CN106154005A - 一种电表箱箱体的加工工艺 - Google Patents

一种电表箱箱体的加工工艺 Download PDF

Info

Publication number
CN106154005A
CN106154005A CN201510145100.8A CN201510145100A CN106154005A CN 106154005 A CN106154005 A CN 106154005A CN 201510145100 A CN201510145100 A CN 201510145100A CN 106154005 A CN106154005 A CN 106154005A
Authority
CN
China
Prior art keywords
box body
electric meter
injection
meter box
processing technique
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510145100.8A
Other languages
English (en)
Inventor
唐征
刘传洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sage Enjoys Intelligent Science And Technology Ltd
Original Assignee
Anhui Sage Enjoys Intelligent Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sage Enjoys Intelligent Science And Technology Ltd filed Critical Anhui Sage Enjoys Intelligent Science And Technology Ltd
Priority to CN201510145100.8A priority Critical patent/CN106154005A/zh
Publication of CN106154005A publication Critical patent/CN106154005A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种电表箱箱体的加工工艺，包括以下步骤：选料：选取聚碳酸酯颗粒20-40％和ABS塑料60-80％颗粒，经搅拌机充分混合；上料：吸料机把混合颗粒吸到烘料箱内；烘干：在烘料箱内对混合颗粒进行烘干，烘干3-5分钟；注塑：烘干后的混合颗粒经吸料机送到料筒中，注塑机利用模具把混合颗粒注塑成型；冷却：对模具进行水循环使注塑电表箱箱体冷却成型。本发明加工工艺采用PC聚碳酸酯和ABS塑料颗粒混合经过注塑机挤压成型的箱体，具有绝缘性能好，抗紫外线、耐老化、耐酸雨、耐盐雾、耐高温、耐低温、抗冲击性能强的优点。

Description

一种电表箱箱体的加工工艺
技术领域
本发明涉及电表箱生产加工技术领域，尤其是涉及一种电表箱箱体的加工工艺。
背景技术
电表箱是电表的保护装置。市政、小区、电信、电力、农网、工厂、企业、机关、热力、消防等公用设施的地方就需要安装电表。电表箱一般是沿电力设施到用户的一个终端铺设，每户都需要一个电表箱，因此电表箱的用量极大。如今现使用的电表箱材质多为冷轧铁皮和塑料，铁皮表箱的铁壳绝缘性能差、易生锈、防水密封能力存在安全隐患，直接容易导致人体触电伤害，且由于表箱制作过程中铁皮酸洗，喷塑过程中会造成很大的环境污染且不环保。
发明内容
本发明的目的就是为了克服上述现有技术的缺陷，提供了一种电表箱箱体的加工工艺，该加工工艺采用PC聚碳酸酯和ABS塑料颗粒混合经过注塑机挤压成型的箱体，具有绝缘性能好，抗紫外线、耐老化、耐酸雨、耐盐雾、耐高温、耐低温、抗冲击性能强的优点。
本发明所要求解决的技术问题可以通过以下技术方案来实现：
一种电表箱箱体的加工工艺，包括以下步骤：
S1、选料：选取聚碳酸酯颗粒20-40％和ABS塑料60-80％颗粒，经搅拌机充分混合；
S2、上料：吸料机把混合颗粒吸到烘料箱内；
S3、烘干：在烘料箱内对混合颗粒进行烘干，烘干3-5分钟；
S4、注塑：烘干后的混合颗粒经吸料机送到料筒中，注塑机利用模具把混合颗粒注塑成型；
S5、冷却：对模具进行水循环使注塑电表箱箱体冷却成型。
进一步地，所述S3烘料箱的温度为90-110℃。
进一步地，所述S4料筒分为三段。
进一步地，所述S4料筒一段温度为270-280℃，二段温度为240-260℃，三段温度为220-240℃。
进一步地，所述S4模具温度为120-150℃。
进一步地，所述S5模具温度为50-70℃。
本发明的有益效果：一种电表箱箱体的加工工艺，该加工工艺采用PC聚碳酸酯和ABS塑料颗粒混合经过注塑机挤压成型的箱体，具有绝缘性能好，抗紫外线、耐老化、耐酸雨、耐盐雾、耐高温、耐低温、抗冲击性能强的优点。
具体实施方式
实施例1：
一种电表箱箱体的加工工艺，包括以下步骤：
S1、选料：选取聚碳酸酯颗粒20％和ABS塑料80％颗粒，经搅拌机充分混合；
S2、上料：吸料机把混合颗粒吸到烘料箱内；
S3、烘干：在烘料箱内对混合颗粒进行烘干，烘干3分钟，烘料箱的温度为110℃；
S4、注塑：烘干后的混合颗粒经吸料机送到料筒中，注塑机利用模具把混合颗粒注塑成型；料筒分为三段，料筒一段温度为280℃，二段温度为260℃，三段温度为240℃；模具的温度为150℃。
S5、冷却：对模具进行水循环使注塑电表箱箱体冷却成型，模具温度为70℃。
实施例2：
一种电表箱箱体的加工工艺，包括以下步骤：
S1、选料：选取聚碳酸酯颗粒40％和ABS塑料60％颗粒，经搅拌机充分混合；
S2、上料：吸料机把混合颗粒吸到烘料箱内；
S3、烘干：在烘料箱内对混合颗粒进行烘干，烘干4分钟，烘料箱的温度为100℃；
S4、注塑：烘干后的混合颗粒经吸料机送到料筒中，注塑机利用模具把混合颗粒注塑成型；料筒分为三段，料筒一段温度为275℃，二段温度为255℃，三段温度为230℃；模具的温度为130℃。
S5、冷却：对模具进行水循环使注塑电表箱箱体冷却成型，模具温度为60℃。
实施例3：
一种电表箱箱体的加工工艺，包括以下步骤：
S1、选料：选取聚碳酸酯颗粒30％和ABS塑料70％颗粒，经搅拌机充分混合；
S2、上料：吸料机把混合颗粒吸到烘料箱内；
S3、烘干：在烘料箱内对混合颗粒进行烘干，烘干5分钟，烘料箱的温度为90℃；
S4、注塑：烘干后的混合颗粒经吸料机送到料筒中，注塑机利用模具把混合颗粒注塑成型；料筒分为三段，料筒一段温度为270℃，二段温度为240℃，三段温度为220℃；模具的温度为120℃。
S5、冷却：对模具进行水循环使注塑电表箱箱体冷却成型，模具温度为50℃。
一种电表箱箱体的加工工艺，该加工工艺采用PC聚碳酸酯和ABS塑料颗粒混合经过注塑机挤压成型的箱体，具有绝缘性能好，抗紫外线、耐老化、耐酸雨、耐盐雾、耐高温、耐低温、抗冲击性能强的优点。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等同物界定。

Claims (6)

1.一种电表箱箱体的加工工艺，其特征在于，包括以下步骤：
S1、选料：选取聚碳酸酯颗粒20-40％和ABS塑料60-80％颗粒，经搅拌机充分混合；
S2、上料：吸料机把混合颗粒吸到烘料箱内；
S3、烘干：在烘料箱内对混合颗粒进行烘干，烘干3-5分钟；
S4、注塑：烘干后的混合颗粒经吸料机送到料筒中，注塑机利用模具把混合颗粒注塑成型；
S5、冷却：对模具进行水循环使注塑电表箱箱体冷却成型。
2.按照权利要求1所述的一种电表箱箱体的加工工艺，其特征在于：所述S3烘料箱的温度为90-110℃。
3.按照权利要求1所述的一种电表箱箱体的加工工艺，其特征在于：所述S4料筒分为三段。
4.按照权利要求3所述的一种电表箱箱体的加工工艺，其特征在于：所述S4料筒一段温度为270-280℃，二段温度为240-260℃，三段温度为220-240℃。
5.按照权利要求1所述的一种电表箱箱体的加工工艺，其特征在于：所述S4模具温度为120-150℃。
6.按照权利要求1所述的一种电表箱箱体的加工工艺，其特征在于：所述S5模具温度为50-70℃。
CN201510145100.8A 2015-03-27 2015-03-27 一种电表箱箱体的加工工艺 Pending CN106154005A (zh)