts for 29%-41%,To wool fiber、Cashmere fiber and aethiops vegetabilis fiber carry out anti pilling process、Ferment treatment and soft treatment,Anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent,Phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%,Ferment treatment system uses protease to process,Protease consumption is the 0.1-0.2% of wool fiber weight,The softening agent that soft treatment is selected is water-soluble organic silicon softening agent,Water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight;
2), recombing technique:
Sequentially passing through silver mixing grilling combing grilling becomes bar operation to complete recombing;
3), spinning process:
Using generally known spinning process, sequentially pass through scalp acupuncture two pin three pin four pin rove-deposit spun yarn yarn steaming from winder-doubling-double twisting yarn steaming operation, make the yarn for weaving worsted fabric, spinning process uses compact spinning spun yarn equipment;
4), weaving and repair technology:
Use generally known weaving and repair technology, yarn weaving is become grey cloth, and makes grey cloth nonwoven defect and float by repairing;
5), postfinishing process:
Grey cloth dry through open width braying crabbing of singing-high speed braying-bakings-increase depths and manage and ripe repair middle inspection-bristle-cropping tank steaming-decatizing-shrinking processes, make worsted fabric;
6) test drying property:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the sample of width as test sample;
Step 2: be placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into after sealing in dry-cleaning instrument, takes out, then repeated washing twice after dry-cleaning 30min;
Step 3: sample is flat on temperature 20 ± 2 DEG C, in the environment of humidity 65 ± 3%, is put on balance after balancing 12 hours and weighs, and claims to obtain the front weight of sample leaching;
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent FFA in 499.5ml distilled water), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute;
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, the airer for clothes hanging with sample is placed in temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, sample weight is measured, until sample recovers weight before leaching after 30 minutes;
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Claims (1)
1. antistatic strip fabric, it is characterized in that: include fabric body, described fabric body surface is provided with microgroove precoat, microgroove precoat is connected with fabric body line, coarse groove rectangle billet cloth it is distributed on described microgroove precoat, described billet cloth alternate in the horizontal direction, and be fixed on microgroove precoat with line, the bottom surface of described fabric body is provided with tapetum, tapetum bottom surface is provided with antistatic backing, offer lower floor's pore on described antistatic backing, described microgroove precoat offers upper strata pore;
The process of antistatic strip fabric is:
1), yarn variety design:
nullSelect wool fiber、Cashmere fiber and aethiops vegetabilis fiber,Described wool fiber is by rabbit fur fibre、Beautiful promise superfine wool、Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form,In described blending rabbit wool fiber fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%,Described beautiful promise superfine wool accounts for 15%-19%,Described Angora goat wool fibre accounts for 26%-30%,Described mercerized wool fiber accounts for 29%-41%,To wool fiber、Cashmere fiber and aethiops vegetabilis fiber carry out anti pilling process、Ferment treatment and soft treatment,Anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent,Phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%,Ferment treatment system uses protease to process,Protease consumption is the 0.1-0.2% of wool fiber weight,The softening agent that soft treatment is selected is water-soluble organic silicon softening agent,Water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight;
2), recombing technique:
Sequentially passing through silver mixing grilling combing grilling becomes bar operation to complete recombing;
3), spinning process:
Using generally known spinning process, sequentially pass through scalp acupuncture two pin three pin four pin rove-deposit spun yarn yarn steaming from winder-doubling-double twisting yarn steaming operation, make the yarn for weaving worsted fabric, spinning process uses compact spinning spun yarn equipment;
4), weaving and repair technology:
Use generally known weaving and repair technology, yarn weaving is become grey cloth, and makes grey cloth nonwoven defect and float by repairing;
5), postfinishing process:
Grey cloth dry through open width braying crabbing of singing-high speed braying-bakings-increase depths and manage and ripe repair middle inspection-bristle-cropping tank steaming-decatizing-shrinking processes, make worsted fabric;
6) test drying property:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the sample of width as test sample;
Step 2: be placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into after sealing in dry-cleaning instrument, takes out, then repeated washing twice after dry-cleaning 30min;
Step 3: sample is flat on temperature 20 ± 2 DEG C, in the environment of humidity 65 ± 3%, is put on balance after balancing 12 hours and weighs, and claims to obtain the front weight of sample leaching;
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent FFA in 499.5ml distilled water), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute;
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, the airer for clothes hanging with sample is placed in temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, sample weight is measured, until sample recovers weight before leaching after 30 minutes;
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.