CN105420537A - Mine spray lance - Google Patents
Mine spray lance Download PDFInfo
- Publication number
- CN105420537A CN105420537A CN201510982334.8A CN201510982334A CN105420537A CN 105420537 A CN105420537 A CN 105420537A CN 201510982334 A CN201510982334 A CN 201510982334A CN 105420537 A CN105420537 A CN 105420537A
- Authority
- CN
- China
- Prior art keywords
- speed
- alloy material
- room temperature
- min again
- warming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mine spray lance which comprises a metal body made from a thermally treated alloy material, wherein the alloy material comprises the following components: 1-2% of Si, 0.5% of N, 0.9% of B, 1.1% of Mg, 0.7% of Au, 0.6% of Tc and Cu and inevitable impurities in balancing amount. The alloy material is thermally treated through the following steps: 1) heating to 615 DEG C at the speed of 10 DEG C/min, and performing heat preservation for 3 h; 2) cooling to room temperature at the speed of 10 DEG C/min; 3) heating to 715 DEG C at the speed of 20 DEG C/min, and performing heating preservation for 2 h; and 4) cooling to room temperature at the speed of 20 DEG C/min. the metal body of the mine spray lance has good properties and a long service life.
Description
Technical field
The present invention relates to mine spray bar.
Background technology
The work under bad environment of mine spray bar, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of mine spray bar, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of mine spray bar of design, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1~2%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
Preferably, mine spray bar, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
Preferably, mine spray bar, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:2%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of mine spray bar, its metal master is made by through heat treated alloy material, metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of mine spray bar, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1~2%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
Embodiment 2
Mine spray bar, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
Embodiment 3
Mine spray bar, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:2%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. mine spray bar, is characterized in that, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1~2%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
2. mine spray bar according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:1%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.
3. mine spray bar according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
Si:2%,
N:0.5%,
B:0.9%,
Mg:1.1%,
Au:0.7%,
Tc:0.6%,
Surplus is Cu and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 615 DEG C with the speed of 10 DEG C/min, be incubated 3 hours;
2) room temperature is cooled to the speed of 10 DEG C/min again;
3) be warming up to 715 DEG C with the speed of 20 DEG C/min again, be incubated 2 hours;
4) room temperature is cooled to the speed of 20 DEG C/min again.