CN109161272A - One kind having anti-oxidant building coating of insect prevention and preparation method thereof - Google Patents
One kind having anti-oxidant building coating of insect prevention and preparation method thereof Download PDFInfo
- Publication number
- CN109161272A CN109161272A CN201811035607.8A CN201811035607A CN109161272A CN 109161272 A CN109161272 A CN 109161272A CN 201811035607 A CN201811035607 A CN 201811035607A CN 109161272 A CN109161272 A CN 109161272A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- insect
- oxidant
- building coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to have anti-oxidant building coating of insect prevention and preparation method thereof, parts by weights meter includes following components: poly- acrylic emulsion 30-60 parts, 10-20 parts of diatomite, 10-18 parts of titanium dioxide, 7-20 parts of polyamide, 5-10 parts of calcium oxide, 8-20 parts of calcium carbonate.The present invention is improved for original building coating, it is added on the basis of original paint ingredient by containing phosphorus by multiple groups, fluorine, the compound of the elements such as chlorine mixes insect-proof agent, make it have insect prevention effect, addition is by organic antibacterial agent simultaneously, one of inorganic antiseptic and natural antibacterial agent a variety of mix antibacterial agent, not only making the coating of this product has the effect of antibacterial bacteriostatic, also there is anti-oxidant and wear-resistant effect simultaneously, prevent it from being influenced by weather and the phenomenon that aging occur, the design improves building coating, not only increase the use quality and service life of building coating, it is also all improved to the environment of indoor decoration and inhabitation simultaneously.
Description
Technical field
It is specifically a kind of that there is the anti-oxidant building coating of insect prevention and its preparation side the present invention relates to building material technical field
Method.
Background technique
Paint finishing can bond very well with basis material and be formed the material of complete and tough and tensile protective film in body surface, claim
For coating, coating and paint are identical concepts, and paint is people's habit title used for a long time, just sharp always after introducing China
Used in building trade, the effect of coating may be summarized to be three aspects: protective effect, decoration function, specific function effect.It applies
The general composition of material: including film forming matter, pigments and fillers, solvent, auxiliary agent.
Chinese patent discloses a kind of anion building coating and preparation method thereof, (Authorization Notice No.
CN106147428A), which is able to solve the few defect of building materials coating anion burst size, the method for the present invention preparation
A kind of anion building materials coating anion burst size reaches 1500-5000/cm3, anion burst size within 48 hours
It greatly improves；The production technology of anion building materials coating more simplifies simultaneously,
It can be mass produced.
Chinese patent discloses a kind of constructional coatings composed and preparation method thereof, (Authorization Notice No. CN105331212A),
The patented technology has excellent performance, has both the multiple effect of heat-insulated, energy saving, resistance to ultraviolet, impact resistance and service life length, while ring
It ensures safety, it is nontoxic to human body and environment, and preparation cost is cheap, cost performance is high.
According to above-mentioned two patent documents combine ageing resistance obtained by building coating in the market, for building coating and
Insect prevention is incomplete, is easy that coating is made to breed entomogenous fungi, and for a long time using aging is easy, reduce coating uses the longevity
Life secondly, coating uses mould easy to breed for a long time, and is corroded, seriously affects the use quality and inhabitation ring of coating
The quality in border.Therefore, those skilled in the art provide a kind of with anti-oxidant building coating of insect prevention and preparation method thereof, with solution
Certainly the problems mentioned above in the background art.
Summary of the invention
The purpose of the present invention is to provide one kind to have anti-oxidant building coating of insect prevention and preparation method thereof, above-mentioned to solve
The problem of being proposed in background technique.
To achieve the above object, the invention provides the following technical scheme: a kind of have the anti-oxidant building coating of insect prevention, by weight
Amount point meter includes following components: poly- acrylic emulsion 30-60 parts, 10-20 parts of diatomite, 10-18 parts of titanium dioxide, polyamide 7-20
Part, increases 5-10 parts of calcium oxide, 8-20 parts of calcium carbonate, 10-25 parts of nano silica, 5-10 parts of bentonite, 1-5 parts of defoaming agent
Agent 1-5 parts of modeling, 1-6 parts of dispersing agent, 5-15 parts of insect-proof agent, 4-13 parts of antibacterial agent, 1-10 parts of quick dry agent and 10-25 parts of dimethylbenzene.
As a further solution of the present invention: parts by weights meter includes following components: poly- acrylic emulsion 35-50 parts, diatomite
12-18 parts, 12-16 parts of titanium dioxide, 10-16 parts of polyamide, 6-9 parts of calcium oxide, 9-17 parts of calcium carbonate, nano silica
13-24 parts, 7-9 parts of bentonite, 2-4 parts of defoaming agent, 2-4 parts of plasticizer, 1.5-4.5 parts of dispersing agent, 7-12 parts of insect-proof agent, antibacterial
5-10 parts of agent, 3-8 parts of quick dry agent and 14-20 parts of dimethylbenzene.
As further scheme of the invention: parts by weights meter includes following components: poly- acrylic emulsion 40-45 parts, diatom
13-16 parts native, 13-15 parts of titanium dioxide, 12-14 parts of polyamide, 6.5-8 parts of calcium oxide, 10-13 parts of calcium carbonate, nano-silica
17-20 parts of SiClx, 7.5-8.5 parts of bentonite, 2.5-3.5 parts of defoaming agent, 2.5-3.5 parts of plasticizer, 2-4 parts of dispersing agent, insect prevention
9-11 parts of agent, 6-9 parts of antibacterial agent, 4-7 parts of quick dry agent and 15-18 parts of dimethylbenzene.
As further scheme of the invention: parts by weights meter includes following components: 42 parts of poly- acrylic emulsion, diatomite
15 parts, 14 parts of titanium dioxide, 13 parts of polyamide, 7 parts of calcium oxide, 11 parts of calcium carbonate, 18 parts of nano silica, 8 parts of bentonite,
3 parts of defoaming agent, 3 parts of plasticizer, 3.5 parts of dispersing agent, 10 parts of insect-proof agent, 8 parts of antibacterial agent, 6 parts of quick dry agent and 16 parts of dimethylbenzene.
As further scheme of the invention: the insect-proof agent is the compound for containing the elements such as phosphorus, fluorine, chlorine by multiple groups
It mixes.
As the present invention further scheme: the antibacterial agent is by organic antibacterial agent, inorganic antiseptic and natural anti-
One of microbial inoculum a variety of mixes.
Above-mentioned one kind has anti-oxidant building coating of insect prevention and preparation method thereof, the preparation method comprises the following steps:
Step 1): a certain amount of diatomite, titanium dioxide, polyamide, calcium oxide, calcium carbonate, nanometer are weighed according to material rate
Silica and bentonite are sequentially placed into batch mixer, are uniformly mixed, and are crushed.
Step 2: sending the mixture in step 1 into batch mixer, and poly- acrylic emulsion and dimethylbenzene be added, and carries out sufficiently mixed
It closes.
Step 3): after step 2 uniformly mixing 5min, insect-proof agent and antibacterial agent are added into batch mixer, and carries out abundant
Uniformly mixing.
Step 4): it is synchronous that the deionized water for accounting for raw material heavy amount 50% is added by the resulting mixture of step 3, first clockwise
After uniform stirring 1-2h, another mistake hour hands uniform stirring 1-2h, intermediate temperature is heated to 70 DEG C, while centre is slowly added to defoam
Agent, plasticizer, dispersing agent and quick dry agent, completion to be mixed can be obtained this product.
Compared with prior art, the beneficial effects of the present invention are: the present invention is improved for original building coating,
It is added on the basis of original paint ingredient and insect-proof agent is mixed by the compound for containing the elements such as phosphorus, fluorine, chlorine by multiple groups,
Insect prevention effect is made it have, building coating is avoided to influence its service life using entomogenous fungi is bred for a long time, while being added by having
One of machine antibacterial agent, inorganic antiseptic and natural antibacterial agent or it is a variety of mix antibacterial agent, not only make the painting of this product
Material has the effect of antibacterial bacteriostatic, and energy anticorrosive mildewproof, enhances the use quality and service life of coating, and originally set
The coating of meter also has anti-oxidant and wear-resistant effect simultaneously, prevents it from being influenced by weather and the phenomenon that aging occur, this
Design improves building coating, not only increases the use quality and service life of building coating, while also to interior
Decoration and the environment of inhabitation be all improved.
Detailed description of the invention
Fig. 1 is a kind of ingredient schematic diagram with the anti-oxidant building coating of insect prevention and preparation method thereof；
Fig. 2 is a kind of flow diagram with the anti-oxidant building coating of insect prevention and preparation method thereof.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Please refer to Fig. 1~2, in the embodiment of the present invention,
Embodiment 1:
One kind having the anti-oxidant building coating of insect prevention, and parts by weights meter includes following components: poly- acrylic emulsion 30-60 parts, diatomite
10-20 parts, 10-18 parts of titanium dioxide, 7-20 parts of polyamide, 5-10 parts of calcium oxide, 8-20 parts of calcium carbonate, nano silica
10-25 parts, 5-10 parts of bentonite, 1-5 parts of defoaming agent, 1-5 parts of plasticizer, 1-6 parts of dispersing agent, 5-15 parts of insect-proof agent, antibacterial agent
4-13 parts, 1-10 parts of quick dry agent and 10-25 parts of dimethylbenzene.
Further, the insect-proof agent is to contain the compounds of the elements such as phosphorus, fluorine, chlorine by multiple groups to mix.
Further, the antibacterial agent be by one of organic antibacterial agent, inorganic antiseptic and natural antibacterial agent or
It is a variety of to mix.
Further, there is anti-oxidant building coating of insect prevention and preparation method thereof, the preparation method comprises the following steps:
Step 1): a certain amount of diatomite, titanium dioxide, polyamide, calcium oxide, calcium carbonate, nanometer are weighed according to material rate
Silica and bentonite are sequentially placed into batch mixer, are uniformly mixed, and are crushed.
Step 2: sending the mixture in step 1 into batch mixer, and poly- acrylic emulsion and dimethylbenzene be added, and carries out sufficiently mixed
It closes.
Step 3): after step 2 uniformly mixing 5min, insect-proof agent and antibacterial agent are added into batch mixer, and carries out abundant
Uniformly mixing.
Step 4): it is synchronous that the deionized water for accounting for raw material heavy amount 50% is added by the resulting mixture of step 3, first clockwise
After uniform stirring 1-2h, another mistake hour hands uniform stirring 1-2h, intermediate temperature is heated to 70 DEG C, while centre is slowly added to defoam
Agent, plasticizer, dispersing agent and quick dry agent, completion to be mixed can be obtained this product.
Embodiment 2:
One kind having the anti-oxidant building coating of insect prevention, and parts by weights meter includes following components: poly- acrylic emulsion 35-50 parts, diatomite
12-18 parts, 12-16 parts of titanium dioxide, 10-16 parts of polyamide, 6-9 parts of calcium oxide, 9-17 parts of calcium carbonate, nano silica
13-24 parts, 7-9 parts of bentonite, 2-4 parts of defoaming agent, 2-4 parts of plasticizer, 1.5-4.5 parts of dispersing agent, 7-12 parts of insect-proof agent, antibacterial
5-10 parts of agent, 3-8 parts of quick dry agent and 14-20 parts of dimethylbenzene.
Further, the insect-proof agent is to contain the compounds of the elements such as phosphorus, fluorine, chlorine by multiple groups to mix.
Further, the antibacterial agent be by one of organic antibacterial agent, inorganic antiseptic and natural antibacterial agent or
It is a variety of to mix.
Further, there is anti-oxidant building coating of insect prevention and preparation method thereof, the preparation method comprises the following steps:
Step 1): a certain amount of diatomite, titanium dioxide, polyamide, calcium oxide, calcium carbonate, nanometer are weighed according to material rate
Silica and bentonite are sequentially placed into batch mixer, are uniformly mixed, and are crushed.
Step 2: sending the mixture in step 1 into batch mixer, and poly- acrylic emulsion and dimethylbenzene be added, and carries out sufficiently mixed
It closes.
Step 3): after step 2 uniformly mixing 5min, insect-proof agent and antibacterial agent are added into batch mixer, and carries out abundant
Uniformly mixing.
Step 4): it is synchronous that the deionized water for accounting for raw material heavy amount 50% is added by the resulting mixture of step 3, first clockwise
After uniform stirring 1-2h, another mistake hour hands uniform stirring 1-2h, intermediate temperature is heated to 70 DEG C, while centre is slowly added to defoam
Agent, plasticizer, dispersing agent and quick dry agent, completion to be mixed can be obtained this product.
Embodiment 3:
One kind having the anti-oxidant building coating of insect prevention, and parts by weights meter includes following components: poly- acrylic emulsion 40-45 parts, diatomite
13-16 parts, 13-15 parts of titanium dioxide, 12-14 parts of polyamide, 6.5-8 parts of calcium oxide, 10-13 parts of calcium carbonate, nanometer titanium dioxide
17-20 parts of silicon, 7.5-8.5 parts of bentonite, 2.5-3.5 parts of defoaming agent, 2.5-3.5 parts of plasticizer, 2-4 parts of dispersing agent, insect-proof agent
9-11 parts, 6-9 parts of antibacterial agent, 4-7 parts of quick dry agent and 15-18 parts of dimethylbenzene.
Further, the insect-proof agent is to contain the compounds of the elements such as phosphorus, fluorine, chlorine by multiple groups to mix.
Further, the antibacterial agent be by one of organic antibacterial agent, inorganic antiseptic and natural antibacterial agent or
It is a variety of to mix.
Further, there is anti-oxidant building coating of insect prevention and preparation method thereof, the preparation method comprises the following steps:
Step 1): a certain amount of diatomite, titanium dioxide, polyamide, calcium oxide, calcium carbonate, nanometer are weighed according to material rate
Silica and bentonite are sequentially placed into batch mixer, are uniformly mixed, and are crushed；
Step 2: the mixture in step 1 is sent into batch mixer, and poly- acrylic emulsion and dimethylbenzene is added, is sufficiently mixed；
Step 3): after step 2 uniformly mixing 5min, insect-proof agent and antibacterial agent are added into batch mixer, and carry out full and uniform
Mixing；
Step 4): it is synchronous that the deionized water for accounting for raw material heavy amount 50% is added by the resulting mixture of step 3, it is first clockwise uniform
After stirring 1-2h, another mistake hour hands uniform stirring 1-2h, intermediate temperature is heated to 70 DEG C, at the same centre be slowly added to defoaming agent,
Plasticizer, dispersing agent and quick dry agent, completion to be mixed can be obtained this product.
Embodiment 4:
One kind having the anti-oxidant building coating of insect prevention, and parts by weights meter includes following components: 42 parts of poly- acrylic emulsion, diatomite 15
Part, 8 parts of bentonite, disappears at 14 parts of titanium dioxide, 13 parts of polyamide, 7 parts of calcium oxide, 11 parts of calcium carbonate, 18 parts of nano silica
3 parts of infusion, 3 parts of plasticizer, 3.5 parts of dispersing agent, 10 parts of insect-proof agent, 8 parts of antibacterial agent, 6 parts of quick dry agent and 16 parts of dimethylbenzene.
Further, the insect-proof agent is to contain the compounds of the elements such as phosphorus, fluorine, chlorine by multiple groups to mix.
Further, the antibacterial agent be by one of organic antibacterial agent, inorganic antiseptic and natural antibacterial agent or
It is a variety of to mix.
Further, there is anti-oxidant building coating of insect prevention and preparation method thereof, the preparation method comprises the following steps:
Step 1): a certain amount of diatomite, titanium dioxide, polyamide, calcium oxide, calcium carbonate, nanometer are weighed according to material rate
Silica and bentonite are sequentially placed into batch mixer, are uniformly mixed, and are crushed；
Step 2: the mixture in step 1 is sent into batch mixer, and poly- acrylic emulsion and dimethylbenzene is added, is sufficiently mixed；
Step 3): after step 2 uniformly mixing 5min, insect-proof agent and antibacterial agent are added into batch mixer, and carry out full and uniform
Mixing；
Step 4): it is synchronous that the deionized water for accounting for raw material heavy amount 50% is added by the resulting mixture of step 3, it is first clockwise uniform
After stirring 1-2h, another mistake hour hands uniform stirring 1-2h, intermediate temperature is heated to 70 DEG C, at the same centre be slowly added to defoaming agent,
Plasticizer, dispersing agent and quick dry agent, completion to be mixed can be obtained this product.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. one kind has the anti-oxidant building coating of insect prevention, which is characterized in that parts by weights meter includes following components: poly- acrylic emulsion
30-60 parts, 10-20 parts of diatomite, 10-18 parts of titanium dioxide, 7-20 parts of polyamide, 5-10 parts of calcium oxide, 8-20 parts of calcium carbonate,
10-25 parts of nano silica, 5-10 parts of bentonite, 1-5 parts of defoaming agent, 1-5 parts of plasticizer, 1-6 parts of dispersing agent, insect-proof agent 5-
15 parts, 4-13 parts of antibacterial agent, 1-10 parts of quick dry agent and 10-25 parts of dimethylbenzene.
2. according to claim 1 a kind of with the anti-oxidant building coating of insect prevention, which is characterized in that parts by weights meter, packet
Containing following components: poly- acrylic emulsion 35-50 parts, 12-18 parts of diatomite, 12-16 parts of titanium dioxide, 10-16 parts of polyamide, calcium oxide
6-9 parts, 9-17 parts of calcium carbonate, 13-24 parts of nano silica, 7-9 parts of bentonite, 2-4 parts of defoaming agent, 2-4 parts of plasticizer, point
1.5-4.5 parts of powder, 7-12 parts of insect-proof agent, 5-10 parts of antibacterial agent, 3-8 parts of quick dry agent and 14-20 parts of dimethylbenzene.
3. according to claim 1 a kind of with the anti-oxidant building coating of insect prevention, which is characterized in that parts by weights meter, packet
Containing following components: poly- acrylic emulsion 40-45 parts, 13-16 parts of diatomite, 13-15 parts of titanium dioxide, 12-14 parts of polyamide, calcium oxide
6.5-8 parts, 10-13 parts of calcium carbonate, 17-20 parts of nano silica, 7.5-8.5 parts of bentonite, 2.5-3.5 parts of defoaming agent, increasing
Agent 2.5-3.5 parts of modeling, 2-4 parts of dispersing agent, 9-11 parts of insect-proof agent, 6-9 parts of antibacterial agent, 4-7 parts of quick dry agent and dimethylbenzene 15-18
Part.
4. according to claim 1 a kind of with the anti-oxidant building coating of insect prevention, which is characterized in that parts by weights meter, packet
Containing following components: 42 parts of poly- acrylic emulsion, 15 parts of diatomite, 14 parts of titanium dioxide, 13 parts of polyamide, 7 parts of calcium oxide, calcium carbonate 11
Part, 18 parts of nano silica, 8 parts of bentonite, 3 parts of defoaming agent, 3 parts of plasticizer, 3.5 parts of dispersing agent, 10 parts of insect-proof agent, antibacterial
8 parts of agent, 6 parts of quick dry agent and 16 parts of dimethylbenzene.
A kind of there is the anti-oxidant building coating of insect prevention 5. according to claim 1, which is characterized in that the insect-proof agent be by
The compound that multiple groups contain the elements such as phosphorus, fluorine, chlorine mixes.
A kind of there is the anti-oxidant building coating of insect prevention 6. according to claim 1, which is characterized in that the antibacterial agent be by
One of organic antibacterial agent, inorganic antiseptic and natural antibacterial agent a variety of mix.
7. according to claim 1 a kind of with anti-oxidant building coating of insect prevention and preparation method thereof, which is characterized in that system
Preparation Method are as follows:
Step 1): a certain amount of diatomite, titanium dioxide, polyamide, calcium oxide, calcium carbonate, nanometer are weighed according to material rate
Silica and bentonite are sequentially placed into batch mixer, are uniformly mixed, and are crushed；
Step 2: the mixture in step 1 is sent into batch mixer, and poly- acrylic emulsion and dimethylbenzene is added, is sufficiently mixed；
Step 3): after step 2 uniformly mixing 5min, insect-proof agent and antibacterial agent are added into batch mixer, and carry out full and uniform
Mixing；
Step 4): it is synchronous that the deionized water for accounting for raw material heavy amount 50% is added by the resulting mixture of step 3, it is first clockwise uniform
After stirring 1-2h, another mistake hour hands uniform stirring 1-2h, intermediate temperature is heated to 70 DEG C, at the same centre be slowly added to defoaming agent,
Plasticizer, dispersing agent and quick dry agent, completion to be mixed can be obtained this product.