CN106318073A - Waterborne protective coating - Google Patents
Waterborne protective coating Download PDFInfo
- Publication number
- CN106318073A CN106318073A CN201610722509.6A CN201610722509A CN106318073A CN 106318073 A CN106318073 A CN 106318073A CN 201610722509 A CN201610722509 A CN 201610722509A CN 106318073 A CN106318073 A CN 106318073A
- Authority
- CN
- China
- Prior art keywords
- protective coating
- water
- parts
- aqueous protective
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a waterborne protective coating. The waterborne protective coating is prepared from, by mass, 12-27 parts of polyacrylic emulsion, 10-18 parts of propylene glycol, 15-30 parts of butyl stearate, 6-10 parts of graphene, 8-10 parts of a formaldehyde absorbent, 10-20 parts of a thickening agent and 30-50 parts of water. The waterborne protective coating is free of cobalt and lead, is separately used, and has the advantages of being light in paint color, good in quality, resistant to low temperature and high humidity and the like, the surfaces of all buildings can be coated with the waterborne protective coating, drying is quick, the waterborne protective coating is free of sagging and bubbling, a paint film is smooth and has the excellent physical and chemical performance, and the waterborne protective coating has the quite good protection and decorating effects on building textures.
Description
Technical field
The present invention relates to a kind of house ornamentation paint field, in particular it relates to a kind of aqueous protective coating.
Background technology
The oil paint generally existed mainly uses containing the banana oil of a large amount of poisonous and harmful substances, thinner as dilute
Releasing agent, impayable environment-friendly advantage is the feature that water paint is maximum.Developing water coating the most energetically, along with
The raising that aqueous protective coating is required by people, is badly in need of there is breakthrough on aqueous protective coating production method is improved in recent years.
Summary of the invention
For above-mentioned deficiency present in prior art, the technical problem to be solved is to provide a kind of effective
Aqueous protective coating.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of aqueous protective coating, including propylene
Yogurt liquid, propylene glycol, butyl stearate, Graphene, formaldehyde absorbent, thickening agent, water, the mass fraction of each component is: propylene
Yogurt liquid 12-27, propylene glycol 10-18, butyl stearate 15-30, Graphene 6-10, formaldehyde absorbent 8-10, thickening agent 10-
20, water 30-50.
As preferably, the mass fraction of each component of described aqueous protective coating is: acrylic emulsion 23, propylene glycol 15, hard
Fat acid butyl ester 22, Graphene 7, formaldehyde absorbent 8, thickening agent 20, water 50.
As preferably, described acrylic emulsion solid content is 23-50wt%.
As preferably, described drier is the mixture of polyacrylate and polyurethane.
As preferably, described water is deionized water.
As preferably, the preparation method of described aqueous protective coating, it is characterised in that comprise the steps:
1) acrylic emulsion is added in a mixing bowl, add propylene glycol, butyl stearate, stir；
2) being uniformly added into Graphene to a mixing bowl, high-speed stirred is disperseed；
3) it is uniformly added into formaldehyde absorbent, thickening agent, stirs；
4) pour into the water of mass fraction, heat 20 minutes；
5) filtering, filtrate stands,.
The aqueous protective coating of the present invention does not contains cobalt, lead, is used alone, and color is shallow, quality is good, high humidity low temperature resistant, anti-paint
Etc. feature；Being applied to various building surface, be dried rapidly, not sagging, non-foaming, paint film is smooth, have the physicochemical property of excellence, right
Building material plays well protection, decoration function.
Detailed description of the invention
The present invention provide a kind of aqueous protective coating, including acrylic emulsion, propylene glycol, butyl stearate, Graphene,
Formaldehyde absorbent, thickening agent, water, the mass fraction of each component is: acrylic emulsion 12-27, propylene glycol 10-18, stearic acid fourth
Ester 15-30, Graphene 6-10, formaldehyde absorbent 8-10, thickening agent 10-20, water 30-50.
As preferably, the mass fraction of each component of described aqueous protective coating is: acrylic emulsion 23, propylene glycol 15, hard
Fat acid butyl ester 22, Graphene 7, formaldehyde absorbent 8, thickening agent 20, water 50.
As preferably, described acrylic emulsion solid content is 23-50wt%.
As preferably, described drier is the mixture of polyacrylate and polyurethane.
As preferably, described water is deionized water.
As preferably, the preparation method of described aqueous protective coating, it is characterised in that comprise the steps:
1) acrylic emulsion is added in a mixing bowl, add propylene glycol, butyl stearate, stir；
2) being uniformly added into Graphene to a mixing bowl, high-speed stirred is disperseed；
3) it is uniformly added into formaldehyde absorbent, thickening agent, stirs；
4) pour into the water of mass fraction, heat 20 minutes；
5) filtering, filtrate stands,.
The above, be only to presently preferred embodiments of the present invention, the present invention not do the restriction of other forms, appoints
What those skilled in the art changed possibly also with the technology contents of the disclosure above or be modified as changing on an equal basis etc.
Effect embodiment.Every without departing from the present invention program content, the technical spirit of the foundation present invention is to made for any of the above embodiments any
Simple modification, equivalent variations and remodeling, all fall within protection scope of the present invention.
Claims (6)
1. an aqueous protective coating, it is characterised in that: include acrylic emulsion, propylene glycol, butyl stearate, Graphene, first
Aldehyde absorbent, thickening agent, water, the mass fraction of each component is: acrylic emulsion 12-27, propylene glycol 10-18, butyl stearate
15-30, Graphene 6-10, formaldehyde absorbent 8-10, thickening agent 10-20, water 30-50.
Aqueous protective coating the most according to claim 1, it is characterised in that: the quality of each component of described aqueous protective coating
Number is: acrylic emulsion 23, propylene glycol 15, butyl stearate 22, Graphene 7, formaldehyde absorbent 8, thickening agent 20, water 50.
Aqueous protective coating the most according to claim 2, it is characterised in that: described acrylic emulsion solid content is 23-
50wt%。
Aqueous protective coating the most according to claim 2, it is characterised in that: described drier is polyacrylate and poly-ammonia
The mixture of ester.
Aqueous protective coating the most according to claim 2, it is characterised in that: described water is deionized water, pure water or steaming
One in distilled water.
6. 1) acrylic emulsion is added in a mixing bowl, add propylene glycol, butyl stearate, stir；
2) being uniformly added into Graphene to a mixing bowl, high-speed stirred is disperseed；
3) it is uniformly added into formaldehyde absorbent, thickening agent, stirs；
4) pour into the water of mass fraction, heat 20 minutes；
5) filtering, filtrate stands,.