CN105815899A - 一种贝壳饰品的制作方法 - Google Patents

一种贝壳饰品的制作方法 Download PDF

Info

Publication number
CN105815899A
CN105815899A CN201510928204.6A CN201510928204A CN105815899A CN 105815899 A CN105815899 A CN 105815899A CN 201510928204 A CN201510928204 A CN 201510928204A CN 105815899 A CN105815899 A CN 105815899A
Authority
CN
China
Prior art keywords
shell
layer
hydroxide solution
washing
ornament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510928204.6A
Other languages
English (en)
Inventor
郑在好
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jinxindi Jewelry Co Ltd
Original Assignee
Anhui Jinxindi Jewelry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jinxindi Jewelry Co Ltd filed Critical Anhui Jinxindi Jewelry Co Ltd
Priority to CN201510928204.6A priority Critical patent/CN105815899A/zh
Publication of CN105815899A publication Critical patent/CN105815899A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种贝壳饰品的制作方法，贝壳水洗除去残余物后，在氢氧化钠溶液、氢氧化钾溶液或稀次氯酸钠溶液中浸泡，水洗去除角质层。将已除去角质层的样品在氢氧化钠溶液或氢氧化钾溶液中浸泡，水洗去除棱柱层，得到贝壳珍珠层，将贝壳珍珠层水洗晾干后用透明胶粘黏成胚体，然后切割后镶嵌在饰品外壳上制成贝壳饰品。该方法操作简单，最大程度的保持了贝壳图案的完整性和独特性，制成的饰品价格低廉，适用于大规模推广。

Description

一种贝壳饰品的制作方法
技术领域
本发明属于贝壳饰品技术领域，具体涉及一种贝壳饰品的制作方法。
背景技术
贝壳饰品因其色彩靓丽、图案独特，价格低廉等特性受到人们的喜爱。随着社会的发展和需求，目前贝壳用于装饰、制作纽扣、制作马赛克版等。但是，一般贝壳在处理的时候，往往是打磨角质层，保留内部棱柱层和珍珠层。并且去除角质层后用压膜工具烘压成平面，对珍珠层的图案造成破坏。中国专利:申请号CN201310515195.9公开将贝壳水洗除去残余物后，在氢氧化钠溶液、氢氧化钾溶液或稀次氯酸钠溶液中浸泡，水洗去除角质层盘；将已除去角质层的样品在氢氧化钠溶液或氢氧化钾溶液中浸泡，水洗去除棱柱层，得到贝壳珍珠层的技术，但是没有解决如何保持图案完整和独特的问题。
发明内容
本发明的目的在于针对上述存在的问题和不足，提出一种操作简单、具有完整和独特图案的贝壳饰品的制作方法。
为实现上述目的，本发明采用了以下技术方案：一种贝壳饰品的制作方法，包括以下步骤：
第一步，将贝壳内外表面的灰尘和杂质清洗掉；
第二步，将清洗后的贝壳放置在50℃下于0.04mol/L的氢氧化钠溶液或氢氧化钾溶液中浸泡10～40分钟，水洗去除角质层；
第三步，将已除去角质层的贝壳放置在50℃下于3mol/L的氢氧化钠溶液或氢氧化钾溶液中浸泡30～60分钟，水洗去除棱柱层，得到贝壳珍珠层；
第四步，将贝壳珍珠层放置在50℃下于0.01mol/L的稀盐酸或醋酸溶液中浸泡1-10分钟，水洗去除杂质，晾干；
第五步，将晾干后的贝壳珍珠层用透明的胶粘剂粘贴成2-8mm的珍珠层胚体，压平；
第六步，将压平的珍珠层胚体镶嵌在饰品外壳上制作成戒指或吊坠。
以上所述胶黏剂是改性丙烯酸酯。
本发明的有益效果：利用贝壳的化学特性，用氢氧化钠溶液或氢氧化钾溶液将角质层和棱柱层去除，保持图案的完整性，将珍珠层清理干净用透明的胶粘剂粘贴成2-8mm的珍珠层胚体，此胚体因为每层珍珠层的图案不同，所以贴在一起显示的图案都是独一无二的。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述。
实施例1：
一种贝壳戒指的制作方法，包括以下步骤：
第一步，将贝壳内外表面的灰尘和杂质清洗掉；
第二步，将清洗后的贝壳放置在50℃下于0.04mol/L的氢氧化钠溶液中浸泡10分钟，水洗去除角质层；
第三步，将已除去角质层的贝壳放置在50℃下于3mol/L的氢氧化钠溶液中浸泡30分钟，水洗去除棱柱层，得到贝壳珍珠层；
第四步，将贝壳珍珠层放置在50℃下于0.01mol/L的稀盐酸中浸泡1分钟，水洗去除杂质，晾干；
第五步，将晾干后的贝壳珍珠层用透明的改性丙烯酸酯胶粘剂粘贴成2mm的珍珠层胚体，压平；
第六步，将压平的珍珠层胚体切割后镶嵌在金属环上制作成戒指。
实施例2：
一种贝壳吊坠的制作方法，包括以下步骤：
第一步，将贝壳内外表面的灰尘和杂质清洗掉；
第二步，将清洗后的贝壳放置在50℃下于0.04mol/L的氢氧化钾溶液中浸泡40分钟，水洗去除角质层；
第三步，将已除去角质层的贝壳放置在50℃下于3mol/L的氢氧化钾溶液中浸泡60分钟，水洗去除棱柱层，得到贝壳珍珠层；
第四步，将贝壳珍珠层放置在0.01mol/L的醋酸溶液中浸泡10分钟，水洗去除杂质。漂洗，晾干；
第五步，将晾干后的贝壳珍珠层用透明的胶粘剂粘贴成8mm的珍珠层胚体，压平；
第六步，将压平的珍珠层胚体镶嵌在吊坠外壳上制作成吊坠。
以上所述的实施例，只是本发明的较优选的具体方式之一，本领域的技术员在发明技术方案范围内进行的通常变化和替换都应包含在本发明的保护范围内。

Claims (2)

1.一种贝壳饰品的制作方法，包括以下步骤：
第一步，将贝壳内外表面的灰尘和杂质清洗掉；
第二步，将清洗后的贝壳放置在50℃下于0.04mol/L的氢氧化钠溶液或氢氧化钾溶液中浸泡10～40分钟，水洗去除角质层；
第三步，将已除去角质层的贝壳放置在50℃下于3mol/L的氢氧化钠溶液或氢氧化钾溶液中浸泡30～60分钟，水洗去除棱柱层，得到贝壳珍珠层；
第四步，将贝壳珍珠层放置在0.01mol/L的稀盐酸或醋酸溶液中浸泡1-10分钟，水洗去除杂质，晾干；
第五步，将晾干后的贝壳珍珠层用透明的胶粘剂粘贴成2-8mm的珍珠层胚体，压平；
第六步，将压平的珍珠层胚体镶嵌在饰品外壳上制作成戒指或吊坠。
2.权利要求1所述一种贝壳的处理方法，其特征在于:所述胶黏剂是改性丙烯酸酯。
CN201510928204.6A 2015-12-15 2015-12-15 一种贝壳饰品的制作方法 Pending CN105815899A (zh)