CN107173889A - A kind of making of anti-drilling hair side material and method of testing - Google Patents

A kind of making of anti-drilling hair side material and method of testing Download PDF

Info

Publication number
CN107173889A
CN107173889A CN201610139140.6A CN201610139140A CN107173889A CN 107173889 A CN107173889 A CN 107173889A CN 201610139140 A CN201610139140 A CN 201610139140A CN 107173889 A CN107173889 A CN 107173889A
Authority
CN
China
Prior art keywords
sample
fabric
wool
weight
wool fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610139140.6A
Other languages
Chinese (zh)
Inventor
卞平芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610139140.6A priority Critical patent/CN107173889A/en
Publication of CN107173889A publication Critical patent/CN107173889A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of making of anti-drilling hair side material and method of testing, the fabric is comfortable, ventilative, fabric is generally not in bore hair phenomenon, it is ensured that overall outward appearance, will not give people uncomfortable sensation, fabric drying property can be completed in the test short time, test result is quickly timely, is conducive to enterprise simple and practical to drying fabric production and technology g uarantee, method of testing, special detection device need not be configured, testing cost is low.

Description

A kind of making of anti-drilling hair side material and method of testing
Technical field
The present invention relates to a kind of making of anti-drilling hair side material and method of testing, belong to fabric technical field.
Background technology
Clothes has gradually been received by most consumers because of its warmth retention property, lightweight flexible, aesthetic property and comfortableness.And brill hair phenomenon generally occurs in some fabrics for being used to manufacture clothes at present; it not only have impact on overall outward appearance; and uncomfortable sensation can be given people; and existing anti-drilling hair is typically that one layer of adhesive is applied on fabric; to fill up longitude and latitude intertwined point; to prevent hair from getting out, this structure is airtight, hygroscopicity is poor, and dress for a long time causes discomfort.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided a kind of making of comfortable, ventilative anti-drilling hair side material and method of testing.
The object of the present invention is achieved like this：
A kind of making of anti-drilling hair side material and method of testing are：
1）, yarn variety design：
From wool fiber, cashmere fiber and marine alga Carbon fibe, the wool fiber is formed by rabbit fur fibre, beautiful promise superfine wool, the four kinds of fiber blend braidings of Angora goat wool fibre and mercerized wool fiber, and percentage by weight shared by each composition is respectively in described blending rabbit wool fiber fabric：The rabbit fur fibre accounts for 18%-22%, the beautiful promise superfine wool accounts for 15%-19%, the Angora goat wool fibre accounts for 26%-30%, the mercerized wool fiber accounts for 29%-41%, to wool fiber, cashmere fiber and marine alga Carbon fibe carry out anti pilling processing, ferment treatment and soft treatment, anti pilling processing is used as anti pilling agent from phosphate antimony oxide mixture, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is handled using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing technique：
Sequentially pass through silver mixing-grilling-combing-grilling-into bar process complete recombing；
3）, spinning process：
Using generally known spinning process, the pin of pin-tri- of scalp acupuncture-bis--tetra- pins-rove-storage-spun yarn-yarn steaming-is sequentially passed through from winder-doubling-double twisting-yarn steaming process, the yarn for weaving worsted fabric is made, spinning process uses compact spinning spun yarn equipment；
4）, weaving and repair technology：
Using generally known weaving and repair technology, by yarn weaving into fabric, and fabric nonwoven defect and float are caused by repairing；
5）, postfinishing process：
Fabric by singing-open width braying-crabbing-baking-high speed braying-baking-increases depths reason-ripe and repaiies-middle inspection-bristle-cropping-tank steaming-decatizing-shrinking processes, and worsted fabric is made；
6）Test drying property：
Step one：Lead in 40cm on the sample of width and take the cm of 10 cm × 20 two pieces of sample as test sample；
Step 2：Sample is placed in washing appearance device, 300ml tetrachloro-ethylenes are added as dry cleaning agent, is put into after sealing in dry-cleaning instrument, is taken out after dry-cleaning 30min, then repeated washing is twice；
Step 3：Sample is flat in the environment of 20 ± 2 DEG C of temperature, humidity 65 ± 3%, balance is put on balance after 12 hours and weighed, claims to obtain the preceding weight of sample leaching；
Step 4：Reagent 500ml is added in beaker（Preparation of reagents method：0.5ml bleeding agents FFA is added in 499.5ml distilled water）, the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute；
Step 5：By the sample after moisture absorption, a folding is hung on airer for clothes for two along its length, the airer for clothes for hanging with sample is placed under 20 ± 2 DEG C of temperature, the environmental condition of humidity 65 ± 3%, and records the time, every measuring sample weight after 30 minutes, until sample recovers before leaching untill weight；
Step 6：The time that sample recovers weight before leaching is recorded, as fabric spontaneously dries the time.
Compared with prior art, the beneficial effects of the invention are as follows：
Water imbibition can be completed in the test short time, and test result is quickly timely, be conducive to enterprise to be produced to water imbibition fabric and technology g uarantee, and method of testing is simple and practical, it is not necessary to configure special detection device, testing cost is low.
Embodiment
The present invention relates to a kind of making of anti-drilling hair side material and method of testing：
1）, yarn variety design：
From wool fiber, cashmere fiber and marine alga Carbon fibe, the wool fiber is formed by rabbit fur fibre, beautiful promise superfine wool, the four kinds of fiber blend braidings of Angora goat wool fibre and mercerized wool fiber, and percentage by weight shared by each composition is respectively in described blending rabbit wool fiber fabric：The rabbit fur fibre accounts for 18%-22%, the beautiful promise superfine wool accounts for 15%-19%, the Angora goat wool fibre accounts for 26%-30%, the mercerized wool fiber accounts for 29%-41%, to wool fiber, cashmere fiber and marine alga Carbon fibe carry out anti pilling processing, ferment treatment and soft treatment, anti pilling processing is used as anti pilling agent from phosphate antimony oxide mixture, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is handled using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing technique：
Sequentially pass through silver mixing-grilling-combing-grilling-into bar process complete recombing；
3）, spinning process：
Using generally known spinning process, the pin of pin-tri- of scalp acupuncture-bis--tetra- pins-rove-storage-spun yarn-yarn steaming-is sequentially passed through from winder-doubling-double twisting-yarn steaming process, the yarn for weaving worsted fabric is made, spinning process uses compact spinning spun yarn equipment；
4）, weaving and repair technology：
Using generally known weaving and repair technology, by yarn weaving into fabric, and fabric nonwoven defect and float are caused by repairing；
5）, postfinishing process：
Fabric by singing-open width braying-crabbing-baking-high speed braying-baking-increases depths reason-ripe and repaiies-middle inspection-bristle-cropping-tank steaming-decatizing-shrinking processes, and worsted fabric is made；
6）Test drying property：
Step one：Lead in 40cm on the sample of width and take the cm of 10 cm × 20 two pieces of sample as test sample；
Step 2：Sample is placed in washing appearance device, 300ml tetrachloro-ethylenes are added as dry cleaning agent, is put into after sealing in dry-cleaning instrument, is taken out after dry-cleaning 30min, then repeated washing is twice；
Step 3：Sample is flat in the environment of 20 ± 2 DEG C of temperature, humidity 65 ± 3%, balance is put on balance after 12 hours and weighed, claims to obtain the preceding weight of sample leaching；
Step 4：Reagent 500ml is added in beaker（Preparation of reagents method：0.5ml bleeding agents FFA is added in 499.5ml distilled water）, the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute；
Step 5：By the sample after moisture absorption, a folding is hung on airer for clothes for two along its length, the airer for clothes for hanging with sample is placed under 20 ± 2 DEG C of temperature, the environmental condition of humidity 65 ± 3%, and records the time, every measuring sample weight after 30 minutes, until sample recovers before leaching untill weight；
Step 6：The time that sample recovers weight before leaching is recorded, as fabric spontaneously dries the time.

Claims (1)

1. making and the method for testing of a kind of anti-drilling hair side material, it is characterised in that：
1）, yarn variety design：
From wool fiber, cashmere fiber and marine alga Carbon fibe, the wool fiber is formed by rabbit fur fibre, beautiful promise superfine wool, the four kinds of fiber blend braidings of Angora goat wool fibre and mercerized wool fiber, and percentage by weight shared by each composition is respectively in described blending rabbit wool fiber fabric：The rabbit fur fibre accounts for 18%-22%, the beautiful promise superfine wool accounts for 15%-19%, the Angora goat wool fibre accounts for 26%-30%, the mercerized wool fiber accounts for 29%-41%, to wool fiber, cashmere fiber and marine alga Carbon fibe carry out anti pilling processing, ferment treatment and soft treatment, anti pilling processing is used as anti pilling agent from phosphate antimony oxide mixture, phosphate antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is handled using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2）, recombing technique：
Sequentially pass through silver mixing-grilling-combing-grilling-into bar process complete recombing；
3）, spinning process：
Using generally known spinning process, the pin of pin-tri- of scalp acupuncture-bis--tetra- pins-rove-storage-spun yarn-yarn steaming-is sequentially passed through from winder-doubling-double twisting-yarn steaming process, the yarn for weaving worsted fabric is made, spinning process uses compact spinning spun yarn equipment；
4）, weaving and repair technology：
Using generally known weaving and repair technology, by yarn weaving into fabric, and fabric nonwoven defect and float are caused by repairing；
5）, postfinishing process：
Fabric by singing-open width braying-crabbing-baking-high speed braying-baking-increases depths reason-ripe and repaiies-middle inspection-bristle-cropping-tank steaming-decatizing-shrinking processes, and worsted fabric is made；
6）Test drying property：
Step one：Lead in 40cm on the sample of width and take the cm of 10 cm × 20 two pieces of sample as test sample；
Step 2：Sample is placed in washing appearance device, 300ml tetrachloro-ethylenes are added as dry cleaning agent, is put into after sealing in dry-cleaning instrument, is taken out after dry-cleaning 30min, then repeated washing is twice；
Step 3：Sample is flat in the environment of 20 ± 2 DEG C of temperature, humidity 65 ± 3%, balance is put on balance after 12 hours and weighed, claims to obtain the preceding weight of sample leaching；
Step 4：Reagent 500ml is added in beaker（Preparation of reagents method：0.5ml bleeding agents FFA is added in 499.5ml distilled water）, the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute；
Step 5：By the sample after moisture absorption, a folding is hung on airer for clothes for two along its length, the airer for clothes for hanging with sample is placed under 20 ± 2 DEG C of temperature, the environmental condition of humidity 65 ± 3%, and records the time, every measuring sample weight after 30 minutes, until sample recovers before leaching untill weight；
Step 6：The time that sample recovers weight before leaching is recorded, as fabric spontaneously dries the time.
CN201610139140.6A 2016-03-12 2016-03-12 A kind of making of anti-drilling hair side material and method of testing Pending CN107173889A (en)