CN105542600A - Elastic external wall emulsion paint and preparation method thereof - Google Patents
Elastic external wall emulsion paint and preparation method thereof Download PDFInfo
- Publication number
- CN105542600A CN105542600A CN201610009519.5A CN201610009519A CN105542600A CN 105542600 A CN105542600 A CN 105542600A CN 201610009519 A CN201610009519 A CN 201610009519A CN 105542600 A CN105542600 A CN 105542600A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- agent
- elastic
- emulsion paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to elastic external wall emulsion paint and a preparation method thereof. The emulsion paint is prepared from, by weight, 160-180 parts of deionized water, 0.5-2 parts of PH regulator, 140-160 parts of titanium dioxide, 1-5 parts of hydroxyethyl cellulose, 5-8 parts of dispersing agent, 1-5 parts of anti-foaming agent, 1-5 parts of wetting agent, 90-110 parts of wollastonite in powder, 180-220 parts of calcium powder, 10-20 parts of propylene glycol, 5-10 parts of coalescing agent, 0-10 parts of emulsion modifier, 45-55 parts of styrene-acrylic emulsion, 240-260 parts of elastic emulsion, 0-5 parts of ammonium hydroxide and 1-5 parts of thickening agent. The emulsion paint is green and environmentally friendly, the quality of the emulsion meets the national standard, and meanwhile the emulsion paint is high in weather resistance, water resistance and adsorption performance.
Description
Technical field
The present invention relates to a kind of elastic outer wall emulsion paint and preparation method thereof, belong to building coating technical field.
Background technology
Exterior wall latex paint take macromolecule emulsion as a class coating of film forming matter, is that base-material adds the formulated class water-borne coatings of pigment, filler and various auxiliary agent with synthetic resin emulsion.The major function of exterior wall latex paint is decoration and architecture protection object plane, makes buildings appearance neat and artistic, thus reaches the object of beautifying urban environment, can play the effect of architecture protection beyond the region of objective existence wall simultaneously, extend its work-ing life.
Exterior wall latex paint also exists poor water resistance in the market, weathering resistance is poor, the shortcoming that adhesive ability is not strong, for a long time being exposed to the phenomenons such as air floating coat easily occurs ftractureing, peels off, shedding, variable color, makes it lose original ornamental and protectiveness.Meanwhile, existing exterior wall latex paint because of containing formaldehyde or benzene solvent etc. polluted air, affect environmental quality.
Summary of the invention
The object of the invention is to: a kind of environmental protection is provided, simultaneously good weatherability, water-tolerant, elastic outer wall emulsion paint that sticking power is high and preparation method thereof.
In order to realize foregoing invention object, the invention provides following technical scheme:
A kind of elastic outer wall emulsion paint, comprises the raw material of following weight part: deionized water 160-180 part, PH adjusting agent 0.5-2 part, titanium dioxide 140-160 part, Natvosol 1-5 part, dispersion agent 5-8 part, defoamer 1-5 part, wetting agent 1-5 part, wollastonite powder 90-110 part, dicalcium powder 180-220 part, propylene glycol 10-20 part, film coalescence aid 5-10 part, emulsion modifying agent 0-10 part, benzene emulsion 45-55 part, elastic emulsion 240-260 part, ammoniacal liquor 0-5 part, thickening material 1-5 part.
Preferably, described elastic outer wall emulsion paint, comprises the raw material of following weight part: deionized water 170 parts, PH adjusting agent 1 part, titanium dioxide 150 parts, Natvosol 3 parts, dispersion agent 6 parts, defoamer 3 parts, wetting agent 2 parts, wollastonite powder 100 parts, dicalcium powder 200 parts, propylene glycol 15 parts, film coalescence aid 6 parts, emulsion modifying agent 8 parts, benzene emulsion 50 parts, elastic emulsion 250 parts, ammoniacal liquor 1 part, thickening material 2 parts.
Preferably, described elastic emulsion is acrylic ester elastic emulsion.
Preferably, described PH conditioning agent is the one in sodium carbonate, sodium bicarbonate.
Preferably, described Natvosol model is 30000S.
Preferably, a kind of preparation method of elastic outer wall emulsion paint, concrete steps are as follows:
(1) by ionized water, PH adjusting agent, titanium dioxide, Natvosol, dispersion agent, defoamer, wetting agent adds in dispersion machine, high speed dispersion 10-20 minute under rotating speed is 1250 revs/min of conditions;
(2) then wollastonite powder is added, dicalcium powder, propylene glycol, film coalescence aid, high speed dispersion 30-40 minute under rotating speed is 1250 revs/min of conditions;
(3) finally add defoamer, emulsion modifying agent, benzene emulsion, after stirring, then add elastic emulsion under rotating speed is 300-500 rev/min of condition, rotating speed is adjusted to 300-500 rev/min and stirs and can fillingly dispatch from the factory by ammoniacal liquor, thickening material.
Preferably, the mass ratio of the defoamer in step (1) and step (3) is 1:1.
Beneficial effect of the present invention is: elastic outer wall emulsion paint provided by the invention environmental protection, and quality meets national standard, and meanwhile, good weatherability, water-tolerant, sticking power are high.
Embodiment
Embodiment 1
A kind of elastic outer wall emulsion paint, comprises the raw material of following weight part: deionized water 160 parts, PH adjusting agent 0.5 part, titanium dioxide 140 parts, Natvosol 1 part, dispersion agent 5 parts, defoamer 1 part, wetting agent 1 part, wollastonite powder 90 parts, dicalcium powder 180 parts, propylene glycol 10 parts, film coalescence aid 5 parts, benzene emulsion 45 parts, elastic emulsion 240 parts, thickening material 1 part.
The preparation method of above-mentioned elastic outer wall emulsion paint, concrete steps are as follows:
(1) by ionized water, PH adjusting agent, titanium dioxide, Natvosol, dispersion agent, defoamer, wetting agent adds in dispersion machine, high speed dispersion 10 minutes under rotating speed is 1250 revs/min of conditions;
(2) then wollastonite powder is added, dicalcium powder, propylene glycol, film coalescence aid, high speed dispersion 30 minutes under rotating speed is 1250 revs/min of conditions;
(3) finally add defoamer, emulsion modifying agent, benzene emulsion, after stirring, then add elastic emulsion under rotating speed is 300 revs/min of conditions, rotating speed is adjusted to 300 revs/min and stirs and can fillingly dispatch from the factory by ammoniacal liquor, thickening material.
Wherein, the mass ratio of the defoamer in step (1) and step (3) is 1:1.
Embodiment 2
A kind of elastic outer wall emulsion paint, comprises the raw material of following weight part: deionized water 170 parts, PH adjusting agent 1 part, titanium dioxide 150 parts, Natvosol 3 parts, dispersion agent 6 parts, defoamer 3 parts, wetting agent 2 parts, wollastonite powder 100 parts, dicalcium powder 200 parts, propylene glycol 15 parts, film coalescence aid 6 parts, emulsion modifying agent 8 parts, benzene emulsion 50 parts, elastic emulsion 250 parts, ammoniacal liquor 1 part, thickening material 2 parts.
The preparation method of above-mentioned elastic outer wall emulsion paint, concrete steps are as follows:
(1) by ionized water, PH adjusting agent, titanium dioxide, Natvosol, dispersion agent, defoamer, wetting agent adds in dispersion machine, high speed dispersion 15 minutes under rotating speed is 1250 revs/min of conditions;
(2) then wollastonite powder is added, dicalcium powder, propylene glycol, film coalescence aid, high speed dispersion 35 minutes under rotating speed is 1250 revs/min of conditions;
(3) finally add defoamer, emulsion modifying agent, benzene emulsion, after stirring, then add elastic emulsion under rotating speed is 400 revs/min of conditions, rotating speed is adjusted to 400 revs/min and stirs and can fillingly dispatch from the factory by ammoniacal liquor, thickening material.
Wherein, the mass ratio of the defoamer in step (1) and step (3) is 1:1.
Embodiment 3
A kind of elastic outer wall emulsion paint, comprises the raw material of following weight part: deionized water 180 parts, PH adjusting agent 2 parts, titanium dioxide 160 parts, Natvosol 5 parts, dispersion agent 8 parts, defoamer 5 parts, wetting agent 5 parts, wollastonite powder 110 parts, dicalcium powder 220 parts, propylene glycol 20 parts, film coalescence aid 10 parts, emulsion modifying agent 10 parts, benzene emulsion 55 parts, elastic emulsion 260 parts, ammoniacal liquor 5 parts, thickening material 5 parts.
The preparation method of above-mentioned elastic outer wall emulsion paint, concrete steps are as follows:
(1) by ionized water, PH adjusting agent, titanium dioxide, Natvosol, dispersion agent, defoamer, wetting agent adds in dispersion machine, high speed dispersion 20 minutes under rotating speed is 1250 revs/min of conditions;
(2) then wollastonite powder is added, dicalcium powder, propylene glycol, film coalescence aid, high speed dispersion 40 minutes under rotating speed is 1250 revs/min of conditions;
(3) finally add defoamer, emulsion modifying agent, benzene emulsion, after stirring, then add elastic emulsion under rotating speed is 500 revs/min of conditions, rotating speed is adjusted to 500 revs/min and stirs and can fillingly dispatch from the factory by ammoniacal liquor, thickening material.
Wherein, the mass ratio of the defoamer in step (1) and step (3) is 1:1.
In embodiment 1-3: elastic emulsion is acrylic ester elastic emulsion; PH conditioning agent is the one in sodium carbonate, sodium bicarbonate; Natvosol model is 30000S.
Claims (7)
1. an elastic outer wall emulsion paint, is characterized in that: the raw material comprising following weight part: deionized water 160-180 part, PH adjusting agent 0.5-2 part, titanium dioxide 140-160 part, Natvosol 1-5 part, dispersion agent 5-8 part, defoamer 1-5 part, wetting agent 1-5 part, wollastonite powder 90-110 part, dicalcium powder 180-220 part, propylene glycol 10-20 part, film coalescence aid 5-10 part, emulsion modifying agent 0-10 part, benzene emulsion 45-55 part, elastic emulsion 240-260 part, ammoniacal liquor 0-5 part, thickening material 1-5 part.
2. elastic outer wall emulsion paint according to claim 1, is characterized in that: the raw material comprising following weight part: deionized water 170 parts, PH adjusting agent 1 part, titanium dioxide 150 parts, Natvosol 3 parts, dispersion agent 6 parts, defoamer 3 parts, wetting agent 2 parts, wollastonite powder 100 parts, dicalcium powder 200 parts, propylene glycol 15 parts, film coalescence aid 6 parts, emulsion modifying agent 8 parts, benzene emulsion 50 parts, elastic emulsion 250 parts, ammoniacal liquor 1 part, thickening material 2 parts.
3. elastic outer wall emulsion paint according to claim 1, is characterized in that: described elastic emulsion is acrylic ester elastic emulsion.
4. elastic outer wall emulsion paint according to claim 1, is characterized in that: described PH conditioning agent is the one in sodium carbonate, sodium bicarbonate.
5. elastic outer wall emulsion paint according to claim 1, is characterized in that: described Natvosol model is 30000S.
6. a preparation method for elastic outer wall emulsion paint, is characterized in that: concrete steps are as follows:
(1) by ionized water, PH adjusting agent, titanium dioxide, Natvosol, dispersion agent, defoamer, wetting agent adds in dispersion machine, high speed dispersion 10-20 minute under rotating speed is 1250 revs/min of conditions;
(2) then wollastonite powder is added, dicalcium powder, propylene glycol, film coalescence aid, high speed dispersion 30-40 minute under rotating speed is 1250 revs/min of conditions;
(3) finally add defoamer, emulsion modifying agent, benzene emulsion, after stirring, then add elastic emulsion under rotating speed is 300-500 rev/min of condition, rotating speed is adjusted to 300-500 rev/min and stirs and can fillingly dispatch from the factory by ammoniacal liquor, thickening material.
7. the preparation method of elastic outer wall emulsion paint according to claim 6, is characterized in that: the mass ratio of the defoamer in step (1) and step (3) is 1:1.