CN105506447A - Kinking device of baling head - Google Patents

Kinking device of baling head Download PDF

Info

Publication number
CN105506447A
CN105506447A CN201510983475.1A CN201510983475A CN105506447A CN 105506447 A CN105506447 A CN 105506447A CN 201510983475 A CN201510983475 A CN 201510983475A CN 105506447 A CN105506447 A CN 105506447A
Authority
CN
China
Prior art keywords
speed
alloy material
hours
room temperature
min again
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510983475.1A
Other languages
Chinese (zh)
Inventor
单坤林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Original Assignee
CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd filed Critical CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Priority to CN201510983475.1A priority Critical patent/CN105506447A/en
Publication of CN105506447A publication Critical patent/CN105506447A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kinking device of a baling head. The kinking device of the baling head comprises a metal main body made of a heat-treated alloy material; the alloy material comprises the following components: 1-2% of As, 0.5% of B, 0.9% of C, 0.7% of Mg, 0.8% of Au, 0.3% of Po and the balance of Fe and inevitable impurities; heat treatment is performed on the alloy material by the following steps: 1) increasing the temperature to 615 DEG C at a rate of 15 DEG C per minute and preserving heat for 3.5 hours; 2) reducing the temperature to a room temperature at a rate of 25 DEG C pre minute; 3) increasing the temperature to 715 DEG C at a rate of 20 DEG C per minute again and preserving heat for 3 hours; and 4) cooling the temperature to the room temperature at a rate of 25 DEG C per minute again. The metal main body of the kinking device of the baling head of the present invention is good in properties and long in service life.

Description

Packing head winding device
Technical field
The present invention relates to packing head winding device.
Background technology
The work under bad environment of packing head winding device, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of packing head winding device, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of packing of design head winding device, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, packing head winding device, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, packing head winding device, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of packing head winding device, its metal master is made by through heat treated alloy material, metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of packing head winding device, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 2
Packing head winding device, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 3
Packing head winding device, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (3)

1. packing head winding device, it is characterized in that, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
2. packing head winding device according to claim 1, it is characterized in that, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
3. packing head winding device according to claim 1, it is characterized in that, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
B:0.5%,
C:0.9%,
Mg:0.7%,
Au:0.8%,
Po:0.3%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
CN201510983475.1A 2015-12-24 2015-12-24 Kinking device of baling head Pending CN105506447A (en)