CN105648744A - 耐洗性能好的手术布的制备方法 - Google Patents
耐洗性能好的手术布的制备方法 Download PDFInfo
- Publication number
- CN105648744A CN105648744A CN201610004894.0A CN201610004894A CN105648744A CN 105648744 A CN105648744 A CN 105648744A CN 201610004894 A CN201610004894 A CN 201610004894A CN 105648744 A CN105648744 A CN 105648744A
- Authority
- CN
- China
- Prior art keywords
- cotton
- washing
- solution
- preparation
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐洗性能好的手术布的制备方法，包括以下步骤：对棉布进行膨化预处理；一次水洗；对预处理后的棉布进行交联改性处理：将一次水洗后的棉布放入浴比1:15的水中，加入棉布重量的10~15%的交联剂溶液，然后升高温度至约42~47℃，处理时间1.2~1.5h，所述的交联剂溶液的质量百分比浓度为10~15%；二次水洗；对二次水洗后的棉布进行载银处理：将二次水洗后的棉布放入浴比1:25的水中，加入棉布重量的30~40%的银氨溶液，再加入还原剂溶液，然后升高温度至约35~40℃，处理时间2~2.5h；三次水洗；挤水；烘干。本发明提高了手术布的力学强度，能够反复多次清洗也不易破损，耗损小。
Description
技术领域
本发明涉及手术布领域，特别是涉及一种耐洗性能好的手术布的制备方法。
背景技术
医疗用布是医疗卫生部门所必需的。为了保障人民的健康，减少交叉感染和病毒、病菌传播渠道，医疗卫生器具的卫生越来越为人们所重视，并且随着医学科学的迅速发展，对医疗卫生用纺织品要求越来越高。这样，从安全、卫生、防毒等方面考虑，多功能“用即弃”产品越来越多。
常用的手术布类有两种：一种是以传统纺织布制成的手术布类，它的特点是可以反复多次清洗、消毒、灭菌、重复使用，但容易破损，耗损大。另一种经环氧乙烷灭菌的单独分装好的一次性布类，主要材料是非织造布，它的特点是一次性使用，使用方便，即取即用，防水防渗透性强，缺点是无菌包开启后要一次性用完，多余的难以再次包装再次消毒使用。
发明内容
本发明主要解决的技术问题是提供一种耐洗性能好的手术布的制备方法，提高了手术布的力学强度，耐洗性能好，能够反复多次清洗也不易破损，耗损小。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种耐洗性能好的手术布的制备方法，包括以下步骤：
（1）在恒温下对棉布进行膨化预处理；
（2）一次水洗：用水洗涤数次，使棉布不含碱；
（3）对预处理后的棉布进行交联改性处理：将一次水洗后的棉布放入浴比1:15的水中，加入棉布重量的10~15%的交联剂溶液，然后升高温度至约42~47℃，处理时间1.2~1.5h，所述的交联剂溶液的质量百分比浓度为10~15%；
（4）二次水洗：用水洗涤数次，使棉布不含交联剂溶液；
（5）对二次水洗后的棉布进行载银处理：将二次水洗后的棉布放入浴比1:25的水中，加入棉布重量的30~40%的银氨溶液，再加入还原剂溶液，然后升高温度至约35~40℃，处理时间2~2.5h；
（6）三次水洗：用水洗涤数次，使棉布既不含银氨溶液也不含还原剂溶液；
（7）挤水：对三次水洗后的棉布的进行挤水，使棉布的含水量为其重量的8~15%；
（8）烘干：将挤水后的棉布放入真空干燥箱中进行烘干。
在本发明一个较佳实施例中，步骤（1）中以氢氧化钠溶液为润胀剂，在30~35℃的恒温下进行膨化预处理，氢氧化钠溶液的质量百分比浓度为10%~15%，处理时间15~18min。
在本发明一个较佳实施例中，步骤（2）的一次水洗的温度为35~45℃。
在本发明一个较佳实施例中，步骤（3）中所述的交联剂溶液为氯化钙溶液。
在本发明一个较佳实施例中，步骤（4）的二次水洗的温度为30~35℃。
在本发明一个较佳实施例中，步骤（5）中所述的银氨溶液的浓度为25~35mmol/L，还原剂溶液的质量浓度为5~15mmol/L。
在本发明一个较佳实施例中，步骤（5）中所述的还原剂为葡萄糖、过氧化氢或鞣酸。
在本发明一个较佳实施例中，步骤（6）的三次水洗的温度为30~35℃。
在本发明一个较佳实施例中，步骤（8）中真空干燥箱的烘干温度为90~100℃。
本发明的有益效果是：本发明提高了手术布的力学强度，耐洗性能好，能够反复多次清洗也不易破损，耗损小。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1
一种耐洗性能好的手术布的制备方法，包括以下步骤：
（1）在恒温下对棉布进行膨化预处理：以氢氧化钠溶液为润胀剂，在30℃的恒温下进行膨化预处理，氢氧化钠溶液的质量百分比浓度为12%，处理时间18min；
（2）一次水洗：用水洗涤数次，使棉布不含碱，一次水洗的温度为45℃；
（3）对预处理后的棉布进行交联改性处理：将一次水洗后的棉布放入浴比1:15的水中，加入棉布重量的13%的交联剂溶液，然后升高温度至约42℃，处理时间1.5h，所述的交联剂溶液的质量百分比浓度为15%，所述的交联剂溶液为氯化钙溶液；
（4）二次水洗：用水洗涤数次，使棉布不含交联剂溶液，二次水洗的温度为30℃；
（5）对二次水洗后的棉布进行载银处理：将二次水洗后的棉布放入浴比1:25的水中，加入棉布重量的40%的银氨溶液，再加入还原剂溶液，然后升高温度至约35℃，处理时间2.5h，所述的银氨溶液的浓度为35mmol/L，还原剂溶液的质量浓度为10mmol/L，所述的还原剂为葡萄糖；
（6）三次水洗：用水洗涤数次，使棉布既不含银氨溶液也不含还原剂溶液，三次水洗的温度为35℃；
（7）挤水：对三次水洗后的棉布的进行挤水，使棉布的含水量为其重量的10%；
（8）烘干：将挤水后的棉布放入真空干燥箱中进行烘干，真空干燥箱的烘干温度为95℃。
实施例2
一种耐洗性能好的手术布的制备方法，包括以下步骤：
（1）在恒温下对棉布进行膨化预处理：以氢氧化钠溶液为润胀剂，在33℃的恒温下进行膨化预处理，氢氧化钠溶液的质量百分比浓度为10%，处理时间17min；
（2）一次水洗：用水洗涤数次，使棉布不含碱，一次水洗的温度为35℃；
（3）对预处理后的棉布进行交联改性处理：将一次水洗后的棉布放入浴比1:15的水中，加入棉布重量的15%的交联剂溶液，然后升高温度至约47℃，处理时间1.2h，所述的交联剂溶液的质量百分比浓度为12%，所述的交联剂溶液为氯化钙溶液；
（4）二次水洗：用水洗涤数次，使棉布不含交联剂溶液，二次水洗的温度为33℃；
（5）对二次水洗后的棉布进行载银处理：将二次水洗后的棉布放入浴比1:25的水中，加入棉布重量的35%的银氨溶液，再加入还原剂溶液，然后升高温度至约40℃，处理时间2.2h，所述的银氨溶液的浓度为30mmol/L，还原剂溶液的质量浓度为7mmol/L，所述的还原剂为鞣酸；
（6）三次水洗：用水洗涤数次，使棉布既不含银氨溶液也不含还原剂溶液，三次水洗的温度为32℃；
（7）挤水：对三次水洗后的棉布的进行挤水，使棉布的含水量为其重量的15%；
（8）烘干：将挤水后的棉布放入真空干燥箱中进行烘干，真空干燥箱的烘干温度为100℃。
实施例3
一种耐洗性能好的手术布的制备方法，包括以下步骤：
（1）在恒温下对棉布进行膨化预处理：以氢氧化钠溶液为润胀剂，在35℃的恒温下进行膨化预处理，氢氧化钠溶液的质量百分比浓度为15%，处理时间15min；
（2）一次水洗：用水洗涤数次，使棉布不含碱，一次水洗的温度为40℃；
（3）对预处理后的棉布进行交联改性处理：将一次水洗后的棉布放入浴比1:15的水中，加入棉布重量的10%的交联剂溶液，然后升高温度至约45℃，处理时间1.4h，所述的交联剂溶液的质量百分比浓度为10%，所述的交联剂溶液为氯化钙溶液；
（4）二次水洗：用水洗涤数次，使棉布不含交联剂溶液，二次水洗的温度为35℃；
（5）对二次水洗后的棉布进行载银处理：将二次水洗后的棉布放入浴比1:25的水中，加入棉布重量的30%的银氨溶液，再加入还原剂溶液，然后升高温度至约38℃，处理时间2h，所述的银氨溶液的浓度为25mmol/L，还原剂溶液的质量浓度为15mmol/L，所述的还原剂为过氧化氢；
（6）三次水洗：用水洗涤数次，使棉布既不含银氨溶液也不含还原剂溶液，三次水洗的温度为30℃；
（7）挤水：对三次水洗后的棉布的进行挤水，使棉布的含水量为其重量的8%；
（8）烘干：将挤水后的棉布放入真空干燥箱中进行烘干，真空干燥箱的烘干温度为90℃。
本发明耐洗性能好的手术布的制备方法的有益效果是：本发明提高了手术布的力学强度，耐洗性能好，能够反复多次清洗也不易破损，耗损小。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (9)
1.一种耐洗性能好的手术布的制备方法，其特征在于，包括以下步骤：
（1）在恒温下对棉布进行膨化预处理；
（2）一次水洗：用水洗涤数次，使棉布不含碱；
（3）对预处理后的棉布进行交联改性处理：将一次水洗后的棉布放入浴比1:15的水中，加入棉布重量的10~15%的交联剂溶液，然后升高温度至约42~47℃，处理时间1.2~1.5h，所述的交联剂溶液的质量百分比浓度为10~15%；
（4）二次水洗：用水洗涤数次，使棉布不含交联剂溶液；
（5）对二次水洗后的棉布进行载银处理：将二次水洗后的棉布放入浴比1:25的水中，加入棉布重量的30~40%的银氨溶液，再加入还原剂溶液，然后升高温度至约35~40℃，处理时间2~2.5h；
（6）三次水洗：用水洗涤数次，使棉布既不含银氨溶液也不含还原剂溶液；
（7）挤水：对三次水洗后的棉布的进行挤水，使棉布的含水量为其重量的8~15%；
（8）烘干：将挤水后的棉布放入真空干燥箱中进行烘干。
2.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（1）中以氢氧化钠溶液为润胀剂，在30~35℃的恒温下进行膨化预处理，氢氧化钠溶液的质量百分比浓度为10%~15%，处理时间15~18min。
3.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（2）的一次水洗的温度为35~45℃。
4.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（3）中所述的交联剂溶液为氯化钙溶液。
5.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（4）的二次水洗的温度为30~35℃。
6.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（5）中所述的银氨溶液的浓度为25~35mmol/L，还原剂溶液的质量浓度为5~15mmol/L。
7.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（5）中所述的还原剂为葡萄糖、过氧化氢或鞣酸。
8.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（6）的三次水洗的温度为30~35℃。
9.根据权利要求1所述的耐洗性能好的手术布的制备方法，其特征在于，步骤（8）中真空干燥箱的烘干温度为90~100℃。