CN105803631A - Drying process of stripe fabric - Google Patents
Drying process of stripe fabric Download PDFInfo
- Publication number
- CN105803631A CN105803631A CN201610144409.XA CN201610144409A CN105803631A CN 105803631 A CN105803631 A CN 105803631A CN 201610144409 A CN201610144409 A CN 201610144409A CN 105803631 A CN105803631 A CN 105803631A
- Authority
- CN
- China
- Prior art keywords
- fabric
- sample
- fiber
- wool
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a drying process of a stripe fabric. The drying process is characterized in that the stripe fabric comprises a fabric body, the surface of the fabric body is provided with a pinstripe fabric layer, the pinstripe fabric layer is connected with the fabric body with threads, coarse grain short rectangular stripe cloth is distributed on the pinstripe fabric layer, the short rectangular stripe cloth is arranged in a staggered mode in the horizontal direction and fixed to the pinstripe fabric layer with threads, the bottom face of the fabric body is provided with a villus layer, and the bottom face of the villus layer is provided with an anti-static layer. According to the drying process of the stripe fabric, the short stripe cloth protrudes out of the plane where the pinstripe fabric layer is located, the layering feeling of the stripe fabric is enhanced, the heat preservation property of the stripe fabric is enhanced through the villus layer, and meanwhile static electricity resistance is improved through the anti-static layer.
Description
Technical field
The present invention relates to the drying process of strip fabric, belong to fabric technical field.
Background technology
Traditional fabric is generally single layer structure, and function is comparatively single.In recent years along with the development of textile industry, occurring in that double-layer fabric, double-layer fabric is three dimensional structure, has solid layer feeling, and abundant degree and intensity are all relatively good, but do not possess electrostatic-proof function.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that the drying process of the good strip fabric of solid layer feeling.
The object of the present invention is achieved like this:
The technique of strip fabric is:
1), yarn variety design:
nullSelect wool fiber、Cashmere fiber and aethiops vegetabilis fiber，Described wool fiber is by rabbit fur fibre、Beautiful promise superfine wool、Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form，In described blending rabbit wool fiber fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%，Described beautiful promise superfine wool accounts for 15%-19%，Described Angora goat wool fibre accounts for 26%-30%，Described mercerized wool fiber accounts for 29%-41%，To wool fiber、Cashmere fiber and aethiops vegetabilis fiber carry out anti pilling process、Ferment treatment and soft treatment，Anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent，Phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%，Ferment treatment system uses protease to process，Protease consumption is the 0.1-0.2% of wool fiber weight，The softening agent that soft treatment is selected is water-soluble organic silicon softening agent，Water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2), recombing technique:
Sequentially pass through silver mixing grilling combing grilling slivering operation and complete recombing；
3), spinning process:
Adopting generally known spinning process, sequentially pass through scalp acupuncture two pin three pin four pin rove-deposit spun yarn yarn steaming from winder-doubling-double twisting yarn steaming operation, make the yarn for weaving worsted fabric, spinning process adopts compact spinning spun yarn equipment；
4), weaving and repair technology:
Adopt generally known weaving and repair technology, yarn weaving is become grey cloth, and is made grey cloth nonwoven defect and float by repairing；
5), postfinishing process:
Grey cloth dry through open width braying crabbing of singing-high speed braying-bakings-increase depths and manage and ripe repair middle inspection-bristle-cropping tank steaming-decatizing-shrinking processes, make worsted fabric；
6) test drying property:
Step one: take two pieces of the sample of 10cm × 20cm on the sample of the logical width of 40cm as test sample；
Step 2: be placed on by sample in washing appearance device, adds 300ml tetrachloroethylene as Dry Cleaners, is put in dry-cleaning instrument, takes out, then repeated washing twice after dry-cleaning 30min after sealing；
Step 3: sample is flat on temperature 20 ± 2 DEG C, under the environment of humidity 65 ± 3%, is put on balance and weighs after balancing 12 hours, claims to obtain the front weight of sample leaching；
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent FFA in 499.5ml distilled water), the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute；
Step 5: be two be hung on airer for clothes by the folding along its length of the sample after moisture absorption, the airer for clothes hanging with sample is placed in temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, sample weight is measured, until sample recovers the front weight of leaching after 30 minutes；
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Compared with prior art, the invention has the beneficial effects as follows:
In the drying process of strip fabric of the present invention, billet cloth protrudes the place plane of microgroove precoat, enhances the stereovision of strip fabric, and tapetum enhances the warmth retention property of strip fabric, and antistatic backing improves static electricity resistance simultaneously.
Detailed description of the invention
The present invention relates to the drying process of strip fabric, the technique of strip fabric is:
1), yarn variety design:
nullSelect wool fiber、Cashmere fiber and aethiops vegetabilis fiber，Described wool fiber is by rabbit fur fibre、Beautiful promise superfine wool、Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form，In described blending rabbit wool fiber fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%，Described beautiful promise superfine wool accounts for 15%-19%，Described Angora goat wool fibre accounts for 26%-30%，Described mercerized wool fiber accounts for 29%-41%，To wool fiber、Cashmere fiber and aethiops vegetabilis fiber carry out anti pilling process、Ferment treatment and soft treatment，Anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent，Phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%，Ferment treatment system uses protease to process，Protease consumption is the 0.1-0.2% of wool fiber weight，The softening agent that soft treatment is selected is water-soluble organic silicon softening agent，Water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2), recombing technique:
Sequentially pass through silver mixing grilling combing grilling slivering operation and complete recombing；
3), spinning process:
Adopting generally known spinning process, sequentially pass through scalp acupuncture two pin three pin four pin rove-deposit spun yarn yarn steaming from winder-doubling-double twisting yarn steaming operation, make the yarn for weaving worsted fabric, spinning process adopts compact spinning spun yarn equipment；
4), weaving and repair technology:
Adopt generally known weaving and repair technology, yarn weaving is become grey cloth, and is made grey cloth nonwoven defect and float by repairing；
5), postfinishing process:
Grey cloth dry through open width braying crabbing of singing-high speed braying-bakings-increase depths and manage and ripe repair middle inspection-bristle-cropping tank steaming-decatizing-shrinking processes, make worsted fabric；
6) test drying property:
Step one: take two pieces of the sample of 10cm × 20cm on the sample of the logical width of 40cm as test sample；
Step 2: be placed on by sample in washing appearance device, adds 300ml tetrachloroethylene as Dry Cleaners, is put in dry-cleaning instrument, takes out, then repeated washing twice after dry-cleaning 30min after sealing；
Step 3: sample is flat on temperature 20 ± 2 DEG C, under the environment of humidity 65 ± 3%, is put on balance and weighs after balancing 12 hours, claims to obtain the front weight of sample leaching；
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent FFA in 499.5ml distilled water), the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute；
Step 5: be two be hung on airer for clothes by the folding along its length of the sample after moisture absorption, the airer for clothes hanging with sample is placed in temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, sample weight is measured, until sample recovers the front weight of leaching after 30 minutes；
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Claims (1)
1. strip fabric, it is characterised in that: the technique of strip fabric is:
1), yarn variety design:
nullSelect wool fiber、Cashmere fiber and aethiops vegetabilis fiber，Described wool fiber is by rabbit fur fibre、Beautiful promise superfine wool、Angora goat wool fibre and the four kinds of fiber blend braidings of mercerized wool fiber form，In described blending rabbit wool fiber fabric, percentage by weight shared by each composition is respectively as follows: described rabbit fur fibre and accounts for 18%-22%，Described beautiful promise superfine wool accounts for 15%-19%，Described Angora goat wool fibre accounts for 26%-30%，Described mercerized wool fiber accounts for 29%-41%，To wool fiber、Cashmere fiber and aethiops vegetabilis fiber carry out anti pilling process、Ferment treatment and soft treatment，Anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent，Phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%，Ferment treatment system uses protease to process，Protease consumption is the 0.1-0.2% of wool fiber weight，The softening agent that soft treatment is selected is water-soluble organic silicon softening agent，Water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2), recombing technique:
Sequentially pass through silver mixing grilling combing grilling slivering operation and complete recombing；
3), spinning process:
Adopting generally known spinning process, sequentially pass through scalp acupuncture two pin three pin four pin rove-deposit spun yarn yarn steaming from winder-doubling-double twisting yarn steaming operation, make the yarn for weaving worsted fabric, spinning process adopts compact spinning spun yarn equipment；
4), weaving and repair technology:
Adopt generally known weaving and repair technology, yarn weaving is become grey cloth, and is made grey cloth nonwoven defect and float by repairing；
5), postfinishing process:
Grey cloth dry through open width braying crabbing of singing-high speed braying-bakings-increase depths and manage and ripe repair middle inspection-bristle-cropping tank steaming-decatizing-shrinking processes, make worsted fabric；
6) test drying property:
Step one: take two pieces of the sample of 10cm × 20cm on the sample of the logical width of 40cm as test sample；
Step 2: be placed on by sample in washing appearance device, adds 300ml tetrachloroethylene as Dry Cleaners, is put in dry-cleaning instrument, takes out, then repeated washing twice after dry-cleaning 30min after sealing；
Step 3: sample is flat on temperature 20 ± 2 DEG C, under the environment of humidity 65 ± 3%, is put on balance and weighs after balancing 12 hours, claims to obtain the front weight of sample leaching；
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent FFA in 499.5ml distilled water), the sample after dry-cleaning is placed in beaker abundant moisture absorption 1 minute；
Step 5: be two be hung on airer for clothes by the folding along its length of the sample after moisture absorption, the airer for clothes hanging with sample is placed in temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, sample weight is measured, until sample recovers the front weight of leaching after 30 minutes；
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.