CN105713470A - 一种抗静电涂料及其制备方法 - Google Patents

一种抗静电涂料及其制备方法 Download PDF

Info

Publication number
CN105713470A
CN105713470A CN201510382263.8A CN201510382263A CN105713470A CN 105713470 A CN105713470 A CN 105713470A CN 201510382263 A CN201510382263 A CN 201510382263A CN 105713470 A CN105713470 A CN 105713470A
Authority
CN
China
Prior art keywords
preparation
antistatic
carbon black
coupling agent
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510382263.8A
Other languages
English (en)
Inventor
何金宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUAINING COUNTY BAOYOU INDUSTRY AND TRADE Co Ltd
Original Assignee
HUAINING COUNTY BAOYOU INDUSTRY AND TRADE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUAINING COUNTY BAOYOU INDUSTRY AND TRADE Co Ltd filed Critical HUAINING COUNTY BAOYOU INDUSTRY AND TRADE Co Ltd
Priority to CN201510382263.8A priority Critical patent/CN105713470A/zh
Publication of CN105713470A publication Critical patent/CN105713470A/zh
Pending legal-status Critical Current

Abstract

本发明公开的是一种抗静电涂料及其制备方法，其特征在于，以重量份数计，包括树脂清漆90-100份，高结构炭黑5-35份，溶剂15-50份、偶联剂0.1-0.3份；其制备方法，包括以下几个步骤：将炭黑在65-100℃烘干后，将炭黑用偶联剂进行喷淋处理；将处理后的炭黑、树脂、溶剂按顺序依次加入容器中搅拌，边加边搅拌成初混物；球磨60-120min即得。本发明的涂料材料成本低，抗静电性能却和抗静电塑料一样；涂装于物体上，使物体具有抗静电性能，同时不破坏物体固有的其它性能。

Description

一种抗静电涂料及其制备方法
技术领域
本发明涉及一种抗静电涂料及其制备方法，属于涂料领域。
背景技术
目前，抗静电产品主流的制造方法是采用抗静电塑料进行注塑加工、制模而成，这种制造方法存在很多缺陷：第一，抗静电塑料价格昂贵，是普通塑料的4-10倍，其制模产品是普通塑料的3-5倍；第二，抗静电塑料由于经过改性，其它某些方面的性能有所下降（如冲击强度、拉伸强度、流动性等），其制模产品的性能，尤其是机械性能就不如普通塑料的好；第三，由于抗静电塑料的材料收缩率于普通材料不同，不能利用现有的模具成型。需要另外设计制造模具，因此成本高、周期长；第四，如果是抗静电剂改性的抗静电塑料，其抗静电性能是不稳定的，会随着湿度、时间的变化而变化。
本发明的涂料材料成本低，抗静电性能却和抗静电塑料一样；涂装于物体上，使物体具有抗静电性能，同时不破坏物体固有的其它性能。因此，一种高强度防水石膏砌块及其制备方法是很有必要的。
发明内容
本发明目的是，用来弥补现有技术的不足，而提供一种抗静电涂料及其制备方法。
为了实现上述目的，本发明的技术方案如下：
一种抗静电涂料及其制备方法，以重量份数计，包括树脂清漆90-100份，高结构炭黑5-35份，溶剂15-50份、偶联剂0.1-0.3份。
所述树脂清漆为丙烯酸酯树脂、环氧树脂或者聚酯。
所述溶剂环己酮或者丙酮。
所述偶联剂为钛酸酯偶联剂。
一种抗静电涂料及其制备方法，包括以下几个步骤：将炭黑在65-100℃烘干后，将炭黑用偶联剂进行喷淋处理；将处理后的炭黑、树脂、溶剂按顺序依次加入容器中搅拌，边加边搅拌成初混物；球磨60-120min即得。
本发明的有益效果如下：
本发明制备工艺简单，涂料材料成本低，抗静电性能却和抗静电塑料一样；涂装于物体上，使物体具有抗静电性能，同时不破坏物体固有的其它性能。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1：
本实施例中，一种抗静电涂料及其制备方法，以重量份数计，包括树脂清漆100份，高结构炭黑15份，溶剂35份、偶联剂0.2份。
所述树脂清漆为丙烯酸酯树脂。
所述溶剂环己酮。
所述偶联剂为钛酸酯偶联剂。
一种抗静电涂料及其制备方法，包括以下几个步骤：将炭黑在80℃烘干后，将炭黑用偶联剂进行喷淋处理；将处理后的炭黑、树脂、溶剂按顺序依次加入容器中搅拌，边加边搅拌成初混物；球磨90min即得。
本发明制备工艺简单，涂料材料成本低，抗静电性能却和抗静电塑料一样；涂装于物体上，使物体具有抗静电性能，同时不破坏物体固有的其它性能。经测试，其表面电阻率为1010-1012Ω/口。
实施例2：
本实施例中，一种抗静电涂料及其制备方法，以重量份数计，包括树脂清漆95份，高结构炭黑25份，溶剂30份、偶联剂0.2份。
所述树脂清漆为环氧树脂。
所述溶剂丙酮。
所述偶联剂为钛酸酯偶联剂。
一种抗静电涂料及其制备方法，包括以下几个步骤：将炭黑在70℃烘干后，将炭黑用偶联剂进行喷淋处理；将处理后的炭黑、树脂、溶剂按顺序依次加入容器中搅拌，边加边搅拌成初混物；球磨60min即得。
本发明制备工艺简单，涂料材料成本低，抗静电性能却和抗静电塑料一样；涂装于物体上，使物体具有抗静电性能，同时不破坏物体固有的其它性能。经测试，其表面电阻率为109-1012Ω/口。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (5)

1.一种抗静电涂料及其制备方法，其特征在于，以重量份数计，包括树脂清漆90-100份，高结构炭黑5-35份，溶剂15-50份、偶联剂0.1-0.3份。
2.根据权利要求1所述的一种抗静电涂料及其制备方法，其特征在于，所述树脂清漆为丙烯酸酯树脂、环氧树脂或者聚酯。
3.根据权利要求1所述的一种抗静电涂料及其制备方法，其特征在于，所述溶剂环己酮或者丙酮。
4.根据权利要求1所述的一种抗静电涂料及其制备方法，其特征在于，所述偶联剂为钛酸酯偶联剂。
5.根据权利要求1所述的一种抗静电涂料及其制备方法，其特征在于，包括以下几个步骤：将炭黑在65-100℃烘干后，将炭黑用偶联剂进行喷淋处理；将处理后的炭黑、树脂、溶剂按顺序依次加入容器中搅拌，边加边搅拌成初混物；球磨60-120min即得。
CN201510382263.8A 2015-07-03 2015-07-03 一种抗静电涂料及其制备方法 Pending CN105713470A (zh)