CN105774060A - 防静电蕾丝面料 - Google Patents

防静电蕾丝面料 Download PDF

Info

Publication number
CN105774060A
CN105774060A CN201610129644.XA CN201610129644A CN105774060A CN 105774060 A CN105774060 A CN 105774060A CN 201610129644 A CN201610129644 A CN 201610129644A CN 105774060 A CN105774060 A CN 105774060A
Authority
CN
China
Prior art keywords
fabric
fiber
wool
yarn
static
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610129644.XA
Other languages
English (en)
Inventor
钟俊杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Xiangfei Fashion Co Ltd
Original Assignee
Jiangyin Xiangfei Fashion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Xiangfei Fashion Co Ltd filed Critical Jiangyin Xiangfei Fashion Co Ltd
Priority to CN201610129644.XA priority Critical patent/CN105774060A/zh
Publication of CN105774060A publication Critical patent/CN105774060A/zh
Pending legal-status Critical Current

Abstract

本发明涉及防静电蕾丝面料，其特征在于：包括面料本体，所述面料本体表面设有细纹面料层，细纹面料层与面料本体用线连接，所述细纹面料层上分布粗纹长方形短条布，所述短条布在水平方向上交错排列，并用线固定在细纹面料层上，所述面料本体的底面设有绒毛层，绒毛层底面设有防静电层。本发明防静电蕾丝面料中短条布凸出细纹面料层的所在平面，增强了条纹面料的层次感，绒毛层增强了条纹面料的保暖性，同时防静电层提高了防静电性。

Description

防静电蕾丝面料
技术领域
本发明涉及防静电蕾丝面料，属于面料技术领域。
背景技术
传统的面料通常为单层结构，功能较为单一。近几年随着纺织工业的发展，出现了双层面料，双层面料为三维结构，具有立体层次感，厚实度和强度都比较好，但不具备防静电功能。
发明内容
本发明的目的在于克服上述不足，提供立体层次感较好的防静电蕾丝面料。
本发明的目的是这样实现的：
防静电蕾丝面料，包括若干面料块，面料块与面料块之间通过纺丝线连接，其中每个面料块由径线和纬线交织混纺而成，所述径线为粘胶纤维，纤度为126~185dtex，经密度为34.2~38.5根/cm，所述纬线为铜氨纤维，纤度为112~228dtex，经密度为29.8~43.8根/cm，所述面料块上覆盖有蕾丝层，所述面料块的底面设有绒毛层，绒毛层底面设有防静电层，所述防静电层上开设有下层气孔，所述细纹面料层上开设有上层气孔；
防静电蕾丝面料的制作工艺为：
1）、纱线品种设计：
选用羊毛纤维、羊绒纤维和海藻炭纤维，所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成，所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为：所述兔毛纤维占18%-22%，所述美丽诺超细羊毛纤维占15%-19%，所述安哥拉山羊毛纤维占26%-30%，所述丝光羊毛纤维占29%-41%，对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理，抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂，磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4％，酶处理系使用蛋白酶进行处理，蛋白酶用量为羊毛纤维重量的0.1-0.2％，柔软处理选用的柔软剂为水溶性有机硅柔软剂，水溶性有机硅柔软剂用量为羊毛纤维重量的6-8％；
2）、复精梳工艺：
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳；
3）、纺纱工艺：
采用一般公知的纺纱工艺，依次经过头针—二针—三针—四针—粗纱－存放—细纱—蒸纱—自络筒－并线－倍捻—蒸纱工序，制成用于织造精纺面料的纱线，细纱工序采用紧密纺细纱设备；
4）、织造和修补工艺：
采用一般公知的织造和修补工艺，将纱线织造成坯布，并通过修补使得坯布无纺疵和织疵；
5）、后整理工艺：
坯布经过烧毛—平幅洗呢—煮呢—烘呢－高速洗呢－烘呢－增深处理—熟修—中检－刷毛－剪毛—罐蒸－蒸呢－预缩工序，制成精纺面料。
与现有技术相比，本发明的有益效果是：
本发明防静电蕾丝面料中短条布凸出细纹面料层的所在平面，增强了条纹面料的层次感，绒毛层增强了条纹面料的保暖性，同时防静电层提高了防静电性。
具体实施方式
本发明涉及防静电蕾丝面料，包括面料本体，所述面料本体表面设有细纹面料层，细纹面料层与面料本体用线连接，所述细纹面料层上分布粗纹长方形短条布，所述短条布在水平方向上交错排列，并用线固定在细纹面料层上，所述面料本体的底面设有绒毛层，绒毛层底面设有防静电层，所述防静电层上开设有下层气孔，所述细纹面料层上开设有上层气孔。
制作防静电蕾丝面料的工艺方法为：
1）、纱线品种设计：
选用羊毛纤维、羊绒纤维和海藻炭纤维，所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成，所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为：所述兔毛纤维占18%-22%，所述美丽诺超细羊毛纤维占15%-19%，所述安哥拉山羊毛纤维占26%-30%，所述丝光羊毛纤维占29%-41%，对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理，抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂，磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4％，酶处理系使用蛋白酶进行处理，蛋白酶用量为羊毛纤维重量的0.1-0.2％，柔软处理选用的柔软剂为水溶性有机硅柔软剂，水溶性有机硅柔软剂用量为羊毛纤维重量的6-8％；
2）、复精梳工艺：
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳；
3）、纺纱工艺：
采用一般公知的纺纱工艺，依次经过头针—二针—三针—四针—粗纱－存放—细纱—蒸纱—自络筒－并线－倍捻—蒸纱工序，制成用于织造精纺面料的纱线，细纱工序采用紧密纺细纱设备；
4）、织造和修补工艺：
采用一般公知的织造和修补工艺，将纱线织造成坯布，并通过修补使得坯布无纺疵和织疵；
5）、后整理工艺：
坯布经过烧毛—平幅洗呢—煮呢—烘呢－高速洗呢－烘呢－增深处理—熟修—中检－刷毛－剪毛—罐蒸－蒸呢－预缩工序，制成精纺面料。

Claims (1)

1.防静电蕾丝面料，其特征在于：包括若干面料块，面料块与面料块之间通过纺丝线连接，其中每个面料块由径线和纬线交织混纺而成，所述径线为粘胶纤维，纤度为126~185dtex，经密度为34.2~38.5根/cm，所述纬线为铜氨纤维，纤度为112~228dtex，经密度为29.8~43.8根/cm，所述面料块上覆盖有蕾丝层，所述面料块的底面设有绒毛层，绒毛层底面设有防静电层，所述防静电层上开设有下层气孔，所述细纹面料层上开设有上层气孔；
防静电蕾丝面料的工艺方法为：
1）、纱线品种设计：
选用羊毛纤维、羊绒纤维和海藻炭纤维，所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成，所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为：所述兔毛纤维占18%-22%，所述美丽诺超细羊毛纤维占15%-19%，所述安哥拉山羊毛纤维占26%-30%，所述丝光羊毛纤维占29%-41%，对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理，抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂，磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4％，酶处理系使用蛋白酶进行处理，蛋白酶用量为羊毛纤维重量的0.1-0.2％，柔软处理选用的柔软剂为水溶性有机硅柔软剂，水溶性有机硅柔软剂用量为羊毛纤维重量的6-8％；
2）、复精梳工艺：
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳；
3）、纺纱工艺：
采用一般公知的纺纱工艺，依次经过头针—二针—三针—四针—粗纱－存放—细纱—蒸纱—自络筒－并线－倍捻—蒸纱工序，制成用于织造精纺面料的纱线，细纱工序采用紧密纺细纱设备；
4）、织造和修补工艺：
采用一般公知的织造和修补工艺，将纱线织造成坯布，并通过修补使得坯布无纺疵和织疵；
5）、后整理工艺：
坯布经过烧毛—平幅洗呢—煮呢—烘呢－高速洗呢－烘呢－增深处理—熟修—中检－刷毛－剪毛—罐蒸－蒸呢－预缩工序，制成精纺面料。
CN201610129644.XA 2016-03-09 2016-03-09 防静电蕾丝面料 Pending CN105774060A (zh)