CN105714553A - 一种吸波无纺布的制备方法 - Google Patents

一种吸波无纺布的制备方法 Download PDF

Info

Publication number
CN105714553A
CN105714553A CN201510595810.0A CN201510595810A CN105714553A CN 105714553 A CN105714553 A CN 105714553A CN 201510595810 A CN201510595810 A CN 201510595810A CN 105714553 A CN105714553 A CN 105714553A
Authority
CN
China
Prior art keywords
woven fabrics
wave
preparation
absorbing
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510595810.0A
Other languages
English (en)
Inventor
吕绪林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yilin Plastic Industry Co Ltd
Original Assignee
Anhui Yilin Plastic Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yilin Plastic Industry Co Ltd filed Critical Anhui Yilin Plastic Industry Co Ltd
Priority to CN201510595810.0A priority Critical patent/CN105714553A/zh
Publication of CN105714553A publication Critical patent/CN105714553A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种吸波无纺布的制备方法，吸波无纺布的制备方法包括以下步骤：（1）制备无纺布吸波涂液：丙酮作溶剂，加适量分散剂OP将不同比例的乙炔炭黑吸波剂分散均匀，经超声处理，或用研磨机研磨后,加入水性粘结剂中制得吸波涂料；（2）无纺布经去离子水浸泡1h处理以除去表面可能残留的胶浆类物质,将吸波涂料调整至适当粘度,均匀刷涂于无纺布上，室温固化，即得无纺布织物涂层吸波材料。本发明的吸波无纺布相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富。

Description

一种吸波无纺布的制备方法
技术领域
本发明涉及一种吸波无纺布的制备方法，属于新型无纺布材料技术领域。
背景技术
随着对雷达吸波材料实际应用需求的提高,采用单一吸波剂和单层吸波涂层远不能满足薄、轻、宽、强的要求。因此,设计和制备具有多元复合吸波剂和多层结构的吸波材料成为研究的重点。织物材料具有面密度低、柔韧性好、加工方便、价格低廉等优点,因此,织物涂层吸波材料与传统铝板上的涂层吸波材料相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富。同时,若将织物的网眼孔隙结构直接用于吸波材料的结构设计,可改变电磁波进入材料内部后的传播路线,使入射电磁波在吸波材料内部通过一系列的散射反射吸收过程得到最大损耗,因此织物涂层吸波材料有望发展为一种新型的吸波材料。
本发明的吸波无纺布相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富，因此本发明的是很有必要的。
发明内容
本发明目的是补充现有技术，而提供一种吸波无纺布的制备方法。
为了实现上述目的，本发明的技术方案如下：
一种吸波无纺布的制备方法，其特征在于，制备方法包括以下步骤：（1）制备无纺布吸波涂液：丙酮作溶剂，加适量分散剂将不同比例的乙炔炭黑吸波剂分散均匀，经超声处理10-20min，或用研磨机研磨2-3次后,加入水性粘结剂中制得吸波涂料；（2）无纺布经80-100℃去离子水浸泡1h前处理以除去表面可能残留的胶浆类物质,将吸波涂料调整至适当粘度,均匀刷涂于无纺布上，室温固化，即得无纺布织物涂层吸波材料。
所述分散剂为OP-10。
所述水性粘结剂为羧甲基纤维素钠。
本发明的有益效果如下：
本发明的吸波无纺布相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1：
本实施例中，一种吸波无纺布的制备方法，其特征在于，制备方法包括以下步骤：（1）制备无纺布吸波涂液：丙酮作溶剂，加适量分散剂将不同比例的乙炔炭黑吸波剂分散均匀，经超声处理15min后,加入水性粘结剂中制得吸波涂料；（2）无纺布经90℃去离子水浸泡1h前处理以除去表面可能残留的胶浆类物质,将吸波涂料调整至适当粘度,均匀刷涂于无纺布上，室温固化，即得无纺布织物涂层吸波材料。
所述分散剂为OP-10。
所述水性粘结剂为羧甲基纤维素钠。
本发明的吸波无纺布相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富。
实施例2：
本实施例中，一种吸波无纺布的制备方法，其特征在于，制备方法包括以下步骤：（1）制备无纺布吸波涂液：丙酮作溶剂，加适量分散剂将不同比例的乙炔炭黑吸波剂分散均匀，经超声处理20min后,加入水性粘结剂中制得吸波涂料；（2）无纺布经100℃去离子水浸泡1h前处理以除去表面可能残留的胶浆类物质,将吸波涂料调整至适当粘度,均匀刷涂于无纺布上，室温固化，即得无纺布织物涂层吸波材料。
所述分散剂为OP-10。
所述水性粘结剂为羧甲基纤维素钠。
本发明的吸波无纺布相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富。
实施例3：
本实施例中，一种吸波无纺布的制备方法，其特征在于，制备方法包括以下步骤：（1）制备无纺布吸波涂液：丙酮作溶剂，加适量分散剂将不同比例的乙炔炭黑吸波剂分散均匀，用研磨机研磨3次后,加入水性粘结剂中制得吸波涂料；（2）无纺布经100℃去离子水浸泡1h前处理以除去表面可能残留的胶浆类物质,将吸波涂料调整至适当粘度,均匀刷涂于无纺布上，室温固化，即得无纺布织物涂层吸波材料。
所述分散剂为OP-10。
所述水性粘结剂为羧甲基纤维素钠。
本发明的吸波无纺布相比密度较低、可直接覆盖于各种外形复杂的装备表面,易于按照要求加工成型,原料丰富。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种吸波无纺布的制备方法，其特征在于，制备方法包括以下步骤：（1）制备无纺布吸波涂液：丙酮作溶剂，加适量分散剂将不同比例的乙炔炭黑吸波剂分散均匀，经超声处理10-20min，或用研磨机研磨2-3次后,加入水性粘结剂中制得吸波涂料；（2）无纺布经80-100℃去离子水浸泡1h前处理以除去表面可能残留的胶浆类物质,将吸波涂料调整至适当粘度,均匀刷涂于无纺布上，室温固化，即得无纺布织物涂层吸波材料。
2.根据权利要求1所述的一种吸波无纺布的制备方法，其特征在于，所述分散剂为OP-10。
3.根据权利要求1所述的一种吸波无纺布的制备方法，其特征在于，所述水性粘结剂为羧甲基纤维素钠。
CN201510595810.0A 2015-09-18 2015-09-18 一种吸波无纺布的制备方法 Pending CN105714553A (zh)