CN105778646A - Anti-cracking, water-proof and weather-resistant building coating - Google Patents
Anti-cracking, water-proof and weather-resistant building coating Download PDFInfo
- Publication number
- CN105778646A CN105778646A CN201610173885.4A CN201610173885A CN105778646A CN 105778646 A CN105778646 A CN 105778646A CN 201610173885 A CN201610173885 A CN 201610173885A CN 105778646 A CN105778646 A CN 105778646A
- Authority
- CN
- China
- Prior art keywords
- building coating
- parts
- waterproof
- cracking resistance
- resistant building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-cracking, water-proof and weather-resistant building coating. The components of the building coating include polyvinyl alcohol, polyacrylamide emulsion, silica sol, polyamide, quick lime, castor oil, potassium oxide, zinc oxide, aluminium oxide, polyvinyl acetate, methyl methacrylate, phenol-formaldehyde resin, ground calcium carbonate, bentonite and the like. The building coating provided by the invention has strong cohesive force, can resist cracking, and enhances the water-proof effect; the building coating can be constructed on wet or dry base planes of a variety of materials, has good waterproof property, and does not have toxicity and harm, and the long service life is long; moreover, after the coating forms a film, all the property indexes, i.e. rigidity, water resistance, alkali resistance and scrubbing resistance, are high, and furthermore, the building coating has excellent corrosion resistance as well as excellent weather resistance.
Description
Technical field
The present invention relates to a kind of construction timber material formula and preparation method thereof, be specifically related to a kind of cracking resistance, waterproof, weather resistant building coating.
Background technology
Coating; it is be coated in protected or decorated body surface; and the continuous film coating of firm attachment can be formed with coated article; because coating is exposed in air; cold and hot change, air oxidation etc. act on; the phenomenons such as coating easily ftractures, efflorescence, peeling, variable color, are that coating loses original decoration defencive function.This problem cause puzzlement all can to the resident lived, and integrates, so should develop, the elastic water-proof crack resisting coating product that decoration, anticracking, water proof lamp are multi-functional.
Building coating as a class for the coating products of house decoration, some buildings to mildew-resistant, fire prevention, insulation, corrosion-resistant etc. have particular/special requirement, waterproof, antifreeze, cracking resistance are had particular/special requirement by some buildings, have to being decorated with particular/special requirement.Livability improves function mainly for indoor application, it is simply that contribute to improving the function of living environment, such as sound-proofing, sound absorption properties, anti-condensation etc..It is applied to body surface and can form a class I liquid I of the solid-state film with protection decoration or property (such as insulation, anticorrosion, mark etc.) or the general name of solid material.Coating type is various, purposes is extremely wide.Playing an important role in national economy and people's lives, year use coating content is the important indicator of a national living standard per capita.And popularizing along with humanity concept, and the composition of novel harmonious society, the water-fast anti-crack building coating designing a kind of covering power height, fast drying, resistance to water, cracking resistance and resistance to wiping excellent is very important.
At present, human body and environment are had bigger harm by existing water-repellent paint, and, it is easy to cause aging, dry and cracked, deform, fracture, the phenomenon such as layering, for complex-shaped place, constructional difficulties, and to Seepage, difficult quality guarantee, every few years, substantial amounts of fund and labour force will be spent to reprocess so that cost constantly rises, and have impact on the service life of building.
Summary of the invention
Goal of the invention: the present invention is directed to deficiency of the prior art, it is proposed to a kind of material cohesive force is strong, cracking resistance improves waterproof effect；Can on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life；And hardness after coating film forming, resistance to water, alkali resistance and scrubbing resistance number of times performance indications are all higher, there is the antiseptic property of excellence simultaneously, there is again the cracking resistance of fabulous weather resistance, waterproof, weather resistant building coating.
Technical scheme: a kind of cracking resistance, waterproof, weather resistant building coating of the present invention, the component including following mass parts forms:
nullPolyvinyl alcohol 30-80 part，Poly-acrylic emulsion 15-30 part，Ludox 15-20 part，Polyamide 10-15 part，Quick lime 5-10 part，Oleum Ricini 20-25 part，Defoamer 5-20 part，Plasticizer 5-10 part，Potassium oxide 12-15 part，Zinc oxide 2-10 part，Aluminium sesquioxide 10-12 part，Polyvinyl acetate 30-50 part，Methyl methacrylate 15-30 part，Phenolic resin 15-25 part，Ground calcium carbonate 10-15 part，Bentonite 5-10 part，Nano silicon 1-10 part，Dispersant 1-3 part，Quick dry agent 0.2-1.5 part，Coalescents 0.3-3 part，Segregation two fluororesin 10-15 part、Acrylic resin 5-15 part、Butyl 20-30 part、Dimethylbenzene 15-20 part、Saturated terminal carboxyl polyester resin 10-20 part，Deionized water 80-100 part.
Further, described defoamer is any one or at least two combination in dimethicone, capryl alcohol or organosilicon.
Further, described plasticizer is dibutyl phthalate.
Further, described dispersant is sodium lauryl sulphate.
Further, described dispersant is sodium lauryl sulphate.
Further, described quick dry agent is propylene glycol.
Further, described coalescents is alcohol ester 12.
The preparation method that the invention also discloses above-mentioned a kind of cracking resistance, waterproof, weather resistant building coating, comprises the steps:
(1) polyvinyl alcohol is taken according to proportioning raw materials, poly-acrylic emulsion, Ludox, polyamide, quick lime, Oleum Ricini,, potassium oxide, zinc oxide, aluminium sesquioxide, polyvinyl acetate, methyl methacrylate, phenolic resin, ground calcium carbonate, bentonite is sufficiently mixed in batch mixer, pulverizes and makes uniform compound A；
(2) taking nano silicon according to proportioning raw materials, segregation two fluororesin, acrylic resin, butyl, dimethylbenzene, saturated terminal carboxyl polyester resin carry out being sufficiently mixed uniformly in batch mixer, prepare compound B；
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 24-48 hour；
(4) in foam material pond, add the deionized water of the 40-60% producing building coating weight, then pass into steam heating 13-15h, control water temperature 50-75 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A；
(5) cancelling infusion, plasticizer, dispersant, quick dry agent according to proportioning raw materials, coalescents mixes, and adds the deionized water of remaining weight, uniform in stirrer for mixing, makes uniform mixed liquid B；
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 85-90 DEG C, add additive, must not have suspended impurity, reach transparent till；
(7) gained mixture repressurization being shaped, moulding pressure is 18MPa-30MPa, and pressing time is 6-8h, places 6-18h, obtain building coating after cooling.
Beneficial effect: building coating cohesive force provided by the invention is strong, cracking resistance improves waterproof effect；Can on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life；And hardness after coating film forming, resistance to water, alkali resistance and scrubbing resistance number of times performance indications are all higher, there is the antiseptic property of excellence simultaneously, there is again fabulous weather resistance.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of cracking resistance, waterproof, weather resistant building coating, the component including following mass parts forms:
Polyvinyl alcohol 30 parts, poly-acrylic emulsion 15 parts, Ludox 15 parts, polyamide 10 parts, quick lime 5 parts, Oleum Ricini 20 parts, defoamer 5 parts, plasticizer 5 parts, potassium oxide 12 parts, zinc oxide 2 parts, aluminium sesquioxide 10 parts, polyvinyl acetate 30 parts, methyl methacrylate 15 parts, 15 parts of phenolic resin, ground calcium carbonate 10 parts, bentonite 5 parts, nano silicon 1 part, dispersant 1 part, quick dry agent 0.2 part, coalescents 0.3 part, segregation two fluororesin 10 parts, acrylic resin 5 parts, butyl 20 parts, dimethylbenzene 15 parts, saturated terminal carboxyl polyester resin 10 parts, deionized water 80 parts.
Further, described defoamer is dimethicone.
Further, described plasticizer is dibutyl phthalate.
Further, described dispersant is sodium lauryl sulphate.
Further, described dispersant is sodium lauryl sulphate.
Further, described quick dry agent is propylene glycol.
Further, described coalescents is alcohol ester 12.
The preparation method that the invention also discloses above-mentioned a kind of cracking resistance, waterproof, weather resistant building coating, comprises the steps:
(1) polyvinyl alcohol is taken according to proportioning raw materials, poly-acrylic emulsion, Ludox, polyamide, quick lime, Oleum Ricini,, potassium oxide, zinc oxide, aluminium sesquioxide, polyvinyl acetate, methyl methacrylate, phenolic resin, ground calcium carbonate, bentonite is sufficiently mixed in batch mixer, pulverizes and makes uniform compound A；
(2) taking nano silicon according to proportioning raw materials, segregation two fluororesin, acrylic resin, butyl, dimethylbenzene, saturated terminal carboxyl polyester resin carry out being sufficiently mixed uniformly in batch mixer, prepare compound B；
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 24 hours；
(4) in foam material pond, add the deionized water of to produce building coating weight 40%, then pass into steam heating 13h, control water temperature 50 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A；
(5) cancelling infusion, plasticizer, dispersant, quick dry agent according to proportioning raw materials, coalescents mixes, and adds the deionized water of remaining weight, uniform in stirrer for mixing, makes uniform mixed liquid B；
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 85 DEG C, add additive, must not have suspended impurity, reach transparent till；
(7) gained mixture repressurization being shaped, moulding pressure is 18MPa, and pressing time is 6h, places 6h, obtain building coating after cooling.
Embodiment 2
A kind of cracking resistance, waterproof, weather resistant building coating, the component including following mass parts forms:
Polyvinyl alcohol 80 parts, poly-acrylic emulsion 30 parts, Ludox 20 parts, polyamide 15 parts, quick lime 10 parts, Oleum Ricini 25 parts, defoamer 20 parts, plasticizer 10 parts, potassium oxide 15 parts, zinc oxide 10 parts, aluminium sesquioxide 12 parts, polyvinyl acetate 50 parts, methyl methacrylate 30 parts, 25 parts of phenolic resin, ground calcium carbonate 15 parts, bentonite 10 parts, nano silicon 10 parts, dispersant 3 parts, quick dry agent 1.5 parts, coalescents 3 parts, segregation two fluororesin 15 parts, acrylic resin 15 parts, butyl 30 parts, dimethylbenzene 20 parts, saturated terminal carboxyl polyester resin 20 parts, deionized water 100 parts.
Further, described defoamer is capryl alcohol.
Further, described plasticizer is dibutyl phthalate.
Further, described dispersant is sodium lauryl sulphate.
Further, described dispersant is sodium lauryl sulphate.
Further, described quick dry agent is propylene glycol.
Further, described coalescents is alcohol ester 12.
The preparation method that the invention also discloses above-mentioned a kind of cracking resistance, waterproof, weather resistant building coating, comprises the steps:
(1) polyvinyl alcohol is taken according to proportioning raw materials, poly-acrylic emulsion, Ludox, polyamide, quick lime, Oleum Ricini,, potassium oxide, zinc oxide, aluminium sesquioxide, polyvinyl acetate, methyl methacrylate, phenolic resin, ground calcium carbonate, bentonite is sufficiently mixed in batch mixer, pulverizes and makes uniform compound A；
(2) taking nano silicon according to proportioning raw materials, segregation two fluororesin, acrylic resin, butyl, dimethylbenzene, saturated terminal carboxyl polyester resin carry out being sufficiently mixed uniformly in batch mixer, prepare compound B；
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 48 hours；
(4) in foam material pond, add the deionized water of to produce building coating weight 60%, then pass into steam heating 15h, control water temperature 75 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A；
(5) cancelling infusion, plasticizer, dispersant, quick dry agent according to proportioning raw materials, coalescents mixes, and adds the deionized water of remaining weight, uniform in stirrer for mixing, makes uniform mixed liquid B；
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 90 DEG C, add additive, must not have suspended impurity, reach transparent till；
(7) gained mixture repressurization being shaped, moulding pressure is 30MPa, and pressing time is 8h, places 18h, obtain building coating after cooling.
Embodiment 3
A kind of cracking resistance, waterproof, weather resistant building coating, the component including following mass parts forms:
Polyvinyl alcohol 55 parts, poly-acrylic emulsion 20 parts, Ludox 17 parts, polyamide 12 parts, quick lime 7 parts, Oleum Ricini 22 parts, defoamer 10 parts, plasticizer 7 parts, potassium oxide 13 parts, zinc oxide 6 parts, aluminium sesquioxide 11 parts, polyvinyl acetate 40 parts, methyl methacrylate 20 parts, 17 parts of phenolic resin, ground calcium carbonate 12 parts, bentonite 7 parts, nano silicon 5 parts, dispersant 2 parts, quick dry agent 1 part, coalescents 2 parts, segregation two fluororesin 12 parts, acrylic resin 10 parts, butyl 25 parts, dimethylbenzene 17 parts, saturated terminal carboxyl polyester resin 15 parts, deionized water 90 parts.
Further, described defoamer is dimethicone, capryl alcohol two kinds combination.
Further, described plasticizer is dibutyl phthalate.
Further, described dispersant is sodium lauryl sulphate.
Further, described dispersant is sodium lauryl sulphate.
Further, described quick dry agent is propylene glycol.
Further, described coalescents is alcohol ester 12.
The preparation method that the invention also discloses above-mentioned a kind of cracking resistance, waterproof, weather resistant building coating, comprises the steps:
(1) polyvinyl alcohol is taken according to proportioning raw materials, poly-acrylic emulsion, Ludox, polyamide, quick lime, Oleum Ricini,, potassium oxide, zinc oxide, aluminium sesquioxide, polyvinyl acetate, methyl methacrylate, phenolic resin, ground calcium carbonate, bentonite is sufficiently mixed in batch mixer, pulverizes and makes uniform compound A；
(2) taking nano silicon according to proportioning raw materials, segregation two fluororesin, acrylic resin, butyl, dimethylbenzene, saturated terminal carboxyl polyester resin carry out being sufficiently mixed uniformly in batch mixer, prepare compound B；
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 36 hours；
(4) in foam material pond, add the deionized water of to produce building coating weight 50%, then pass into steam heating 14h, control water temperature 60 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A；
(5) cancelling infusion, plasticizer, dispersant, quick dry agent according to proportioning raw materials, coalescents mixes, and adds the deionized water of remaining weight, uniform in stirrer for mixing, makes uniform mixed liquid B；
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 87 DEG C, add additive, must not have suspended impurity, reach transparent till；
(7) gained mixture repressurization being shaped, moulding pressure is 24MPa, and pressing time is 7h, places 12h, obtain building coating after cooling.
Building coating cohesive force provided by the invention is strong, and cracking resistance improves waterproof effect；Can on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life；And hardness after coating film forming, resistance to water, alkali resistance and scrubbing resistance number of times performance indications are all higher, there is the antiseptic property of excellence simultaneously, there is again fabulous weather resistance.
The above, it it is only presently preferred embodiments of the present invention, not the present invention is done any pro forma restriction, although the present invention is disclosed above with preferred embodiment, but it is not limited to the present invention, any those skilled in the art, without departing within the scope of technical solution of the present invention, when the technology contents of available the disclosure above makes a little change or is modified to the Equivalent embodiments of equivalent variations, in every case it is the content without departing from technical solution of the present invention, according to any simple modification that above example is made by the technical spirit of the present invention, equivalent variations and modification, all still fall within the scope of technical solution of the present invention.
Claims (7)
1. a cracking resistance, waterproof, weather resistant building coating, it is characterised in that: include the component composition of following mass parts:
nullPolyvinyl alcohol 30-80 part，Poly-acrylic emulsion 15-30 part，Ludox 15-20 part，Polyamide 10-15 part，Quick lime 5-10 part，Oleum Ricini 20-25 part，Defoamer 5-20 part，Plasticizer 5-10 part，Potassium oxide 12-15 part，Zinc oxide 2-10 part，Aluminium sesquioxide 10-12 part，Polyvinyl acetate 30-50 part，Methyl methacrylate 15-30 part，Phenolic resin 15-25 part，Ground calcium carbonate 10-15 part，Bentonite 5-10 part，Nano silicon 1-10 part，Dispersant 1-3 part，Quick dry agent 0.2-1.5 part，Coalescents 0.3-3 part，Segregation two fluororesin 10-15 part、Acrylic resin 5-15 part、Butyl 20-30 part、Dimethylbenzene 15-20 part、Saturated terminal carboxyl polyester resin 10-20 part，Deionized water 80-100 part.
2. a kind of cracking resistance, waterproof, weather resistant building coating according to claim 1, it is characterised in that: described defoamer is any one or at least two combination in dimethicone, capryl alcohol or organosilicon.
3. a kind of cracking resistance, waterproof, weather resistant building coating according to claim 1, it is characterised in that: described plasticizer is dibutyl phthalate.
4. a kind of cracking resistance, waterproof, weather resistant building coating according to claim 1, it is characterised in that: described dispersant is sodium lauryl sulphate.
5. a kind of cracking resistance, waterproof, weather resistant building coating according to claim 1, it is characterised in that: described dispersant is sodium lauryl sulphate.
6. a kind of cracking resistance, waterproof, weather resistant building coating according to claim 1, it is characterised in that: described quick dry agent is propylene glycol.
7. a kind of cracking resistance, waterproof, weather resistant building coating according to claim 1, it is characterised in that: described coalescents is alcohol ester 12.