CN105542528A - Flame-resistant waterproof antibacterial decorative coating - Google Patents

Flame-resistant waterproof antibacterial decorative coating Download PDF

Info

Publication number
CN105542528A
CN105542528A CN201610035549.3A CN201610035549A CN105542528A CN 105542528 A CN105542528 A CN 105542528A CN 201610035549 A CN201610035549 A CN 201610035549A CN 105542528 A CN105542528 A CN 105542528A
Authority
CN
China
Prior art keywords
parts
oxalic acid
resistant waterproof
fire
copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610035549.3A
Other languages
Chinese (zh)
Inventor
黄伟洪
姚增科
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610035549.3A priority Critical patent/CN105542528A/en
Publication of CN105542528A publication Critical patent/CN105542528A/en
Pending legal-status Critical Current

Abstract

The invention relates to a flame-resistant waterproof antibacterial decorative coating which comprises the following ingredients in parts by mass: 18-22 parts of calcium chloride, 20-24 parts of polytetrafluoroethylene, 16-20 parts of 1-hydroxycyclohexyl phenyl ketone, 20-24 parts of nano-aluminum dioxide, 16-20 parts of oxalic acid, 20-24 parts of copper sulfate, 16-20 parts of hydroxypropyl methyl cellulose, 22-26 parts of oxalic acid polyester, 16-20 parts of cobalt naphthenate, 20-24 parts of iso-octyl methacrylate, 16-20 parts of tris(2-butoxyethyl) phosphate, 20-24 parts of perlite powder, 16-20 parts of dioctyl phthalate, 20-24 parts of hexamethylene diisocyanate, 16-20 parts of talcum powder, 20-24 parts of lignin, 16-20 parts of methylcellulose, 20-24 parts of diethylene glycol monobutyl ether, 16-20 parts of copper 8-hydroxyquinoline, 20-24 parts of tea polyphenol and 16-20 parts of chlorothalonil. A preparation process or method for the flame-resistant waterproof antibacterial decorative coating is simple. The prepared product has relatively excellent flame-resistant, acid/alkali-resistant, waterproof and antibacterial properties, and is applicable to the decoration field.

Description

The antibacterial decorative paint of a kind of fire-resistant waterproof
Technical field
The present invention relates to the antibacterial decorative paint of a kind of fire-resistant waterproof, belong to formulation for coating material technical field.
Background technology
In order to make building decorative product surface have fire-retardant, waterproof, the function such as antibacterial, need at decorative material surface applying coating.Coating is that coating once applies obtained solid-state continuous film, is to protect, insulation, and the matrix coating building and ornament materials obtains thin layer to the objects such as decoration.
Summary of the invention
The object of the present invention is to provide the antibacterial decorative paint of a kind of fire-resistant waterproof, to realize the fire-resistant waterproof antibacterial of decorative paint better.
To achieve these goals, technical scheme of the present invention is as follows.
The antibacterial decorative paint of a kind of fire-resistant waterproof, be made up of the component of following mass fraction: 18 ~ 22 parts, calcium chloride, tetrafluoroethylene 20 ~ 24 parts, hydroxycyclohexan benzophenone 16 ~ 20 parts, 20 ~ 24 parts, nanometer titanium dioxide aluminium, oxalic acid 16 ~ 20 parts, 20 ~ 24 parts, copper sulfate, Vltra tears 16 ~ 20 parts, oxalic acid polyester 22 ~ 26 parts, cobalt naphthenate 16 ~ 20 parts, Isooctyl methacrylate 20 ~ 24 parts, tributoxyethyl phosphate 16 ~ 20 parts, perlite powder 20 ~ 24 parts, dioctyl phthalate (DOP) 16 ~ 20 parts, hexamethylene diisocyanate 20 ~ 24 parts, talcum powder 16 ~ 20 parts, 20 ~ 24 parts, xylogen, methylcellulose gum 16 ~ 20 parts, butyl carbitol 20 ~ 24 parts, copper 8-quinolinolate 16 ~ 20 parts, tea-polyphenol 20 ~ 24 parts, m-tetrachlorophthalodinitrile 16 ~ 20 parts.
Further, the antibacterial decorative paint of above-mentioned fire-resistant waterproof, be made up of the component of following mass fraction: 18 parts, calcium chloride, tetrafluoroethylene 20 parts, hydroxycyclohexan benzophenone 16 parts, 20 parts, nanometer titanium dioxide aluminium, oxalic acid 16 parts, 20 parts, copper sulfate, Vltra tears 16 parts, oxalic acid polyester 22 parts, cobalt naphthenate 16 parts, Isooctyl methacrylate 20 parts, tributoxyethyl phosphate 16 parts, perlite powder 20 parts, dioctyl phthalate (DOP) 16 parts, hexamethylene diisocyanate 20 parts, talcum powder 16 parts, 20 parts, xylogen, methylcellulose gum 16 parts, butyl carbitol 20 parts, copper 8-quinolinolate 16 parts, tea-polyphenol 20 parts, m-tetrachlorophthalodinitrile 16 parts.
Further, the antibacterial decorative paint of above-mentioned fire-resistant waterproof, be made up of the component of following mass fraction: 20 parts, calcium chloride, tetrafluoroethylene 22 parts, hydroxycyclohexan benzophenone 18 parts, 22 parts, nanometer titanium dioxide aluminium, oxalic acid 18 parts, 22 parts, copper sulfate, Vltra tears 18 parts, oxalic acid polyester 24 parts, cobalt naphthenate 18 parts, Isooctyl methacrylate 22 parts, tributoxyethyl phosphate 18 parts, perlite powder 22 parts, dioctyl phthalate (DOP) 18 parts, hexamethylene diisocyanate 22 parts, talcum powder 18 parts, 22 parts, xylogen, methylcellulose gum 18 parts, butyl carbitol 22 parts, copper 8-quinolinolate 18 parts, tea-polyphenol 22 parts, m-tetrachlorophthalodinitrile 18 parts.
Further, the antibacterial decorative paint of above-mentioned fire-resistant waterproof, be made up of the component of following mass fraction: 22 parts, calcium chloride, tetrafluoroethylene 24 parts, hydroxycyclohexan benzophenone 20 parts, 24 parts, nanometer titanium dioxide aluminium, oxalic acid 20 parts, 24 parts, copper sulfate, Vltra tears 20 parts, oxalic acid polyester 26 parts, cobalt naphthenate 20 parts, Isooctyl methacrylate 24 parts, tributoxyethyl phosphate 20 parts, perlite powder 24 parts, dioctyl phthalate (DOP) 20 parts, hexamethylene diisocyanate 24 parts, talcum powder 20 parts, 24 parts, xylogen, methylcellulose gum 20 parts, butyl carbitol 24 parts, copper 8-quinolinolate 20 parts, tea-polyphenol 24 parts, m-tetrachlorophthalodinitrile 20 parts.
Further, above-mentioned fire-resistant waterproof antibacterial decorative paint preparation method step is as follows:
(1) by the calcium chloride of described mass fraction, tetrafluoroethylene, hydroxycyclohexan benzophenone, nanometer titanium dioxide aluminium, oxalic acid, copper sulfate, Vltra tears, oxalic acid polyester, cobalt naphthenate, Isooctyl methacrylate, tributoxyethyl phosphate, dioctyl phthalate (DOP), hexamethylene diisocyanate, xylogen, methylcellulose gum, butyl carbitol, copper 8-quinolinolate, tea-polyphenol, m-tetrachlorophthalodinitrile is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the perlite powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the talcum powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.
This beneficial effect of the invention is: the antibacterial decorative paint process of preparing of this fire-resistant waterproof is simple, and prepared product has comparatively superior fire-retardant, acid and alkali-resistance, water-proof antibiotic performance, is adapted at furnishing fields and uses, improve product performance.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
Embodiment 1
The antibacterial decorative paint of fire-resistant waterproof in the present embodiment, be made up of the component of following mass fraction: 18 parts, calcium chloride, tetrafluoroethylene 20 parts, hydroxycyclohexan benzophenone 16 parts, 20 parts, nanometer titanium dioxide aluminium, oxalic acid 16 parts, 20 parts, copper sulfate, Vltra tears 16 parts, oxalic acid polyester 22 parts, cobalt naphthenate 16 parts, Isooctyl methacrylate 20 parts, tributoxyethyl phosphate 16 parts, perlite powder 20 parts, dioctyl phthalate (DOP) 16 parts, hexamethylene diisocyanate 20 parts, talcum powder 16 parts, 20 parts, xylogen, methylcellulose gum 16 parts, butyl carbitol 20 parts, copper 8-quinolinolate 16 parts, tea-polyphenol 20 parts, m-tetrachlorophthalodinitrile 16 parts.
Above-mentioned fire-resistant waterproof antibacterial decorative paint preparation method step is as follows:
(1) calcium chloride of described mass fraction, tetrafluoroethylene, hydroxycyclohexan benzophenone, nanometer titanium dioxide aluminium, oxalic acid, copper sulfate, Vltra tears, oxalic acid polyester, cobalt naphthenate, Isooctyl methacrylate, tributoxyethyl phosphate, dioctyl phthalate (DOP), hexamethylene diisocyanate, xylogen, methylcellulose gum, butyl carbitol, copper 8-quinolinolate, tea-polyphenol, m-tetrachlorophthalodinitrile are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion 5400r/min, jitter time is 60min;
(2) add the perlite powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion 5200r/min, and jitter time is 50min;
(3) add the talcum powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion 4800r/min, and jitter time is 40min; Mix rear obtained this product.
Embodiment 2
The antibacterial decorative paint of fire-resistant waterproof in the present embodiment, be made up of the component of following mass fraction: 20 parts, calcium chloride, tetrafluoroethylene 22 parts, hydroxycyclohexan benzophenone 18 parts, 22 parts, nanometer titanium dioxide aluminium, oxalic acid 18 parts, 22 parts, copper sulfate, Vltra tears 18 parts, oxalic acid polyester 24 parts, cobalt naphthenate 18 parts, Isooctyl methacrylate 22 parts, tributoxyethyl phosphate 18 parts, perlite powder 22 parts, dioctyl phthalate (DOP) 18 parts, hexamethylene diisocyanate 22 parts, talcum powder 18 parts, 22 parts, xylogen, methylcellulose gum 18 parts, butyl carbitol 22 parts, copper 8-quinolinolate 18 parts, tea-polyphenol 22 parts, m-tetrachlorophthalodinitrile 18 parts.
Above-mentioned fire-resistant waterproof antibacterial decorative paint preparation method step is as follows:
(1) calcium chloride of described mass fraction, tetrafluoroethylene, hydroxycyclohexan benzophenone, nanometer titanium dioxide aluminium, oxalic acid, copper sulfate, Vltra tears, oxalic acid polyester, cobalt naphthenate, Isooctyl methacrylate, tributoxyethyl phosphate, dioctyl phthalate (DOP), hexamethylene diisocyanate, xylogen, methylcellulose gum, butyl carbitol, copper 8-quinolinolate, tea-polyphenol, m-tetrachlorophthalodinitrile are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion 5200r/min, jitter time is 45min;
(2) add the perlite powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion 5000r/min, and jitter time is 40min;
(3) add the talcum powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion 4700r/min, and jitter time is 30min; Mix rear obtained this product.
Embodiment 3
The antibacterial decorative paint of fire-resistant waterproof in the present embodiment, be made up of the component of following mass fraction: 22 parts, calcium chloride, tetrafluoroethylene 24 parts, hydroxycyclohexan benzophenone 20 parts, 24 parts, nanometer titanium dioxide aluminium, oxalic acid 20 parts, 24 parts, copper sulfate, Vltra tears 20 parts, oxalic acid polyester 26 parts, cobalt naphthenate 20 parts, Isooctyl methacrylate 24 parts, tributoxyethyl phosphate 20 parts, perlite powder 24 parts, dioctyl phthalate (DOP) 20 parts, hexamethylene diisocyanate 24 parts, talcum powder 20 parts, 24 parts, xylogen, methylcellulose gum 20 parts, butyl carbitol 24 parts, copper 8-quinolinolate 20 parts, tea-polyphenol 24 parts, m-tetrachlorophthalodinitrile 20 parts.
Above-mentioned fire-resistant waterproof antibacterial decorative paint preparation method step is as follows:
(1) calcium chloride of described mass fraction, tetrafluoroethylene, hydroxycyclohexan benzophenone, nanometer titanium dioxide aluminium, oxalic acid, copper sulfate, Vltra tears, oxalic acid polyester, cobalt naphthenate, Isooctyl methacrylate, tributoxyethyl phosphate, dioctyl phthalate (DOP), hexamethylene diisocyanate, xylogen, methylcellulose gum, butyl carbitol, copper 8-quinolinolate, tea-polyphenol, m-tetrachlorophthalodinitrile are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) add the perlite powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the talcum powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion 4600r/min, and jitter time is 20min; Mix rear obtained this product.
Carry out performance measurement for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured data are as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has good acid and alkali-resistance, fire protection flame retarding, waterproof, anti-microbial property.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.

Claims (5)

1. the antibacterial decorative paint of fire-resistant waterproof, it is characterized in that: be made up of the component of following mass fraction: 18 ~ 22 parts, calcium chloride, tetrafluoroethylene 20 ~ 24 parts, hydroxycyclohexan benzophenone 16 ~ 20 parts, 20 ~ 24 parts, nanometer titanium dioxide aluminium, oxalic acid 16 ~ 20 parts, 20 ~ 24 parts, copper sulfate, Vltra tears 16 ~ 20 parts, oxalic acid polyester 22 ~ 26 parts, cobalt naphthenate 16 ~ 20 parts, Isooctyl methacrylate 20 ~ 24 parts, tributoxyethyl phosphate 16 ~ 20 parts, perlite powder 20 ~ 24 parts, dioctyl phthalate (DOP) 16 ~ 20 parts, hexamethylene diisocyanate 20 ~ 24 parts, talcum powder 16 ~ 20 parts, 20 ~ 24 parts, xylogen, methylcellulose gum 16 ~ 20 parts, butyl carbitol 20 ~ 24 parts, copper 8-quinolinolate 16 ~ 20 parts, tea-polyphenol 20 ~ 24 parts, m-tetrachlorophthalodinitrile 16 ~ 20 parts.
2. the antibacterial decorative paint of fire-resistant waterproof according to claim 1, it is characterized in that: the antibacterial decorative paint of described fire-resistant waterproof is made up of the component of following mass fraction: 18 parts, calcium chloride, tetrafluoroethylene 20 parts, hydroxycyclohexan benzophenone 16 parts, 20 parts, nanometer titanium dioxide aluminium, oxalic acid 16 parts, 20 parts, copper sulfate, Vltra tears 16 parts, oxalic acid polyester 22 parts, cobalt naphthenate 16 parts, Isooctyl methacrylate 20 parts, tributoxyethyl phosphate 16 parts, perlite powder 20 parts, dioctyl phthalate (DOP) 16 parts, hexamethylene diisocyanate 20 parts, talcum powder 16 parts, 20 parts, xylogen, methylcellulose gum 16 parts, butyl carbitol 20 parts, copper 8-quinolinolate 16 parts, tea-polyphenol 20 parts, m-tetrachlorophthalodinitrile 16 parts.
3. the antibacterial decorative paint of fire-resistant waterproof according to claim 1, it is characterized in that: the antibacterial decorative paint of described fire-resistant waterproof is made up of the component of following mass fraction: 20 parts, calcium chloride, tetrafluoroethylene 22 parts, hydroxycyclohexan benzophenone 18 parts, 22 parts, nanometer titanium dioxide aluminium, oxalic acid 18 parts, 22 parts, copper sulfate, Vltra tears 18 parts, oxalic acid polyester 24 parts, cobalt naphthenate 18 parts, Isooctyl methacrylate 22 parts, tributoxyethyl phosphate 18 parts, perlite powder 22 parts, dioctyl phthalate (DOP) 18 parts, hexamethylene diisocyanate 22 parts, talcum powder 18 parts, 22 parts, xylogen, methylcellulose gum 18 parts, butyl carbitol 22 parts, copper 8-quinolinolate 18 parts, tea-polyphenol 22 parts, m-tetrachlorophthalodinitrile 18 parts.
4. the antibacterial decorative paint of fire-resistant waterproof according to claim 1, it is characterized in that: the antibacterial decorative paint of described fire-resistant waterproof is made up of the component of following mass fraction: 22 parts, calcium chloride, tetrafluoroethylene 24 parts, hydroxycyclohexan benzophenone 20 parts, 24 parts, nanometer titanium dioxide aluminium, oxalic acid 20 parts, 24 parts, copper sulfate, Vltra tears 20 parts, oxalic acid polyester 26 parts, cobalt naphthenate 20 parts, Isooctyl methacrylate 24 parts, tributoxyethyl phosphate 20 parts, perlite powder 24 parts, dioctyl phthalate (DOP) 20 parts, hexamethylene diisocyanate 24 parts, talcum powder 20 parts, 24 parts, xylogen, methylcellulose gum 20 parts, butyl carbitol 24 parts, copper 8-quinolinolate 20 parts, tea-polyphenol 24 parts, m-tetrachlorophthalodinitrile 20 parts.
5. the antibacterial decorative paint of fire-resistant waterproof according to claim 1, is characterized in that: described fire-resistant waterproof antibacterial decorative paint preparation method step is as follows:
(1) by the calcium chloride of described mass fraction, tetrafluoroethylene, hydroxycyclohexan benzophenone, nanometer titanium dioxide aluminium, oxalic acid, copper sulfate, Vltra tears, oxalic acid polyester, cobalt naphthenate, Isooctyl methacrylate, tributoxyethyl phosphate, dioctyl phthalate (DOP), hexamethylene diisocyanate, xylogen, methylcellulose gum, butyl carbitol, copper 8-quinolinolate, tea-polyphenol, m-tetrachlorophthalodinitrile is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the perlite powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the talcum powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.
CN201610035549.3A 2016-01-19 2016-01-19 Flame-resistant waterproof antibacterial decorative coating Pending CN105542528A (en)