CN105776847A - Pigment for lampwork and calligraphy colored glaze and application method thereof - Google Patents
Pigment for lampwork and calligraphy colored glaze and application method thereof Download PDFInfo
- Publication number
- CN105776847A CN105776847A CN201610070183.3A CN201610070183A CN105776847A CN 105776847 A CN105776847 A CN 105776847A CN 201610070183 A CN201610070183 A CN 201610070183A CN 105776847 A CN105776847 A CN 105776847A
- Authority
- CN
- China
- Prior art keywords
- parts
- calligraphy
- component
- pigment
- carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a pigment for lampwork and calligraphy colored glaze and an application method thereof and belongs to the technical field of pigments for the colored glaze.The pigment for the lampwork and calligraphy colored glaze is prepared from, by mass, a component A including alkali powder, quartz sand, borax, calcite, porcelain clay and carbonate, a component B including potassium permanganate, alkali powder, quartz sand, borax, sodium nitrate, porcelain clay, sodium fluosilicate, antimony oxide and carbonate, and a component C including quartz sand, borax, sodium nitrate, porcelain clay, sodium fluosilicate and carbonate.The pigment for the lampwork and calligraphy colored glaze is special in material, writing is smooth when the pigment is used for preparing the lampwork and calligraphy colored glaze, and the prepared colored glaze is good in visual effect.The invention further provides the simple and convenient application method.Calligraphy is introduced in the thermal forming process, and the calligraphy technique and the lampwork technique are organically fused.
Description
Technical field
The present invention relates to a kind of pigment for lamp work calligraphy coloured glaze and application process thereof, belong to coloured glaze pigment technology field.
Background technology
In coloured glaze product, lamp work coloured glaze is the class product through lamp work processes.Lamp work technique is with motley Glass rod for main material, oxygen is used to heat (bocca temperature is about 400 DEG C～800 DEG C) with liquefied gas to Glass rod, making the bar fast melt after heating, the overall process then being carried out each money product moulding by operative employee by other small tool such as pliers, blade operates.
On the product that the elite final body of lamp work technique prepares now traditionally, and being embodied on word, and effectively use table, introduce calligraphy in thermoforming process, the technique organically blent by calligraphy skill and lamp work skill was not reported.It addition, the pigment being used for writing is required that comparison is high, it is necessary to pigment material is unique, needs good fusion between each pigment bar.
Summary of the invention
It is an object of the invention to provide a kind of pigment for lamp work calligraphy coloured glaze, its material is unique, and fluent writing when preparing lamp work calligraphy coloured glaze with it, the coloured glaze visual effect of preparation is good；Present invention also offers a kind of simple and convenient application process, it introduces calligraphy in thermoforming process simultaneously, calligraphy skill and lamp work skill is organically blent.
The described pigment for lamp work calligraphy coloured glaze, is made up of the raw material of following mass fraction respectively:
(1) component A: 30-45 part ground caustic, 110-115 part quartz sand, 1-3 part borax, 10-15 part calcite, 2-3 part china clay, 14-16 part carbonate；
(2) B component: 15-18 part potassium permanganate, 30-40 part ground caustic, 115-118 part quartz sand, 1-3 part borax, 4-6 part sodium nitrate, 0.5-1.5 part china clay, 0.5-1.5 part prodan, 1.0-1.5 part stibium oxide, 10-15 part carbonate；
(3) component C: 115-118 part quartz sand, 1-3 part borax, 4-6 part sodium nitrate, 1-2 part china clay, 0.5-1 part prodan, 10-13 part carbonate.
Preferably, it is made up of the raw material of following mass fraction:
(1) component A: 40 parts of ground caustics, 113 parts of quartz sands, 2 parts of boraxs, 12 parts of calcites, 3 parts of china clay, 15.2 parts of carbonate；
(2) B component: 16 parts of potassium permanganate, 40 parts of ground caustics, 117 parts of quartz sands, 2 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 1.2 parts of stibium oxide, 12 parts of carbonate；
(3) component C: 117 parts of quartz sands, 2 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 12 parts of carbonate.
The application process of the described pigment for lamp work calligraphy coloured glaze, comprises the following steps:
(1) being mixed by the raw material in A, B and component C respectively, then melt 15-20 hour at 1280-1450 DEG C, then feeding tie rod is standby, is respectively prepared yellow quartz color, black and crystal；
(2) after product basic forming, heat head by movable type and the bar shaped pigment of gained in product regional area and step (1) is heated, add calligraphy skill and write.
Compared with prior art, the method have the advantages that
(1) the pigment material for lamp work calligraphy coloured glaze described in is unique, fluent writing when preparing lamp work calligraphy coloured glaze with it, the coloured glaze visual effect of preparation is good, forms exclusive calligraphy colored glaze art, not only embodies China's calligraphy skill of extensive knowledge and profound scholarship but also can embody the cultural end that China is deep；
(2) application process of the pigment for lamp work calligraphy coloured glaze described in, simple and convenient, there is good economic benefit.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated, but it is not limiting as the enforcement of the present invention.
Embodiment 1
The described pigment for lamp work calligraphy coloured glaze, is made up of the raw material of following mass fraction respectively:
(1) component A: 40 parts of ground caustics, 113 parts of quartz sands, 2 parts of boraxs, 12 parts of calcites, 3 parts of china clay, 15.2 parts of carbonate；
(2) B component: 16 parts of potassium permanganate, 40 parts of ground caustics, 117 parts of quartz sands, 2 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 1.2 parts of stibium oxide, 12 parts of carbonate；
(3) component C: 117 parts of quartz sands, 2 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 12 parts of carbonate.
The application process of the described pigment for lamp work calligraphy coloured glaze, comprises the following steps:
(1) being mixed by the raw material in A, B and component C respectively, then melt 15 hours at 1280 DEG C, then feeding tie rod is standby, is respectively prepared yellow quartz color, black and crystal；
(2) after product basic forming, heat head by movable type and the bar shaped pigment of gained in product regional area and step (1) is heated, add calligraphy skill and write.
Embodiment 2
The described pigment for lamp work calligraphy coloured glaze, is made up of the raw material of following mass fraction respectively:
(1) component A: 30 parts of ground caustics, 110 parts of quartz sands, 3 parts of boraxs, 15 parts of calcites, 3 parts of china clay, 14 parts of carbonate；
(2) B component: 15 parts of potassium permanganate, 40 parts of ground caustics, 115 parts of quartz sands, 1 part of borax, 6 parts of sodium nitrates, 0.5 part of china clay, 0.5 part of prodan, 0.5 part of stibium oxide, 15 parts of carbonate；
(3) component C: 118 parts of quartz sands, 3 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 13 parts of carbonate.
The application process of the described pigment for lamp work calligraphy coloured glaze, comprises the following steps:
(1) being mixed by the raw material in A, B and component C respectively, then melt 20 hours at 1450 DEG C, then feeding tie rod is standby, is respectively prepared yellow quartz color, black and crystal；
(2) after product basic forming, heat head by movable type and the bar shaped pigment of gained in product regional area and step (1) is heated, add calligraphy skill and write.
Embodiment 3
The described pigment for lamp work calligraphy coloured glaze, is made up of the raw material of following mass fraction respectively:
(1) component A: 45 parts of ground caustics, 115 parts of quartz sands, 1 part of borax, 10 parts of calcites, 2 parts of china clay, 16 parts of carbonate；
(2) B component: 18 parts of potassium permanganate, 30 parts of ground caustics, 118 parts of quartz sands, 3 parts of boraxs, 4 parts of sodium nitrates, 1 part of china clay, 1.5 parts of prodans, 1.5 parts of stibium oxide, 10 parts of carbonate；
(3) component C: 115 parts of quartz sands, 1 part of borax, 4 parts of sodium nitrates, 2 parts of china clay, 1 part of prodan, 10 parts of carbonate.
The application process of the described pigment for lamp work calligraphy coloured glaze, comprises the following steps:
(1) being mixed by the raw material in A, B and component C respectively, then melt 18 hours at 1400 DEG C, then feeding tie rod is standby, is respectively prepared yellow quartz color, black and crystal；
(2) after product basic forming, heat head by movable type and the bar shaped pigment of gained in product regional area and step (1) is heated, add calligraphy skill and write.
Claims (3)
1. the pigment for lamp work calligraphy coloured glaze, it is characterised in that be made up of the raw material of following mass fraction respectively:
(1) component A: 30-45 part ground caustic, 110-115 part quartz sand, 1-3 part borax, 10-15 part calcite, 2-3 part china clay, 14-16 part carbonate；
(2) B component: 15-18 part potassium permanganate, 30-40 part ground caustic, 115-118 part quartz sand, 1-3 part borax, 4-6 part sodium nitrate, 0.5-1.5 part china clay, 0.5-1.5 part prodan, 1.0-1.5 part stibium oxide, 10-15 part carbonate；
(3) component C: 115-118 part quartz sand, 1-3 part borax, 4-6 part sodium nitrate, 1-2 part china clay, 0.5-1 part prodan, 10-13 part carbonate.
2. the pigment for lamp work calligraphy coloured glaze according to claim 1, it is characterised in that be made up of the raw material of following mass fraction:
(1) component A: 40 parts of ground caustics, 113 parts of quartz sands, 2 parts of boraxs, 12 parts of calcites, 3 parts of china clay, 15.2 parts of carbonate；
(2) B component: 16 parts of potassium permanganate, 40 parts of ground caustics, 117 parts of quartz sands, 2 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 1.2 parts of stibium oxide, 12 parts of carbonate；
(3) component C: 117 parts of quartz sands, 2 parts of boraxs, 6 parts of sodium nitrates, 1 part of china clay, 0.5 part of prodan, 12 parts of carbonate.
3. the application process of the pigment for lamp work calligraphy coloured glaze described in a claim 1, it is characterised in that comprise the following steps:
(1) being mixed by the raw material in A, B and component C respectively, then melt 15-20 hour at 1280-1450 DEG C, then feeding tie rod is standby, is respectively prepared yellow quartz color, black and crystal；
(2) after product basic forming, heat head by movable type and the bar shaped pigment of gained in product regional area and step (1) is heated, add calligraphy skill and write.