CN105623697B - 一种瘦焦煤参与的炼焦煤配煤方法 - Google Patents
一种瘦焦煤参与的炼焦煤配煤方法 Download PDFInfo
- Publication number
- CN105623697B CN105623697B CN201410715512.6A CN201410715512A CN105623697B CN 105623697 B CN105623697 B CN 105623697B CN 201410715512 A CN201410715512 A CN 201410715512A CN 105623697 B CN105623697 B CN 105623697B
- Authority
- CN
- China
- Prior art keywords
- coal
- coking coal
- coking
- thin
- daf
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种瘦焦煤参与的炼焦煤配煤方法,其炼焦煤组分wt%为:1/3焦煤:8%~18%,干燥无灰基挥发分32%≤Vdaf≤34%的肥煤:10%~18%,干燥无灰基挥发分28%≤Vdaf<32%的肥煤:8%~14%,粘结指数G≥78的焦煤:30%~50%,粘结指数75≤G<78的焦煤:0%~25%,瘦焦煤:10%~30%.炼焦煤灰分8%~9.5%、硫分0.6%~0.9%、挥发份25%~27%、镜质组反射率分布连续且成正态分布。本发明瘦焦煤的配加比例达30%,炼焦煤的镜质组反射率分布连续且成正态分布,在保护优质炼焦煤的同时,实现企业的低成本配煤,所生产的焦炭灰分在12.5%以下、硫分在1.0%以下,完全能够满足大型高炉用焦需求。
Description
技术领域
本发明属于冶金焦生产技术领域,特别是涉及到一种配加有瘦焦煤的炼焦煤配煤方法。
背景技术
中国煤炭分类中,根据不同的变质程度,将烟煤从低到高分成不同的煤牌号,主要包括气煤、1/3焦煤、肥煤、焦煤、瘦煤等。在生产实践中,重复测量同一种煤种的变质程度时,常会遇到测定结果分属于相邻的不同煤牌号的情况。煤牌号是人为划分的,而煤阶是逐步过渡的,同一煤种可能是由两种或两种以上煤牌号的煤所组成。因此,在常规测量结果中不能清楚的展现被测量煤的煤阶分布情况。
镜质组反射率可以清楚的看出被测煤种的煤阶分布情况,在所形成的煤岩镜质组反射率分布图上呈现出一个连续的分布状态、可以正确的展示真实的单种煤情况。
利用煤岩配煤方法进行炼焦配煤,往往镜质组反射率分布图在1.5%~1.70%之间出现凹口,造成镜质组反射率分布图正态分布特性较差,从而导致焦炭质量下降,不能满足新型大高炉用焦需求。同时,由于瘦焦煤的镜质组最大反射率平均值在1.5%~1.8%之间,因此,如何将瘦焦煤应用到炼焦配煤中,对我国有效地利用弱变质程度煤来进行配煤炼焦生产具有重要的社会效益和经济效益。
瘦焦煤的灰分Ad:9.0%~12.0%;挥发分Vdaf:10%~20%;G值:20~80、Y值:6~10mm。不同区域、不同成因环境、不同地质结构的煤,其特性亦不同,因此,已有的利用瘦焦煤的配煤方案不可简单借鉴。如果在炼焦配煤中直接配入瘦焦煤,有可能实现配合煤镜质组反射率的连续,但不能保证其成正态分布;同时,所炼焦炭中灰分含量可能会超标,将导致焦炭质量较差,不能满足大型高炉用焦质量要求。
发明内容
本发明旨在提供一种瘦焦煤配比达30%,从而扩大炼焦煤配煤种类,生产焦炭质量较好,可有效降低炼焦成本,满足大型高炉用焦需求的炼焦煤配煤方法。
为达此目的,本发明采取了如下技术解决方案:
一种瘦焦煤参与的炼焦煤配煤方法,其特征在于,在配煤方案中配入瘦焦煤,其炼焦煤组分及重量百分比为:
1/3焦煤:8%~18%;
干燥无灰基挥发分32%≤Vdaf≤34%的肥煤:10%~18%;
干燥无灰基挥发分28%≤Vdaf<32%的肥煤:8%~14%;
粘结指数G≥78的焦煤:30%~50%;
粘结指数75≤G<78的焦煤:0%~25%;
瘦焦煤:10%~30%;
炼焦煤质量参数为:灰分8%~9.5%、硫分0.6%~0.9%、挥发份25%~27%、镜质组反射率分布连续且成正态分布。
所述瘦焦煤的煤质为:
镜质组最大反射率范围分布在1.4%~2.0%;
镜质组最大反射率的平均值在1.5%~1.8%;
灰分Ad:9.0%~12%,挥发分Vdaf:10%~20%,G值:20~80,Y值:6~10mm。
本发明的有益效果为:
本发明结合煤炭资源状况,对配煤和煤种的选择进行优化,选择与瘦焦煤相匹配的煤种进行配煤,瘦焦煤的配加比例高达30%,并使炼焦煤的镜质组反射率分布连续且成正态分布,在保护优质炼焦煤的同时,实现企业的低成本配煤。本发明对于降低企业炼焦成本具有重大实际意义,且操作简单,易于实现,所生产的焦炭质量较好,炼焦所得焦炭的灰分在12.5%以下、硫分在1.0%以下,完全能够满足大型高炉用焦需求。
具体实施方式
对备煤车间日常生产的各单种煤进行煤质分析测定,煤质的镜质组反射率测定方法按照国家标准GB6948-2008《煤镜质组反射率测定方法》进行测定,焦炭反应性和反应后强度按国家标准GB/T 4000-2008进行检测。具体实施例如下:
实施例1:
炼焦煤组分及重量百分比为:
1/3焦煤:16%;
干燥无灰基挥发分32%≤Vdaf≤34%肥煤:10%;
干燥无灰基挥发分28%≤Vdaf<32%肥煤:10%;
粘结指数G≥78焦煤:34%;
粘结指数75≤G<78焦煤:10%;
瘦焦煤:20%。
瘦焦煤煤质指标:灰分:9.1%,挥发分:19.64%,G值:72,Y值:6.5mm。
炼焦煤的煤质指标:灰分Ad:8.34%,硫分Std:0.63%,灰发分Vdaf:26.38%。
炼焦煤镜质组反射率分布结果如表1。
表1 实施例1炼焦煤镜质组反射率分布结果(%)
在6米以上焦炉所得焦炭的质量:焦炭抗碎强度M40:89.38%;焦炭反应后强度CSR:63.60%;灰分Ad:11.61%;硫分Std:0.60%。
实施例2:
炼焦煤组分及重量百分比:
1/3焦煤:10%;
干燥无灰基挥发分32%≤Vdaf≤34%肥煤:16%;
干燥无灰基挥发分28%≤Vdaf<32%肥煤:8%;
粘结指数G≥78焦煤1#:30%;
粘结指数G≥78焦煤2#:12%;
粘结指数75≤G<78焦煤:0%;
瘦焦煤:24%。
瘦焦煤煤质指标:灰分:9.2%,挥发分:19.18%,G值:64.3,Y值:9.3mm。
炼焦煤煤质指标:灰分Ad:9.30%,硫分Std:0.90%,灰发分Vdaf:26.51%。
炼焦煤镜质组反射率分布结果见表2。
表2 实施例2炼焦煤镜质组反射率分布结果(%)
在6米以上焦炉所得焦炭的质量:焦炭抗碎强度M40:89.47%;焦炭反应后强度CSR:65.18%;灰分Ad:12.09%;硫分Std:0.75%。
实施例3:
炼焦煤组分及重量百分比:
1/3焦煤:8%;
干燥无灰基挥发分32%≤Vdaf≤34%肥煤:16%;
干燥无灰基挥发分28%≤Vdaf<32%肥煤:8%;
粘结指数G≥78焦煤1#:34%;
粘结指数G≥78焦煤2#:12%;
粘结指数75≤G<78焦煤:0%;
瘦焦煤:22%。
瘦焦煤煤质指标:灰分:11.29%,挥发分:18.70%,G值:74,Y值:7.5mm。
配合煤的煤质指标:灰分Ad:9.29%;硫分Std:0.90%;灰发分Vdaf:26.34%。
炼焦煤镜质组反射率分布结果见表3。
表3 实施例3炼焦煤镜质组反射率分布结果(%)
在6米以上焦炉所得焦炭的质量:焦炭抗碎强度M40:87.30%;焦炭反应后强度CSR:63.20%;灰分Ad:12.33%;硫分Std:0.53%。
Claims (1)
1.一种瘦焦煤参与的炼焦煤配煤方法,其特征在于,在配煤方案中配入瘦焦煤,其炼焦煤组分及重量百分比为:
1/3焦煤:8%~18%;
干燥无灰基挥发分32%≤Vdaf≤34%的肥煤:10%~18%;
干燥无灰基挥发分28%≤Vdaf<32%的肥煤:8%~14%;
粘结指数G≥78的焦煤:30%~50%;
粘结指数75≤G<78的焦煤:0%~25%;
瘦焦煤:10%~30%;
炼焦煤质量参数为:灰分8%~9.5%、硫分0.6%~0.9%、挥发份25%~27%、镜质组反射率分布连续且成正态分布;
所述瘦焦煤的煤质为:
镜质组最大反射率范围分布在1.4%~2.0%;
镜质组最大反射率的平均值在1.5%~1.8%;
灰分Ad:9.0%~12%,挥发分Vdaf:10%~20%,G值:20~80,Y值:6~10mm。