CN105153766A - Quick-dry diatom ooze paint - Google Patents
Quick-dry diatom ooze paint Download PDFInfo
- Publication number
- CN105153766A CN105153766A CN201510693665.XA CN201510693665A CN105153766A CN 105153766 A CN105153766 A CN 105153766A CN 201510693665 A CN201510693665 A CN 201510693665A CN 105153766 A CN105153766 A CN 105153766A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- rapid
- siccative
- curing cutback
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses quick-dry diatom ooze paint which comprises, by mass, 20-30 parts of diatom ooze, 17-30 parts of nitrocellulose, 10-15 parts of driers, 3-10 parts of formaldehyde absorbents, 10-16 parts of alkali lignin, 7-9 parts of modified polyester fibers and 50-70 parts of water. The quick-dry diatom ooze paint does not contain cobalt or lead, can be independently used, and has the advantages of being light in paint color, good in quality, resistant to low temperature and high humidity and the like. The surfaces of various buildings can be coated with the paint under the self-drying or low-temperature roasting condition, drying is quick, sagging and foaming are not caused, paint films are flat, physical and chemical properties are excellent, and building materials are well protected and decorated.
Description
Technical field
The present invention relates to a kind of house ornamentation paint field, specifically, the present invention relates to a kind of rapid-curing cutback diatom ooze coating.
Background technology
Just greatly developing from dryness coating both at home and abroad at present, this just needs to use siccative, major part siccative is Naphthenates, oxidation catalysis can be played and promote polymerization, accelerate drying varniss, and in the naphthenate kind developed, cobalt naphthenate is that wherein people study and apply maximum one the most, in the process of Reactive Synthesis cobalt naphthenate, cobalt dichloride is wherein a kind of intermediate reaction material.Cobalt iso-octoate and rose vitriol also can as terebines in addition.As the most ancient a kind of paint additive, although consumption only accounts for one of percentage of coating total amount left and right, it has tremendous influence to the performance of coating and paint film, and therefore it is also most important a kind of paint additive.Along with the raising that people require rapid-curing cutback diatom ooze coating, be badly in need of there is breakthrough in recent years on rapid-curing cutback diatom ooze coating production method is improved.
Summary of the invention
For above shortcomings in prior art, technical problem to be solved by this invention is to provide a kind of effective rapid-curing cutback diatom ooze coating.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of rapid-curing cutback diatom ooze coating, comprise diatom ooze, nitrocellulose, siccative, formaldehyde absorbent, alkali wood xylogen, modified polyester fiber, water, the mass fraction of each component is: diatom ooze 20-30, nitrocellulose 17-30, siccative 10-15, formaldehyde absorbent 3-10, alkali wood xylogen 10-16, modified polyester fiber 7-9, water 50-70.
As preferably, the mass fraction of each component of described rapid-curing cutback diatom ooze coating is: diatom ooze 25, nitrocellulose 22, siccative 12, formaldehyde absorbent 10, alkali wood xylogen 15, modified polyester fiber 8, water 60.
As preferably, described diatom ooze solid content is 42-63wt%.
As preferably, described siccative is light rare earth chloride siccative, and radioactivity is less than 10
-7curie/kilogram.
As preferably, described formaldehyde absorbent is gac.
As preferably, the preparation method of described rapid-curing cutback diatom ooze coating, is characterized in that comprising the steps:
1) diatom ooze is added in a mixing bowl, add nitrocellulose, siccative, formaldehyde absorbent, stir;
2) evenly add alkali wood xylogen to a mixing bowl, high-speed stirring is disperseed;
3) evenly add modified polyester fiber, stir;
4) pour the water of given mass fraction into, heat 20 minutes;
5) filter, filtrate leaves standstill, and can use.
Rapid-curing cutback diatom ooze coating of the present invention, not containing cobalt, lead, is used alone, and has that paint look shallow, quality is good, a feature such as low temperature resistant, anti-high humidity; Under dry or low-temperature bake condition, various building surface can be applied to, drying rapidly, not sagging, non-foaming, paint film is smooth, have excellent physicochemical property, plays good protection, decoration function to building material.
Embodiment
A kind of rapid-curing cutback diatom ooze coating provided by the invention, comprise diatom ooze, nitrocellulose, siccative, formaldehyde absorbent, alkali wood xylogen, modified polyester fiber, water, the mass fraction of each component is: diatom ooze 20-30, nitrocellulose 17-30, siccative 10-15, formaldehyde absorbent 3-10, alkali wood xylogen 10-16, modified polyester fiber 7-9, water 50-70.
As preferably, the mass fraction of each component of described rapid-curing cutback diatom ooze coating is: diatom ooze 27, nitrocellulose 22, siccative 12, formaldehyde absorbent 10, alkali wood xylogen 15, modified polyester fiber 8, water 60.
As preferably, described diatom ooze solid content is 42-63wt%.
As preferably, described siccative is light rare earth chloride siccative, and radioactivity is less than 10
-7curie/kilogram.
As preferably, described formaldehyde absorbent is gac.
As preferably, the preparation method of described rapid-curing cutback diatom ooze coating, is characterized in that comprising the steps:
1) diatom ooze is added in a mixing bowl, add nitrocellulose, siccative, formaldehyde absorbent, stir;
2) evenly add alkali wood xylogen to a mixing bowl, high-speed stirring is disperseed;
3) evenly add modified polyester fiber, stir;
4) pour the water of given mass fraction into, heat 20 minutes;
5) filter, filtrate leaves standstill, and can use.
The above is only to preferred embodiment of the present invention, not does other forms of restriction to the present invention, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the Equivalent embodiments of equal change.Everyly do not depart from the present invention program's content, according to technical spirit of the present invention to any simple modification made for any of the above embodiments, equivalent variations and remodeling, all drop in protection scope of the present invention.
Claims (6)
1. a rapid-curing cutback diatom ooze coating, it is characterized in that: comprise diatom ooze, nitrocellulose, siccative, formaldehyde absorbent, alkali wood xylogen, modified polyester fiber, water, the mass fraction of each component is: diatom ooze 20-30, nitrocellulose 17-30, siccative 10-15, formaldehyde absorbent 3-10, alkali wood xylogen 10-16, modified polyester fiber 7-9, water 50-70.
2. rapid-curing cutback diatom ooze coating according to claim 1, is characterized in that: the mass fraction of each component of described rapid-curing cutback diatom ooze coating is: diatom ooze 25, nitrocellulose 22, siccative 12, formaldehyde absorbent 10, alkali wood xylogen 15, modified polyester fiber 8, water 60.
3. rapid-curing cutback diatom ooze coating according to claim 2, is characterized in that: described diatom ooze solid content is 42-63wt%.
4. rapid-curing cutback diatom ooze coating according to claim 2, is characterized in that: described siccative is light rare earth chloride siccative, and radioactivity is less than 10
-7curie/kilogram.
5. rapid-curing cutback diatom ooze coating according to claim 2, is characterized in that: described formaldehyde absorbent is gac.
6. the preparation method of rapid-curing cutback diatom ooze coating described in claim 1, is characterized in that comprising the steps:
1) diatom ooze is added in a mixing bowl, add nitrocellulose, siccative, formaldehyde absorbent, stir;
2) evenly add alkali wood xylogen to a mixing bowl, high-speed stirring is disperseed;
3) evenly add modified polyester fiber, stir;
4) pour the water of given mass fraction into, heat 20 minutes;
5) filter, filtrate leaves standstill, and can use.