CN105543723A - Wire way device - Google Patents

Wire way device Download PDF

Info

Publication number
CN105543723A
CN105543723A CN201510983450.1A CN201510983450A CN105543723A CN 105543723 A CN105543723 A CN 105543723A CN 201510983450 A CN201510983450 A CN 201510983450A CN 105543723 A CN105543723 A CN 105543723A
Authority
CN
China
Prior art keywords
speed
alloy material
hours
room temperature
min again
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510983450.1A
Other languages
Chinese (zh)
Inventor
单坤林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Original Assignee
CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd filed Critical CHANGSHU XINYE MACHINERY MANUFACTURING Co Ltd
Priority to CN201510983450.1A priority Critical patent/CN105543723A/en
Publication of CN105543723A publication Critical patent/CN105543723A/en
Pending legal-status Critical Current

Abstract

The invention discloses a wire way device. The wire way device comprises a metal body produced by a thermally treated alloy material; the alloy material comprises the following components: 1-2% of As, 0.5% of Se, 0.7% of N, 0.9% of K, 0.8% of Ga, 0.9% of La, and the balance of Fe and inevitable impurities; and the alloy material is thermally treated through the following steps: 1) a temperature of 625 DEG C is raised at a speed of 15 DEG C/min, and is kept by 3.5 hours; 2) the room temperature is reduced to at a speed of 25 DEG C/min; 3) a temperature of 725 DEG C is raised at a speed of 20 DEG C/min, and is kept by 3 hours; and 4) the room temperature is reduced to at a speed of 25 DEG C/min. The wire way device is excellent in performance of the metal body and long in service life.

Description

Drawing lines device
Technical field
The present invention relates to drawing lines device.
Background technology
The work under bad environment of drawing lines device, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of drawing lines device, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of drawing lines device of design, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1～2%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, drawing lines device, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, drawing lines device, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of drawing lines device, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of drawing lines device, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1～2%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 2
Drawing lines device, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 3
Drawing lines device, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (3)

1. drawing lines device, is characterized in that, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1～2%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
2. drawing lines device according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
3. drawing lines device according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%，
Se:0.5%，
N:0.7%，
K:0.9%，
Ga:0.8%，
La:0.9%，
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 625 DEG C with the speed of 15 DEG C/min, be incubated 3.5 hours;
2) room temperature is cooled to the speed of 25 DEG C/min again;
3) be warming up to 725 DEG C with the speed of 20 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
CN201510983450.1A 2015-12-24 2015-12-24 Wire way device Pending CN105543723A (en)