CN105506764A - 一种用于三维打印的浸胶聚碳酸酯丝料及其制备方法 - Google Patents
一种用于三维打印的浸胶聚碳酸酯丝料及其制备方法 Download PDFInfo
- Publication number
- CN105506764A CN105506764A CN201510984993.5A CN201510984993A CN105506764A CN 105506764 A CN105506764 A CN 105506764A CN 201510984993 A CN201510984993 A CN 201510984993A CN 105506764 A CN105506764 A CN 105506764A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- merlon
- melt adhesive
- parts
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
检测项目 | 纯聚碳酸酯 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
熔融流动指数(g/10min) | 12 | 21 | 26 | 22 | 23 |
冲击强度(J/m) | 863 | 898 | 925 | 913 | 917 |
拉伸强度(MPa) | 62 | 67 | 78 | 72 | 75 |
Claims (3)