CN105799241A - 环保型蕾丝面料 - Google Patents
环保型蕾丝面料 Download PDFInfo
- Publication number
- CN105799241A CN105799241A CN201610143857.8A CN201610143857A CN105799241A CN 105799241 A CN105799241 A CN 105799241A CN 201610143857 A CN201610143857 A CN 201610143857A CN 105799241 A CN105799241 A CN 105799241A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- wool
- fabric layer
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及环保型蕾丝面料,其特征在于:包括第一面料层、第二面料层和第三面料层,第二面料层位于第一面料层和第三面料层之间,第二面料层的两侧设有截面呈正三角形的凸起,第一面料层朝向第二面料层的一侧设有截面呈正三角形的第一凹槽,第三面料层朝向第二面料层的一侧设有截面呈正三角形的第二凹槽,第二面料层的凸起分别与第一面料层的第一凹槽和第三面料层的第二凹槽相配合,所述第一面料层上开设有下层气孔,所述第三面料层上开设有上层气孔。环保型蕾丝面料具有良好的咬合性能,没有使用任何化学粘接剂,环保性强,质地柔软,穿着舒适。
Description
技术领域
本发明涉及环保型蕾丝面料,属于面料技术领域。
背景技术
随着人类生活水平的提高,人们对制成衣物的面料的性能要求也越来越高。人们的首要要求就是衣料的环保性,希望衣料尽量少用或者不用污染高的化学物质,例如化学粘接剂。目前,市场上的多层面料大部分是采用化学粘接剂进行粘接。这样,衣服的环保性能就不高。新衣服往往需要晾晒很久,才能穿着。这势必影响人们对衣物的正常使用。因此,人们希望制成衣服的面料尽可能少用化学粘接剂,提高衣服的环保性能。
发明内容
本发明的目的在于克服上述不足,提供不采用化学粘接剂,环保性能高的环保型蕾丝面料。
本发明的目的是这样实现的:
环保型蕾丝面料,面料层与面料层之间通过纺丝线连接,其中每个面料层由径线和纬线交织混纺而成,所述径线为粘胶纤维,所述每个面料层上覆盖有蕾丝层;
该面料的制作方法为:
1)、纱线品种设计:
选用羊毛纤维、羊绒纤维和海藻炭纤维,所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成,所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为:所述兔毛纤维占18%-22%,所述美丽诺超细羊毛纤维占15%-19%,所述安哥拉山羊毛纤维占26%-30%,所述丝光羊毛纤维占29%-41%,对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳;
3)、纺纱工艺:
采用一般公知的纺纱工艺,依次经过头针—二针—三针—四针—粗纱-存放—细纱—蒸纱—自络筒-并线-倍捻—蒸纱工序,制成用于织造精纺面料的纱线,细纱工序采用紧密纺细纱设备;
4)、织造和修补工艺:
采用一般公知的织造和修补工艺,将纱线织造成坯布,并通过修补使得坯布无纺疵和织疵;
5)、后整理工艺:
坯布经过烧毛—平幅洗呢—煮呢—烘呢-高速洗呢-烘呢-增深处理—熟修—中检-刷毛-剪毛—罐蒸-蒸呢-预缩工序,制成精纺面料。
与现有技术相比,本发明的有益效果是:
本发明环保型蕾丝面料具有良好的咬合性能,整个过程中没有使用任何化学粘接剂,提高了面料的环保性,质地柔软,穿着舒适。
具体实施方式
本发明涉及环保型蕾丝面料,面料层与面料层之间通过纺丝线连接,其中每个面料层由径线和纬线交织混纺而成,所述径线为粘胶纤维,所述每个面料层上覆盖有蕾丝层;
该面料的制作方法为:
1)、纱线品种设计:
选用羊毛纤维、羊绒纤维和海藻炭纤维,所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成,所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为:所述兔毛纤维占18%-22%,所述美丽诺超细羊毛纤维占15%-19%,所述安哥拉山羊毛纤维占26%-30%,所述丝光羊毛纤维占29%-41%,对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳;
3)、纺纱工艺:
采用一般公知的纺纱工艺,依次经过头针—二针—三针—四针—粗纱-存放—细纱—蒸纱—自络筒-并线-倍捻—蒸纱工序,制成用于织造精纺面料的纱线,细纱工序采用紧密纺细纱设备;
4)、织造和修补工艺:
采用一般公知的织造和修补工艺,将纱线织造成坯布,并通过修补使得坯布无纺疵和织疵;
5)、后整理工艺:
坯布经过烧毛—平幅洗呢—煮呢—烘呢-高速洗呢-烘呢-增深处理—熟修—中检-刷毛-剪毛—罐蒸-蒸呢-预缩工序,制成精纺面料。
Claims (1)
1.环保型蕾丝面料,其特征在于:面料层与面料层之间通过纺丝线连接,其中每个面料层由径线和纬线交织混纺而成,所述径线为粘胶纤维,所述每个面料层上覆盖有蕾丝层;
该面料的制作方法为:
1)、纱线品种设计:
选用羊毛纤维、羊绒纤维和海藻炭纤维,所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成,所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为:所述兔毛纤维占18%-22%,所述美丽诺超细羊毛纤维占15%-19%,所述安哥拉山羊毛纤维占26%-30%,所述丝光羊毛纤维占29%-41%,对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳;
3)、纺纱工艺:
采用一般公知的纺纱工艺,依次经过头针—二针—三针—四针—粗纱-存放—细纱—蒸纱—自络筒-并线-倍捻—蒸纱工序,制成用于织造精纺面料的纱线,细纱工序采用紧密纺细纱设备;
4)、织造和修补工艺:
采用一般公知的织造和修补工艺,将纱线织造成坯布,并通过修补使得坯布无纺疵和织疵;
5)、后整理工艺:
坯布经过烧毛—平幅洗呢—煮呢—烘呢-高速洗呢-烘呢-增深处理—熟修—中检-刷毛-剪毛—罐蒸-蒸呢-预缩工序,制成精纺面料。